CN103741484A - 一种耐酸碱的腈纶织物的制备方法 - Google Patents

一种耐酸碱的腈纶织物的制备方法 Download PDF

Info

Publication number
CN103741484A
CN103741484A CN201310687510.6A CN201310687510A CN103741484A CN 103741484 A CN103741484 A CN 103741484A CN 201310687510 A CN201310687510 A CN 201310687510A CN 103741484 A CN103741484 A CN 103741484A
Authority
CN
China
Prior art keywords
acrylic fabric
acid
alkali
acrylic fibers
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310687510.6A
Other languages
English (en)
Inventor
袁洪兵
陈红霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GOLDSUN HOLDING GROUP CO Ltd
Jiangsu Goldsun Textile Science and Technology Co Ltd
Original Assignee
GOLDSUN HOLDING GROUP CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GOLDSUN HOLDING GROUP CO Ltd filed Critical GOLDSUN HOLDING GROUP CO Ltd
Priority to CN201310687510.6A priority Critical patent/CN103741484A/zh
Publication of CN103741484A publication Critical patent/CN103741484A/zh
Pending legal-status Critical Current

Abstract

一种耐酸碱的腈纶织物的制备方法，包括以下步骤：（1）取聚氨酯树脂一定量，加热到110℃～130℃；（2）取腈纶织物一块，将加热到110℃～130℃的聚氨酯涂布到腈纶织物上表面，腈纶织物上表面聚氨酯层厚度为0.09mm～0.13mm；（3）室温下将液态酚醛树脂涂布在腈纶织物的下表面，涂布的酚醛树脂层厚度为0.11mm～0.16mm；（4）涂布完成后将腈纶织物在60℃～70℃下晾晒5～10h，制备得耐酸碱的腈纶织物。

Description

一种耐酸碱的腈纶织物的制备方法
技术领域
本发明涉及一种腈纶织物的制备方法，特别是涉及一种耐酸碱的腈纶织物的制备方法。
背景技术
在一些工业生产中，员工需要穿着特制的工作服，这些工作服需要具备较强的防备性能，例如抗静电、耐高温、耐酸碱等。其中耐酸碱性能是其中一个比较重要的性能。在生产酸液或碱液的车间中，工作服需要具备较强的耐酸碱性能，若工作服的耐酸碱性能较差，在受到酸液或碱液腐蚀时，会对工作服产生一定的腐蚀，严重的可能会腐蚀到员工。因此，制备一种耐酸碱的工作服是刻不容缓的。
发明内容
要解决的技术问题：普通的腈纶织物耐酸碱性能差的问题。
技术方案：本发明公开了一种耐酸碱的腈纶织物的制备方法，耐酸碱的腈纶织物的制备方法包括以下步骤：（1）取聚氨酯树脂一定量，加热到110℃～130℃；（2）取腈纶织物一块，将加热到110℃～130℃的聚氨酯涂布到腈纶织物上表面，腈纶织物上表面聚氨酯层厚度为0.09mm～0.13mm；（3）室温下将液态酚醛树脂涂布在腈纶织物的下表面，涂布的酚醛树脂层厚度为0.11mm～0.16mm；（4）涂布完成后将腈纶织物在60℃～70℃下晾晒5～10h，制备得耐酸碱的腈纶织物。
其中，将聚氨酯树脂加热的温度优选到110℃。腈纶织物上表面聚氨酯层厚度优选为0.13mm。涂布的酚醛树脂层厚度优选为0.11mm。腈纶织物优选在70℃下晾晒10h。
有益效果：本发明方法制备得到的腈纶织物具有优异的耐酸碱特性，可耐2.5wt%的草酸溶液喷洒后25h至35h无腐蚀现象产生，耐4.5wt%的氢氧化钙溶液喷洒后50h至60h无腐蚀现象产生。
具体实施方式
实施例1
一种耐酸碱的腈纶织物的制备方法，包括以下步骤：（1）取聚氨酯树脂一定量，加热到130℃；（2）取腈纶织物一块，将加热到130℃的聚氨酯涂布到腈纶织物上表面，腈纶织物上表面聚氨酯层厚度为0.09mm；（3）室温下将液态酚醛树脂涂布在腈纶织物的下表面，涂布的酚醛树脂层厚度为0.11mm；（4）涂布完成后将腈纶织物在70℃下晾晒5h，制备得耐酸碱的腈纶织物。
实施例2
一种耐酸碱的腈纶织物的制备方法，包括以下步骤：（1）取聚氨酯树脂一定量，加热到120℃；（2）取腈纶织物一块，将加热到120℃的聚氨酯涂布到腈纶织物上表面，腈纶织物上表面聚氨酯层厚度为0.11mm；（3）室温下将液态酚醛树脂涂布在腈纶织物的下表面，涂布的酚醛树脂层厚度为0.14mm；（4）涂布完成后将腈纶织物在60℃下晾晒10h，制备得耐酸碱的腈纶织物。
实施例3
一种耐酸碱的腈纶织物的制备方法，包括以下步骤：（1）取聚氨酯树脂一定量，加热到110℃；（2）取腈纶织物一块，将加热到110℃的聚氨酯涂布到腈纶织物上表面，腈纶织物上表面聚氨酯层厚度为0.13mm；（3）室温下将液态酚醛树脂涂布在腈纶织物的下表面，涂布的酚醛树脂层厚度为0.16mm；（4）涂布完成后将腈纶织物在65℃下晾晒8h，制备得耐酸碱的腈纶织物。
将实施例1、实施例2、实施例3制备得到的腈纶织物进行耐酸碱试验。将实施例1、实施例2、实施例3的表面均匀喷洒上2.5wt%的草酸溶液，室温下放置时间分别为25h、30h、35h。再将实施例1、实施例2、实施例3的表面均匀喷洒上4.5wt%的氢氧化钙溶液，室温下放置时间分别为50h、55h、60h。结果见下表。
  实施例1 实施例2 实施例3
2.5wt%的草酸溶液 25h后无腐蚀现象 30h后无腐蚀现象 35h后无腐蚀现象
4.5wt%的氢氧化钙溶液 50h后无腐蚀现象 55h后无腐蚀现象 60h后无腐蚀现象
制备得到的腈纶织物具有优异的耐弱酸和弱碱的特性，可以用于一定程度上防备酸碱的腐蚀，提高工作服的安全系数。

Claims (5)

1. 一种耐酸碱的腈纶织物的制备方法，其特征在于耐酸碱的腈纶织物的制备方法包括以下步骤：（1）取聚氨酯树脂一定量，加热到110℃～130℃；（2）取腈纶织物一块，将加热到110℃～130℃的聚氨酯涂布到腈纶织物上表面，腈纶织物上表面聚氨酯层厚度为0.09mm～0.13mm；（3）室温下将液态酚醛树脂涂布在腈纶织物的下表面，涂布的酚醛树脂层厚度为0.11mm～0.16mm；（4）涂布完成后将腈纶织物在60℃～70℃下晾晒5～10h，制备得耐酸碱的腈纶织物。
2. 根据权利要求1所述的一种耐酸碱的腈纶织物的制备方法，其特征在于将聚氨酯树脂加热到110℃。
3. 根据权利要求1所述的一种耐酸碱的腈纶织物的制备方法，其特征在于腈纶织物上表面聚氨酯层厚度为0.13mm。
4. 根据权利要求1所述的一种耐酸碱的腈纶织物的制备方法，其特征在于涂布的酚醛树脂层厚度为0.11mm。
5. 根据权利要求1所述的一种耐酸碱的腈纶织物的制备方法，其特征在于腈纶织物在70℃下晾晒10h。
CN201310687510.6A 2013-12-17 2013-12-17 一种耐酸碱的腈纶织物的制备方法 Pending CN103741484A (zh)