CN103771689A - 一种高效节能电光源滤紫外线低羟基石英管的制备方法 - Google Patents

一种高效节能电光源滤紫外线低羟基石英管的制备方法 Download PDF

Info

Publication number
CN103771689A
CN103771689A CN201410034082.1A CN201410034082A CN103771689A CN 103771689 A CN103771689 A CN 103771689A CN 201410034082 A CN201410034082 A CN 201410034082A CN 103771689 A CN103771689 A CN 103771689A
Authority
CN
China
Prior art keywords
preparation
pickling
quartz
quartz pipe
hydroxyl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410034082.1A
Other languages
English (en)
Inventor
黄锋
顾向军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG HUITONG TEXTILE EQUIPMENT CO Ltd
Original Assignee
NANTONG HUITONG TEXTILE EQUIPMENT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG HUITONG TEXTILE EQUIPMENT CO Ltd filed Critical NANTONG HUITONG TEXTILE EQUIPMENT CO Ltd
Priority to CN201410034082.1A priority Critical patent/CN103771689A/zh
Publication of CN103771689A publication Critical patent/CN103771689A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高效节能电光源滤紫外线低羟基石英管的制备方法，精选天然石英石块，将符合的石英石块破碎、酸浸泡，对初步除杂的石英石块进行第一次高温焙烧，进过水淬再粉碎、酸洗，在进行烘干磁选，掺杂氧化物，将混合物投炉制备石英管，对石英管进行酸洗烘干，第二次高温脱羟，对产品进行筛选；本发明的石英管其羟基含量远小于现有同类产品的含量，提高石英管产品的光效，增加光通过率，且产品对低波段的紫外线具有很好的过滤作用，有利于保护人体健康。

Description

一种高效节能电光源滤紫外线低羟基石英管的制备方法
技术领域
本发明涉及一种石英管的制备方法，尤其涉及一种高效节能点官员滤紫外线低羟基石英管的工艺方法。
背景技术
现有市场中的照明产品种类繁多，使用的材料也各有差异，因为各自制造工艺的差别产品的性能也各有差异。
石英管作为新型照明材料，被越来越多的照明企业作为主打原料来使用加工，但在制作工艺方法上，由于石英管在国内是新兴材料，方法上会各有不同，而制作出的石英管产品也各有差异，尤其是在解决提高光效、增加光通量和使用寿命上是急需解决的问题。
发明内容
本发明针对现有技术的不足，提供了一种提高光效、增加光通量和使用寿命的高效节能电光源滤紫外线低羟基石英管的方法。
本发明通过以下技术方案实现：
一种制高效节能电光源滤紫外线低羟基石英管的制备方法，精选天然石英石块，将符合的石英石块破碎、酸浸泡，对初步除杂的石英石块进行第一次高温焙烧，进过水淬再粉碎、酸洗，在进行烘干磁选，掺杂氧化物，将混合物投炉制备石英管，对石英管进行酸洗烘干，第二次高温脱羟，对产品进行筛选。
所述精选天然石英石块为通过切片化验其SiO2及其杂含量，确定符合标准的石英石块。
所述酸浸泡、酸洗所用酸包括HCL和HF。
所述第一次高温焙烧温度为960℃。
所述粉碎、酸洗将石英石块进一步粉碎，形成石英石粉，将石英石粉进行2小时酸洗泡，使石英粉内杂质分解为化学漂浮物逐步排出，降低Fe、k、Ne、Li等12项杂质含量。
所述第二次高温脱羟温度为1100℃。
所述产品筛选通过对产品OHˉ检测，OHˉ含量≤5ppm为合格。
与现有技术相比，具有的有益效果为：本发明的石英管其羟基含量远小于现有同类产品的含量，提高石英管产品的光效，增加光通过率，且产品对低波段的紫外线具有很好的过滤作用，有利于保护人体健康。
具体实施方式
实施例，本发明一种高效节能电光源滤紫外线低羟基石英管的制备方法包括如下步骤，精选天然石英石块，将符合的石英石块破碎、酸浸泡，对初步除杂的石英石块进行第一次高温焙烧，进过水淬再粉碎、酸洗，在进行烘干磁选，掺杂氧化物，将混合物投炉制备石英管，对石英管进行酸洗烘干，第二次高温脱羟，对产品进行筛选；精选天然石英石块为通过切片化验其SiO2及其杂含量，确定符合标准的石英石块；酸浸泡、酸洗所用酸包括HCL和HF；第一次高温焙烧温度为960℃；粉碎、酸洗将石英石块进一步粉碎，形成石英石粉，将石英石粉进行2小时酸洗泡，使石英粉内杂质分解为化学漂浮物逐步排出，降低Fe、k、Ne、Li等12项杂质含量；第二次高温脱羟温度为1100℃；产品筛选通过对产品OHˉ检测，OHˉ含量≤5ppm为合格。

Claims (7)

1.一种高效节能电光源滤紫外线低羟基石英管的制备方法，其特征在于：精选天然石英石块，将符合的石英石块破碎、酸浸泡，对初步除杂的石英石块进行第一次高温焙烧，进过水淬再粉碎、酸洗，在进行烘干磁选，掺杂氧化物，将混合物投炉制备石英管，对石英管进行酸洗烘干，第二次高温脱羟，对产品进行筛选。
2.如权利要求1所述制备方法，其特征在于：所述精选天然石英石块为通过切片化验其SiO2及其杂含量，确定符合标准的石英石块。
3.如权力要求1所述制备方法，其特征在于：所述酸浸泡、酸洗所用酸包括HCL和HF。
4.如权力要求1所述制备方法，其特征在于：所述第一次高温焙烧温度为960℃。
5.如权力要求1所述制备方法，其特征在于：所述酸浸泡时间为进行2小时的酸洗泡，使石英粉内杂质分解为化学漂浮物逐步排出，降低Fe、k、Ne、Li等12项杂质含量。
6.如权力要求1所述制备方法，其特征在于：所述第二次高温脱羟温度为1100℃。
7.如权力要求1所述制备方法，其特征在于：所述产品筛选通过对产品OHˉ检测，OHˉ含量≤5ppm为合格。
CN201410034082.1A 2014-01-24 2014-01-24 一种高效节能电光源滤紫外线低羟基石英管的制备方法 Pending CN103771689A (zh)