CN109266163A - A kind of ceramic coating with preferable wearability - Google Patents
A kind of ceramic coating with preferable wearability Download PDFInfo
- Publication number
- CN109266163A CN109266163A CN201810842275.8A CN201810842275A CN109266163A CN 109266163 A CN109266163 A CN 109266163A CN 201810842275 A CN201810842275 A CN 201810842275A CN 109266163 A CN109266163 A CN 109266163A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- ceramic coating
- sandstone
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of ceramic coating with preferable wearability, it is related to ceramic coating technical field, composition material includes: 13-28 parts of pure acrylate elastic emulsion by weight, 20-28 parts of epoxy resin, 15-27 parts of polyethylene micropowder wax, 9-12 parts of high-carbon black pigment, 17-23 parts of sodium metasilicate, 2-8 parts of anti-aging agent, 5-12 parts of succinic anhydride, 14-23 parts of polyacrylic acid, 2-6 parts of phenolic resin, 18-26 parts of polytrifluorochloroethylene, 14-25 parts of powder ethylene propylene diene rubber, 18-25 parts of polyphenylene sulfide, 2-5 parts of river sand, 4-8 parts of sandstone, 2-5 parts of graphite powder, 1-3 parts of silver powder, 3-8 parts of delustering agent.Usefulness of the present invention is to reinforce the antiwear characteristic of ceramic coating, and it is good to be allowed to performance.
Description
Technical field
The present invention relates to ceramic coating technical field, especially a kind of ceramic coating with preferable wearability.
Background technique
Coating Industry in Our Country is with a long history, and output and consumption figure are in rank first, and development prospect is wide, just
It is being increasingly becoming national economy new growth point.The early detection U.S., Japan, South Korea have some ceramic coatings in terms of research,
Report, but Related product is had not seen in its domestic market；With the development of society, ceramic coating occupy in many fields it is important
Status, and the approval by many consumers, ceramic use environment is sufficiently complex, this is greatly reduced using ceramics
Service life increases cost, so traditional ceramic material can no longer meet increasingly harsh job requirement and therefore develop one
The novel ceramic protective material of kind.
Summary of the invention
The present invention overcomes the disadvantages of the prior art, provides a kind of ceramic coating with preferable wearability, can reinforce
It is good to be allowed to performance for the antiwear characteristic of ceramic coating.
In order to solve the above-mentioned technical problem, the present invention is achieved by the following technical solutions:
A kind of ceramic coating with preferable wearability, composition material include: pure acrylate elastic emulsion 13-28 by weight
Part, 20-28 parts of epoxy resin, 15-27 parts of polyethylene micropowder wax, 9-12 parts of high-carbon black pigment, 17-23 parts of sodium metasilicate, anti-aging agent
2-8 parts, 5-12 parts of succinic anhydride, 14-23 parts of polyacrylic acid, 2-6 parts of phenolic resin, 18-26 parts of polytrifluorochloroethylene, powder three
First EP rubbers 14-25 parts, 18-25 parts of polyphenylene sulfide, 2-5 parts of river sand, 4-8 parts of sandstone, 2-5 parts of graphite powder, 1-3 parts of silver powder,
3-8 parts of delustering agent.
Preferably, a kind of ceramic coating with preferable wearability, composition material include: that group is become a useful person by weight
Material include: by weight 15 parts of pure acrylate elastic emulsion, 24 parts of epoxy resin, 18 parts of polyethylene micropowder wax, 10 parts of high-carbon black pigment,
19 parts of sodium metasilicate, 4 parts of anti-aging agent, 8 parts of succinic anhydride, 17 parts of polyacrylic acid, 4 parts of phenolic resin, 22 parts of polytrifluorochloroethylene, powder
18 parts of last ethylene propylene diene rubber, 22 parts of polyphenylene sulfide, 4 parts of river sand, 6 parts of sandstone, 4 parts of graphite powder, 2 parts of silver powder, 5 parts of delustering agent.
Preferably, the delustering agent is fumed silica matting agent.
Preferably, a kind of ceramic coating with preferable wearability, making step are as follows: each constituent is pressed
Recipe ratio weighs, spare；River sand, sandstone are pulverized into powder, it is spare；By pure acrylate elastic emulsion, high-carbon black pigment, river sand,
Sandstone, anti-aging agent, phenolic resin, polytrifluorochloroethylene, powder ethylene propylene diene rubber, polyphenylene sulfide, delustering agent are put into container,
Disperse 10-15min under conditions of revolving speed 500-560rpm/min with dispersion machine, until be uniformly mixed, then by epoxy resin, poly-
Ethylene micro mist wax, succinic anhydride, polyacrylic acid, graphite powder, silver powder, sodium metasilicate pour into, and continue with dispersion machine in revolving speed 400-
Disperse 20-25min under conditions of 450rpm/min.
Compared with prior art, the beneficial effects of the present invention are:
By the way that this variety of material with higher abrasion resistance of such as river sand, sandstone, graphite powder, silver powder are added in recipe ingredient
Material, so that coating be enabled also to have higher wear-resisting property, it is not easy to wear.
Specific embodiment
It is that preferred embodiment of the present invention will be described below, it should be understood that preferred embodiment described herein is only
For instruction and explanation of the present invention, it is not intended to limit the present invention.
A kind of ceramic coating with preferable wearability, making step are as follows: each constituent weighed by recipe ratio, it is standby
With；River sand, sandstone are pulverized into powder, it is spare；By pure acrylate elastic emulsion, high-carbon black pigment, river sand, sandstone, anti-aging agent, phenol
Urea formaldehyde, polytrifluorochloroethylene, powder ethylene propylene diene rubber, polyphenylene sulfide, delustering agent are put into container, with dispersion machine in revolving speed
Disperse 12min under conditions of 530rpm/min, until be uniformly mixed, then by epoxy resin, polyethylene micropowder wax, succinic anhydride,
Polyacrylic acid, graphite powder, silver powder, sodium metasilicate pour into, and continue to be dispersed under conditions of revolving speed 430rpm/min with dispersion machine
23min.
Embodiment 1
A kind of ceramic coating with preferable wearability, composition material include: that composition material wraps by weight by weight
Include: 15 parts of pure acrylate elastic emulsion, 24 parts of epoxy resin, 18 parts of polyethylene micropowder wax, 10 parts of high-carbon black pigment, 19 parts of sodium metasilicate,
4 parts of anti-aging agent, 8 parts of succinic anhydride, 17 parts of polyacrylic acid, 4 parts of phenolic resin, 22 parts of polytrifluorochloroethylene, powder EPDM
18 parts of rubber, 22 parts of polyphenylene sulfide, 4 parts of river sand, 6 parts of sandstone, 4 parts of graphite powder, 2 parts of silver powder, 5 parts of delustering agent.
Preferably, delustering agent is fumed silica matting agent.
Embodiment 2
A kind of ceramic coating with preferable wearability, composition material include: 13 parts of pure acrylate elastic emulsion, ring by weight
20 parts of oxygen resin, 9 parts of high-carbon black pigment, 17 parts of sodium metasilicate, 2 parts of anti-aging agent, 5 parts of succinic anhydride, gathers 15 parts of polyethylene micropowder wax
14 parts of acrylic acid, 2 parts of phenolic resin, 18 parts of polytrifluorochloroethylene, 14 parts of powder ethylene propylene diene rubber, 18 parts of polyphenylene sulfide, river
Husky 2 parts, 4 parts of sandstone, 2 parts of graphite powder, 1 part of silver powder, 3 parts of delustering agent.
Embodiment 3
A kind of ceramic coating with preferable wearability, composition material include: 28 parts of pure acrylate elastic emulsion, ring by weight
28 parts of oxygen resin, 27 parts of polyethylene micropowder wax, 12 parts of high-carbon black pigment, 23 parts of sodium metasilicate, 8 parts of anti-aging agent, 12 parts of succinic anhydride,
23 parts of polyacrylic acid, 6 parts of phenolic resin, 26 parts of polytrifluorochloroethylene, 25 parts of powder ethylene propylene diene rubber, 25 parts of polyphenylene sulfide,
5 parts of river sand, 8 parts of sandstone, 5 parts of graphite powder, 3 parts of silver powder, 8 parts of delustering agent.
Finally, it should be noted that these are only the preferred embodiment of the present invention, it is not intended to restrict the invention, although
Referring to embodiment, invention is explained in detail, for those skilled in the art, still can be to aforementioned
Technical solution documented by each embodiment is modified or equivalent replacement of some of the technical features, but it is all
Within the spirit and principles in the present invention, any modification, equivalent replacement, improvement and so on should be included in protection of the invention
Within the scope of.
Claims (4)
1. a kind of ceramic coating with preferable wearability, which is characterized in that composition material includes: pure acrylate elastic cream by weight
13-28 parts of liquid, 20-28 parts of epoxy resin, 15-27 parts of polyethylene micropowder wax, 9-12 parts of high-carbon black pigment, 17-23 parts of sodium metasilicate,
2-8 parts of anti-aging agent, 5-12 parts of succinic anhydride, 14-23 parts of polyacrylic acid, 2-6 parts of phenolic resin, 18-26 parts of polytrifluorochloroethylene,
14-25 parts of powder ethylene propylene diene rubber, 18-25 parts of polyphenylene sulfide, 2-5 parts of river sand, 4-8 parts of sandstone, 2-5 parts of graphite powder, silver powder
1-3 parts, 3-8 parts of delustering agent.
2. a kind of ceramic coating with preferable wearability according to claim 1, which is characterized in that composition material is by weight
Measuring part includes: 15 parts of pure acrylate elastic emulsion, 24 parts of epoxy resin, 18 parts of polyethylene micropowder wax, 10 parts of high-carbon black pigment, sodium metasilicate
19 parts, 4 parts of anti-aging agent, 8 parts of succinic anhydride, 17 parts of polyacrylic acid, 4 parts of phenolic resin, 22 parts of polytrifluorochloroethylene, powder ternary
18 parts of EP rubbers, 22 parts of polyphenylene sulfide, 4 parts of river sand, 6 parts of sandstone, 4 parts of graphite powder, 2 parts of silver powder, 5 parts of delustering agent.
3. a kind of ceramic coating with preferable wearability according to claim 1 or 2, which is characterized in that the delustring
Agent is fumed silica matting agent.
4. a kind of ceramic coating with preferable wearability according to claim 1 or 2, which is characterized in that making step
It is as follows: each constituent is weighed by recipe ratio, it is spare；River sand, sandstone are pulverized into powder, it is spare；By pure acrylate elastic cream
Liquid, high-carbon black pigment, river sand, sandstone, anti-aging agent, phenolic resin, polytrifluorochloroethylene, powder ethylene propylene diene rubber, polyphenylene sulfide
In ether, delustering agent investment container, disperse 10-15min under conditions of revolving speed 500-560rpm/min with dispersion machine, until mixing is equal
It is even, then epoxy resin, polyethylene micropowder wax, succinic anhydride, polyacrylic acid, graphite powder, silver powder, sodium metasilicate are poured into, continued
Disperse 20-25min under conditions of revolving speed 400-450rpm/min with dispersion machine.