CN103880325A - Diatomite wall material with dreamy effect and construction method thereof - Google Patents
Diatomite wall material with dreamy effect and construction method thereof Download PDFInfo
- Publication number
- CN103880325A CN103880325A CN201410040013.1A CN201410040013A CN103880325A CN 103880325 A CN103880325 A CN 103880325A CN 201410040013 A CN201410040013 A CN 201410040013A CN 103880325 A CN103880325 A CN 103880325A
- Authority
- CN
- China
- Prior art keywords
- wall material
- weight parts
- kieselguhr
- kieselguhr wall
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a diatomite wall material with a dreamy effect and a construction method thereof, and belongs to the field of a building material. The diatomite wall material with the dreamy effect contains the following components in parts by weight: 20-52 parts of 250-500 mesh calcined diatomite, 24-48 parts of 35-825 mesh silica sand powder, 10-30 parts of 325-1200 mesh natural color sand, 3-10 parts of nanometer titania, 0.4-1.2 parts of methylcellulose, and 6-20 parts of reusable dispersion emulsion powder. After the wall body is constructed by using the diatomite wall material with the dreamy effect and the construction method thereof provided by the invention, the product is beautiful in product, the texture is close to the dream adornment style of the royal family, and the requirements of people on the decorativeness of the diatomite wall material are met.
Description
Technical field
The present invention relates to building decoration field, particularly a kind of kieselguhr wall material and constructional method thereof with dreamlike effect.
Background technology
Diatomite is a kind of biogenic silicastone, it mainly by ancient times diatom remains formed, there is the characteristics such as exquisiteness, loose, light weight, porous, water-absorbent and perviousness be strong.Along with people are more and more higher to the requirement of the living environment feature of environmental protection, diatomite becomes the very welcome new indoor decoration material of one gradually, has added diatomaceous wall material and has had advantages such as regulating the room temperature, eliminate peculiar smell, absorption and decomposing harmful substances.At present, although utilize kieselguhr wall material can on wall body surface, produce certain texture, ornamental to increase it, still there is in this respect improved space.
In human development history, because the ascendancy of imperial noble to social life, imperial noble's building decoration has embodied a concentrated reflection of each epoch skillful craftsman's consummate technique, makes building decoration have high aesthetic value.But, use traditional finishing pattern to reach imperial noble's building decorative effect, there is distinct disadvantage long in time limit, expense is high, seriously limit the demand of general public.
Therefore,, if a kind of kieselguhr wall material and construction technology thereof with imperial noble's decorated style texture can be provided, must meet to a certain extent people to the ornamental requirement of kieselguhr wall material.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of kieselguhr wall material and constructional method thereof with dreamlike effect.
For solving the problems of the technologies described above, technical scheme provided by the invention is as follows:
There is a kieselguhr wall material for dreamlike effect, the component that contains following weight part:
250～500 order calcined diatomites: 20～52 weight parts;
35～825 order quartz sand powders: 24～48 weight parts;
325～1200 order natural colour sands: 10～30 weight parts;
Nano titanium oxide: 3～10 weight parts;
Methylcellulose gum: 0.4～1.2 weight part;
Redispersible latex powder: 6～20 weight parts;
The kieselguhr wall material further, with dreamlike effect also contains the component of following weight part:
Mineral dye: 1～30 weight part.
Preferably, described in there is the kieselguhr wall material of dreamlike effect, the content of each component is as follows:
250～500 order calcined diatomites: 30～42 weight parts;
175～725 order quartz sand powders: 30～40 weight parts;
550～1150 order natural colour sands: 15～25 weight parts;
Nano titanium oxide: 5～7 weight parts;
Methylcellulose gum: 0.7～0.9 weight part;
Redispersible latex powder: 12～14 weight parts.
The kieselguhr wall material further, with dreamlike effect also contains the component of following weight part:
Mineral dye: 1～30 weight part.
More preferably, described in there is the kieselguhr wall material of dreamlike effect, the content of each component is as follows:
250～500 order calcined diatomites: 36 weight parts;
225～675 order quartz sand powders: 36 weight parts;
625～925 order natural colour sands: 20 weight parts;
Nano titanium oxide: 6 weight parts;
Methylcellulose gum: 0.8 weight part;
Redispersible latex powder: 13 weight parts.
The kieselguhr wall material further, with dreamlike effect also contains the component of following weight part:
Mineral dye: 1～30 weight part.
The preparation method of the above-mentioned kieselguhr wall material with dreamlike effect is: mentioned component is mixed according to corresponding parts by weight, stir.
A constructional method for the above-mentioned kieselguhr wall material with dreamlike effect, comprising:
Step 1: wall body is carried out to base treatment;
Step 2: kieselguhr wall material and water are mixed according to the ratio of weight ratio 1: 0.4～0.6;
Step 3: criticize and scrape two times constructions; First pass is criticized after the wall material of scraping parches completely and is brushed one deck basement membrane, then criticizes and scrapes second time; Scrape after second time immediately with Roller brush wall body entirety plucking, in the time that wall material to 3～5 one-tenths is dry, be closed flat press polish with receiving light trowel, when operation, noted making the wall body irregular duck eye of surperficial appearance and duck eye to be evenly distributed unanimously;
Step 4: after wall material complete drying, the two times constructions of painting; Wherein first pass colouring is to dip in upper yellow ultramarine point gently with crash towel to wipe on wall material surface, and the duck eye inside described in step 3 is not clipped in attention; After the pigment of first pass colouring parches, on first pass yellow ultramarine, evenly point is wiped the pigment except yellow second time, and overall even, the shade of pigment that second time point wiped unanimously.
Wherein,
In step 1, described wall body is carried out to base treatment be: wall body entirety has been scraped to water-proof putty brushing basement membrane, protected wall body corner with U.S. line paper; If wall body base material difference, also should stick in junction bandage or grid cloth processing; Require that wall body humidity is less than 10%, pH is less than 10, wall body overall leveling, closely knit, clean without floating dust, without cracking hollowing after being disposed;
In step 2, construction temperature is not less than 5 DEG C; Described kieselguhr wall material and the weight ratio of water are preferably 1: 0.5; The described working method that kieselguhr wall material and water are mixed is as follows: the water that first adds water consumption 80% in container, add again described kieselguhr wall material to leave standstill 3～5 minutes, then stir 8～10 minutes with electric mixer, when stirring, slowly add the water of residue 20%, leave standstill 3～5 minutes, then with electric mixer stir 8～10 minutes;
Preferably, after being mixed, kieselguhr wall material and water leaves standstill 30～60 minutes again;
In step 3, it is 0.7～0.9mm that described first pass is criticized the wall material thickness of scraping, and the second time batch of wall material thickness of scraping is 0.6～0.8mm; The operative body of described receipts light trowel is made of stainless steel, and thickness is 0.03mm, and the plane set deformation volume of operative body is 0.03mm.
The present invention has following beneficial effect:
After utilizing kieselguhr wall material of the present invention and constructional method thereof to construct on wall body, finished product effect is attractive in appearance, and texture approaches dreamlike decorated style, has met people to the ornamental requirement of kieselguhr wall material.
Embodiment
For making the technical problem to be solved in the present invention, technical scheme and advantage clearer, be described in detail below in conjunction with specific embodiment.
The method using in following embodiment if no special instructions, is ordinary method.
Material, reagent etc. used in following embodiment, if no special instructions, all can obtain from commercial channels.
On the one hand, the invention provides a kind of kieselguhr wall material with dreamlike effect, it is to allocate by various ingredients the powder body material forming, and concrete component refers to following examples.
Embodiment 1:
The kieselguhr wall material with dreamlike effect contains the component of following weight part: 250～500 order calcined diatomites: 20 weight parts; 35～825 order quartz sand powders: 48 weight parts; 325～1200 order natural colour sands: 10 weight parts; Nano titanium oxide: 10 weight parts; Methylcellulose gum: 0.4 weight part; Redispersible latex powder: 20 weight parts.
Embodiment 2:
The kieselguhr wall material with dreamlike effect contains the component of following weight part: 250～500 order calcined diatomites: 52 weight parts; 35～825 order quartz sand powders: 24 weight parts; 325～1200 order natural colour sands: 30 weight parts; Nano titanium oxide: 3 weight parts; Methylcellulose gum: 1.2 weight parts; Redispersible latex powder: 6 weight parts.
Embodiment 3:
On the basis of embodiment 1, add mineral dye: 1 weight part.
Embodiment 4:
On the basis of embodiment 2, add mineral dye: 30 weight parts.
Embodiment 5:
The kieselguhr wall material with dreamlike effect contains the component of following weight part: 250～500 order calcined diatomites: 42 weight parts; 175～725 order quartz sand powders: 30 weight parts; 550～1150 order natural colour sands: 25 weight parts; Nano titanium oxide: 5 weight parts; Methylcellulose gum: 0.9 weight part; Redispersible latex powder: 12 weight parts.
Embodiment 6:
The kieselguhr wall material with dreamlike effect contains the component of following weight part: 250～500 order calcined diatomites: 30 weight parts; 175～725 order quartz sand powders: 40 weight parts; 550～1150 order natural colour sands: 15 weight parts; Nano titanium oxide: 7 weight parts; Methylcellulose gum: 0.7 weight part; Redispersible latex powder: 14 weight parts.
Embodiment 7:
On the basis of embodiment 5, add mineral dye: 1 weight part.
Embodiment 8:
On the basis of embodiment 6, add mineral dye: 30 weight parts.
Embodiment 9:
The kieselguhr wall material with dreamlike effect contains the component of following weight part: 250～500 order calcined diatomites: 36 weight parts; 225～675 order quartz sand powders: 36 weight parts; 625～925 order natural colour sands: 20 weight parts; Nano titanium oxide: 6 weight parts; Methylcellulose gum: 0.8 weight part; Redispersible latex powder: 13 weight parts.
Embodiment 10:
On the basis of embodiment 9, add mineral dye: 1 weight part.
Embodiment 11:
On the basis of embodiment 9, add mineral dye: 30 weight parts.
The present invention utilizes natural colour sand and calcined diatomite meticulously to allocate, then adds a kind of novel environment friendly wall body finishing material that quartz sand powder, nano titanium oxide, methylcellulose gum and redispersible latex powder are prepared into.
Through actual verification, make by the above-mentioned kieselguhr wall material with dreamlike effect provided by the invention the wall body decorative pattern obtaining, there is dense dreamlike texture, meet people to the ornamental requirement of kieselguhr wall material.And the effect that wherein uses effect that kieselguhr wall material that embodiment 5 to 8 provides obtains to be better than embodiment 1 to 4, embodiment 9 to 11 is better than embodiment 5 to 8.Meanwhile, in above-described embodiment, added the kieselguhr wall material of mineral dye with respect to the kieselguhr wall material that does not add mineral dye, the effect obtaining is more attractive in appearance true to nature.
Embodiment 12:
The constructional method of a kind of above-mentioned kieselguhr wall material with dreamlike effect provided by the invention, specific as follows:
Step 1: wall body is carried out to base treatment;
According to the common way in this area, wall body is processed, made it be suitable for the construction of follow-up kieselguhr wall material.Want to obtain the decorative effect better with dreamlike effect, wall body should entirety have been scraped water-proof putty brushing basement membrane, and wall body corner protects with U.S. line paper; If wall body base material difference, also should stick in junction bandage or grid cloth processing; Require that wall body humidity is less than 10%, pH is less than 10, wall body overall leveling, closely knit, clean without floating dust, without cracking hollowing after being disposed;
Step 2: kieselguhr wall material and water are mixed according to the ratio of weight ratio 1: 0.4～0.6;
In this step, the water yield can not too much can not be very few, and the weight ratio of kieselguhr wall material and water is preferably 1: 0.5, otherwise all can be not easy to follow-up construction, even affects the texture effect of finished product.Stir evenly, the application property of material is better; In order to obtain the decorative effect better with dreamlike effect, optionally with the following method kieselguhr wall material and water are mixed: the water that first adds water consumption 80% in container, add again kieselguhr wall material to leave standstill 3～5 minutes, then stir 8～10 minutes with electric mixer, when stirring, slowly add the water of residue 20%, leave standstill 3～5 minutes, then stir and it was mixed in 8～10 minutes with electric mixer; After mixing, leave standstill again 30～60 minutes better effects if;
Step 3: criticize and scrape two times constructions; First pass is criticized after the wall material of scraping parches completely and is brushed one deck basement membrane, then criticizes and scrapes second time; Scrape after second time immediately with Roller brush wall body entirety plucking, in the time that wall material to 3～5 one-tenths is dry, be closed flat press polish with receiving light trowel, when operation, noted making the wall body irregular duck eye of surperficial appearance and duck eye to be evenly distributed unanimously;
In this step, in order to obtain the decorative effect better with dreamlike effect, it is 0.7～0.9mm that first pass is criticized the wall material thickness of scraping, and the second time batch of wall material thickness of scraping is 0.6～0.8mm; The present invention adopts two times batches of modes of scraping to construct, and first pass is criticized after the wall material of scraping parches completely and brushed one deck basement membrane, then criticizes and scrapes second time; Scrape after second time immediately with Roller brush wall body entirety plucking, in the time that wall material to 3～5 one-tenths is dry, be closed flat press polish with receiving light trowel, when operation, noted making the wall body irregular duck eye of surperficial appearance and duck eye to be evenly distributed unanimously.
Meanwhile, the operative body stainless steel of the receipts light trowel using in this step is made, and thickness is 0.03mm, and the plane set deformation volume of operative body is 0.03mm.
Step 4: after wall material complete drying, the two times constructions of painting; Wherein first pass colouring is to dip in upper yellow ultramarine point gently with crash towel to wipe on wall material surface, and the duck eye inside described in step 3 is not clipped in attention; After the pigment of first pass colouring parches, on first pass yellow ultramarine, evenly point is wiped the pigment except yellow second time, and overall even, the shade of pigment that second time point wiped unanimously.
In this step, in order to obtain the decorative effect better with dreamlike effect, scrape the wall material surface of completion to criticizing and go up again twice pigment processing, when colouring, must note the method for colouring, pigment is not clipped to duck eye inside, thereby reached decorative effect true to nature.
Contriver is through concentrating on studies discovery, and in order to use the texture that presents dreamlike decorated style containing diatomaceous wall material, first key point is the formula of kieselguhr wall material; Second key point is constructional method, every opportunity all over construction, working method and other concrete working method etc. of colouring while comprising ratio, the stirring means of kieselguhr wall material and water, two times constructions; The 3rd key point is material, thickness and the elastic performance of the receipts light trowel of use, and these factors all can have influence on the texture effect of the finished product after kieselguhr wall unit construction.
Through research for many years, the talent is according to the texture feature of dreamlike decorated style in invention, develop kieselguhr wall material and the constructional method thereof with dreamlike effect of the present invention, thereby can make the wall body decorative pattern that obtains texture and approach dreamlike decorated style, meet people to the ornamental requirement of kieselguhr wall material.
To sum up, after utilizing kieselguhr wall material of the present invention and constructional method thereof to construct on wall body, finished product effect is attractive in appearance, and texture approaches dreamlike decorated style, has met people to the ornamental requirement of kieselguhr wall material.And, in kieselguhr wall material provided by the invention, do not contain any harmful material, not only can not distribute the obnoxious flavoures such as formaldehyde, benzene, ammonia, radon, but also there is absorption, the function of resolving harmful gas, and there is certain equilibrium temperature function, possess transport, the simple feature of constructing simultaneously.
The present invention has improved the utilization of diatomite in finishing material, for living and brought selection more healthy, environmental protection at home.
The above is the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of principle of the present invention; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (10)
1. there is a kieselguhr wall material for dreamlike effect, the component that contains following weight part:
250～500 order calcined diatomites: 20～52 weight parts;
35～825 order quartz sand powders: 24～48 weight parts;
325～1200 order natural colour sands: 10～30 weight parts;
Nano titanium oxide: 3～10 weight parts;
Methylcellulose gum: 0.4～1.2 weight part;
Redispersible latex powder: 6～20 weight parts.
2. the kieselguhr wall material with dreamlike effect according to claim 1, is characterized in that, the component that contains following weight part:
250～500 order calcined diatomites: 30～42 weight parts;
175～725 order quartz sand powders: 30～40 weight parts;
550～1150 order natural colour sands: 15～25 weight parts;
Nano titanium oxide: 5～7 weight parts;
Methylcellulose gum: 0.7～0.9 weight part;
Redispersible latex powder: 12～14 weight parts.
3. the kieselguhr wall material with dreamlike effect according to claim 1, is characterized in that, the component that contains following weight part:
250～500 order calcined diatomites: 36 weight parts;
225～675 order quartz sand powders: 36 weight parts;
625～925 order natural colour sands: 20 weight parts;
Nano titanium oxide: 6 weight parts;
Methylcellulose gum: 0.8 weight part;
Redispersible latex powder: 13 weight parts.
4. according to the kieselguhr wall material with dreamlike effect described in any one in claims 1 to 3, it is characterized in that, also contain mineral dye 1～30 weight part.
5. the constructional method of the kieselguhr wall material with dreamlike effect described in any one in claim 1 to 4, is characterized in that, comprises the steps:
Step 1: wall body is carried out to base treatment;
Step 2: kieselguhr wall material and water are mixed according to the ratio of weight ratio 1: 0.4～0.6;
Step 3: criticize and scrape two times constructions; First pass is criticized after the wall material of scraping parches completely and is brushed one deck basement membrane, then criticizes and scrapes second time; Scrape after second time immediately with Roller brush wall body entirety plucking, in the time that wall material to 3～5 one-tenths is dry, be closed flat press polish with receiving light trowel, when operation, noted making the wall body irregular duck eye of surperficial appearance and duck eye to be evenly distributed unanimously;
Step 4: after wall material complete drying, the two times constructions of painting; Wherein first pass colouring is to dip in upper yellow ultramarine point gently with crash towel to wipe on wall material surface, and the duck eye inside described in step 3 is not clipped in attention; After the pigment of first pass colouring parches, on first pass yellow ultramarine, evenly point is wiped the pigment except yellow second time, and overall even, the shade of pigment that second time point wiped unanimously.
6. the constructional method of the kieselguhr wall material with dreamlike effect according to claim 5, is characterized in that, in step 3, it is 0.7～0.9mm that described first pass is criticized the wall material thickness of scraping, and the second time batch of wall material thickness of scraping is 0.6～0.8mm.
7. according to the constructional method of the kieselguhr wall material with dreamlike effect described in claim 5 or 6, it is characterized in that, in step 3, the operative body of described receipts light trowel is made of stainless steel, thickness is 0.03mm, and the plane set deformation volume of operative body is 0.03mm.
8. according to the constructional method of the kieselguhr wall material with dreamlike effect described in claim 5 or 6, it is characterized in that, in step 1, described wall body is carried out to base treatment be: wall body entirety has been scraped to water-proof putty brushing basement membrane, protected wall body corner with U.S. line paper; If wall body base material difference, also should stick in junction bandage or grid cloth processing; Require that wall body humidity is less than 10%, pH is less than 10, wall body overall leveling, closely knit, clean without floating dust, without cracking hollowing after being disposed.
9. according to the constructional method of the kieselguhr wall material with dreamlike effect described in claim 5 or 6, it is characterized in that, in step 2, described kieselguhr wall material and the weight ratio of water are 1: 0.5.
10. the constructional method of the kieselguhr wall material with dreamlike effect according to claim 5, is characterized in that, in step 2, construction temperature is not less than 5 DEG C; The described working method that kieselguhr wall material and water are mixed is as follows: the water that first adds water consumption 80% in container, add again described kieselguhr wall material to leave standstill 3～5 minutes, then stir 8～10 minutes with electric mixer, when stirring, slowly add the water of residue 20%, leave standstill 3～5 minutes, then with electric mixer stir 8～10 minutes; After being mixed, kieselguhr wall material and water leaves standstill 30～60 minutes again.