CN103881523A - 一种吸收电磁波led散热涂料及其制备方法 - Google Patents

一种吸收电磁波led散热涂料及其制备方法 Download PDF

Info

Publication number
CN103881523A
CN103881523A CN201410050682.7A CN201410050682A CN103881523A CN 103881523 A CN103881523 A CN 103881523A CN 201410050682 A CN201410050682 A CN 201410050682A CN 103881523 A CN103881523 A CN 103881523A
Authority
CN
China
Prior art keywords
parts
minute
coating
nano
electromagnetic wave
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410050682.7A
Other languages
English (en)
Inventor
程实
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410050682.7A priority Critical patent/CN103881523A/zh
Publication of CN103881523A publication Critical patent/CN103881523A/zh
Pending legal-status Critical Current

Abstract

一种吸收电磁波LED散热涂料，由下列重量份的原料制成：氨基树脂30-35、环氧树脂20-25、650低分子聚酰胺8-11、氨基聚酰胺8-11、偏苯三酸三辛酯14-17、甲乙酮15-18、纳米纤维素晶体5-7、铝粉6-8、纳米三氧化钨2-3、氧化锆3-6、硅烷偶联剂2-4、成膜助剂4-5。本发明涂料添加了纳米纤维素晶体，改善了氨基树脂硬脆的缺点，具有良好的韧性，耐撞击；通过添加铝粉、纳米三氧化钨、氧化锆，使得涂料导热性，耐磨性提高，还具有催化氧化有机物、吸收电磁波的作用，健康而且耐老化；本发明的成膜助剂，使涂料成膜性好，易于涂装。

Description

一种吸收电磁波LED散热涂料及其制备方法
技术领域
本发明属于涂料技术领域，特别涉及一种吸收电磁波LED散热涂料及其制备方法。
背景技术
随着LED灯使用范围的迅速扩大，延长LED灯使用寿命也已成为急需解决的问题,LED功率加大，散热问题也就越来越被人注重。目前采用导热胶解决 LED 灯散热问题，但是其所使用的材料存在耐温与耐老化比较差，对基材粘结力小、散热效果不佳以及施工不便的技术问题，难以满足人们对 LED 灯散热的要求。
发明内容
本发明的目的是提供一种吸收电磁波LED散热涂料及其制备方法，本发明涂料具有韧性好、导热性好、耐磨性好、催化氧化有机物、吸收电磁波的特点。
本发明所采用的技术方案是：
一种吸收电磁波LED散热涂料，其特征在于由下列重量份的原料制成：氨基树脂30-35、环氧树脂20-25、650低分子聚酰胺8-11、氨基聚酰胺8-11、偏苯三酸三辛酯14-17、甲乙酮15-18、纳米纤维素晶体5-7、铝粉6-8、纳米三氧化钨2-3、氧化锆3-6、硅烷偶联剂2-4、成膜助剂4-5。
所述的成膜助剂由以下重量份的原料制得：乙二醇乙醚醋酸酯6-9、2-氧乙酸基丁导酸2-4、丙烯酸3-5、聚乙烯醇缩丁醛2-4、六甲基磷酰三胺3-5、乙酸香叶酯3-5、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.5-1、羟甲基丙基纤维素2-3、纳米甲壳素0.3-0.5、可塑性淀粉1-2、过氧化乙酰0.2-0.4、丙二醇单甲醚乙酸酯15-18；制备方法是：将乙二醇乙醚醋酸酯、六甲基磷酰三胺、乙酸香叶酯、羟甲基丙基纤维素、纳米甲壳素、可塑性淀粉、丙二醇单甲醚乙酸酯混合，搅拌5-10分钟，加热至60-70℃，在4000-6000转/分下搅拌18-25分钟，再加入2-氧乙酸基丁导酸、丙烯酸、聚乙烯醇缩丁醛、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，搅拌反应15-30分钟；再降温至20-25℃，再加入其它剩余成分，搅拌反应45-60分钟，即得。
所述的吸收电磁波LED散热涂料的制备方法，其特征在于包括以下步骤：将偏苯三酸三辛酯、甲乙酮、纳米纤维素晶体、铝粉、纳米三氧化钨、氧化锆混合，在1100-1300转/分下搅拌反应10-20分钟，然后升温至40-50℃，加入氨基树脂、环氧树脂、650低分子聚酰胺、氨基聚酰胺、硅烷偶联剂，继续搅拌20-30分钟，再加入其它剩余成分，继续搅拌反应30-40分钟，研磨得到浆料，即得。
本发明的有益效果
本发明涂料添加了纳米纤维素晶体，改善了氨基树脂硬脆的缺点，具有良好的韧性，耐撞击；通过添加铝粉、纳米三氧化钨、氧化锆，使得涂料导热性，耐磨性提高，还具有催化氧化有机物、吸收电磁波的作用，健康而且耐老化；本发明的成膜助剂，使涂料成膜性好，易于涂装。
具体实施方式
一种吸收电磁波LED散热涂料，由下列重量份(公斤)的原料制成：氨基树脂33、环氧树脂23、650低分子聚酰胺9、氨基聚酰胺9、偏苯三酸三辛酯16、甲乙酮17、纳米纤维素晶体6、铝粉7、纳米三氧化钨2.7、氧化锆5、硅烷偶联剂3、成膜助剂4.5。
所述的成膜助剂由以下重量份（公斤）的原料制得：乙二醇乙醚醋酸酯8、2-氧乙酸基丁导酸3、丙烯酸4、聚乙烯醇缩丁醛3、六甲基磷酰三胺4、乙酸香叶酯4、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.7、羟甲基丙基纤维素2.5、纳米甲壳素0.4、可塑性淀粉1.5、过氧化乙酰0.3、丙二醇单甲醚乙酸酯17；制备方法是：将乙二醇乙醚醋酸酯、六甲基磷酰三胺、乙酸香叶酯、羟甲基丙基纤维素、纳米甲壳素、可塑性淀粉、丙二醇单甲醚乙酸酯混合，搅拌8分钟，加热至65℃，在5000转/分下搅拌20分钟，再加入2-氧乙酸基丁导酸、丙烯酸、聚乙烯醇缩丁醛、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，搅拌反应26分钟；再降温至24℃，再加入其它剩余成分，搅拌反应50分钟，即得。
所述的吸收电磁波LED散热涂料的制备方法，包括以下步骤：将偏苯三酸三辛酯、甲乙酮、纳米纤维素晶体、铝粉、纳米三氧化钨、氧化锆混合，在1200转/分下搅拌反应15分钟，然后升温至45℃，加入氨基树脂、环氧树脂、650低分子聚酰胺、氨基聚酰胺、硅烷偶联剂，继续搅拌25分钟，再加入其它剩余成分，继续搅拌反应35分钟，研磨得到浆料，即得。
将本发明涂料涂于LED壳体上，在80℃和300W 紫外光辐照条件下人工加速老化试验，耐老化时间4600小时，耐温高温290℃，粘结剪切力18MPa.，导热系数290 W/(m·℃）。

Claims (2)

1.一种吸收电磁波LED散热涂料，其特征在于由下列重量份的原料制成：氨基树脂30-35、环氧树脂20-25、650低分子聚酰胺8-11、氨基聚酰胺8-11、偏苯三酸三辛酯14-17、甲乙酮15-18、纳米纤维素晶体5-7、铝粉6-8、纳米三氧化钨2-3、氧化锆3-6、硅烷偶联剂2-4、成膜助剂4-5；
所述的成膜助剂由以下重量份的原料制得：乙二醇乙醚醋酸酯6-9、2-氧乙酸基丁导酸2-4、丙烯酸3-5、聚乙烯醇缩丁醛2-4、六甲基磷酰三胺3-5、乙酸香叶酯3-5、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.5-1、羟甲基丙基纤维素2-3、纳米甲壳素0.3-0.5、可塑性淀粉1-2、过氧化乙酰0.2-0.4、丙二醇单甲醚乙酸酯15-18；制备方法是：将乙二醇乙醚醋酸酯、六甲基磷酰三胺、乙酸香叶酯、羟甲基丙基纤维素、纳米甲壳素、可塑性淀粉、丙二醇单甲醚乙酸酯混合，搅拌5-10分钟，加热至60-70℃，在4000-6000转/分下搅拌18-25分钟，再加入2-氧乙酸基丁导酸、丙烯酸、聚乙烯醇缩丁醛、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，搅拌反应15-30分钟；再降温至20-25℃，再加入其它剩余成分，搅拌反应45-60分钟，即得。
2.根据权利要求1所述的吸收电磁波LED散热涂料的制备方法，其特征在于包括以下步骤：将偏苯三酸三辛酯、甲乙酮、纳米纤维素晶体、铝粉、纳米三氧化钨、氧化锆混合，在1100-1300转/分下搅拌反应10-20分钟，然后升温至40-50℃，加入氨基树脂、环氧树脂、650低分子聚酰胺、氨基聚酰胺、硅烷偶联剂，继续搅拌20-30分钟，再加入其它剩余成分，继续搅拌反应30-40分钟，研磨得到浆料，即得。
CN201410050682.7A 2014-02-14 2014-02-14 一种吸收电磁波led散热涂料及其制备方法 Pending CN103881523A (zh)