CN103787649B - 防腐陶瓷材料及其制备方法 - Google Patents
防腐陶瓷材料及其制备方法 Download PDFInfo
- Publication number
- CN103787649B CN103787649B CN201310715285.2A CN201310715285A CN103787649B CN 103787649 B CN103787649 B CN 103787649B CN 201310715285 A CN201310715285 A CN 201310715285A CN 103787649 B CN103787649 B CN 103787649B
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic material
- acid
- raw material
- hour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
防腐陶瓷材料及其制备方法，包括以下按重量份数计的原料：聚氨酯改性环氧树脂20-30份，石英粉5-10份，氮化硅10-15份，硼氢化钠10-15份，氧化硅20-30份，环己烷溶液30-40份。本发明的配方中利用耐酸碱的聚氨酯改性环氧树脂和氮化硅为原料，制备的陶瓷材料硬度和耐酸碱性能都得到提高，使得在酸碱度较高的空间里，陶瓷产品或通过陶瓷焊接的物品寿命增长。
Description
技术领域
本发明涉及一种防腐陶瓷材料及其制备方法。
背景技术
陶瓷材料被广泛地作为柜台的材料，耐热、耐酸碱成为筛选陶瓷材料的参考标准。目前，常用的陶瓷材料耐腐蚀能力较差，尤其作为实验台的材料，时间一长就出现坑坑洼洼，不仅影响美观还影响实验设备的摆放，针对实验室的特殊环境，本发明提出一种耐酸碱的陶瓷材料。
发明内容
针对现有技术的不足，本发明提供了一种防腐陶瓷材料及其制备方法。
为解决现有技术问题本发明采用的技术方案为：防腐陶瓷材料，包括以下按重量份数计的原料：聚氨酯改性环氧树脂20-30份，石英粉5-10份，氮化硅10-15份，硼氢化钠10-15份，氧化硅20-30份，环己烷溶液30-40份。
所述的防腐陶瓷材料的制备方法，包括以下步骤：
（1）按重量份数称取原料；
（2）将原料混合均匀放入搅拌器中，待反应进行0.5-1.5小时后，在100KPa下抽真空5-10分钟；
（3）在惰性气体保护下对上述处理的原料煅烧，煅烧温度为1000-1200℃，加热时间为25-40小时得毛坯件；
（4）再将毛坯件在温度为800-1000℃下煅烧1-1.5小时后，放入120-180℃干燥箱中，保温处理24-48小时得防腐陶瓷材料。
优选的是，所述惰性气体为氮气。
本发明的有益效果：配方中利用耐酸碱的聚氨酯改性环氧树脂和氮化硅为原料，制备的陶瓷材料硬度和耐酸碱性能都得到提高，使得在酸碱度较高的空间里，陶瓷产品或通过陶瓷焊接的物品寿命增长。
具体实施方式
下面通过具体实施例对本发明作进一步详细介绍。
实施例1
防腐陶瓷材料，包括以下按重量份数计的原料：聚氨酯改性环氧树脂20份，石英粉5份，氮化硅10份，硼氢化钠10份，氧化硅20份，环己烷溶液30份。
所述的防腐陶瓷材料的制备方法，包括以下步骤：
（1）按重量份数称取原料；
（2）将原料混合均匀放入搅拌器中，待反应进行0.5小时后，在100KPa下抽真空5分钟；
（3）在氮气保护下对上述处理的原料煅烧，煅烧温度为1000℃，加热时间为25小时得毛坯件；
（4）再将毛坯件在温度为800℃下煅烧1小时后，放入120℃干燥箱中，保温处理24小时得防腐陶瓷材料。
实施例2
防腐陶瓷材料，包括以下按重量份数计的原料：聚氨酯改性环氧树脂30份，石英粉10份，氮化硅15份，硼氢化钠15份，氧化硅30份，环己烷溶液40份。
所述的防腐陶瓷材料的制备方法，包括以下步骤：
（1）按重量份数称取原料；
（2）将原料混合均匀放入搅拌器中，待反应进行1.5小时后，在100KPa下抽真空10分钟；
（3）在氮气保护下对上述处理的原料煅烧，煅烧温度为1200℃，加热时间为40小时得毛坯件；
（4）再将毛坯件在温度为1000℃下煅烧1.5小时后，放入180℃干燥箱中，保温处理48小时得防腐陶瓷材料。
实施例3
防腐陶瓷材料，包括以下按重量份数计的原料：聚氨酯改性环氧树脂25份，石英粉8份，氮化硅12份，硼氢化钠13份，氧化硅25份，环己烷溶液35份。
所述的防腐陶瓷材料的制备方法，包括以下步骤：
（1）按重量份数称取原料；
（2）将原料混合均匀放入搅拌器中，待反应进行1.0小时后，在100KPa下抽真空8分钟；
（3）在氮气保护下对上述处理的原料煅烧，煅烧温度为1100℃，加热时间为30小时得毛坯件；
（4）再将毛坯件在温度为900℃下煅烧1.2小时后，放入160℃干燥箱中，保温处理30小时得防腐陶瓷材料。
将本发明的防腐陶瓷材料与普通的陶瓷材料进行对比试验，取相同重量的材料分别放入PH从0-14的溶液中观察腐蚀情况，所得结果如下：本发明的防腐陶瓷材料耐酸碱的PH为4.5-8.6，普通的陶瓷材料耐酸碱的PH为5.5-7.2。
另外，本发明不限于上述实施方式，只要在不超出本发明的范围内，可以采取各种方式实施本发明。
Claims (2)
1.防腐陶瓷材料，其特征在于：按重量份数计称取原料聚氨酯改性环氧树脂20-30份，石英粉5-10份，氮化硅10-15份，硼氢化钠10-15份，氧化硅20-30份，环己烷溶液30-40份；将原料混合均匀放入搅拌器中，待反应进行0.5-1.5小时后，在100KPa下抽真空5-10分钟；在惰性气体保护下对上述处理的原料煅烧，煅烧温度为1000-1200℃，加热时间为25-40小时得毛坯件；再将毛坯件在温度为800-1000℃下煅烧1-1.5小时后，放入120-180℃干燥箱中，保温处理24-48小时得防腐陶瓷材料。
2.根据权利要求1所述的防腐陶瓷材料，其特征在于：所述惰性气体为氮气。