CN106400461B - A method of promoting THPC inflaming retarding fabric light shine fastness - Google Patents
A method of promoting THPC inflaming retarding fabric light shine fastness Download PDFInfo
- Publication number
- CN106400461B CN106400461B CN201610898057.7A CN201610898057A CN106400461B CN 106400461 B CN106400461 B CN 106400461B CN 201610898057 A CN201610898057 A CN 201610898057A CN 106400461 B CN106400461 B CN 106400461B
- Authority
- CN
- China
- Prior art keywords
- thpc
- fire
- retardant
- tentering
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of method promoting THPC inflaming retarding fabric light shine fastness, concrete technology flow process is：Fabric turns over seam → desizing, kiering, mercerising → tentering → fire-retardant → oxygen Low Temperature Plasma Treating → dyeing → washing drying → tentering → preshrunk → test package, wherein desizing, kiering, mercerising process are fully until pH≤7 of fabric eluent, fire-retardant process, which is followed successively by, pads THPC fire retardants working solution, ammonia cure, oxidation washing and drying tentering, the concentration of THPC fire retardants improves 8% 10% compared with normal value in THPC fire retardant working solutions, the flow velocity of ammonia cure process ammonia is 500 700mL/s, and the time of ammonia cure is no less than 5s.The wicking capacity of the present invention treated THPC inflaming retarding fabrics promotes 56 times, surface polar groups（‑OOH、‑OH、‑C=O）It dramatically increases, dyestuff dye uptake is also multiplied, and can preferably meet the needs of client is to color.
Description
Technical field
The invention belongs to light shine THPC inflaming retarding fabric technical fields, and in particular to a kind of promotion THPC inflaming retarding fabrics are fast light
According to the method for fastness.
Background technology
Some gorgeous degree are very high（Such as bright red, Exocarpium Citri Rubrum, fluorescein）Pure cotton cloth, all be use reactive dyeing, if
The cotton of this color needs to be that THPC is fire-retardant, and THPC fire retardants have very strong reproducibility, it is easy to destroy activity dye
The molecular structure of material causes such cotton fire retardant such as bright red, Exocarpium Citri Rubrum, fluorescein, and light only has 1-2 grades, in some illumination
Such fabric, such as offshore drilling platform, oil field prospecting and Southeast Asia area are worn under the strong environment of condition, as long as may
The color of clothes as several days, more than ten days will fade seriously, very unsightly.Annoying textile printing and dyeing always for many years
Boundary, it is well known that high brightness fire retardant protective clothing is constantly subjected to the favor of many industries, and light difference usually enables a wearer to very awkward
, often there is back in a word used for translation and shirtfront color is different, in the case where clothes is also intact, it has to which the clothes more renewed causes
Great waste.
Invention content
The technical problem to be solved by the present invention is to provide a kind of methods promoting THPC inflaming retarding fabric light shine fastness.
The present invention adopts the following technical scheme that a kind of promotion THPC inflaming retarding fabrics light shine is firm to solve above-mentioned technical problem
The method of degree, it is characterised in that concrete technology flow process is：Fabric turns over seam → desizing, kiering, mercerising → tentering → fire-retardant → oxygen
Low Temperature Plasma Treating → dyeing → washing drying → tentering → preshrunk → test package, wherein desizing, kiering, mercerising process
Fully until fabric eluent pH≤7, fire-retardant process be followed successively by pad THPC fire retardants working solution, ammonia cure, oxidation washing and
Tentering is dried, the concentration of THPC fire retardants improves 8%-10% compared with normal value in THPC fire retardant working solutions, ammonia cure process ammonia
Flow velocity is 500-700mL/s, and the time of ammonia cure is no less than 5s.
The wicking capacity of the present invention treated THPC inflaming retarding fabrics promotes 5-6 times, surface polar groups（-OOH、-OH、-
C=O）It dramatically increases, dyestuff dye uptake is also multiplied, and can preferably meet the needs of client is to color.
Specific implementation mode
Detailed description of the present invention particular content in conjunction with the embodiments.
Embodiment
Under normal circumstances, cotton is all to first pass through dyeing, and it is fire-retardant to be then THPC again.It is contemplated that change sequence,
That is cotton is first that THPC is fire-retardant to be gone to dye again, thus overcomes destruction of the fire retardant to reactive dye, simultaneously because
THPC is fire-retardant itself to have very strong washability, will not be dyed because of rear road, washing makes its flame retardant property decay.But THPC
Fire retardant base closed cotton fiber can reactive group, then if going dyeing, basic color yield is very low, that is, dye level
Not enough, cannot still meet using needs.How finish THPC it is fire-retardant after increase cotton fiber can reactive group（Such as-OOH ,-
OH、-C=O）, the present invention solved using the method for oxygen Low Temperature Plasma Treating.Through experimental test：Wicking that treated
Ability has 5-6 times of promotion, surface polar groups（-OOH、-OH、-C=O）It dramatically increases, dyestuff dye uptake is also at double
Increase, can meet the needs of client is to color.
Concrete technology flow process is：Fabric turns over seam → desizing, kiering, mercerising → tentering → fire-retardant（Pad THPC fire retardant works
Make liquid → ammonia cure → oxidation is washed → and dries tentering）→ oxygen plasma treatment → dyeing → washing drying → tentering → preshrunk →
Test package, description of the process：1, fire-retardant preceding desizing, kiering and mercerising must be abundant, and cloth cover cannot contain alkalinity；2, when fire-retardant,
The concentration of THPC fire retardants and the flow of ammonia cure cannot be less than 5 seconds, otherwise, dye than normally improving 8%-10%, the time of ammonia cure
Flame retardant property can decline after color；3, Low Temperature Plasma Treating：To use the equipment based on glow discharge ripe in the market；
4, it dyes：In principle as common dyeing technique, the usage amount of dyestuff and auxiliary agent is determined by sample first.
The present invention solves the problems, such as that the fire-retardant rear lights of the cotton THPC of vital staining are too low, while also improving this
The bright-colored degree of class inflaming retarding fabric, wide market.
Have been shown and described above the basic principle of the present invention, main feature and advantage, do not depart from spirit of that invention and
Under the premise of range, the present invention also has various changes and modifications, these changes and improvements both fall within claimed invention
Range.
Claims (1)
1. a kind of method promoting THPC inflaming retarding fabric light shine fastness, it is characterised in that concrete technology flow process is：Fabric turns over seam
→ desizing, kiering, mercerising → tentering → fire-retardant → oxygen Low Temperature Plasma Treating → dyeing → washing drying → tentering → pre-
Contracting → test package, wherein desizing, kiering, mercerising process are fully until pH≤7 of fabric eluent, fire-retardant process are followed successively by leaching
It rolls THPC fire retardants working solution, ammonia cure, oxidation washing and dries tentering, the concentration of THPC fire retardants in THPC fire retardant working solutions
8%-10% is improved compared with normal value, the flow velocity of ammonia cure process ammonia is 500-700mL/s, and the time of ammonia cure is no less than 5s；The base
The material of cloth is cotton.