CN113738060A - 一种高强无缝地坪 - Google Patents
一种高强无缝地坪 Download PDFInfo
- Publication number
- CN113738060A CN113738060A CN202110967777.5A CN202110967777A CN113738060A CN 113738060 A CN113738060 A CN 113738060A CN 202110967777 A CN202110967777 A CN 202110967777A CN 113738060 A CN113738060 A CN 113738060A
- Authority
- CN
- China
- Prior art keywords
- layer
- composite
- terrace
- strength seamless
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高强无缝地坪，其结构包括基层，基层表面右下至上依次铺设隔离层、泥浆层、复合加固层、表面层；所述复合加固层由以下质量百分比的原料组分构成：脲醛树脂30～35％、聚氯乙烯4～6％、复合粉体10～15％、功能混合料20～25％、癸二酸二甲酯15～20％、丁酸芐脂5～8％、邻苯二甲酸和碳酸氢镁混合物4～6％。所述泥浆层为C10混凝土，且泥浆层的内部掺有金刚砂骨料。本发明中通过在表面层以及复合加固层中添加金刚砂骨料、磨砂球以及石英粉等原料进行混合制备特殊原料，能够大大增强地坪固化成型后的整体强度，并能够提升表面强度、韧性和耐磨性。
Description
技术领域
本发明涉及地坪技术领域，尤其是一种高强无缝地坪。
背景技术
地坪是指使用特定材料和工艺对原有地面进行施工处理并呈现出一定装饰性和功能性的地面。一些高端商业项目、精密加工企业的厂房、高要求的实验室等场所需要地坪整体无缝。根据中国专利文献CN103590578A所提供的一种耐拉升防滑的复合地坪材料，具有良好的耐拉伸和防滑的性能，但是依然需要考虑到地坪的强度、施工工艺的调整以及材料的配合性。中国专利CN103450417B公开的一种高硬度耐压的地坪材料，通过材料配比制备得到的地坪材料具有高硬度和耐压的特点。
但是因为无缝地坪需要达到近乎密封的效果，在施工到成型的整个过程中，地坪材料的硬度以及材料相互的搭配很关键。并且地坪的每层分布和两层之间的施工处理也会影响到最终成品。如果材料硬度较低，地坪材料的稳定性会较差，会容易产生形变等问题，想要解决目前常规的地坪的强度问题，需要进一步的对材料组成、材料制备以及材料配比进行开发，来提升地坪的强度以及达到更好的无缝效果。
发明内容
本发明的目的是提供一种高强的无缝地坪。
本发明提供的高强无缝地坪，其结构包括基层，基层表面由下至上依次铺设隔离层、泥浆层、复合加固层、表面层。
所述隔离层由防水底漆、聚酯丙烯酸酯以及固化剂制作而成，且防水底漆、聚酯丙烯酸酯以及固化剂的质量比为6：3：0.7。将防水底漆、聚酯丙烯酸酯以及固化剂置于45-60摄氏度的条件下进行混合搅拌均匀后，利用喷涂设备将上述所得到的混合料均匀的喷涂在基层表面，需保证喷涂厚度为0.8mm，待其干燥后，即形成隔离层。
所述泥浆层为C10混凝土，且泥浆层的内部掺有金刚砂骨料。
所述复合加固层由以下质量百分比的原料组分构成：
脲醛树脂30～35％、聚氯乙烯4～6％、复合粉体10～15％、功能混合料20～25％、癸二酸二甲酯15～20％、丁酸芐脂5～8％、邻苯二甲酸和碳酸氢镁混合物4～6％。
其中，所述功能混合料是由不饱和聚酯树脂、过氧化甲乙酮和环烷酸钴苯乙烯按照1：0.3：0.1的重量比配制而成。不饱和聚酯树脂优选为双酚A型不饱聚酯树脂或聚酯环氧丙烯酸树脂。
所述复合粉体是由金刚砂骨料和石英粉按照5：1的重量比配制而成。
优选的是，所述复合加固层中，功能混合料和复合粉体的用量重量比为1：2。
所述复合加固层的施工方法：将复合加固层的原料组分混合搅拌均匀，然后加入少量的水，搅拌混均，加水量的控制，以得到膏状混合料为准。将得到的混合料立即涂覆在泥浆层表面，抹平，复合加固层厚度控制在0.4-0.5cm。脲醛树脂与水混合之后形成的溶液具备粘合性，可以使复合加固层紧密粘接在泥浆层表面。
所述表面层由以下质量百分比的原料组成：
多元醇30～35％、十二烷基硫酸钠15～20％、丙酮6～10％、硅酸镁15～20％、硅酸三钙10～15％、聚乙烯腊5～10％、磨砂球10～15％、二羟基丁烷5～10％。所述多元醇优选二丙二醇或新戊二醇。
复合加固层施工完成后，放置至少48小时，自然干燥，使其中的水分蒸发完全除去。然后在复合加固层表面涂覆表面层。
表面层施工方法是：将各原料投入混合容器中，在90℃环境下搅拌均匀，搅拌时间至少2分钟，静置1分钟后，继续搅拌反复进行，直至产生细柔无结块浆状流体，并保温30-60min，静置冷却成粉状物；将粉状物中加清水，粉状物与水的配比为5kg：3L，搅拌形成粘稠液；将粘稠液均匀喷涂在复合加固层表面，待粘稠液在复合加固层表面自然干燥后，再次喷涂；每次喷涂时都需要现场配制新的粘稠液，即取粉状物与水混合搅拌，制成粘稠液；然后自然干燥，喷涂的次数至少两次，最终得到0.2-0.3cm后的表面层。
优选的是，铺设隔离层之前，所述基层需要进行表面处理。表面处理步骤为依次进行打磨、抛光和清理，其中，打磨选用研磨机依次以60、100、120、150目的砂纸打磨表面，使用抛光机抛光后，将表面细粉尘清除。
施工复合加固层之前，也需要对泥浆层进行表面处理。表面处理步骤为依次进行打磨、抛光和清理，其中，打磨选用研磨机依次以60、100、120、150目的砂纸打磨表面，使用抛光机抛光后，将表面细粉尘清除。
优选的是，所述基层、隔离层、复合加固层、表面层的厚度依次为0.3-0.4cm、0.2-0.3cm、0.4-0.5cm和0.2-0.3cm。
与现有技术相比，本发明的有益之处在于：
本发明的无缝地坪中，通过在表面层以及复合加固层中添加金刚砂骨料、磨砂球以及石英粉等原料进行混合制备特殊原料，能够大大增强地坪固化成型后的整体强度，并能够提升表面强度、韧性和耐磨性，复合加固层可以在加固保证强度的同时，达到与找平层同样的作用。在施工之后，因为表面层原料的制备特性使地坪整体具有更好的耐水性，提高使用强度，并且地坪的每层厚度以及铺设连接面通过合理的控制可以增加地坪整体的连接密封性，可以更好的提高强度和地坪的无缝效果。
本发明的其它优点、目标和特征将部分通过下面的说明体现，部分还将通过对本发明的研究和实践而为本领域的技术人员所理解。
附图说明
图1为本发明的高强无缝地坪的结构示意图。
图中标号：1-基层，2-隔离层，3-泥浆层，4-复合加固层，5-表面层。
具体实施方式
以下结合附图对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
如图1所示，本发明提供的高强无缝地坪，其结构包括基层1，所述基层1的表面由下至上依次铺设隔离层2，泥浆层3、复合加固层4、表面层5。所述泥浆层3为C10混凝土，泥浆层的内部掺有金刚砂骨料。
实施例1
如图1所示的高强无缝地坪，其中：
所述隔离层2由防水底漆、聚酯丙烯酸酯以及固化剂按照质量比6：3：0.7制成。防水底漆采用的是家庭装修中常用的厨房卫生间防水涂料浆料。固化剂采用的是市面上购买的地坪密闭固化剂。将防水底漆、聚酯丙烯酸酯以及固化剂置于45摄氏度的条件下进行混合搅拌均匀后，利用喷涂设备将上述所得到的混合料均匀的喷涂在基层表面，需保证喷涂厚度为0.8mm，待其干燥后，即形成隔离层。
所述复合加固层4由以下质量百分比的原料制备组成：
脲醛树脂40％、聚氯乙烯5％、复合粉体10％、功能混合料20％、癸二酸二甲酯15％、丁酸芐脂5％、邻苯二甲酸和碳酸氢镁混合物5％。所述功能混合料是由双酚A型不饱聚酯树脂、过氧化甲乙酮和环烷酸钴苯乙烯按照1：0.3：0.1的重量比配制而成。邻苯二甲酸和碳酸氢镁等重量比进行混合。
所述表面层5由以下质量百分比的原料制备组成：
二丙二醇30％、十二烷基硫酸钠15％、丁酮6％、硅酸镁15％、硅酸三钙10％、聚乙烯腊5％、磨砂球10％、二羟基丁烷9％。
实施例2
如图1所示的高强无缝地坪，其中：
所述隔离层2由防水底漆、聚酯丙烯酸酯以及固化剂按照质量比6：3：0.7制成。防水底漆采用的是家庭装修中常用的厨房卫生间防水涂料浆料。固化剂采用的是市面上购买的地坪密闭固化剂。将防水底漆、聚酯丙烯酸酯以及固化剂置于60摄氏度的条件下进行混合搅拌均匀后，利用喷涂设备将上述所得到的混合料均匀的喷涂在基层表面，需保证喷涂厚度为0.8mm，待其干燥后，即形成隔离层。
所述复合加固层4由以下质量百分比的原料制备组成：
脲醛树脂30％、聚氯乙烯5％、复合粉体15％、功能混合料25％、癸二酸二甲酯15％、丁酸芐脂5％、邻苯二甲酸和碳酸氢镁混合物5％。所述功能混合料是由聚酯环氧丙烯酸树脂、过氧化甲乙酮和环烷酸钴苯乙烯按照1：0.3：0.1的重量比配制而成。邻苯二甲酸和碳酸氢镁等重量比进行混合。
所述表面层5由以下质量百分比的原料制备组成：
新戊二醇35％、十二烷基硫酸钠15％、丁酮5％、硅酸镁15％、硅酸三钙10％、聚乙烯腊5％、磨砂球10％、二羟基丁烷5％。
对比例1
一种无缝地坪，其结构与实施例1相比，去掉了复合加固层，其他部分与实施例1相同。
将实施例1、实施例2和对比例1中的地坪进行铅笔强度、耐磨性、耐冲击性测试，具体测试结果见下表：
由表中可以看出，与不含有复合加固层的地坪相比，本发明的地坪的铅笔强度、耐磨性、耐冲击性等性能均具有显著提升。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，虽然本发明已以较佳实施例揭露如上，然而并非用以限定本发明，任何熟悉本专业的技术人员，在不脱离本发明技术方案范围内，当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例，但凡是未脱离本发明技术方案的内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。
Claims (9)
1.一种高强无缝地坪，其特征在于，其结构包括基层，基层表面由下至上依次铺设隔离层、泥浆层、复合加固层、表面层；
所述复合加固层由以下质量百分比的原料组分构成：脲醛树脂30～35％、聚氯乙烯4～6％、复合粉体10～15％、功能混合料20～25％、癸二酸二甲酯15～20％、丁酸芐脂5～8％、邻苯二甲酸和碳酸氢镁混合物4～6％；所述功能混合料是由不饱和聚酯树脂、过氧化甲乙酮和环烷酸钴苯乙烯按照1：0.3：0.1的重量比配制而成；不饱和聚酯树脂选自双酚A型不饱聚酯树脂或聚酯环氧丙烯酸树脂。
2.如权利要求1所述的高强无缝地坪，其特征在于，所述复合粉体是由金刚砂骨料和石英粉按照5：1的重量比配制而成。
3.如权利要求2所述的高强无缝地坪，其特征在于，所述复合加固层中，功能混合料和复合粉体的用量重量比为1：2。
4.如权利要求3所述的高强无缝地坪，其特征在于，所述复合加固层的施工方法：将复合加固层的原料组分混合搅拌均匀，然后加入少量的水，搅拌混均，加水量的控制，以得到膏状混合料为准；将得到的混合料立即涂覆在泥浆层表面，抹平，复合加固层厚度控制在0.4-0.5cm。
5.如权利要求1所述的高强无缝地坪，其特征在于，所述隔离层由防水底漆、聚酯丙烯酸酯以及固化剂制作而成，防水底漆、聚酯丙烯酸酯以及固化剂的质量比为6：3：0.7。
6.如权利要求5所述的高强无缝地坪，其特征在于，将防水底漆、聚酯丙烯酸酯以及固化剂置于45-60摄氏度的条件下进行混合搅拌均匀后，利用喷涂设备将上述所得到的混合料均匀的喷涂在基层表面，需保证喷涂厚度为0.8mm，待其干燥后，即形成隔离层。
7.如权利要求1所述的高强无缝地坪，其特征在于，所述泥浆层为C10混凝土，且泥浆层的内部掺有金刚砂骨料。
8.如权利要求1所述的高强无缝地坪，其特征在于，所述表面层由以下质量百分比的原料组成：
多元醇30～35％、十二烷基硫酸钠15～20％、丙酮6～10％、硅酸镁15～20％、硅酸三钙10～15％、聚乙烯腊5～10％、磨砂球10～15％、二羟基丁烷5～10％。
9.如权利要求8所述的高强无缝地坪，其特征在于，所述表面层施工方法是：将各原料投入混合容器中，在90℃环境下搅拌均匀，搅拌时间至少2分钟，静置1分钟后，继续搅拌反复进行，直至产生细柔无结块浆状流体，并保温30-60min，静置冷却成粉状物；将粉状物中加清水，粉状物与水的配比为5kg：3L，搅拌形成粘稠液；将粘稠液均匀喷涂在复合加固层表面，待粘稠液在复合加固层表面自然干燥后，再次喷涂；每次喷涂时都需要现场配制新的粘稠液，即取粉状物与水混合搅拌，制成粘稠液；然后自然干燥，喷涂的次数至少两次，最终得到0.2-0.3cm后的表面层。