CN103881440A - 一种玻璃树脂led散热涂料及其制备方法 - Google Patents
一种玻璃树脂led散热涂料及其制备方法 Download PDFInfo
- Publication number
- CN103881440A CN103881440A CN201410050691.6A CN201410050691A CN103881440A CN 103881440 A CN103881440 A CN 103881440A CN 201410050691 A CN201410050691 A CN 201410050691A CN 103881440 A CN103881440 A CN 103881440A
- Authority
- CN
- China
- Prior art keywords
- parts
- minute
- glass resin
- paint
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种玻璃树脂LED散热涂料，由下列重量份的原料制成：氯化聚丙烯树脂6-8、甲基丙烯酸丁酯10-13、玻璃树脂50-60、气相白炭黑8-13、铬络合物偶联剂3-6、间苯二甲胺5-7、硬脂酰苯甲酰甲烷3-5、二苯甲酮1-2、丁基卡必醇19-22、成膜助剂4-5。本发明涂料薄膜坚硬透明、绝缘性能好，且具有耐摩擦、耐热、耐老化、耐辐射、低温不脆化、疏水、防潮、无毒、透光率强的优点；而且通过添加气相白炭黑，增加了涂料的耐磨性和散热性。本发明的成膜助剂，使涂料成膜性好，易于涂装。
Description
技术领域
本发明属于涂料技术领域，特别涉及一种玻璃树脂LED散热涂料及其制备方法。
背景技术
随着LED灯使用范围的迅速扩大，延长LED灯使用寿命也已成为急需解决的问题,LED功率加大，散热问题也就越来越被人注重。目前采用导热胶解决 LED 灯散热问题，但是其所使用的材料存在耐温与耐老化比较差，对基材粘结力小、散热效果不佳以及施工不便的技术问题，难以满足人们对 LED 灯散热的要求。
发明内容
本发明的目的是提供一种玻璃树脂LED散热涂料及其制备方法，本发明涂料具有坚硬透明、绝缘性能好、耐摩擦、耐热、耐老化、耐辐射、低温不脆化、疏水、防潮、无毒、透光率强、散热性好的优点。
本发明所采用的技术方案是：
一种玻璃树脂LED散热涂料，其特征在于由下列重量份的原料制成：氯化聚丙烯树脂6-8、甲基丙烯酸丁酯10-13、玻璃树脂50-60、气相白炭黑8-13、铬络合物偶联剂3-6、间苯二甲胺5-7、硬脂酰苯甲酰甲烷3-5、二苯甲酮1-2、丁基卡必醇19-22、成膜助剂4-5。
所述的成膜助剂由以下重量份的原料制得：乙二醇乙醚醋酸酯6-9、2-氧乙酸基丁导酸2-4、丙烯酸3-5、聚乙烯醇缩丁醛2-4、六甲基磷酰三胺3-5、乙酸香叶酯3-5、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.5-1、羟甲基丙基纤维素2-3、纳米甲壳素0.3-0.5、可塑性淀粉1-2、过氧化乙酰0.2-0.4、丙二醇单甲醚乙酸酯15-18；制备方法是：将乙二醇乙醚醋酸酯、六甲基磷酰三胺、乙酸香叶酯、羟甲基丙基纤维素、纳米甲壳素、可塑性淀粉、丙二醇单甲醚乙酸酯混合，搅拌5-10分钟，加热至60-70℃，在4000-6000转/分下搅拌18-25分钟，再加入2-氧乙酸基丁导酸、丙烯酸、聚乙烯醇缩丁醛、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，搅拌反应15-30分钟；再降温至20-25℃，再加入其它剩余成分，搅拌反应45-60分钟，即得。
所述的玻璃树脂LED散热涂料的制备方法，其特征在于包括以下步骤：将二苯甲酮、丁基卡必醇、甲基丙烯酸丁酯混合，在1100-1300转/分下搅拌反应10-20分钟，加入玻璃树脂、铬络合物偶联剂、间苯二甲胺、硬脂酰苯甲酰甲烷，继续搅拌20-30分钟，再加入其它剩余成分，继续搅拌反应40-50分钟，研磨得到浆料，即得。
本发明的有益效果
本发明涂料薄膜坚硬透明、绝缘性能好，且具有耐摩擦、耐热、耐老化、耐辐射、低温不脆化、疏水、防潮、无毒、透光率强的优点；而且通过添加气相白炭黑，增加了涂料的耐磨性和散热性。本发明的成膜助剂，使涂料成膜性好，易于涂装。
具体实施方式
一种玻璃树脂LED散热涂料，由下列重量份（公斤）的原料制成：氯化聚丙烯树脂7、甲基丙烯酸丁酯12、玻璃树脂55、气相白炭黑11、铬络合物偶联剂4、间苯二甲胺6、硬脂酰苯甲酰甲烷4、二苯甲酮1.5、丁基卡必醇21、成膜助剂4.5。
所述的成膜助剂由以下重量份（公斤）的原料制得：乙二醇乙醚醋酸酯8、2-氧乙酸基丁导酸3、丙烯酸4、聚乙烯醇缩丁醛3、六甲基磷酰三胺4、乙酸香叶酯4、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.7、羟甲基丙基纤维素2.5、纳米甲壳素0.4、可塑性淀粉1.5、过氧化乙酰0.3、丙二醇单甲醚乙酸酯17；制备方法是：将乙二醇乙醚醋酸酯、六甲基磷酰三胺、乙酸香叶酯、羟甲基丙基纤维素、纳米甲壳素、可塑性淀粉、丙二醇单甲醚乙酸酯混合，搅拌8分钟，加热至65℃，在5000转/分下搅拌20分钟，再加入2-氧乙酸基丁导酸、丙烯酸、聚乙烯醇缩丁醛、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，搅拌反应26分钟；再降温至24℃，再加入其它剩余成分，搅拌反应50分钟，即得。
所述的玻璃树脂LED散热涂料的制备方法，包括以下步骤：将二苯甲酮、丁基卡必醇、甲基丙烯酸丁酯混合，在1200转/分下搅拌反应15分钟，加入玻璃树脂、铬络合物偶联剂、间苯二甲胺、硬脂酰苯甲酰甲烷，继续搅拌25分钟，再加入其它剩余成分，继续搅拌反应45分钟，研磨得到浆料，即得。
将本发明涂料涂于LED壳体上，在80℃和300W 紫外光辐照条件下人工加速老化试验，耐老化时间4500小时，耐温高温260℃，粘结剪切力16MPa.，导热系数270 W/(m·℃）。
Claims (2)
1.一种玻璃树脂LED散热涂料，其特征在于由下列重量份的原料制成：氯化聚丙烯树脂6-8、甲基丙烯酸丁酯10-13、玻璃树脂50-60、气相白炭黑8-13、铬络合物偶联剂3-6、间苯二甲胺5-7、硬脂酰苯甲酰甲烷3-5、二苯甲酮1-2、丁基卡必醇19-22、成膜助剂4-5；
所述的成膜助剂由以下重量份的原料制得：乙二醇乙醚醋酸酯6-9、2-氧乙酸基丁导酸2-4、丙烯酸3-5、聚乙烯醇缩丁醛2-4、六甲基磷酰三胺3-5、乙酸香叶酯3-5、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.5-1、羟甲基丙基纤维素2-3、纳米甲壳素0.3-0.5、可塑性淀粉1-2、过氧化乙酰0.2-0.4、丙二醇单甲醚乙酸酯15-18；制备方法是：将乙二醇乙醚醋酸酯、六甲基磷酰三胺、乙酸香叶酯、羟甲基丙基纤维素、纳米甲壳素、可塑性淀粉、丙二醇单甲醚乙酸酯混合，搅拌5-10分钟，加热至60-70℃，在4000-6000转/分下搅拌18-25分钟，再加入2-氧乙酸基丁导酸、丙烯酸、聚乙烯醇缩丁醛、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，搅拌反应15-30分钟；再降温至20-25℃，再加入其它剩余成分，搅拌反应45-60分钟，即得。
2.根据权利要求1所述的玻璃树脂LED散热涂料的制备方法，其特征在于包括以下步骤：将二苯甲酮、丁基卡必醇、甲基丙烯酸丁酯混合，在1100-1300转/分下搅拌反应10-20分钟，加入玻璃树脂、铬络合物偶联剂、间苯二甲胺、硬脂酰苯甲酰甲烷，继续搅拌20-30分钟，再加入其它剩余成分，继续搅拌反应40-50分钟，研磨得到浆料，即得。