CN104439071A - 一种精铸件制壳工艺 - Google Patents

一种精铸件制壳工艺 Download PDF

Info

Publication number
CN104439071A
CN104439071A CN201410671264.XA CN201410671264A CN104439071A CN 104439071 A CN104439071 A CN 104439071A CN 201410671264 A CN201410671264 A CN 201410671264A CN 104439071 A CN104439071 A CN 104439071A
Authority
CN
China
Prior art keywords
waterglass
dewaxing
coating
precision castings
sclerosis
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410671264.XA
Other languages
English (en)
Inventor
何拥军
何嘉圣
何嘉贤
赖卫华
伍斌华
杨学
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LIUZHOU JINTE MACHINERY Co Ltd
Original Assignee
LIUZHOU JINTE MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIUZHOU JINTE MACHINERY Co Ltd filed Critical LIUZHOU JINTE MACHINERY Co Ltd
Priority to CN201410671264.XA priority Critical patent/CN104439071A/zh
Publication of CN104439071A publication Critical patent/CN104439071A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种精铸件制壳工艺，包括以下步骤：（1）按工艺要求配比涂料；（2）在蜡模表面分别涂抹面层涂料，过渡层涂料和加固层涂料，且涂抹时要多次上下移动和转动；（3）在硬化池中加入氯化铵进行硬化处理；（4）脱蜡，脱蜡时水的温度小于100℃，脱蜡时间为20---30分钟；（5）脱蜡后的壳模干燥4-8小时，即可装炉进行高温焙烧。采用本发明的制壳工艺，使得铸件质量得到提高，在得到高质量铸件的基础上降低了生产成本。

Description

一种精铸件制壳工艺
技术领域
本发明属于铸造技术领域，特别涉及一种精铸件制壳工艺。
背景技术
目前，熔模铸造生产工艺主要包括制模、制壳和模壳焙烧浇注三道工序过程，其中制壳工序是将制模工序制的蜡模组，通过涂料、撒砂、硬化、风干的多次循环过程形成涂料模组，再进行脱蜡（熔失蜡模）就形成了模壳，壳内型腔就是零件模型。
现在科技发展日新月异，铸造工艺水平也在飞快发展，对于熔模铸造而言，现有的水玻璃加硅砂工艺，铸件表面粗糙度较高，铸件毛坯质量较差，为解决这一问题，所研发的硅溶胶加锆砂工艺，虽然毛坯质量得到了提高，但是也大大提高了生产成本。
发明内容
为了解决铸件表面粗糙度较高，铸件毛坯质量较差的问题，本发明提供一种精铸件制壳工艺。
本发明的技术方案是：一种精铸件制壳工艺，包括以下步骤：（1）按工艺要求配比涂料：面层涂料：水玻璃28-30%，石英粉45-47%，硅微粉10%，洗涤剂0.05%，正辛醇0.05-0.1%，水占水玻璃的重量比为15%；过渡层涂料：水玻璃28-30%，石英粉55-57%，洗涤剂0.05%，正辛醇0.05-0.1%，水占水玻璃的重量比为15%；加固层涂料：水玻璃40-50%，石英粉20-25%，高铝粉20-25% ；（2）在蜡模表面分别涂抹面层涂料，过渡层涂料和加固层涂料，且涂抹时要多次上下移动和转动；（3）在硬化池中加入氯化铵进行硬化处理；（4）脱蜡，脱蜡时水的温度小于100℃，脱蜡时间为20---30分钟；（5）脱蜡后的壳模干燥4-8小时，即可装炉进行高温焙烧。
优选地，面层涂料浸涂后要求涂料流平且均匀地覆盖在蜡模表面上，然后用手工抛砂。
优选地，在所述步骤（3）中硬化池中加入0.05—0.1%渗透剂，以提高壳模的硬化速度。
优选地，所述渗透剂为JFC或OP—10。
优选地，所述面层的硬化时间为8—10分钟，加固层为15-30分钟；面层和过渡层硬化后的风干时间不小于2小时，加固层硬化后的风干时间为30---45分钟。
优选地，在所述步骤（4）脱蜡时脱蜡水中可以补加1%的工业盐酸或3%---8%的氯化铵，以使壳模在脱蜡时得到补充硬化。
本发明的有益效果：采用本发明的制壳工艺，使得铸件质量得到提高，在得到高质量铸件的基础上降低了生产成本。
具体实施方式
对本发明提供的实施方式作进一步详细的说明：
一种精铸件制壳工艺，包括以下步骤：（1）按工艺要求配比涂料：面层涂料：水玻璃28-30%，石英粉45-47%，硅微粉10%，洗涤剂0.05%，正辛醇0.05-0.1%，水占水玻璃的重量比为15%；过渡层涂料：水玻璃28-30%，石英粉55-57%，洗涤剂0.05%，正辛醇0.05-0.1%，水占水玻璃的重量比为15%；加固层涂料：水玻璃40-50%，石英粉20-25%，高铝粉20-25% ；（2）在蜡模表面分别涂抹面层涂料，过渡层涂料和加固层涂料，且涂抹时要多次上下移动和转动；（3）在硬化池中加入氯化铵进行硬化处理；（4）脱蜡，脱蜡时水的温度小于100℃，脱蜡时间为20---30分钟；（5）脱蜡后的壳模干燥4-8小时，即可装炉进行高温焙烧。
其中，面层涂料浸涂后要求涂料流平且均匀地覆盖在蜡模表面上，然后用手工抛砂。
本发明中在所述步骤（3）中硬化池中加入0.05—0.1%渗透剂，以提高壳模的硬化速度。
本发明中所述渗透剂为JFC或OP—10。
本发明中所述面层的硬化时间为8—10分钟，加固层为15-30分钟；面层和过渡层硬化后的风干时间不小于2小时，加固层硬化后的风干时间为30---45分钟。

Claims (6)

1.一种精铸件制壳工艺，其特征在于，包括以下步骤：（1）按工艺要求配比涂料：面层涂料：水玻璃28-30%，石英粉45-47%，硅微粉10%，洗涤剂0.05%，正辛醇0.05-0.1%，水占水玻璃的重量比为15%；过渡层涂料：水玻璃28-30%，石英粉55-57%，洗涤剂0.05%，正辛醇0.05-0.1%，水占水玻璃的重量比为15%；加固层涂料：水玻璃40-50%，石英粉20-25%，高铝粉20-25% ；（2）在蜡模表面分别涂抹面层涂料，过渡层涂料和加固层涂料，且涂抹时要多次上下移动和转动；（3）在硬化池中加入氯化铵进行硬化处理；（4）脱蜡，脱蜡时水的温度小于100℃，脱蜡时间为20---30分钟；（5）脱蜡后的壳模干燥4-8小时，即可装炉进行高温焙烧。
2.根据权利要求1所述的精铸件制壳工艺，其特征在于，面层涂料浸涂后要求涂料流平且均匀地覆盖在蜡模表面上，然后用手工抛砂。
3. 根据权利要求1所述的精铸件制壳工艺，其特征在于，在所述步骤（3）中硬化池中加入0.05—0.1%渗透剂，以提高壳模的硬化速度。
4. 根据权利要求3所述的精铸件制壳工艺，其特征在于，所述渗透剂为JFC或OP—10。
5. 根据权利要求1所述的精铸件制壳工艺，其特征在于，所述面层的硬化时间为8—10分钟，加固层为15-30分钟；面层和过渡层硬化后的风干时间不小于2小时，加固层硬化后的风干时间为30---45分钟。
6. 根据权利要求1所述的精铸件制壳工艺，其特征在于，在所述步骤（4）脱蜡时脱蜡水中可以补加1%的工业盐酸或3%---8%的氯化铵，以使壳模在脱蜡时得到补充硬化。
CN201410671264.XA 2014-11-21 2014-11-21 一种精铸件制壳工艺 Pending CN104439071A (zh)