CN103938131B - 一种非晶合金组合物及制备方法 - Google Patents

一种非晶合金组合物及制备方法 Download PDF

Info

Publication number
CN103938131B
CN103938131B CN201410120104.6A CN201410120104A CN103938131B CN 103938131 B CN103938131 B CN 103938131B CN 201410120104 A CN201410120104 A CN 201410120104A CN 103938131 B CN103938131 B CN 103938131B
Authority
CN
China
Prior art keywords
cooled
metal composition
amorphous metal
crystaline amorphous
incubated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410120104.6A
Other languages
English (en)
Other versions
CN103938131A (zh
Inventor
王雪莹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HUAXING METAL CO., LTD.
Original Assignee
ANHUI HUAXING METAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HUAXING METAL Co Ltd filed Critical ANHUI HUAXING METAL Co Ltd
Priority to CN201410120104.6A priority Critical patent/CN103938131B/zh
Publication of CN103938131A publication Critical patent/CN103938131A/zh
Application granted granted Critical
Publication of CN103938131B publication Critical patent/CN103938131B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种非晶合金组合物，涉及非晶材料制备技术领域，由以下质量百分比的组分组成：氧化钕3-8%，氧化铁8-15%，氧化钴5-9%，石墨烯2-8%，氧化硼1-4%，碳化硅1-8%，余量为铝及不可避免的杂质。本发明成分简单，价格低，非晶形成能力强，成品质量高，用途广泛。

Description

一种非晶合金组合物及制备方法
技术领域
本发明涉及非晶材料制备技术领域，具体涉及一种非晶合金组合物及制备方法。
背景技术
近20多年来，Nd-Fe-Al系和Nd-Fe-Co-Al系大块金属玻璃的发现引起人们的广泛关注，因为这些大块金属玻璃体系具有不同于其它大块金属玻璃体系的特征。一是在热分析曲线上观测不到玻璃化转变引起的吸热反应，即不能明确确定其玻璃化转变温度；另一个特点是这种材料在室温时呈现明显的硬磁性特征，矫顽力约为300KAm-1。研究发现该材料的磁性与其成分和冷却速率密切相关，当它为非晶带材时，不显示硬磁性；如果采用铜模吸铸法时，获取的大块非晶则有较强的硬磁性，尺寸越大，硬磁性越强。
目前，针对大块非晶金属玻璃制备的主要方法为铜模负压铸造法，该方法虽然可以达到很高的冷却速率，有利于更大尺寸非晶块体的形成，但操作不便，不能加入合金净化剂，且设备比较复杂和昂贵。
发明内容
本发明所要解决的技术问题在于提供一种纯度高，成本低的非晶合金组合物及制备方法。
本发明所要解决的技术问题采用以下技术方案来实现：
一种非晶合金组合物，由以下质量百分比的组分组成：
余量为铝及不可避免的杂质。
各组分的较佳质量份数为：
余量为铝及不可避免的杂质。
一种非晶合金组合物的制备方法，包括如下工艺步骤，
1）按照组分配比称取各原料待用；
2）将氧化钕、氧化铁、氧化钴放入石英坩埚内，抽真空密封，加热至700-1200℃，(石英坩埚底部的参考温度)，保温5-15分钟后冷却至室温；
3）将冷却后的混合物加入石墨烯和碳化硅，并再次加温至700-1200℃，保温10分钟后，水冷至室温；
4）将氧化硼加入水冷后的混合物中，抽真空后开始升温，在升温过程中持续抽真空，加热到温度为800-1000℃时保温5-15分钟；
5）往石英坩埚内的混合溶液快速放入冰水混合物或其它冷却物质，迅速冷却，制得合金。
本发明的有益效果是：本发明成分简单，价格低，非晶形成能力强，成品质量高，用途广泛。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
一种非晶合金组合物，由以下质量百分比的组分组成：
余量为铝及不可避免的杂质。
一种非晶合金组合物的制备方法，包括如下工艺步骤，
1）按照组分配比称取各原料待用；
2）将氧化钕、氧化铁、氧化钴放入石英坩埚内，抽真空密封，加热至700-1200℃，(石英坩埚底部的参考温度)，保温5-15分钟后冷却至室温；
3）将冷却后的混合物加入石墨烯和碳化硅，并再次加温至700-1200℃，保温10分钟后，水冷至室温；
4）将氧化硼加入水冷后的混合物中，抽真空后开始升温，在升温过程中持续抽真空，加热到温度为800-1000℃时保温5-15分钟；
5）往石英坩埚内的混合溶液快速放入冰水混合物或其它冷却物质，迅速冷却，制得合金。
实施例2
一种非晶合金组合物，由以下质量百分比的组分组成：
余量为铝及不可避免的杂质。
一种非晶合金组合物的制备方法，包括如下工艺步骤，
1）按照组分配比称取各原料待用；
2）将氧化钕、氧化铁、氧化钴放入石英坩埚内，抽真空密封，加热至700-1200℃，(石英坩埚底部的参考温度)，保温5-15分钟后冷却至室温；
3）将冷却后的混合物加入石墨烯和碳化硅，并再次加温至700-1200℃，保温10分钟后，水冷至室温；
4）将氧化硼加入水冷后的混合物中，抽真空后开始升温，在升温过程中持续抽真空，加热到温度为800-1000℃时保温5-15分钟；
5）往石英坩埚内的混合溶液快速放入冰水混合物或其它冷却物质，迅速冷却，制得合金。
实施例3
一种非晶合金组合物，由以下质量百分比的组分组成：
余量为铝及不可避免的杂质。
一种非晶合金组合物的制备方法，包括如下工艺步骤，
1）按照组分配比称取各原料待用；
2）将氧化钕、氧化铁、氧化钴放入石英坩埚内，抽真空密封，加热至700-1200℃，(石英坩埚底部的参考温度)，保温5-15分钟后冷却至室温；
3）将冷却后的混合物加入石墨烯和碳化硅，并再次加温至700-1200℃，保温10分钟后，水冷至室温；
4）将氧化硼加入水冷后的混合物中，抽真空后开始升温，在升温过程中持续抽真空，加热到温度为800-1000℃时保温5-15分钟；
5）往石英坩埚内的混合溶液快速放入冰水混合物或其它冷却物质，迅速冷却，制得合金。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (3)

1.一种非晶合金组合物，其特征在于，由以下质量百分比的组分制成：
余量为铝及不可避免的杂质。
2.根据权利要求1所述的一种非晶合金组合物，其特征在于，由以下质量百分比的组分制成：
余量为铝及不可避免的杂质。
3.一种制备权利要求1或2所述非晶合金组合物的方法，其特征在于：包括如下工艺步骤，
1)按照组分配比称取各原料待用；
2)将氧化钕、氧化铁、氧化钴放入石英坩埚内，抽真空密封，加热至700-1200℃，保温5-15分钟后冷却至室温；
3)将冷却后的混合物加入石墨烯和碳化硅，并再次加温至700-1200℃，保温10分钟后，水冷至室温；
4)将氧化硼加入水冷后的混合物中，抽真空后开始升温，在升温过程中持续抽真空，加热到温度为800-1000℃时保温5-15分钟；
5)将石英坩埚内的混合溶液快速放入冰水混合物，迅速冷却，制得合金。
CN201410120104.6A 2014-03-27 2014-03-27 一种非晶合金组合物及制备方法 Active CN103938131B (zh)