CN103909211B - 一种自剥落消失模铸造专用涂料 - Google Patents

一种自剥落消失模铸造专用涂料 Download PDF

Info

Publication number
CN103909211B
CN103909211B CN201410118509.6A CN201410118509A CN103909211B CN 103909211 B CN103909211 B CN 103909211B CN 201410118509 A CN201410118509 A CN 201410118509A CN 103909211 B CN103909211 B CN 103909211B
Authority
CN
China
Prior art keywords
parts
peeling
cast mold
paint specially
disappearing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410118509.6A
Other languages
English (en)
Other versions
CN103909211A (zh
Inventor
孙健
陈光云
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JI'AN HUICHENG INDUSTRIAL DEVELOPMENT Co Ltd
Original Assignee
JI'AN HUICHENG INDUSTRIAL DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JI'AN HUICHENG INDUSTRIAL DEVELOPMENT Co Ltd filed Critical JI'AN HUICHENG INDUSTRIAL DEVELOPMENT Co Ltd
Priority to CN201410118509.6A priority Critical patent/CN103909211B/zh
Publication of CN103909211A publication Critical patent/CN103909211A/zh
Application granted granted Critical
Publication of CN103909211B publication Critical patent/CN103909211B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种自剥落消失模铸造专用涂料，其特征是由下述按质量份的原料：25‑35份的棕刚玉，45‑55份的长石粉，15‑25份的高铝矾土，1.5‑2.5份的硅溶液，3.5‑4.5份的白乳胶，0.4‑0.6份的纤维素钠，1.5‑2.5份的膨润土和75‑95份的水均匀混合配制而成。其优点在于浇注铸件冷却到一定温度，涂料壳成片脱落。所得铸件表面光洁，清理时间大大缩短，降低了生产成本，提高工作过效率，改善了劳动环境。

Description

一种自剥落消失模铸造专用涂料
技术领域
本发明涉及一种涂料，尤其涉及一种消失模铸造专用涂料。
背景技术
消失模铸造又称实型铸造，采用泡沫塑料珠粒制作模型，在负压状态下浇注，金属液置换泡沫模样，而冷却成铸件的铸造工艺。由于泡沫模样在填箱振动过程中易变形，通常在摸样外表面涂一层耐火涂料而提高模样的强度和刚度，并促使模样高温分解的气体（气化的气体）在负压作用下透过涂料层排到砂型中去。生产中使用现有的涂料，铸件变形，皱皮积碳相当严重，不便清理。
发明内容
本发明的目的在于提供一种自剥落消失模铸造专用涂料，使用这种涂料，浇注铸件冷却到一定温度，涂料壳成片脱落，所得铸件表面光洁，清理时间大大缩短。
本发明是这样来实现的。一种自剥落消失模铸造专用涂料，其特征是由下述按质量份的原料：25-35份的棕刚玉，45-55份的长石粉，15-25份的高铝矾土，1.5-2.5份的硅溶液，3.5-4.5份的白乳胶，0.4-0.6份的纤维素钠，1.5-2.5份的膨润土和75-95份的水均匀混合配制而成。
作为本发明的进一步改进，所述高铝矾土为180—270目且Al₂O₃含量不小于82%，棕刚玉和长石粉均为200目，纤维素钠为中粘度的FM6型号。
按上述配比配制原料，然后加入变频调速搅拌机，先快搅30-60分钟（400r/min）,再慢搅30-60分钟，然后静置20分钟后使用即可。
本发明的有益效果是：本发明具有浸润性好，涂刷性好，触变性及良好的不流淌性、透气性和高、低温强度适中，吸湿性低、脱壳性良好的优点和效果。使用本发明铸造，浇注铸件冷却到一定温度，涂料壳成片脱落。所得铸件表面光洁，清理时间大大缩短，降低了生产成本，提高工作过效率，改善了劳动环境。
具体实施方式
为了便于说明，下面结合实施例详细阐明本发明。
本发明的配制方法为：按配比配制原料，然后加入变频调速搅拌机，先快搅30-60分钟（400r/min）,再慢搅30-60分钟，然后静置20分钟后使用即可。
实施例1
一种自剥落消失模铸造专用涂料，由30份的棕刚玉，50份的长石粉，20份的高铝矾土，2份的硅溶液，4份的白乳胶，0.5份的纤维素钠，2份的膨润土和85份的水经搅拌混合配制而成。
实施例2
一种自剥落消失模铸造专用涂料，由25份的棕刚玉，50份的长石粉，25份的高铝矾土，1.5份的硅溶液， 4.5份的白乳胶，0.4份的纤维素钠，2份的膨润土和95份的水经搅拌混合配制而成。
实施例3
一种自剥落消失模铸造专用涂料，由35份的棕刚玉，50份的长石粉，15份的高铝矾土， 2.5份的硅溶液，3.5份的白乳胶，0.6份的纤维素钠，1.5份的膨润土和75份的水经搅拌混合配制而成，所述长石粉为200目。
实施例4
一种自剥落消失模铸造专用涂料，由30份的棕刚玉，45份的长石粉，25份的高铝矾土，2份的硅溶液，4份的白乳胶，0.5份的纤维素钠，2.5份的膨润土和90份的水经搅拌混合配制而成。所述棕刚玉为200目，纤维素钠为中粘度的FM6型号。
实施例5
一种自剥落消失模铸造专用涂料，25份的棕刚玉，55份的长石粉，20份的高铝矾土，2份的硅溶液，4份的白乳胶，0.5份的纤维素钠，2份的膨润土和85份的水经搅拌混合配制而成，高铝矾土为180—270目且Al₂O₃含量不小于82%。

Claims (6)

1.一种自剥落消失模铸造专用涂料，其特征是由下述按质量份的原料：25-35份的棕刚玉，45-55份的长石粉，15-25份的高铝矾土，1.5-2.5份的硅溶液，3.5-4.5份的白乳胶，0.4-0.6份的纤维素钠，1.5-2.5份的膨润土和75-95份的水均匀混合配制而成。
2.根据权利要求1所述的一种自剥落消失模铸造专用涂料，其特征是由由下述按质量份的原料：30份的棕刚玉，50份的长石粉，20份的高铝矾土，2份的硅溶液，4份的白乳胶，0.5份的纤维素钠，2份的膨润土和85份的水经均匀混合配制而成。
3.根据权利要求1所述的一种自剥落消失模铸造专用涂料，其特征是所述高铝矾土为180—270目且Al₂O₃含量不小于82%。
4.根据权利要求1所述的一种自剥落消失模铸造专用涂料，其特征是所述棕刚玉为200目。
5.根据权利要求1所述的一种自剥落消失模铸造专用涂料，其特征是所述长石粉为200目。
6.根据权利要求1所述的一种自剥落消失模铸造专用涂料，其特征是所述纤维素钠为中粘度的FM6型号。
CN201410118509.6A 2014-03-27 2014-03-27 一种自剥落消失模铸造专用涂料 Expired - Fee Related CN103909211B (zh)