CN103897305A - 化工流程泵防腐内衬的抗强碱复合材料 - Google Patents

化工流程泵防腐内衬的抗强碱复合材料 Download PDF

Info

Publication number
CN103897305A
CN103897305A CN201410118511.3A CN201410118511A CN103897305A CN 103897305 A CN103897305 A CN 103897305A CN 201410118511 A CN201410118511 A CN 201410118511A CN 103897305 A CN103897305 A CN 103897305A
Authority
CN
China
Prior art keywords
powder
parts
diatomite
composite material
strong alkali
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410118511.3A
Other languages
English (en)
Inventor
洪忠保
吴淑芳
凤良云
王维龙
程志强
凤琦
文超
何建军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI WOLONG VALVE Co Ltd
Original Assignee
ANHUI WOLONG VALVE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI WOLONG VALVE Co Ltd filed Critical ANHUI WOLONG VALVE Co Ltd
Priority to CN201410118511.3A priority Critical patent/CN103897305A/zh
Publication of CN103897305A publication Critical patent/CN103897305A/zh
Pending legal-status Critical Current

Abstract

本发明公开了化工流程泵防腐内衬的抗强碱复合材料，化工流程泵防腐内衬的抗强碱复合材料，其特征在于，由以下重量份的原料组成，聚四氟乙烯80-85、聚氯乙烯4-5、聚丙烯短切纤维2-3、铁矿尾渣微粉2-3、碳化硅粉1-2、可再分散乳胶粉1-2、石墨烯1-2、钛酸酯偶联剂NDZ-1012-3、柠檬酸三丁酯1-2、复合改性硅藻土粉1-2。利用本发明的方法制成的复合材料抗强碱性好、制作成本低、加工成型简便。

Description

化工流程泵防腐内衬的抗强碱复合材料
技术领域
本发明涉及化工流程泵防腐内衬的抗强碱复合材料。
背景技术
化工流程泵在化工或石油化工生产中,泵在高温、低温或超低温、高压、易燃、易爆、有毒强腐蚀介质下工作,化工流程泵的特点还有可以在高入口压力、高扬程、高粘度、小流量、高汽蚀条件下工作,对化工泵的性能提出相当苛刻的要求,特别是对耐腐蚀性、不允许泄漏和耐磨损性要求极高.为适应化工生产特殊要求,在化机行业中还专门生产化工专用泵,如塑料泵、玻璃泵、陶瓷泵、石墨泵、屏蔽泵、磁力泵、杂质泵等。对于化工流程泵的防腐抗高温内衬的性能要求提高。
发明内容
本发明的目的是提供一种化工流程泵防腐内衬的抗强碱复合材料，该复合材料耐高温、制作成本低、加工成型简便。
本发明的技术方案如下：
化工流程泵防腐内衬的抗强碱复合材料，其特征在于，由以下重量份的原料组成，聚四氟乙烯80-85、聚氯乙烯4-5、聚丙烯短切纤维2-3、铁矿尾渣微粉2-3、碳化硅粉1-2、可再分散乳胶粉1-2、石墨烯1-2、钛酸酯偶联剂NDZ-101 2-3、柠檬酸三丁酯1-2、复合改性硅藻土粉1-2；
其具体制备工艺为：按上述重量百分比将聚四氟乙烯、聚氯乙烯、聚丙烯短切纤维细磨后，与其他原料混合后，再用胶体磨均匀，最后用70—90目筛过筛即得产品；
所述的复合改性硅藻土粉由下述重量份的原料制得：硅藻土80-90，碳化硅10-20，二氧化钛1-2，仲醇聚氧乙烯醚 0.2-0.4，硅烷偶联剂KH-792 2-3、钛酸四丁酯0.1-0.2、硬酯酸锌2-5、甲基丙烯酸甲酯1-2；制备方法是将硅藻土在800-830℃下煅烧3-4小时，冷却后，放入10-12%盐酸溶液中浸泡1-2小时，取出，用清水反复洗涤干净，烘干得粉末；将所得粉末加入到3-4倍量的水中，搅拌加热至70-80℃，再加入碳化硅、仲醇聚氧乙烯醚、甲基丙烯酸甲酯、硅烷偶联剂KH-792，搅拌20-30分钟，冷却，烘干，得硅藻土复合粉；最后将硅藻土复合粉与其它剩余物料混合，研磨分散即得。
本发明通过对硅藻土改性，结合碳化硅与二氧化钛，增加了材料的耐磨性及耐腐蚀性能。
本发明的主要材料为聚四氟乙烯，辅助材料采用聚丙烯短切纤维、铁矿尾渣微粉等，利用本发明的方法制成的复合材料抗强碱性好、制作成本低、加工成型简便。
具体实施方式
化工流程泵防腐内衬的抗强碱复合材料，由以下重量份的原料组成，聚四氟乙烯80、聚氯乙烯5、聚丙烯短切纤维3、铁矿尾渣微粉2、碳化硅粉2、可再分散乳胶粉1、石墨烯2、钛酸酯偶联剂NDZ-101 2、柠檬酸三丁酯2、复合改性硅藻土粉1；
其具体制备工艺为：按上述重量百分比将聚四氟乙烯、聚氯乙烯、聚丙烯短切纤维细磨后，与其他原料混合后，再用胶体磨均匀，最后用70—90目筛过筛即得产品；
所述的复合改性硅藻土粉由下述重量份的原料制得：硅藻土90，碳化硅10，二氧化钛1，仲醇聚氧乙烯醚 0.4，硅烷偶联剂KH-792 2、钛酸四丁酯0.1、硬酯酸锌5、甲基丙烯酸甲酯1；制备方法是将硅藻土在800-830℃下煅烧3-4小时，冷却后，放入10-12%盐酸溶液中浸泡1-2小时，取出，用清水反复洗涤干净，烘干得粉末；将所得粉末加入到3-4倍量的水中，搅拌加热至70-80℃，再加入碳化硅、仲醇聚氧乙烯醚、甲基丙烯酸甲酯、硅烷偶联剂KH-792，搅拌20-30分钟，冷却，烘干，得硅藻土复合粉；最后将硅藻土复合粉与其它剩余物料混合，研磨分散即得。
使用时，按不同工件称重本发明复合材料注入加工模具，将加工模具送入热压成型机加热至200-280°后，施加以50—100kg/cm2压力5-10分钟将模型固定于加热板，以达融化后硬化，冷却30-50分钟，再以取出模型成品即可；
本发明材料浇注于化工流程泵的内壁，能抗强碱，用于碱液输送，使用寿命可达十年以上。无损坏，较现有化工泵使用寿命有30%提高。

Claims (1)

1.化工流程泵防腐内衬的抗强碱复合材料，其特征在于，由以下重量份的原料组成，聚四氟乙烯80-85、聚氯乙烯4-5、聚丙烯短切纤维2-3、铁矿尾渣微粉2-3、碳化硅粉1-2、可再分散乳胶粉1-2、石墨烯1-2、钛酸酯偶联剂NDZ-101 2-3、柠檬酸三丁酯1-2、复合改性硅藻土粉1-2；
其具体制备工艺为：按上述重量百分比将聚四氟乙烯、聚氯乙烯、聚丙烯短切纤维细磨后，与其他原料混合后，再用胶体磨均匀，最后用70—90目筛过筛即得产品；
所述的复合改性硅藻土粉由下述重量份的原料制得：硅藻土80-90，碳化硅10-20，二氧化钛1-2，仲醇聚氧乙烯醚 0.2-0.4，硅烷偶联剂KH-792 2-3、钛酸四丁酯0.1-0.2、硬酯酸锌2-5、甲基丙烯酸甲酯1-2；制备方法是将硅藻土在800-830℃下煅烧3-4小时，冷却后，放入10-12%盐酸溶液中浸泡1-2小时，取出，用清水反复洗涤干净，烘干得粉末；将所得粉末加入到3-4倍量的水中，搅拌加热至70-80℃，再加入碳化硅、仲醇聚氧乙烯醚、甲基丙烯酸甲酯、硅烷偶联剂KH-792，搅拌20-30分钟，冷却，烘干，得硅藻土复合粉；最后将硅藻土复合粉与其它剩余物料混合，研磨分散即得。
CN201410118511.3A 2014-03-27 2014-03-27 化工流程泵防腐内衬的抗强碱复合材料 Pending CN103897305A (zh)