CN103922594A - 一种大红颜色水晶珠胚及其制备方法 - Google Patents

一种大红颜色水晶珠胚及其制备方法 Download PDF

Info

Publication number
CN103922594A
CN103922594A CN201410104435.0A CN201410104435A CN103922594A CN 103922594 A CN103922594 A CN 103922594A CN 201410104435 A CN201410104435 A CN 201410104435A CN 103922594 A CN103922594 A CN 103922594A
Authority
CN
China
Prior art keywords
parts
red color
color crystal
bead blank
crystal bead
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410104435.0A
Other languages
English (en)
Other versions
CN103922594B (zh
Inventor
杨鑫法
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Xinweixing Crystal Co ltd
Original Assignee
浙江伟兴水晶有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 浙江伟兴水晶有限公司 filed Critical 浙江伟兴水晶有限公司
Priority to CN201410104435.0A priority Critical patent/CN103922594B/zh
Publication of CN103922594A publication Critical patent/CN103922594A/zh
Application granted granted Critical
Publication of CN103922594B publication Critical patent/CN103922594B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种大红颜色水晶珠胚及其制备方法，该大红颜色水晶珠胚是由下列重量份配比成份组成:石英砂100-150份、氧化锌12-18份、纯碱29-54份、碳酸钾18-27份、硼酸12-18份、碳酸钙3-5份、氢氧化铝1-2份、食盐1-2份、镉黄0.2-2.5份、硒粉0.6-1.8份和镉红1-5份。本发明大红颜色水晶珠胚制备时使铜离子在熔制过程中的氧化还原平衡保持稳定，从而获得良好的着色性；不采用含铅的原料，具有光泽度好，颜色鲜艳、整齐、无色差，无花纹，产量高，无铅无污染，生产效益好的优点。

Description

一种大红颜色水晶珠胚及其制备方法
技术领域
    本发明涉及一种大红颜色水晶珠胚及其制备方法。
背景技术
大红颜色水晶珠胚是用来制备大红颜色水晶产品的半成品，现有的大红颜色水晶珠胚工艺采用坩埚制造，存在着色差，颜色参差不齐，有花纹，产品质量不稳定，生产效率低，不适合连续大批量生产，而且用煤烧造成环境污染。
发明内容
    本发明所要解决的技术问题是提供一种着色再现性好，颜色一致无色差、无花纹，产品质量稳定，生产效率高，可适合连续池窑的生产作业的大红颜色水晶珠胚。
为解决上述问题，本发明是通过以下技术方案来实现的：一种大红颜色水晶珠胚，该大红颜色水晶珠胚是由下列重量份配比成份组成: 石英砂100-150份、氧化锌12-18份、纯碱29-54份、碳酸钾18-27份、硼酸12-18份、碳酸钙3-5份、氢氧化铝1-2份、食盐1-2份、镉黄0.2-2.5份、硒粉0.6-1.8份和镉红1-5份。
本发明所要解决的另一技术问题是提供一种大红颜色水晶珠胚的制备方法，
本发明是通过以下技术方案来实现的：所述大红颜色水晶珠胚的制备过程如下：
1）按重量份配比提取石英砂100-150份、氧化锌12-18份、纯碱29-54份、碳酸钾18-27份、硼酸12-18份、碳酸钙3-5份、氢氧化铝1-2份、食盐1-2份、镉黄0.2-2.5份、硒粉0.6-1.8份和镉红1-5份混合均匀；
2）将混合均匀的大红颜色水晶珠胚原料通过造粒机进行造粒；
3）将制成颗粒状的大红颜色水晶珠胚原料放入玻璃水晶池炉中熔制，熔制时保持中性气氛和溶液液面稳定；
4）将水晶溶液经料道均化冷却后模压成大红颜色水晶珠胚；
5）将成型珠胚放入火抛炉抛光、整型、均匀着色，让成型珠胚匀速进入不锈钢管道，管道温度控制在850℃，转速200转/秒，在管道内5分钟，管道出来就是经过整型、颜色一致、无色差、无花纹的大红颜色水晶珠胚。
进一步地，所述在大红颜色水晶珠胚的制备步骤3中，熔制时温度控制在1310℃-1350℃。
进一步地，所述在大红颜色水晶珠胚的制备步骤4中，冷却温度控制在800℃-1000℃。
本发明大红颜色水晶珠胚的有益效果是：所述大红颜色水晶珠胚制备时使铜离子在熔制过程中的氧化还原平衡保持稳定，从而获得良好的着色性；不采用含铅的原料，具有光泽度好，颜色鲜艳、整齐、无色差，无花纹，产量高，无铅无污染，生产效益好的优点。
具体实施方式
以下实施例用于说明本发明，但不用来限制本发明的范围。
实施例1
本发明的一种大红颜色水晶珠胚，该大红颜色水晶珠胚是由下列重量份配比成份组成: 石英砂100份、氧化锌12份、纯碱29份、碳酸钾18份、硼酸12份、碳酸钙3份、氢氧化铝1份、食盐1份、镉黄0.2份、硒粉0.6份和镉红1份。
所述大红颜色水晶珠胚的制备过程如下：
1）按重量份配比提取石英砂100份、氧化锌12份、纯碱29份、碳酸钾18份、硼酸12份、碳酸钙3份、氢氧化铝1份、食盐1份、镉黄0.2份、硒粉0.6份和镉红1份混合均匀；
2）将混合均匀的大红颜色水晶珠胚原料通过造粒机进行造粒；
3）将制成颗粒状的大红颜色水晶珠胚原料放入玻璃水晶池炉中熔制，熔制时保持中性气氛和溶液液面稳定,温度控制在1310℃-1350℃；
4）将水晶溶液经料道均化冷却后模压成大红颜色水晶珠胚，温度控制在800℃-1000℃；
5）将成型珠胚放入火抛炉抛光、整型、均匀着色，让成型珠胚匀速进入不锈钢管道，管道温度控制在850℃，转速200转/秒，在管道内5分钟，管道出来就是经过整型、颜色一致、无色差、无花纹的大红颜色水晶珠胚。
实施例2
其与实施例1不同之处在于，该大红颜色水晶珠胚是由下列重量份配比成份组成: 石英砂150份、氧化锌18份、纯碱54份、碳酸钾27份、硼酸18份、碳酸钙5份、氢氧化铝2份、食盐2份、镉黄2.5份、硒粉1.8份和镉红5份。
实施例3
其与实施例1不同之处在于，该大红颜色水晶珠胚是由下列重量份配比成份组成: 石英砂112份、氧化锌14份、纯碱31份、碳酸钾22份、硼酸15份、碳酸钙4份、氢氧化铝1份、食盐2份、镉黄0.8份、硒粉1.1份和镉红2份。
实施例4
其与实施例1不同之处在于，该大红颜色水晶珠胚是由下列重量份配比成份组成: 石英砂133份、氧化锌16份、纯碱43份、碳酸钾19份、硼酸14份、碳酸钙3份、氢氧化铝2份、食盐1份、镉黄2.1份、硒粉0.9份和镉红4份。
实施例5
其与实施例1不同之处在于，该大红颜色水晶珠胚是由下列重量份配比成份组成: 石英砂147份、氧化锌17份、纯碱48份、碳酸钾25份、硼酸17份、碳酸钙4份、氢氧化铝2份、食盐2份、镉黄2.3份、硒粉1.6份和镉红4份。
实施例6
其与实施例1不同之处在于，该大红颜色水晶珠胚是由下列重量份配比成份组成: 石英砂119份、氧化锌13份、纯碱36份、碳酸钾20份、硼酸13份、碳酸钙5份、氢氧化铝1份、食盐1份、镉黄1.7份、硒粉1.1份和镉红5份。
实施例7
其与实施例1不同之处在于，该大红颜色水晶珠胚是由下列重量份配比成份组成: 石英砂100份、氧化锌12份、纯碱29份、碳酸钾18份、硼酸12份、碳酸钙4份、氢氧化铝2份、食盐2份、镉黄0.35份、硒粉1.2份和镉红2.3份。
实施例8
其与实施例1不同之处在于，该大红颜色水晶珠胚是由下列重量份配比成份组成: 石英砂135份、氧化锌13份、纯碱44份、碳酸钾22份、硼酸15份、碳酸钙3份、氢氧化铝1.5份、食盐2份、镉黄2.1份、硒粉1份和镉红2份。
本发明不局限于上述最佳实施方式，任何人在本发明的启示下得出的其他任何与本发明相同或相近似的产品，均落在本发明的保护范围之内。

Claims (4)

1.一种大红颜色水晶珠胚，其特征在于：该大红颜色水晶珠胚是由下列重量份配比成份组成: 石英砂100-150份、氧化锌12-18份、纯碱29-54份、碳酸钾18-27份、硼酸12-18份、碳酸钙3-5份、氢氧化铝1-2份、食盐1-2份、镉黄0.2-2.5份、硒粉0.6-1.8份和镉红1-5份。
2.一种制备权利要求1所述的大红颜色水晶珠胚的制备方法，其特征在于：该方法包括以下步骤：
1）按重量份配比提取石英砂100-150份、氧化锌12-18份、纯碱29-54份、碳酸钾18-27份、硼酸12-18份、碳酸钙3-5份、氢氧化铝1-2份、食盐1-2份、镉黄0.2-2.5份、硒粉0.6-1.8份和镉红1-5份混合均匀；
2）将混合均匀的大红颜色水晶珠胚原料通过造粒机进行造粒；
3）将制成颗粒状的大红颜色水晶珠胚原料放入玻璃水晶池炉中熔制，熔制时保持中性气氛和溶液液面稳定；
4）将水晶溶液经料道均化冷却后模压成大红颜色水晶珠胚；
5）将成型珠胚放入火抛炉抛光、整型、均匀着色，让成型珠胚匀速进入不锈钢管道，管道温度控制在850℃，转速200转/秒，在管道内5分钟，管道出来就是经过整型、颜色一致、无色差、无花纹的大红颜色水晶珠胚。
3.根据权利要求2所述的大红颜色水晶珠胚制备方法，其特征在于：所述在大红颜色水晶珠胚的制备步骤3中，熔制时温度控制在1310℃-1350℃。
4.根据权利要求2所述的大红颜色水晶珠胚制备方法，其特征在于：所述在大红颜色水晶珠胚的制备步骤4中，冷却温度控制在800℃-1000℃。
CN201410104435.0A 2014-03-20 2014-03-20 一种大红颜色水晶珠胚及其制备方法 Active CN103922594B (zh)