CN103881270B - 一种耐水聚氯乙烯电缆绝缘料及其制备方法 - Google Patents

一种耐水聚氯乙烯电缆绝缘料及其制备方法 Download PDF

Info

Publication number
CN103881270B
CN103881270B CN201410116441.8A CN201410116441A CN103881270B CN 103881270 B CN103881270 B CN 103881270B CN 201410116441 A CN201410116441 A CN 201410116441A CN 103881270 B CN103881270 B CN 103881270B
Authority
CN
China
Prior art keywords
powder
zinc
polyvinyl chloride
water
hour
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410116441.8A
Other languages
English (en)
Other versions
CN103881270A (zh
Inventor
赵兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan Jinshuo plastic products Co., Ltd.
Original Assignee
MAANSHAN JIAYUAN ENVIRONMENTAL PROTECTION TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MAANSHAN JIAYUAN ENVIRONMENTAL PROTECTION TECHNOLOGY Co Ltd filed Critical MAANSHAN JIAYUAN ENVIRONMENTAL PROTECTION TECHNOLOGY Co Ltd
Priority to CN201410116441.8A priority Critical patent/CN103881270B/zh
Publication of CN103881270A publication Critical patent/CN103881270A/zh
Application granted granted Critical
Publication of CN103881270B publication Critical patent/CN103881270B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐水聚氯乙烯电缆绝缘料，其特征在于，由下列重量份的原料制成：SG-3PVC？60-65、煅烧陶土12-14、LLDPE20-23、钙锌稳定剂2-3、氰尿酸锌1-2、氧化锌2-3、硅烷偶联剂KH572？2-3、乙烯-醋酸乙烯共聚物10-12、硅灰石粉15-20、蒙脱石粉6-8、粘土粉13-15、硬脂酸锌2-3、三聚氰胺树脂5-7、对苯二甲酸酯15-17、间苯二甲酸酯8-10、助剂6-8；本发明的电缆绝缘料的抗拉强度高，耐水性能优良，可以长期使用在潮湿的环境中。

Description

一种耐水聚氯乙烯电缆绝缘料及其制备方法
技术领域
本发明涉及高分子材料领域，特别是一种耐水聚氯乙烯电缆绝缘料及其制备方法。
背景技术
PVC电缆料是以聚氯乙烯为基础树脂,添加稳定剂、邻苯二甲酸二辛酯，邻苯二甲酸二异癸酯，对苯二甲酸二辛酯、偏苯三酸三辛酯等增塑剂以及碳酸钙等无机填充物，助剂和润滑剂等添加剂,经过混配捏合挤出而制备的粒子。PVC电缆料可分为：聚氯乙烯绝缘电缆料、聚氯乙烯护套电缆料、阻燃聚氯乙烯绝缘电缆料、阻燃聚氯乙烯护套电缆料、聚氯乙烯弹性体电缆料、聚氯乙烯户外架空绝缘电缆。但是，随着电线电缆应用场合的扩展，对聚氯乙烯电缆料的要求的不断提高，目前的一般聚氯乙烯电缆绝缘料不能满足耐水的需求。
发明内容
本发明的目的是提供一种耐水聚氯乙烯电缆绝缘料及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种耐水聚氯乙烯电缆绝缘料，由下列重量份的原料制成：SG-3PVC60-65、煅烧陶土12-14、LLDPE20-23、钙锌稳定剂2-3、氰尿酸锌1-2、氧化锌2-3、硅烷偶联剂KH5722-3、乙烯-醋酸乙烯共聚物10-12、硅灰石粉15-20、蒙脱石粉6-8、粘土粉13-15、硬脂酸锌2-3、三聚氰胺树脂5-7、对苯二甲酸酯15-17、间苯二甲酸酯8-10、助剂6-8；
所述助剂由下列重量份的原料制成：硅藻土10-12、二缩三丙二醇二丙烯酸酯2-3、氧化锌5-6、玉石粉4-5、3-氨丙基三甲氧基硅烷2-3、交联剂TAC1-2、葡萄糖酸锌1-2、硬脂酸锌1-2、硝酸镁7-9、丁香油1-2、玫瑰精油0.1-0.2；制备方法是将硅藻土粉送入煅烧炉中在700-730℃下煅烧3-4小时，取出，送入10-15%盐酸中浸泡1-2小时，过滤得滤渣，用清水洗涤，烘干，粉碎成200-250目粉末，再将烘干的粉体与二缩三丙二醇二丙烯酸酯、氧化锌、交联剂TAC混合，研磨1-2小时，再加入其它剩余成分，混合研磨1-2小时，即得。
本发明所述耐水聚氯乙烯电缆绝缘料，由以下具体步骤制成：
（1）将SG-3PVC加热至熔融状态，加入煅烧陶土、LLDPE、钙锌稳定剂、氰尿酸锌、氧化锌、硅烷偶联剂KH572、乙烯-醋酸乙烯共聚物、硅灰石粉、蒙脱石粉、助剂，搅拌捏合18-25分钟，送入双螺杆挤出机造粒，得到A料；
（2）将三聚氰胺树脂加热至熔融状态，加入其它剩余成分，搅拌6-10分钟，送入双螺杆挤出机上熔融挤出造粒，得到B料；
（3）将A、B料混合均匀后，在双螺杆挤出机上熔融挤出造粒，即得。
本发明的优异效果是：本发明的电缆绝缘料的抗拉强度高，耐水性能优良，可以长期使用在潮湿的环境中。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种耐水聚氯乙烯电缆绝缘料，由下列重量份（公斤）的原料制成：SG-3PVC60、煅烧陶土12、LLDPE20、钙锌稳定剂2、氰尿酸锌1、氧化锌2、硅烷偶联剂KH5722、乙烯-醋酸乙烯共聚物10、硅灰石粉15、蒙脱石粉6、粘土粉13、硬脂酸锌2、三聚氰胺树脂5、对苯二甲酸酯15、间苯二甲酸酯8、助剂6；
所述助剂由下列重量份（公斤）的原料制成：硅藻土10、二缩三丙二醇二丙烯酸酯3、氧化锌5、玉石粉4、3-氨丙基三甲氧基硅烷2、交联剂TAC2、葡萄糖酸锌1、硬脂酸锌2、硝酸镁9、丁香油2、玫瑰精油0.1；制备方法是将硅藻土送入煅烧炉中在700-730℃下煅烧3-4小时，取出，送入10-15%盐酸中浸泡1-2小时，过滤得滤渣，用清水洗涤，烘干，粉碎成200-250目粉末，再将烘干的粉体与二缩三丙二醇二丙烯酸酯、氧化锌、交联剂TAC混合，研磨1-2小时，再加入其它剩余成分，混合研磨1-2小时，即得。
本发明所述耐水聚氯乙烯电缆绝缘料，由以下具体步骤制成：
（1）将SG-3PVC加热至熔融状态，加入煅烧陶土、LLDPE、钙锌稳定剂、氰尿酸锌、氧化锌、硅烷偶联剂KH572、乙烯-醋酸乙烯共聚物、硅灰石粉、蒙脱石粉、助剂，搅拌捏合18-25分钟，送入双螺杆挤出机造粒，得到A料；
（2）将三聚氰胺树脂加热至熔融状态，加入其它剩余成分，搅拌6-10分钟，送入双螺杆挤出机上熔融挤出造粒，得到B料；
（3）将A、B料混合均匀后，在双螺杆挤出机上熔融挤出造粒，即得。
对本发明材料进行了性能测试，主要情况如下：

Claims (1)

1.一种耐水聚氯乙烯电缆绝缘料，其特征在于，由下列重量份的原料制成：SG-3PVC60-65、煅烧陶土12-14、LLDPE20-23、钙锌稳定剂2-3、氰尿酸锌1-2、氧化锌2-3、硅烷偶联剂KH5722-3、乙烯-醋酸乙烯共聚物10-12、硅灰石粉15-20、蒙脱石粉6-8、粘土粉13-15、硬脂酸锌2-3、三聚氰胺树脂5-7、对苯二甲酸酯15-17、间苯二甲酸酯8-10、助剂6-8；
所述助剂由下列重量份的原料制成：硅藻土10-12、二缩三丙二醇二丙烯酸酯2-3、氧化锌5-6、玉石粉4-5、3-氨丙基三甲氧基硅烷2-3、交联剂TAC1-2、葡萄糖酸锌1-2、硬脂酸锌1-2、硝酸镁7-9、丁香油1-2、玫瑰精油0.1-0.2；制备方法是将硅藻土送入煅烧炉中在700-730℃下煅烧3-4小时，取出，送入10-15%盐酸中浸泡1-2小时，过滤得滤渣，用清水洗涤，烘干，粉碎成200-250目粉末，再将烘干的粉体与二缩三丙二醇二丙烯酸酯、氧化锌、交联剂TAC混合，研磨1-2小时，再加入其它剩余成分，混合研磨1-2小时，即得；
所述耐水聚氯乙烯电缆绝缘料，由以下具体步骤制成：
（1）将SG-3PVC加热至熔融状态，加入煅烧陶土、LLDPE、钙锌稳定剂、氰尿酸锌、氧化锌、硅烷偶联剂KH572、乙烯-醋酸乙烯共聚物、硅灰石粉、蒙脱石粉、助剂，搅拌捏合18-25分钟，送入双螺杆挤出机造粒，得到A料；
（2）将三聚氰胺树脂加热至熔融状态，加入其它剩余成分，搅拌6-10分钟，送入双螺杆挤出机上熔融挤出造粒，得到B料；
（3）将A、B料混合均匀后，在双螺杆挤出机上熔融挤出造粒，即得。
CN201410116441.8A 2014-03-26 2014-03-26 一种耐水聚氯乙烯电缆绝缘料及其制备方法 Expired - Fee Related CN103881270B (zh)