CN103936338B - 整体无缝柔性树脂防腐地坪 - Google Patents

整体无缝柔性树脂防腐地坪 Download PDF

Info

Publication number
CN103936338B
CN103936338B CN201410135293.4A CN201410135293A CN103936338B CN 103936338 B CN103936338 B CN 103936338B CN 201410135293 A CN201410135293 A CN 201410135293A CN 103936338 B CN103936338 B CN 103936338B
Authority
CN
China
Prior art keywords
terrace
resin
weight ratio
anticorrosion
flexible resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410135293.4A
Other languages
English (en)
Other versions
CN103936338A (zh
Inventor
杨光品
赵国清
杨勇昆
田儒友
郎文杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YUNNAN HECHENG ANTI-CORROSION EQUIPMENT Co Ltd
Original Assignee
YUNNAN HECHENG ANTI-CORROSION EQUIPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YUNNAN HECHENG ANTI-CORROSION EQUIPMENT Co Ltd filed Critical YUNNAN HECHENG ANTI-CORROSION EQUIPMENT Co Ltd
Priority to CN201410135293.4A priority Critical patent/CN103936338B/zh
Publication of CN103936338A publication Critical patent/CN103936338A/zh
Application granted granted Critical
Publication of CN103936338B publication Critical patent/CN103936338B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种整体无缝柔性树脂防腐地坪，其特征在于，由A、B、C三组分制成，所述的A组分为有机液体组，是由砂浆用不饱和聚酯树脂、过氧化甲乙酮和环烷酸钴苯乙烯按照1:0.2:0.02重量比配制而成，所述B组分为无机固体组，是由石英砂、石英粉按照4:1的重量比配制而成，所述C组分为聚氯乙烯粉；使用时A、B、C三组分以1:5:0.3的重量比搅拌混合均匀得到树脂砂浆，然后摊平固化定型。采用本发明方法施工的整体无缝柔性树脂防腐地坪，一次性最大施工面积达到了1000㎡，该地坪无开裂和脱落，耐强酸强碱腐蚀，使用寿命在15年以上，正常使用下，基本不用进行维修，维修成本趋于零，保证了防腐地坪的防腐性能。

Description

整体无缝柔性树脂防腐地坪
技术领域
本发明涉及工业防腐领域，具体来说是一种整体无缝柔性树脂防腐地坪。
背景技术
现有的整体树脂防腐地坪主要有环氧树脂防腐地坪和聚酯树脂防腐地坪两种。该两种树脂地坪都是在树脂中搀和耐酸砂和砂粉，将砂粉和树脂拌合均匀，树脂固化后，形成整体的防腐面层。该两种树脂防腐地坪都有优良的耐腐蚀，能耐硫酸、盐酸和硝酸。但是由于树脂固化过程中收缩较大，产生脆性，在大面积施工时容易造成防腐地坪的开裂，还存在强度低，寿命短，维修费用高等问题。因此传统整体无缝树脂防腐地坪仅能用于小面积防腐地坪的施工。
发明内容
本发明目的是针对现有技术中的缺陷，提供一种整体无缝柔性树脂防腐地坪，降低树脂砂浆固化过程中的收缩率，在大面积施工时不产生开裂。依据本发明制成的产品达到了预期的标准，用户给予了一致好评，现已经取得了良好的经济效益。
本发明所采用的技术方案是:一种整体无缝柔性树脂防腐地坪，由A、B、C三组分制成，所述A组分为有机液体组，是由砂浆用不饱和聚酯树脂、过氧化甲乙酮和环烷酸钴苯乙烯按照1:0.2:0.02的重量比配制而成，所述B组分为无机固体组，是由石英砂、石英粉按照4:1的重量比配制而成，所述C组分为聚氯乙烯粉；使用时A、B、C三组分以1:5:0.3的重量比搅拌混合均匀得到树脂砂浆，然后摊平固化定型。
所得整体无缝柔性树脂防腐地坪收缩率为0.1%~0.5%。
采用本发明方法的整体无缝柔性树脂防腐地坪，一次性最大施工面积达到了1000㎡。该地坪无开裂和脱落，耐强酸强碱腐蚀，使用寿命在15年以上，正常使用下，基本不用进行维修，维修成本趋于零，保证了防腐地坪的防腐性能。
具体实施方式
本发明提出的这种整体无缝柔性树脂防腐地坪，由A、B、C三组分组成，所述A组分为有机液体组，是由砂浆用不饱和聚酯树脂、固化剂过氧化甲乙酮和促进剂环烷酸钴苯乙烯按照1:0.2:0.02重量比配制而成，所述B组分为无机固体组，是由石英砂、石英粉按照4:1的重量比配制而成，所述C组分为有机固体组，由聚氯乙烯粉配制而成；使用时A、B、C三组分以1:5:0.3的重量比搅拌混合均匀得到树脂砂浆，然后摊平固化定型。该整体无缝柔性树脂防腐地坪，一次性最大施工面积达到了1000㎡以上，该面积下的地坪无开裂和脱落；耐强酸强碱腐蚀，使用寿命在15年以上，正常使用下，基本不用进行维修，维修成本趋于零。
该树脂防腐地坪加入了聚氯乙烯粉料，当树脂砂浆固化时会释放热量，使该砂浆内部温度迅速上升至80℃左右，此时所加的聚氯乙烯粉料在此温度下融化成流体状，从而流入到所有砂浆缝隙中，当温度恢复到室温后流体聚氯乙烯随之固化，在砂浆内部形成一个有机的网络，填补了传统地坪砂浆之间的缝隙，弥补了传统砂浆地坪收缩率大的弊端，该聚氯乙烯粉料在聚酯树脂固化过程中，利用固化产生的温度，自己形成整体网状固体状态，从而降低了树脂砂浆的收缩率，整体无缝柔性树脂防腐地坪收缩率在0.5%，传统的树脂砂浆地坪收缩率在5%左右，解决了大面积施工时树脂砂浆的开裂问题。由于固化后的整体无缝柔性树脂防腐地内部的聚氯乙烯已形成一个有机网络，从而使得地坪的强度达到增加，不易脱落，维修成不大大降低。
在云南罗平锌电股份有限公司锌电解车间和云南锡业股份有限公司镍电解车间采用本发明方法施工的聚酯树脂砂浆整体地坪，通过实际生产应用，该聚酯树脂整体防腐地坪无开裂、脱落现象产生。使用厂家的维修成本为零。

Claims (2)

1.一种整体无缝柔性树脂防腐地坪，其特征在于，由A、B、C三组分制成，所述的A组分为有机液体组，是由砂浆用不饱和聚酯树脂、过氧化甲乙酮和环烷酸钴苯乙烯按照1:0.2:0.02重量比配制而成，所述B组分为无机固体组，是由石英砂、石英粉按照4:1的重量比配制而成，所述C组分为聚氯乙烯粉；使用时A、B、C三组分以1:5:0.3的重量比搅拌混合均匀得到树脂砂浆，然后摊平固化定型。
2.根据权利要求1所述的整体无缝柔性树脂防腐地坪，其特征在于，该整体无缝柔性树脂防腐地坪收缩率在0.1-0.5%。
CN201410135293.4A 2014-04-04 2014-04-04 整体无缝柔性树脂防腐地坪 Active CN103936338B (zh)