CN103881441A - 一种led散热涂料及其制备方法 - Google Patents

一种led散热涂料及其制备方法 Download PDF

Info

Publication number
CN103881441A
CN103881441A CN201410050703.5A CN201410050703A CN103881441A CN 103881441 A CN103881441 A CN 103881441A CN 201410050703 A CN201410050703 A CN 201410050703A CN 103881441 A CN103881441 A CN 103881441A
Authority
CN
China
Prior art keywords
parts
minute
propyl
acid
acrylate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410050703.5A
Other languages
English (en)
Inventor
程实
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410050703.5A priority Critical patent/CN103881441A/zh
Publication of CN103881441A publication Critical patent/CN103881441A/zh
Pending legal-status Critical Current

Abstract

一种LED散热涂料，由下列重量份的原料制成：有机硅树脂30-35、丙烯酸酯10-15、含氟(甲基)丙烯酸酯3-5、马来酸酐1-2、抗氧剂10100.3-0.6、过氧化二异丙苯0.1-0.2、醋酸丁酯22-24、乌洛托品2-4、异丙基三（二辛基焦磷酸酰氧基）钛酸酯2-4、超细硫酸钡6-8、活性氧化铝1-2、膨化石墨3-5、乳木果油1-2、成膜助剂3-4。本发明涂料粘结力大，对金属、塑料等表面均有良好的附着力，而且热稳定性好，可以在200℃下长期使用，而力学性能不变；通过添加超细硫酸钡、活性氧化铝、膨化石墨、乳木果油，使得涂料体系稳定性好，易于涂装，涂料的散热性好，大大延长了灯具的使用寿命。

Description

一种LED散热涂料及其制备方法
技术领域
本发明属于涂料技术领域，特别涉及一种LED散热涂料及其制备方法。
背景技术
随着LED灯使用范围的迅速扩大，延长LED灯使用寿命也已成为急需解决的问题,LED功率加大，散热问题也就越来越被人注重。目前采用导热胶解决 LED 灯散热问题，但是其所使用的材料存在耐温与耐老化比较差，对基材粘结力小、散热效果不佳以及施工不便的技术问题，难以满足人们对 LED 灯散热的要求。
发明内容
本发明的目的是提供一种LED散热涂料及其制备方法，本发明涂料具有耐老化、散热系数大的优点。
本发明所采用的技术方案是：
一种LED散热涂料，其特征在于由下列重量份的原料制成：有机硅树脂30-35、丙烯酸酯10-15、含氟(甲基)丙烯酸酯3-5、马来酸酐1-2、抗氧剂1010 0.3-0.6、过氧化二异丙苯0.1-0.2、醋酸丁酯22-24、乌洛托品2-4、异丙基三（二辛基焦磷酸酰氧基）钛酸酯2-4、超细硫酸钡6-8、活性氧化铝1-2、膨化石墨3-5、乳木果油1-2、成膜助剂3-4。
所述的成膜助剂由以下重量份的原料制得：乙二醇乙醚醋酸酯6-9、2-氧乙酸基丁导酸2-4、丙烯酸3-5、聚乙烯醇缩丁醛2-4、六甲基磷酰三胺3-5、乙酸香叶酯3-5、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.5-1、羟甲基丙基纤维素2-3、纳米甲壳素0.3-0.5、可塑性淀粉1-2、过氧化乙酰0.2-0.4、丙二醇单甲醚乙酸酯15-18；制备方法是：将乙二醇乙醚醋酸酯、六甲基磷酰三胺、乙酸香叶酯、羟甲基丙基纤维素、纳米甲壳素、可塑性淀粉、丙二醇单甲醚乙酸酯混合，搅拌5-10分钟，加热至60-70℃，在4000-6000转/分下搅拌18-25分钟，再加入2-氧乙酸基丁导酸、丙烯酸、聚乙烯醇缩丁醛、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，搅拌反应15-30分钟；再降温至20-25℃，再加入其它剩余成分，搅拌反应45-60分钟，即得。
所述的LED散热涂料的制备方法，其特征在于包括以下步骤：将丙烯酸酯、含氟(甲基)丙烯酸酯、醋酸丁酯、超细硫酸钡、活性氧化铝、膨化石墨、乳木果油混合，在1100-1300转/分下搅拌反应10-20分钟，然后，升温至40-50℃，加入有机硅树脂、马来酸酐、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，继续搅拌20-30分钟，再加入其它剩余成分，继续搅拌反应30-40分钟，研磨得到浆料，即得。
本发明的有益效果
本发明涂料粘结力大，对金属、塑料等表面均有良好的附着力，而且热稳定性好，耐老化，可以在 200℃下长期使用，而力学性能不变；通过添加超细硫酸钡、活性氧化铝、膨化石墨、乳木果油，使得涂料体系稳定性好，而且易于涂装，涂料的散热性好，大大延长了灯具的使用寿命。
具体实施方式
一种LED散热涂料，由下列重量份(公斤)的原料制成：有机硅树脂33、丙烯酸酯13、含氟(甲基)丙烯酸酯4、马来酸酐1.5、抗氧剂1010 0.4、过氧化二异丙苯0.1、醋酸丁酯23、乌洛托品3、异丙基三（二辛基焦磷酸酰氧基）钛酸酯3、超细硫酸钡7、活性氧化铝1.5、膨化石墨4、乳木果油1.5、成膜助剂3.5。
    所述的成膜助剂由以下重量份（公斤）的原料制得：乙二醇乙醚醋酸酯8、2-氧乙酸基丁导酸3、丙烯酸4、聚乙烯醇缩丁醛3、六甲基磷酰三胺4、乙酸香叶酯4、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.7、羟甲基丙基纤维素2.5、纳米甲壳素0.4、可塑性淀粉1.5、过氧化乙酰0.3、丙二醇单甲醚乙酸酯17；制备方法是：将乙二醇乙醚醋酸酯、六甲基磷酰三胺、乙酸香叶酯、羟甲基丙基纤维素、纳米甲壳素、可塑性淀粉、丙二醇单甲醚乙酸酯混合，搅拌8分钟，加热至65℃，在5000转/分下搅拌20分钟，再加入2-氧乙酸基丁导酸、丙烯酸、聚乙烯醇缩丁醛、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，搅拌反应26分钟；再降温至24℃，再加入其它剩余成分，搅拌反应50分钟，即得。
所述的LED散热涂料的制备方法，包括以下步骤：将丙烯酸酯、含氟(甲基)丙烯酸酯、醋酸丁酯、超细硫酸钡、活性氧化铝、膨化石墨、乳木果油混合，在1200转/分下搅拌反应15分钟，然后，升温至45℃，加入有机硅树脂、马来酸酐、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，继续搅拌25分钟，再加入其它剩余成分，继续搅拌反应35分钟，研磨得到浆料，即得。
将本发明涂料涂于LED壳体上，在80℃和300W 紫外光辐照条件下人工加速老化试验，耐老化时间4400小时，耐温高温260℃，粘结剪切力16MPa.，导热系数270 W/(m·℃）。

Claims (2)

1.一种LED散热涂料，其特征在于由下列重量份的原料制成：有机硅树脂30-35、丙烯酸酯10-15、含氟(甲基)丙烯酸酯3-5、马来酸酐1-2、抗氧剂1010 0.3-0.6、过氧化二异丙苯0.1-0.2、醋酸丁酯22-24、乌洛托品2-4、异丙基三（二辛基焦磷酸酰氧基）钛酸酯2-4、超细硫酸钡6-8、活性氧化铝1-2、膨化石墨3-5、乳木果油1-2、成膜助剂3-4；
 所述的成膜助剂由以下重量份的原料制得：乙二醇乙醚醋酸酯6-9、2-氧乙酸基丁导酸2-4、丙烯酸3-5、聚乙烯醇缩丁醛2-4、六甲基磷酰三胺3-5、乙酸香叶酯3-5、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.5-1、羟甲基丙基纤维素2-3、纳米甲壳素0.3-0.5、可塑性淀粉1-2、过氧化乙酰0.2-0.4、丙二醇单甲醚乙酸酯15-18；制备方法是：将乙二醇乙醚醋酸酯、六甲基磷酰三胺、乙酸香叶酯、羟甲基丙基纤维素、纳米甲壳素、可塑性淀粉、丙二醇单甲醚乙酸酯混合，搅拌5-10分钟，加热至60-70℃，在4000-6000转/分下搅拌18-25分钟，再加入2-氧乙酸基丁导酸、丙烯酸、聚乙烯醇缩丁醛、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，搅拌反应15-30分钟；再降温至20-25℃，再加入其它剩余成分，搅拌反应45-60分钟，即得。
2.根据权利要求1所述的LED散热涂料的制备方法，其特征在于包括以下步骤：将丙烯酸酯、含氟(甲基)丙烯酸酯、醋酸丁酯、超细硫酸钡、活性氧化铝、膨化石墨、乳木果油混合，在1100-1300转/分下搅拌反应10-20分钟，然后，升温至40-50℃，加入有机硅树脂、马来酸酐、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，继续搅拌20-30分钟，再加入其它剩余成分，继续搅拌反应30-40分钟，研磨得到浆料，即得。
CN201410050703.5A 2014-02-14 2014-02-14 一种led散热涂料及其制备方法 Pending CN103881441A (zh)