CN103555130A - 一种led灯的散热涂料及其制备方法 - Google Patents

一种led灯的散热涂料及其制备方法 Download PDF

Info

Publication number
CN103555130A
CN103555130A CN201310440570.8A CN201310440570A CN103555130A CN 103555130 A CN103555130 A CN 103555130A CN 201310440570 A CN201310440570 A CN 201310440570A CN 103555130 A CN103555130 A CN 103555130A
Authority
CN
China
Prior art keywords
parts
minute
paint
heat radiation
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310440570.8A
Other languages
English (en)
Inventor
徐家君
缪晨生
徐升亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANCHANG TIANTAI OPTOELECTRONIC TECHNOLOGY Co Ltd
Original Assignee
TIANCHANG TIANTAI OPTOELECTRONIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANCHANG TIANTAI OPTOELECTRONIC TECHNOLOGY Co Ltd filed Critical TIANCHANG TIANTAI OPTOELECTRONIC TECHNOLOGY Co Ltd
Priority to CN201310440570.8A priority Critical patent/CN103555130A/zh
Publication of CN103555130A publication Critical patent/CN103555130A/zh
Pending legal-status Critical Current

Abstract

一种LED灯的散热涂料，由下列重量份的原料制成：E-12环氧树脂30-35、有机硅树脂12-15、四乙烯五胺5-7、氮化铝粉10-14、醋酸丁酯20-25、正丁醇4-6、三乙醇胺1-2、六亚甲基四胺1-2、乙烯基三(β-甲氧基乙氧基)硅烷2-3、钛白粉2-4、石墨粉1-2、石棉粉3-5、邻二甲苯酸二丁酯6-8、蓖麻油1-2、成膜助剂3-4。本发明通过加入氮化铝粉，导热速率高，散热效果好，可以在200℃下长期使用，而力学性能不变的优点；通过加入钛白粉，使该涂料具有屏蔽紫外线的功能，有益人体健康，通过加入石墨粉，润滑性好，易施工；而且涂料粘结力大、不易脱落、耐老化、使用寿命长。

Description

一种LED灯的散热涂料及其制备方法
技术领域
本发明属于涂料技术领域，涉及一种散热涂料，更具体地说，是一种LED灯的散热涂料及其制备方法。
背景技术
跟着近些年来LED技能作为新一代照明技能受到了广泛注重，LED功率加大，散热疑问也就越来越被人注重。目前大部分采用导热胶解决LED 灯散热问题，但是其所使用的材料存在耐温与耐老化较差以及对基材粘接力小、散热效果不佳和操作不便的技术问题，难以满足人们对LED 灯散热的要求。也有的厂家朝着选用具有较高热传导率的材料着手，但是会增大LED 的生产成本。
发明内容
本发明的目的是提供一种LED灯的散热涂料及其制备方法，本发明涂料具有粘结力大，耐老化、散热系数大、屏蔽紫外线的优点。
本发明所采用的技术方案是：
一种LED灯的散热涂料，其特征在于由下列重量份的原料制成：E-12环氧树脂30-35、有机硅树脂12-15、四乙烯五胺5-7、氮化铝粉10-14、醋酸丁酯20-25、正丁醇4-6、三乙醇胺1-2、六亚甲基四胺1-2、乙烯基三(β-甲氧基乙氧基)硅烷2-3、钛白粉2-4、石墨粉1-2、石棉粉3-5、邻二甲苯酸二丁酯6-8、蓖麻油1-2、成膜助剂3-4；
    所述的成膜助剂由以下重量份的原料制得：纳米玉石粉2-4、交联剂 TAC2-3、醇酯十二4-5、硅烷偶联剂KH550 1-2、苯乙烯3-4、蓖麻油酸1-2、顺丁烯二酸酐2-3、吗啉2-3、过氧化叔戊酸叔丁酯0.3-0.4、异氟尔酮1-2、二甲苯4-5、乙酸乙酯12-13；制备方法是：将纳米玉石粉、吗啉、苯乙烯、蓖麻油酸混合，加入到乙酸乙酯与二甲苯混合溶剂中，搅拌5-10分钟，加热至65-70℃，800-1200转/分下搅拌15-30分钟，再加入醇酯十二、硅烷偶联剂KH550、顺丁烯二酸酐，搅拌反应15-30分钟，再加入其它剩余成分，搅拌反应45-60分钟，即得。
所述的LED灯的散热涂料的制备方法，其特征在于包括以下步骤：将醋酸丁酯、氮化铝粉、正丁醇、三乙醇胺、乙烯基三(β-甲氧基乙氧基)硅烷混合，加热至60-70℃，搅拌反应30-40分钟，然后，升温至75-80℃，加入E-12环氧树脂、有机硅树脂、四乙烯五胺，在1400-1800转/分下搅拌30-40分钟，再加入其它剩余成分，在1400-1800转/分下继续搅拌反应60-80分钟，研磨得到浆料，即得。
本发明的有益效果
本发明通过加入氮化铝粉，导热速率高，散热效果好，可以在200℃下长期使用，而力学性能不变的优点；通过加入钛白粉，使该涂料具有屏蔽紫外线的功能，有益人体健康，通过加入石墨粉，润滑性好，易施工；而且涂料粘结力大、不易脱落、耐老化、使用寿命长。
具体实施方式
一种LED灯的散热涂料，由下列重量份（公斤）的原料制成：E-12环氧树脂32、有机硅树脂13、四乙烯五胺6、氮化铝粉13、醋酸丁酯22、正丁醇5、三乙醇胺1、六亚甲基四胺1、乙烯基三(β-甲氧基乙氧基)硅烷2、钛白粉3、石墨粉1、石棉粉4、邻二甲苯酸二丁酯7、蓖麻油1、成膜助剂3；
    所述的成膜助剂由以下重量份（公斤）的原料制得：纳米玉石粉3、交联剂 TAC2、醇酯十二4、硅烷偶联剂KH550 1、苯乙烯3、蓖麻油酸1、顺丁烯二酸酐2、吗啉2、过氧化叔戊酸叔丁酯0.3、异氟尔酮1、二甲苯4、乙酸乙酯12；制备方法是：将纳米玉石粉、吗啉、苯乙烯、蓖麻油酸混合，加入到乙酸乙酯与二甲苯混合溶剂中，搅拌8分钟，加热至65℃，1000转/分下搅拌20分钟，再加入醇酯十二、硅烷偶联剂KH550、顺丁烯二酸酐，搅拌反应20分钟，再加入其它剩余成分，搅拌反应50分钟，即得。
所述的LED灯的散热涂料的制备方法，包括以下步骤：将醋酸丁酯、氮化铝粉、正丁醇、三乙醇胺、乙烯基三(β-甲氧基乙氧基)硅烷混合，加热至65℃，搅拌反应35分钟，然后升温至75℃，加入E-12环氧树脂、有机硅树脂、四乙烯五胺，在1600转/分下搅拌35分钟，再加入其它剩余成分，在1600转/分下继续搅拌反应70分钟，研磨得到浆料，即得。
将本发明涂料涂于LED灯壳体上，在80℃和300W 紫外光辐照条件下人工加速老化试验，耐老化时间4900 小时，耐温高温250℃，粘结剪切力17MPa.，导热系数250W/（m·K）。

Claims (2)

1.一种LED灯的散热涂料，其特征在于由下列重量份的原料制成：E-12环氧树脂30-35、有机硅树脂12-15、四乙烯五胺5-7、氮化铝粉10-14、醋酸丁酯20-25、正丁醇4-6、三乙醇胺1-2、六亚甲基四胺1-2、乙烯基三(β-甲氧基乙氧基)硅烷2-3、钛白粉2-4、石墨粉1-2、石棉粉3-5、邻二甲苯酸二丁酯6-8、蓖麻油1-2、成膜助剂3-4；
    所述的成膜助剂由以下重量份的原料制得：纳米玉石粉2-4、交联剂 TAC2-3、醇酯十二4-5、硅烷偶联剂KH550 1-2、苯乙烯3-4、蓖麻油酸1-2、顺丁烯二酸酐2-3、吗啉2-3、过氧化叔戊酸叔丁酯0.3-0.4、异氟尔酮1-2、二甲苯4-5、乙酸乙酯12-13；制备方法是：将纳米玉石粉、吗啉、苯乙烯、蓖麻油酸混合，加入到乙酸乙酯与二甲苯混合溶剂中，搅拌5-10分钟，加热至65-70℃，800-1200转/分下搅拌15-30分钟，再加入醇酯十二、硅烷偶联剂KH550、顺丁烯二酸酐，搅拌反应15-30分钟，再加入其它剩余成分，搅拌反应45-60分钟，即得。
2.根据权利要求1所述的LED灯的散热涂料的制备方法，其特征在于包括以下步骤：将醋酸丁酯、氮化铝粉、正丁醇、三乙醇胺、乙烯基三(β-甲氧基乙氧基)硅烷混合，加热至60-70℃，搅拌反应30-40分钟，然后，升温至75-80℃，加入E-12环氧树脂、有机硅树脂、四乙烯五胺，在1400-1800转/分下搅拌30-40分钟，再加入其它剩余成分，在1400-1800转/分下继续搅拌反应60-80分钟，研磨得到浆料，即得。
CN201310440570.8A 2013-09-25 2013-09-25 一种led灯的散热涂料及其制备方法 Pending CN103555130A (zh)