CN103881480A - 一种阻透性led散热涂料及其制备方法 - Google Patents

一种阻透性led散热涂料及其制备方法 Download PDF

Info

Publication number
CN103881480A
CN103881480A CN201410050693.5A CN201410050693A CN103881480A CN 103881480 A CN103881480 A CN 103881480A CN 201410050693 A CN201410050693 A CN 201410050693A CN 103881480 A CN103881480 A CN 103881480A
Authority
CN
China
Prior art keywords
parts
minute
favorable
nano
stirring reaction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410050693.5A
Other languages
English (en)
Inventor
程实
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410050693.5A priority Critical patent/CN103881480A/zh
Publication of CN103881480A publication Critical patent/CN103881480A/zh
Pending legal-status Critical Current

Abstract

一种阻透性LED散热涂料，由下列重量份的原料制成：EVOH树脂55-60、聚芳酰胺浆粕10-14、钛白粉10-14、玻璃纤维4-7、2-丁氧基-乙醇20-25、二苯甲酰基联苯0.1-0.2、硫酸铵2-3、三羟甲基丙烷2-4、柠檬酸三乙酯2-3、成膜助剂3-4。本发明涂料使用了EVOH树脂，使得涂料阻透性好；同时添加了钛白粉，使得涂料分散性好、屏蔽紫外线性能好、耐候性好，耐老化性能好，大大延长了灯具的使用寿命。本发明的成膜助剂，使涂料成膜性好，易于涂装。

Description

一种阻透性LED散热涂料及其制备方法
技术领域
本发明属于涂料技术领域，特别涉及一种阻透性LED散热涂料及其制备方法。
背景技术
随着LED灯使用范围的迅速扩大，延长LED灯使用寿命也已成为急需解决的问题,LED功率加大，散热问题也就越来越被人注重。目前采用导热胶解决 LED 灯散热问题，但是其所使用的材料存在耐温与耐老化比较差，对基材粘结力小、散热效果不佳以及施工不便的技术问题，难以满足人们对 LED 灯散热的要求。
发明内容
本发明的目的是提供一种阻透性LED散热涂料及其制备方法，本发明涂料具有阻透性好、分散性好、屏蔽紫外线性能好、耐候性好、耐老化的优点。
本发明所采用的技术方案是：
一种阻透性LED散热涂料，其特征在于由下列重量份的原料制成：EVOH树脂55-60、聚芳酰胺浆粕10-14、钛白粉10-14、玻璃纤维4-7、2-丁氧基-乙醇20-25、二苯甲酰基联苯0.1-0.2、硫酸铵2-3、三羟甲基丙烷2-4、柠檬酸三乙酯2-3、成膜助剂3-4。
所述的成膜助剂由以下重量份的原料制得：月桂酸甲酯7-10、双环戊二烯3-5、丁烯二酸酐2-4、丙二醇丁醚3-5、1,6-己二醇二丙烯酸酯3-5、异丙基三（二辛基焦磷酸酰氧基）钛酸酯1-2、羧甲基纤维素2-4、纳米甲壳素1-2、纳米纤维素1-2、过氧化苯甲酸0.3-0.4、二乙二醇12-13；制备方法是：将二乙二醇、羧甲基纤维素、纳米甲壳素、纳米纤维素混合，搅拌5-10分钟，加热至60-70℃，在4000-6000转/分下搅拌18-25分钟，再加入月桂酸甲酯、双环戊二烯、丁烯二酸酐、丙二醇丁醚、1,6-己二醇二丙烯酸酯、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，搅拌反应15-30分钟；再降温至20-25℃，再加入其它剩余成分，搅拌反应45-60分钟，即得。
所述的阻透性LED散热涂料的制备方法，其特征在于包括以下步骤：将2-丁氧基-乙醇、柠檬酸三乙酯、硫酸铵、钛白粉混合，在1100-1300转/分下搅拌反应10-20分钟，然后升温至40-50℃，加入EVOH树脂、聚芳酰胺浆粕、二苯甲酰基联苯、三羟甲基丙烷，继续搅拌20-30分钟，再加入其它剩余成分，继续搅拌反应30-40分钟，研磨得到浆料，即得。
本发明的有益效果
本发明涂料使用了EVOH树脂，使得涂料阻透性好；同时添加了钛白粉，使得涂料分散性好、屏蔽紫外线性能好、耐候性好，耐老化性能好，大大延长了灯具的使用寿命。本发明的成膜助剂，使涂料成膜性好，易于涂装。
具体实施方式
一种阻透性LED散热涂料，由下列重量份(公斤)的原料制成：EVOH树脂55、聚芳酰胺浆粕12、钛白粉12、玻璃纤维6、2-丁氧基-乙醇23、二苯甲酰基联苯0.1、硫酸铵2.5、三羟甲基丙烷3、柠檬酸三乙酯2.5、成膜助剂3.5。
所述的成膜助剂由以下重量份（公斤）的原料制得：月桂酸甲酯8、双环戊二烯4、丁烯二酸酐3、丙二醇丁醚4、1,6-己二醇二丙烯酸酯4、异丙基三（二辛基焦磷酸酰氧基）钛酸酯1.5、羧甲基纤维素3、纳米甲壳素1.5、纳米纤维素1.5、过氧化苯甲酸0.3、二乙二醇12；制备方法是：将二乙二醇、羧甲基纤维素、纳米甲壳素、纳米纤维素混合，搅拌7分钟，加热至65℃，在5000转/分下搅拌22分钟，再加入月桂酸甲酯、双环戊二烯、丁烯二酸酐、丙二醇丁醚、1,6-己二醇二丙烯酸酯、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，搅拌反应20分钟；再降温至23℃，再加入其它剩余成分，搅拌反应50分钟，即得。
所述的阻透性LED散热涂料的制备方法，包括以下步骤：将2-丁氧基-乙醇、柠檬酸三乙酯、硫酸铵、钛白粉混合，在1200转/分下搅拌反应15分钟，然后升温至45℃，加入EVOH树脂、聚芳酰胺浆粕、二苯甲酰基联苯、三羟甲基丙烷，继续搅拌25分钟，再加入其它剩余成分，继续搅拌反应35分钟，研磨得到浆料，即得。
将本发明涂料涂于LED壳体上，在80℃和300W 紫外光辐照条件下人工加速老化试验，耐老化时间4600小时，耐温高温280℃，粘结剪切力20MPa.，导热系数280 W/(m·℃）。

Claims (2)

1.一种阻透性LED散热涂料，其特征在于由下列重量份的原料制成：EVOH树脂55-60、聚芳酰胺浆粕10-14、钛白粉10-14、玻璃纤维4-7、2-丁氧基-乙醇20-25、二苯甲酰基联苯0.1-0.2、硫酸铵2-3、三羟甲基丙烷2-4、柠檬酸三乙酯2-3、成膜助剂3-4；
所述的成膜助剂由以下重量份的原料制得：月桂酸甲酯7-10、双环戊二烯3-5、丁烯二酸酐2-4、丙二醇丁醚3-5、1,6-己二醇二丙烯酸酯3-5、异丙基三（二辛基焦磷酸酰氧基）钛酸酯1-2、羧甲基纤维素2-4、纳米甲壳素1-2、纳米纤维素1-2、过氧化苯甲酸0.3-0.4、二乙二醇12-13；制备方法是：将二乙二醇、羧甲基纤维素、纳米甲壳素、纳米纤维素混合，搅拌5-10分钟，加热至60-70℃，在4000-6000转/分下搅拌18-25分钟，再加入月桂酸甲酯、双环戊二烯、丁烯二酸酐、丙二醇丁醚、1,6-己二醇二丙烯酸酯、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，搅拌反应15-30分钟；再降温至20-25℃，再加入其它剩余成分，搅拌反应45-60分钟，即得。
2.根据权利要求1所述的阻透性LED散热涂料的制备方法，其特征在于包括以下步骤：将2-丁氧基-乙醇、柠檬酸三乙酯、硫酸铵、钛白粉混合，在1100-1300转/分下搅拌反应10-20分钟，然后升温至40-50℃，加入EVOH树脂、聚芳酰胺浆粕、二苯甲酰基联苯、三羟甲基丙烷，继续搅拌20-30分钟，再加入其它剩余成分，继续搅拌反应30-40分钟，研磨得到浆料，即得。
CN201410050693.5A 2014-02-14 2014-02-14 一种阻透性led散热涂料及其制备方法 Pending CN103881480A (zh)