CN103819089B - 熔融法制备微晶玻璃的工艺及高平整度的微晶玻璃 - Google Patents
熔融法制备微晶玻璃的工艺及高平整度的微晶玻璃 Download PDFInfo
- Publication number
- CN103819089B CN103819089B CN201410082530.5A CN201410082530A CN103819089B CN 103819089 B CN103819089 B CN 103819089B CN 201410082530 A CN201410082530 A CN 201410082530A CN 103819089 B CN103819089 B CN 103819089B
- Authority
- CN
- China
- Prior art keywords
- oxide
- incubated
- parts
- speed
- hour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (7)