CN103934186A - 一种钢丝护栏的浸塑工艺 - Google Patents
一种钢丝护栏的浸塑工艺 Download PDFInfo
- Publication number
- CN103934186A CN103934186A CN201410132288.8A CN201410132288A CN103934186A CN 103934186 A CN103934186 A CN 103934186A CN 201410132288 A CN201410132288 A CN 201410132288A CN 103934186 A CN103934186 A CN 103934186A
- Authority
- CN
- China
- Prior art keywords
- steel wire
- wire mesh
- guardrail
- plastic dipping
- abs resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于护栏加工的领域，具体涉及一种钢丝护栏的浸塑工艺。一种钢丝护栏的浸塑工艺，包括以下步骤：（1）、除去钢丝网表面的锈；（2）、将钢丝网放入烘箱在220-350℃下加热15-25min；（3）、将ABS树脂粉末均匀喷涂在钢丝网表面，边喷涂边震动钢丝网，除去多余的ABS树脂粉粉末；（4）、将钢丝网在165-210℃下以15-30r/min的速度转动，处理12-20min，冷却固化，得到成品。本发明提供的钢丝护栏的浸塑工艺，通过使用ABS塑料进行浸塑，提高了产品的耐候性，延长了使用时间，同时本加工方法不需要使用流化床，而是将工件在高温下旋转实现浸塑的光滑均匀，降低了生产成本。
Description
技术领域
本发明属于护栏加工的领域，具体涉及一种钢丝护栏的浸塑工艺。
背景技术
在高速路或者铁路的边上，一般都设有安全护栏，护栏为金属材质，为了防止护栏的腐蚀，往往会在护栏表面喷涂防护层，防护层一般采用油漆，油漆虽然喷涂容易，但是在风吹日晒的环境下容易脱落，造成钢筋骨架裸露在空气中造成腐蚀，同样，若是现在为了提高防腐蚀能力，采用浸塑工艺，增加防护层的厚度，但是，喷涂的塑料依然容易老化，造成钢丝护栏的耐久性不足。
发明内容
本发明的目的是提供一种钢丝护栏的浸塑工艺，提高了护栏的耐候性，延长了护栏的使用时间。
本发明通过以下技术方案实现：
一种钢丝护栏的浸塑工艺，包括以下步骤：（1）、除去钢丝网表面的锈；（2）、将钢丝网放入烘箱在220-350℃下加热15-25min；（3）、将ABS树脂粉末均匀喷涂在钢丝网表面，边喷涂边震动钢丝网，除去多余的ABS树脂粉粉末；（4）、将钢丝网在165-210℃下以15-30r/min的速度转动，处理12-20min，冷却固化，得到成品。
本发明的有益效果：本发明提供的钢丝护栏的浸塑工艺，通过使用ABS塑料进行浸塑，提高了产品的耐候性，延长了使用时间，同时本加工方法不需要使用流化床，而是将工件在高温下旋转实现浸塑的光滑均匀，降低了生产成本。
具体实施方式
实施例1
一种钢丝护栏的浸塑工艺，包括以下步骤：（1）、使用1000目的砂纸对钢丝网表面进行打磨，除去钢丝网便面的铁锈，并且增加钢丝网表面的粗糙程度，便于进行浸塑，将打磨好的钢丝网放入5%的稀盐酸中进行浸泡，除去表面的油渍和铁锈，浸泡15min；（2）、将钢丝网放入烘箱在320℃下加热15min；（3）、将ABS树脂磨碎成480目的粉末，将粉末均匀喷涂在热钢丝网表面，边喷涂边震动钢丝网，除去多余的ABS树脂粉粉末；（4）、将涂覆了ABS树脂的钢丝网在190℃下以20r/min的速度转动，处理18min，然后以5℃/min的速度进行冷却固化冷却过程中以15r/min的速度转动工件，得到成品。制得的成品可以有效地防止外界温度、湿度的变化对覆膜的影响，也可以有效的防止由于紫外线照射引起的老化，延长了使用的时间，同时在固化和加热处理时，将工件进行转动，提高了涂覆的均匀性，使树脂在钢丝网上均匀的涂覆，提高了浸塑的质量。
实施例2
一种钢丝护栏的浸塑工艺，包括以下步骤：（1）、使用砂纸打磨钢丝网表面，并使用10%的盐酸清洗钢丝网的表面；（2）、将钢丝网放入烘箱在220℃下加热25min；（3）、将ABS树脂粉末均匀喷涂在钢丝网表面，边喷涂边震动钢丝网，除去多余的ABS树脂粉粉末；（4）、将钢丝网在180℃下以25r/min的速度转动，处理20min，冷却固化，得到成品。
Claims (1)
1.一种钢丝护栏的浸塑工艺，其特征在于，包括以下步骤：（1）、除去钢丝网表面的锈；（2）、将钢丝网放入烘箱在220-350℃下加热15-25min；（3）、将ABS树脂粉末均匀喷涂在钢丝网表面，边喷涂边震动钢丝网，除去多余的ABS树脂粉粉末；（4）、将钢丝网在165-210℃下以15-30r/min的速度转动，处理12-20min，冷却固化，得到成品。