CN103774409A - Anti-infrared disruptive pattern printing process for high-performance blended fabric - Google Patents

Anti-infrared disruptive pattern printing process for high-performance blended fabric Download PDF

Info

Publication number
CN103774409A
CN103774409A CN201410006451.6A CN201410006451A CN103774409A CN 103774409 A CN103774409 A CN 103774409A CN 201410006451 A CN201410006451 A CN 201410006451A CN 103774409 A CN103774409 A CN 103774409A
Authority
CN
China
Prior art keywords
blended fabric
intellectual circle
disperse
performance
industrial
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410006451.6A
Other languages
Chinese (zh)
Other versions
CN103774409B (en
Inventor
周瑾悝
朱鸣英
凌伟兴
汪君英
周东方
赵周洁
周磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XINJIAN TEXTILE CO Ltd ZHEJIANG
Original Assignee
XINJIAN TEXTILE CO Ltd ZHEJIANG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XINJIAN TEXTILE CO Ltd ZHEJIANG filed Critical XINJIAN TEXTILE CO Ltd ZHEJIANG
Priority to CN201410006451.6A priority Critical patent/CN103774409B/en
Publication of CN103774409A publication Critical patent/CN103774409A/en
Priority to GB1511169.3A priority patent/GB2529528A/en
Application granted granted Critical
Publication of CN103774409B publication Critical patent/CN103774409B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to an anti-infrared disruptive pattern printing process for a high-performance blended fabric. The process comprises the following steps: 1, adding industrial caustic soda liquid, LCS, industrial hydrogen peroxide and an oxygen bleaching stabilizer, and carrying out desizing, boiling off and bleaching on blended fabric to be printed in sequence; 2, mercerizing the blended fabric treated in the step 1 in the existence of the industrial caustic soda liquid; 3, adding graphite and a soft crease-resistant finishing agent in the blended fabric treated in the step 2 and carrying mangle treatment; 4, adding thickener, graphite, disperse dyes and intellectual circle dyes in the blended fabric treated in the step 3, printing, and ageing after the printing is finished; 5, carrying out vapor steaming and water scrubbing for rapid reduction on the blended fabric treated by the step 4 by using the industrial caustic soda liquid and industrial sodium hydrosulfite. The high-performance blended fabric treated by adopting the process is relatively good in anti-infrared effect, high in wear-resisting performance, soft, and light and has the heat-preservation performance.

Description

A kind of Camouflage printing with infrared resistance technique of high-performance BLENDED FABRIC
Technical field
The present invention relates to a kind of Camouflage printing with infrared resistance technique of high-performance BLENDED FABRIC.
Background technology
Polyvinyl is the trade name of vinylon, and its performance approaches cotton, have the title of " synthetic cotton ", is hygroscopicity maximum in existing synthetic fiber, and sunlight resistance and weather fastness are fine.Its softness and warmth retention property are good, and also lighter than cotton, and the ABRASION RESISTANCE of polyvinyl and intensity are also good than cotton.
Along with scientific and technological progress, the trial of strength of military power is electronization increasingly, and in modern high technology campaign, being familiar with battlefield surroundings is the very important factor that gains the final victory, for will effectively obtaining enemy's integral deployment, with the object that reaches supervision, follows the tracks of and predict.Therefore in war, many military targets often adopt the hidden technology of camouflage, to resist the various different electronic reconnaissances of enemy and strike.The camouflage effectiveness of camouflage fatigue adopts general visible ray camera installation to detect, and will be difficult to find that it obtains the true and false of image.If be with ultrared reconnaissance equipment but adopt, will be easy to give away one's position, therefore need camouflage fatigue to carry out anti-infrared processing.Chinese patent literature CN102534935 discloses the anti-infrared camouflage fabric of the bright and beautiful blending of a kind of cotton and dyeing and printing process technique thereof, this process using be cotton bright and beautiful BLENDED FABRIC, material cost is higher, equipment in enormous quantities has increased certain cost, anti-infrared effect is not very desirable simultaneously, easily spied out by infrared gear, complex process, not easy to operate.
Summary of the invention
The present invention is directed to the problems referred to above, propose a kind of anti-infrared better effects if, wear-resisting high-strength, stamp and the rear finishing process of the anti-infrared camouflage color high-performance BLENDED FABRIC of soft warming lightweight.
For achieving the above object, the present invention is achieved by the following technical solutions:
A Camouflage printing with infrared resistance technique for high-performance BLENDED FABRIC, comprises the following steps:
(1) add 1.0-2.5g/L industrial lye, 1.0-2.5g/L LCS, 2-4g/L industry hydrogen peroxide and 1.5-2.5g/L hydrogen peroxide bleaching stabilizer, will treat BLENDED FABRIC destarch at 105-115 ℃, kiering and the bleaching 40-50min of stamp;
(2) BLENDED FABRIC of processing through step (1) is carried out to mercerization finish under 180-230g/L industrial lye;
(3) BLENDED FABRIC of processing through step (2) is added to the soft crease-shedding finishing agent of 0.4-1.2g/l graphite and 2.5-4.2g/l, at 150-175 ℃, carry out mangle and process 40-70s;
(4) add thickener 3-8%, graphite 0.1-6%, DISPERSE DYES 0.1-6% and intellectual circle's dyestuff 0.1-6% to carry out stamp the BLENDED FABRIC of processing through step (3); After stamp finishes, at 165-170 ℃, the speed with 35-45m/min is evaporated;
(5) BLENDED FABRIC that will process through step (4) is used 80-120g/L industrial lye and 65-78g/L industrial insurance powder, and with the temperature of 130-150 ℃, the speed of a motor vehicle of 30-45m/min is carried out fast restore gas and steamed washing.
Described DISPERSE DYES is Disperse Blue 2BLN, disperse blue SE-2R, disperse brown H2RL, disperse navy blue ETD, disperse one or more mixtures of emerald green blue S-GL or dispersed ruby H2GFL;
Described intellectual circle's dyestuff is one or more mixtures of intellectual circle blue RSN, intellectual circle's olive T, the green B of intellectual circle, intellectual circle palm fibre BR, intellectual circle ash M or the yellow G of intellectual circle.
The main component of the hydrogen peroxide bleaching stabilizer in described step (1) is sodium silicate.
Soft crease-shedding finishing agent in described step (3) is soft crease-shedding finishing agent JPBC.
Beneficial effect of the present invention is as follows: high-performance BLENDED FABRIC of the present invention, whole fabric is still rich in cotton characteristic in the situation that reducing cotton fiber consumption, even on Local Property, is better than cotton.Whole printing technology process has effectively been contained the weakness of the easy flavescence of high-performance BLENDED FABRIC, makes cloth cover effect, and color and luster meets product demand.Whole anti-infrared camouflage color is not only difficult to find in the time that general visible ray camera installation is detected, under the investigation of infrared ray reconnaissance equipment, also there is extremely excellent hiding and fascination effect, be not easy to be investigated by enemy anti-infrared better effects if, wear-resisting high-strength, soft warming lightweight; The application success of high-performance BLENDED FABRIC reduces large batch of equipment use cost greatly, and take up an official post and so retain its original fine quality in performance, the revolutionary character of anti-infrared camouflage color breaks through and makes this fabric cross over forward major step in fascination camouflage function.
The specific embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated, but protection scope of the present invention is not limited to this.
LCS in the present invention is the product that Dao Dun Chemical Co., Ltd. of Britain produces, soft crease-shedding finishing agent JPBC is the product that Shanghai Xin Lian Chemical Co., Ltd. produces, industrial lye, industrial hydrogen peroxide, hydrogen peroxide bleaching stabilizer, graphite, thickener, Disperse Blue 2BLN, disperse blue SE-2R, disperse brown H2RL, disperse navy blue ETD, disperse emerald green blue S-GL, dispersed ruby H2GFL, intellectual circle blue RSN, intellectual circle's olive T, the green B of intellectual circle, intellectual circle palm fibre BR, intellectual circle's ash M, the yellow G of intellectual circle and sodium hydrosulfite all can adopt commercially available prod, or make by method well known in the art.
embodiment 1
The Camouflage printing with infrared resistance technique of high-performance BLENDED FABRIC of the present invention, comprises the following steps:
(1) add the hydrogen peroxide bleaching stabilizer that 1.5g/L industrial lye, 1.5g/L LCS, 3g/L industry hydrogen peroxide and 2g/L main component are sodium silicate, will treat BLENDED FABRIC destarch at 110 ℃, kiering and the bleaching 45min of stamp;
(2) BLENDED FABRIC of processing through step (1) is carried out to mercerization finish under 205g/L industrial lye;
(3) BLENDED FABRIC of processing through step (2) is added to the soft crease-shedding finishing agent JPBC of 0.8g/l graphite and 4g/l, at 162.5 ℃, carry out mangle and process 55s;
(4) add thickener 5.5%, graphite 3.05%, DISPERSE DYES 3.05% and intellectual circle's dyestuff 3.05% to carry out stamp the BLENDED FABRIC of processing through step (3); After stamp finishes, at 167.5 ℃, the speed with 40m/min is evaporated;
(5) BLENDED FABRIC that will process through step (4) is used 100g/L industrial lye and 70g/L industrial insurance powder, and with the temperature of 140 ℃, the speed of a motor vehicle of 40m/min is carried out fast restore gas and steamed washing.
In the present embodiment, DISPERSE DYES is Disperse Blue 2BLN, disperse blue SE-2R, disperse brown H2RL, disperse navy blue ETD, disperses one or more mixtures of emerald green blue S-GL or dispersed ruby H2GFL; Intellectual circle's dyestuff is one or more mixtures of intellectual circle blue RSN, intellectual circle's olive T, the green B of intellectual circle, intellectual circle palm fibre BR, intellectual circle ash M or the yellow G of intellectual circle, can be according to the selection that needs of actual color.
embodiment 2
The Camouflage printing with infrared resistance technique of high-performance BLENDED FABRIC of the present invention, comprises the following steps:
(1) add the hydrogen peroxide bleaching stabilizer that 1.0g/L industrial lye, 1.0g/L LCS, 2g/L industry hydrogen peroxide and 1.5g/L main component are sodium silicate, will treat BLENDED FABRIC destarch at 105 ℃, kiering and the bleaching 40min of stamp;
(2) BLENDED FABRIC of processing through step (1) is carried out to mercerization finish under 180g/L industrial lye;
(3) BLENDED FABRIC of processing through step (2) is added to the soft crease-shedding finishing agent JPBC of 0.4g/l graphite and 2.5g/l, at 150 ℃, carry out mangle and process 40s;
(4) add thickener 3%, graphite 0.1%, DISPERSE DYES 0.1% and intellectual circle's dyestuff 0.1% to carry out stamp the BLENDED FABRIC of processing through step (3); After stamp finishes, at 165 ℃, the speed with 35m/min is evaporated;
(5) BLENDED FABRIC that will process through step (4) is used 80g/L industrial lye and 65g/L industrial insurance powder, and with the temperature of 130 ℃, the speed of a motor vehicle of 45m/min is carried out fast restore gas and steamed washing.
In the present embodiment, DISPERSE DYES is Disperse Blue 2BLN, disperse blue SE-2R, disperse brown H2RL, disperse navy blue ETD, disperses one or more mixtures of emerald green blue S-GL or dispersed ruby H2GFL; Intellectual circle's dyestuff is one or more mixtures of intellectual circle blue RSN, intellectual circle's olive T, the green B of intellectual circle, intellectual circle palm fibre BR, intellectual circle ash M or the yellow G of intellectual circle, can be according to the selection that needs of actual color.
embodiment 3
The Camouflage printing with infrared resistance technique of high-performance BLENDED FABRIC of the present invention, comprises the following steps:
(1) add the hydrogen peroxide bleaching stabilizer that 2.5g/L industrial lye, 2.5g/L LCS, 4g/L industry hydrogen peroxide and 2.5g/L main component are sodium silicate, will treat BLENDED FABRIC destarch at 115 ℃, kiering and the bleaching 50min of stamp;
(2) BLENDED FABRIC of processing through step (1) is carried out to mercerization finish under 230g/L industrial lye;
(3) BLENDED FABRIC of processing through step (2) is added to the soft crease-shedding finishing agent JPBC of 1.2g/l graphite and 4.2g/l, at 175 ℃, carry out mangle and process 70s;
(4) add thickener 8%, graphite 6%, DISPERSE DYES 6% and intellectual circle's dyestuff 6% to carry out stamp the BLENDED FABRIC of processing through step (3); After stamp finishes, at 170 ℃, the speed with 45m/min is evaporated;
(5) BLENDED FABRIC that will process through step (4) is used 120g/L industrial lye and 78g/L industrial insurance powder, and with the temperature of 150 ℃, the speed of a motor vehicle of 30m/min is carried out fast restore gas and steamed washing.
In the present embodiment, DISPERSE DYES is Disperse Blue 2BLN, disperse blue SE-2R, disperse brown H2RL, disperse navy blue ETD, disperses one or more mixtures of emerald green blue S-GL or dispersed ruby H2GFL; Intellectual circle's dyestuff is one or more mixtures of intellectual circle blue RSN, intellectual circle's olive T, the green B of intellectual circle, intellectual circle palm fibre BR, intellectual circle ash M or the yellow G of intellectual circle, can be according to the selection that needs of actual color.
performance test
by in embodiment 1-3the anti-infrared camouflage facing material of high-performance BLENDED FABRIC carries out the mensuration of reflected value, measures structure as following table 1 and table 2;
Table 1 is the each waveband K/S of the camouflage color anti-infrared reflected value of customer requirement;
The each color reflected value of high-performance BLENDED FABRIC anti-infrared camouflage facing material that table 2, table 3 are produced for my company;
Table 1
Figure 23673DEST_PATH_IMAGE001
Table 2
Figure 846136DEST_PATH_IMAGE002
Table 3
Figure 676951DEST_PATH_IMAGE003
High-performance BLENDED FABRIC of the present invention, whole fabric is still rich in cotton characteristic in the situation that reducing cotton fiber consumption, even on Local Property, is better than cotton.Whole printing technology process has effectively been contained the weakness of the easy flavescence of high-performance BLENDED FABRIC, makes cloth cover effect, and color and luster meets product demand.Whole anti-infrared camouflage color is not only difficult to find in the time that general visible ray camera installation is detected, under the investigation of infrared ray reconnaissance equipment, also there is extremely excellent hiding and fascination effect, be not easy to be investigated by enemy anti-infrared better effects if, wear-resisting high-strength, soft warming lightweight; The application success of high-performance BLENDED FABRIC reduces large batch of equipment use cost greatly, and take up an official post and so retain its original fine quality in performance, the revolutionary character of anti-infrared camouflage color breaks through and makes this fabric cross over forward major step in fascination camouflage function.
Above-described embodiment is only for the inventive concept of the present invention of explaining, but not restriction to rights protection of the present invention, allly utilizes this design to carry out the change of unsubstantiality to the present invention, all should fall into protection scope of the present invention.

Claims (3)

1. a Camouflage printing with infrared resistance technique for high-performance BLENDED FABRIC, is characterized in that comprising the following steps:
(1) add 1.0-2.5g/L industrial lye, 1.0-2.5g/L LCS, 2-4g/L industry hydrogen peroxide and 1.5-2.5g/L hydrogen peroxide bleaching stabilizer, will treat BLENDED FABRIC destarch at 105-115 ℃, kiering and the bleaching 40-50min of stamp;
(2) BLENDED FABRIC of processing through step (1) is carried out to mercerization finish under 180-230g/L industrial lye;
(3) BLENDED FABRIC of processing through step (2) is added to the soft crease-shedding finishing agent of 0.4-1.2g/l graphite and 2.5-4.2g/l, at 150-175 ℃, carry out mangle and process 40-70s;
(4) add thickener 3-8%, graphite 0.1-6%, DISPERSE DYES 0.1-6% and intellectual circle's dyestuff 0.1-6% to carry out stamp the BLENDED FABRIC of processing through step (3); After stamp finishes, at 165-170 ℃, the speed with 35-45m/min is evaporated;
(5) BLENDED FABRIC that will process through step (4) is used 80-120g/L industrial lye and 65-78g/L industrial insurance powder, and with the temperature of 130-150 ℃, the speed of a motor vehicle of 30-45m/min is carried out fast restore gas and steamed washing;
Described DISPERSE DYES is Disperse Blue 2BLN, disperse blue SE-2R, disperse brown H2RL, disperse navy blue ETD, disperse one or more mixtures of emerald green blue S-GL or dispersed ruby H2GFL;
Described intellectual circle's dyestuff is one or more mixtures of intellectual circle blue RSN, intellectual circle's olive T, the green B of intellectual circle, intellectual circle palm fibre BR, intellectual circle ash M or the yellow G of intellectual circle.
2. the Camouflage printing with infrared resistance technique of high-performance BLENDED FABRIC as claimed in claim 1, is characterized in that: the main component of the hydrogen peroxide bleaching stabilizer in described step (1) is sodium silicate.
3. the Camouflage printing with infrared resistance technique of high-performance BLENDED FABRIC as claimed in claim 1, is characterized in that: the soft crease-shedding finishing agent in described step (3) is soft crease-shedding finishing agent JPBC.
CN201410006451.6A 2014-01-06 2014-01-06 A kind of Camouflage printing with infrared resistance technique of high-performance BLENDED FABRIC Active CN103774409B (en)