CN103555195A - 一种led灯的氮化铝散热涂料及其制备方法 - Google Patents

一种led灯的氮化铝散热涂料及其制备方法 Download PDF

Info

Publication number
CN103555195A
CN103555195A CN201310440545.XA CN201310440545A CN103555195A CN 103555195 A CN103555195 A CN 103555195A CN 201310440545 A CN201310440545 A CN 201310440545A CN 103555195 A CN103555195 A CN 103555195A
Authority
CN
China
Prior art keywords
parts
paint
minute
heat radiation
led lamp
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310440545.XA
Other languages
English (en)
Inventor
徐家君
缪晨生
徐升亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANCHANG TIANTAI OPTOELECTRONIC TECHNOLOGY Co Ltd
Original Assignee
TIANCHANG TIANTAI OPTOELECTRONIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANCHANG TIANTAI OPTOELECTRONIC TECHNOLOGY Co Ltd filed Critical TIANCHANG TIANTAI OPTOELECTRONIC TECHNOLOGY Co Ltd
Priority to CN201310440545.XA priority Critical patent/CN103555195A/zh
Publication of CN103555195A publication Critical patent/CN103555195A/zh
Pending legal-status Critical Current

Abstract

一种LED灯的氮化铝散热涂料，由下列重量份的原料制成：有机硅树脂45-48、聚酰胺多胺环氧氯丙烷树脂4-6、三甲基六亚甲基二胺TMD4-6、氮化铝22-24、氮化硼3-5、纳米空心微珠2-3、硅溶胶1-2、桐油2-3、醋酸乙酯14-17、2-丁氧基-乙醇7-9、邻苯二甲酸聚酯3-5、异戊二烯2-3、异丙醇2-3、成膜助剂3-4。本发明通过加入氮化铝粉，导热速率高，散热效果好；通过加入氮化硼，加强了散热效果，耐热老化；通过加入硅溶胶，增强了粘结力，使涂料牢固，又能抗污防尘、耐老化、防火等功能；本涂料使用有机硅树脂作为基材，绝缘性好，有优异的热氧化稳定性。

Description

一种LED灯的氮化铝散热涂料及其制备方法
技术领域
本发明属于涂料技术领域，涉及一种散热涂料，更具体地说，是一种LED灯的氮化铝散热涂料及其制备方法。
背景技术
跟着近些年来LED技能作为新一代照明技能受到了广泛注重，LED功率加大，散热疑问也就越来越被人注重。目前大部分采用导热胶解决LED 灯散热问题，但是其所使用的材料存在耐温与耐老化较差以及对基材粘接力小、散热效果不佳和操作不便的技术问题，难以满足人们对LED 灯散热的要求。也有的厂家朝着选用具有较高热传导率的材料着手，但是会增大LED 的生产成本。
发明内容
本发明的目的是提供一种LED灯的氮化铝散热涂料及其制备方法，本发明涂料具有粘结力强，抗污防尘，耐老化、散热系数大的优点。
本发明所采用的技术方案是：
一种LED灯的氮化铝散热涂料，其特征在于由下列重量份的原料制成：有机硅树脂45-48、聚酰胺多胺环氧氯丙烷树脂4-6、三甲基六亚甲基二胺TMD 4-6、氮化铝22-24、氮化硼3-5、纳米空心微珠2-3、硅溶胶1-2、桐油2-3、醋酸乙酯14-17、2-丁氧基-乙醇7-9、邻苯二甲酸聚酯3-5、异戊二烯2-3、异丙醇2-3、成膜助剂3-4；
    所述的成膜助剂由以下重量份的原料制得：纳米玉石粉1-2、硅烷偶联剂KH-550 1-2、醇酯十二3-4、聚异丁烯1-2、聚乙烯醇缩丁醛1-2、2- 氨基-2-甲基-1-丙醇2-3、衣康酸酯3-4、吗啉2-3、1-羟乙基-2-油基咪唑啉0.2-0.3、二甲苯8-10、过氧化叔戊酸叔丁酯0.3-0.4、乙酯乙酯14-15；制备方法是：将纳米玉石粉、聚异丁烯、聚乙烯醇缩丁醛、2- 氨基-2-甲基-1-丙醇混合，加入到乙酸乙酯与二甲苯混合溶剂中，搅拌5-10分钟，加热至70-75℃，1000-1500转/分下搅拌15-30分钟，再加入醇酯十二、硅烷偶联剂KH550、1-羟乙基-2-油基咪唑啉，搅拌反应15-30分钟，再加入其它剩余成分，搅拌反应45-60分钟，即得。
所述的LED灯的氮化铝散热涂料的制备方法，其特征在于包括以下步骤：将氮化铝、氮化硼、纳米空心微珠、醋酸乙酯、2-丁氧基-乙醇混合，加热至60-70℃，1000-1200转/分下搅拌30-40分钟，然后，升温至70-85℃，加入有机硅树脂、聚酰胺多胺环氧氯丙烷树脂、三甲基六亚甲基二胺TMD、异戊二烯，继续搅拌30-40分钟，再加入其它剩余成分，继续搅拌反应70-80分钟，研磨得到浆料，即得。
本发明的有益效果
本发明通过加入氮化铝粉，导热速率高，散热效果好；通过加入氮化硼，加强了散热效果，耐热老化；通过加入硅溶胶，增强了粘结力，使涂料牢固，又能抗污防尘、耐老化、防火等功能；本涂料使用有机硅树脂作为基材，绝缘性好，有优异的热氧化稳定性。
具体实施方式
一种LED灯的氮化铝散热涂料，由下列重量份（公斤）的原料制成：有机硅树脂47、聚酰胺多胺环氧氯丙烷树脂5、三甲基六亚甲基二胺TMD 5、氮化铝23、氮化硼4、纳米空心微珠2、硅溶胶1、桐油2、醋酸乙酯16、2-丁氧基-乙醇8、邻苯二甲酸聚酯4、异戊二烯2、异丙醇2、成膜助剂3；
所述的成膜助剂由以下重量份（公斤）的原料制得：纳米玉石粉1、硅烷偶联剂KH-550 1、醇酯十二3、聚异丁烯1、聚乙烯醇缩丁醛1、2- 氨基-2-甲基-1-丙醇2、衣康酸酯3、吗啉2、1-羟乙基-2-油基咪唑啉0.2、二甲苯9、过氧化叔戊酸叔丁酯0.3、乙酯乙酯14；制备方法是：将纳米玉石粉、聚异丁烯、聚乙烯醇缩丁醛、2- 氨基-2-甲基-1-丙醇混合，加入到乙酸乙酯与二甲苯混合溶剂中，搅拌7分钟，加热至70℃，1300转/分下搅拌20分钟，再加入醇酯十二、硅烷偶联剂KH550、1-羟乙基-2-油基咪唑啉，搅拌反应20分钟，再加入其它剩余成分，搅拌反应50分钟，即得。
所述的LED灯的氮化铝散热涂料的制备方法，包括以下步骤：将氮化铝、氮化硼、纳米空心微珠、醋酸乙酯、2-丁氧基-乙醇混合，加热至65℃，1100转/分下搅拌35分钟，然后，升温至80℃，加入有机硅树脂、聚酰胺多胺环氧氯丙烷树脂、三甲基六亚甲基二胺TMD、异戊二烯，继续搅拌35分钟，再加入其它剩余成分，继续搅拌反应75分钟，研磨得到浆料，即得。
将本发明涂料涂于LED灯壳体上，在80℃和300W 紫外光辐照条件下人工加速老化试验，耐老化时间6000 小时，耐温高温280℃，粘结剪切力19MPa.，导热系数280W/（m·K）。

Claims (2)

1.一种LED灯的氮化铝散热涂料，其特征在于由下列重量份的原料制成：有机硅树脂45-48、聚酰胺多胺环氧氯丙烷树脂4-6、三甲基六亚甲基二胺TMD 4-6、氮化铝22-24、氮化硼3-5、纳米空心微珠2-3、硅溶胶1-2、桐油2-3、醋酸乙酯14-17、2-丁氧基-乙醇7-9、邻苯二甲酸聚酯3-5、异戊二烯2-3、异丙醇2-3、成膜助剂3-4；
    所述的成膜助剂由以下重量份的原料制得：纳米玉石粉1-2、硅烷偶联剂KH-550 1-2、醇酯十二3-4、聚异丁烯1-2、聚乙烯醇缩丁醛1-2、2- 氨基-2-甲基-1-丙醇2-3、衣康酸酯3-4、吗啉2-3、1-羟乙基-2-油基咪唑啉0.2-0.3、二甲苯8-10、过氧化叔戊酸叔丁酯0.3-0.4、乙酯乙酯14-15；制备方法是：将纳米玉石粉、聚异丁烯、聚乙烯醇缩丁醛、2- 氨基-2-甲基-1-丙醇混合，加入到乙酸乙酯与二甲苯混合溶剂中，搅拌5-10分钟，加热至70-75℃，1000-1500转/分下搅拌15-30分钟，再加入醇酯十二、硅烷偶联剂KH550、1-羟乙基-2-油基咪唑啉，搅拌反应15-30分钟，再加入其它剩余成分，搅拌反应45-60分钟，即得。
2.根据权利要求1所述的LED灯的氮化铝散热涂料的制备方法，其特征在于包括以下步骤：将氮化铝、氮化硼、纳米空心微珠、醋酸乙酯、2-丁氧基-乙醇混合，加热至60-70℃，1000-1200转/分下搅拌30-40分钟，然后，升温至70-85℃，加入有机硅树脂、聚酰胺多胺环氧氯丙烷树脂、三甲基六亚甲基二胺TMD、异戊二烯，继续搅拌30-40分钟，再加入其它剩余成分，继续搅拌反应70-80分钟，研磨得到浆料，即得。
CN201310440545.XA 2013-09-25 2013-09-25 一种led灯的氮化铝散热涂料及其制备方法 Pending CN103555195A (zh)