CN103757940A - Method for making highly sunproof and anti-infrared tent cloth - Google Patents
Method for making highly sunproof and anti-infrared tent cloth Download PDFInfo
- Publication number
- CN103757940A CN103757940A CN201410047084.4A CN201410047084A CN103757940A CN 103757940 A CN103757940 A CN 103757940A CN 201410047084 A CN201410047084 A CN 201410047084A CN 103757940 A CN103757940 A CN 103757940A
- Authority
- CN
- China
- Prior art keywords
- fabric
- tent cloth
- infrared
- high light
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for making highly sunproof and anti-infrared tent cloth. The method comprises the following steps: 1) carrying out open width desizing on fabric; 2) performing heat-setting on the fabric which is subjected to open width desizing at a temperature of 190-200 DEG C for 1 min; 3) carrying out rotary screen printing on the heat-set fabric; 4) putting the fabric which is subjected to rotary screen printing on a long-loop steamer, and carrying out long-loop steaming at a temperature of 185 DEG C and at a speed of 20 m/min under the pressure of 0.4 MPa; 5) putting the fabric which is subjected to long-loop steaming on an open width continuous water washing machine, washing by cold water twice at a speed of 40 m/min, and then drying; 6) carrying out water-proof setting on the dried fabric at a temperature of 190-200 DEG C for 1min. The tent cloth which is made with the method can simultaneously have a near-infrared shielding function, excellent color fastness to light and a high water-proof function. The technical processes are short, the operation is simple and convenient and can be carried out on common dyeing equipment, and the economic cost is low.
Description
Technical field
The present invention relates to dyeing and weaving field, be specifically related to a kind of manufacture method of high light-fast anti-infrared tent cloth.
Background technology
Outdoor exercises, with in textiles and military textiles, especially have the tent cloth of camouflage function and combatant's clothes, not only need to have good camouflage function, also should possess sunlight fastness and the high water-proof function of certain wearing comfort, excellence.But the painted of current camouflage color textiles is mainly that coating dye printing product exists feel poor with coating, and the problem that crock fastness is poor causes the decline of wearability; On market, also have and adopt DISPERSE DYES to carry out the tent cloth of stamp, aspect the third dimension of flower type and definition, high Exposure to Sunlight, counter infrared ray, water proofing property, often cannot take into account; In addition, existing camouflage color textiles is in the open in environment, owing to standing the joint effect of direct irradiation of sunlight and ambient temperature and humidity, be very easy to cause dyestuff generation variable color, look on fabric to wither, fade, also can cause the decline of fabric strength, and then affect water pressure resistance and the Practical Performance of fabric simultaneously.
Summary of the invention
Problem to be solved by this invention is to provide a kind of manufacture method of high light-fast anti-infrared tent cloth, the method has solved when General Decentralized dye printing is made tent cloth spends type third dimension poor, the problem that definition is inadequate, if this method is used for printing camouflage color flower type, can better embody the hidden function of vision, and the tent cloth that adopts this method to make can have color fastness to light and the high water-proof function of near-infrared function of shielding, excellence concurrently simultaneously, technological process is shorter, easy and simple to handle, can on general dyeing apparatus, carry out, financial cost is low.
In order to solve the problems of the technologies described above, the present invention adopts following technical scheme: a kind of manufacture method of high light-fast anti-infrared tent cloth, comprises the following steps:
1) to fabric open-width desizing;
2) by the fabric after open-width desizing in 190-200 ℃ of HEAT SETTING 1min;
3) fabric after HEAT SETTING is carried out to ROTARY SCREAM PRINTING;
4) fabric after ROTARY SCREAM PRINTING being placed on loop steamer in temperature is that 185 ℃, pressure are that 0.4MPa, the speed of a motor vehicle are that under 20m/min, long ring evaporates;
5) the long fabric encircling after evaporating being placed on open width continuous washing machine is cold wash 2 roads under 40m/min in the speed of a motor vehicle, then dries;
6) by the fabric of drying waterproof sizing at 190-200 ℃, shaping time is 1min.
Improved, the technology preparation of described open-width desizing comprises desizing agent 4g/L, refining agent 0.5～1g/L, sheet alkali 4～5g/L and chelated dispersants 2g/L.
Improved, the print paste of described ROTARY SCREAM PRINTING comprises DISPERSE DYES 60g/L, emulsification thickener 650g/L, adhesive 100g/L, anti-infrared finishing agent 8g/L.
Improved, described DISPERSE DYES is to have high light fastness and the reflectance curve DISPERSE DYES consistent with natural environment reflectivity.
Improved, described adhesive is any one in 466 adhesives and RSJ adhesive 7-0.
Improved, the printed nickel net that described ROTARY SCREAM PRINTING is used is NOVA nickel screen.
Improved, the waterproofing agent of described waterproof sizing use is bright one-tenth waterproofing agent AG-710.
The terylene OXFORD improved, described fabric is 500D * 500D.
Beneficial effect:
Adopt after technique scheme, this invents a kind of manufacture method of high light-fast anti-infrared tent cloth, 4.5 grades of the water-fastness COLOR FASTNESS > of the tent cloth making, 6 grades of color fastness to light >, resistance to hydrostatic pressure > 100Kpa, basically identical to ultrared reflection and chlorophyll reflexive property near infrared region, tent cloth has color fastness to light and the high water-proof function of near-infrared function of shielding, excellence, flower type is clear, third dimension is strong, technique is reasonable, and financial cost is low.
The specific embodiment
A manufacture method for high light-fast anti-infrared tent cloth, comprises the following steps:
1), to fabric open-width desizing, the technology preparation of described open-width desizing comprises desizing agent 4g/L, refining agent 0.5～1g/L, sheet alkali 4～5g/L and chelated dispersants 2g/L;
2) by the fabric after open-width desizing in 190-200 ℃ of HEAT SETTING 1min;
3) fabric after HEAT SETTING is carried out to ROTARY SCREAM PRINTING, the printed nickel net that described ROTARY SCREAM PRINTING is used is NOVA nickel screen, the print paste of described ROTARY SCREAM PRINTING comprises DISPERSE DYES 60g/L, emulsification thickener 650g/L, adhesive 100g/L, anti-infrared finishing agent 8g/L, wherein, described DISPERSE DYES is to have high light fastness and the reflectance curve DISPERSE DYES consistent with natural environment reflectivity, emulsification thickener used is the composite slurry of multiple natural slurry and synthetic slurry, and described adhesive is any one in 466 adhesives and RSJ adhesive 7-0;
4) fabric after ROTARY SCREAM PRINTING being placed on loop steamer in temperature is that 185 ℃, pressure are that 0.4MPa, the speed of a motor vehicle are that under 20m/min, long ring evaporates;
5) the long fabric encircling after evaporating being placed on open width continuous washing machine is cold wash 2 roads under 40m/min in the speed of a motor vehicle, then dries;
6) by the fabric of drying waterproof sizing at 190-200 ℃, shaping time is 1min, and the waterproofing agent of described waterproof sizing use is bright one-tenth waterproofing agent AG-710.
Described fabric is the terylene OXFORD of 500D * 500D.
Except above preferred embodiment, the present invention also has other embodiment, and those skilled in the art can make according to the present invention various changes and distortion, only otherwise depart from spirit of the present invention, all should belong to the defined scope of claims of the present invention.
Claims (8)
1. a manufacture method for high light-fast anti-infrared tent cloth, is characterized in that: comprise the following steps:
1) to fabric open-width desizing;
2) by the fabric after open-width desizing in 190-200 ℃ of HEAT SETTING 1min;
3) fabric after HEAT SETTING is carried out to ROTARY SCREAM PRINTING;
4) fabric after ROTARY SCREAM PRINTING being placed on loop steamer in temperature is that 185 ℃, pressure are that 0.4MPa, the speed of a motor vehicle are that under 20m/min, long ring evaporates;
5) the long fabric encircling after evaporating being placed on open width continuous washing machine is cold wash 2 roads under 40m/min in the speed of a motor vehicle, then dries;
6) by the fabric of drying waterproof sizing at 190-200 ℃, shaping time is 1min.
2. the manufacture method of a kind of high light-fast anti-infrared tent cloth according to claim 1, is characterized in that: the technology preparation of described open-width desizing comprises desizing agent 4g/L, refining agent 0.5～1g/L, sheet alkali 4～5g/L and chelated dispersants 2g/L.
3. the manufacture method of a kind of high light-fast anti-infrared tent cloth according to claim 1, is characterized in that: the print paste of described ROTARY SCREAM PRINTING comprises DISPERSE DYES 60g/L, emulsification thickener 650g/L, adhesive 100g/L, anti-infrared finishing agent 8g/L.
4. the manufacture method of a kind of high light-fast anti-infrared tent cloth according to claim 3, is characterized in that: described DISPERSE DYES is to have high light fastness and the reflectance curve DISPERSE DYES consistent with natural environment reflectivity.
5. the manufacture method of a kind of high light-fast anti-infrared tent cloth according to claim 3, is characterized in that: described adhesive is any one in 466 adhesives and RSJ adhesive 7-0.
6. the manufacture method of a kind of high light-fast anti-infrared tent cloth according to claim 1, is characterized in that: the printed nickel net that described ROTARY SCREAM PRINTING is used is NOVA nickel screen.
7. the manufacture method of a kind of high light-fast anti-infrared tent cloth according to claim 1, is characterized in that: the waterproofing agent of described waterproof sizing use is bright one-tenth waterproofing agent AG-710.
8. the manufacture method of a kind of high light-fast anti-infrared tent cloth according to claim 1, is characterized in that: the terylene OXFORD that described fabric is 500D * 500D.