CN103739789A - 一种聚羧酸减水剂的简易合成方法 - Google Patents

一种聚羧酸减水剂的简易合成方法 Download PDF

Info

Publication number
CN103739789A
CN103739789A CN201310749183.2A CN201310749183A CN103739789A CN 103739789 A CN103739789 A CN 103739789A CN 201310749183 A CN201310749183 A CN 201310749183A CN 103739789 A CN103739789 A CN 103739789A
Authority
CN
China
Prior art keywords
water
raw material
simple synthesis
reducer
synthesis method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310749183.2A
Other languages
English (en)
Inventor
宫振鑫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DALIAN MINGYUANQUAN TECHNOLOGY DEVELOPMENT Co Ltd
Original Assignee
DALIAN MINGYUANQUAN TECHNOLOGY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DALIAN MINGYUANQUAN TECHNOLOGY DEVELOPMENT Co Ltd filed Critical DALIAN MINGYUANQUAN TECHNOLOGY DEVELOPMENT Co Ltd
Priority to CN201310749183.2A priority Critical patent/CN103739789A/zh
Publication of CN103739789A publication Critical patent/CN103739789A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种聚羧酸减水剂的简易合成方法，原料组成：a烯丙基聚乙二醇、b顺丁烯二酸酐、c烯丙基磺酸钠、d次硫酸氢钠、e双氧水；合成步骤：将a，b，c，d加入装有适量水的反应釜中，搅拌至完全溶化，混合均匀，用适量水将e稀释后加入反应釜，搅拌1小时，反应结束，加适量液碱将反应物中和至PH至6-7。本发明的方法合成的聚羧酸减水剂减水率较高，能达到26.5，而且其生产方法简单，生产成本低，具备较高的性价比。

Description

一种聚羧酸减水剂的简易合成方法
技术领域
本发明涉及混凝土减水剂，具体是一种聚羧酸减水剂的简易合成方法。
背景技术
萘系高效减水剂在我国诞生,这标志着我国的减水剂研究进入高效减水剂时期，尽管萘系减水剂减水率较高,但混凝土坍落度损失过快,难以满足实际工程的施工要求,而复合产品质量不稳定,往往影响到混凝土的凝结硬化和耐久性:另外, 萘系产品的原料日益缺乏,价格上涨,因此需要研究性能更先进的减水剂新品种,所以非萘系减水剂产品市场前景广阔。为此，聚羧酸系减水剂将是高强高流动性混凝土、大掺量粉煤灰混凝土最重要的组成材料,其前景将会愈来愈广阔。
发明内容
本发明的目的是提供一种聚羧酸减水剂的简易合成方法，该生产方法简单、生产成本低，具有较高的性价比。
本发明的技术方案是这样实现的：聚羧酸减水剂的简易合成方法，原料组成：a烯丙基聚乙二醇、b顺丁烯二酸酐、c烯丙基磺酸钠、d次硫酸氢钠、e双氧水；合成步骤：将a，b，c，d加入装有适量水的反应釜中，搅拌至完全溶化，混合均匀，用适量水将e稀释后加入反应釜，搅拌1小时，反应结束，加适量液碱将反应物中和至PH至6-7。
所述原料的摩尔比为：a：b：c=1:2:0.3～0.5。
所述原料e的用量为a、b和c总重量的1-2%。
所述原料d的用量为a、b和c总重量的0.8-1%。
所述原料的优选摩尔比为：a：b：c=1:2:0.4。
本发明的有益效果为：本发明的方法合成的聚羧酸减水剂减水率较高，能达到26.5，而且其生产方法简单，生产成本低，具备较高的性价比。
具体实施方式
下面结合具体实施例对本发明作进一步解释说明。
实施例1
聚羧酸减水剂的简易合成方法，原料组成：a烯丙基聚乙二醇、b顺丁烯二酸酐、c烯丙基磺酸钠、d次硫酸氢钠、e双氧水；合成步骤：将a，b，c，d加入装有适量水的反应釜中，搅拌至完全溶化，混合均匀，用适量水将e稀释后加入反应釜，搅拌1小时，反应结束，加适量液碱将反应物中和至PH至6-7。
所述原料的摩尔比为：a：b：c=1:2:0.4。
所述原料e的用量为a、b和c总重量的1.5%。
所述原料d的用量为a、b和c总重量的0.8%。
实施例2
聚羧酸减水剂的简易合成方法，原料组成：a烯丙基聚乙二醇、b顺丁烯二酸酐、c烯丙基磺酸钠、d次硫酸氢钠、e双氧水；合成步骤：将a，b，c，d加入装有适量水的反应釜中，搅拌至完全溶化，混合均匀，用适量水将e稀释后加入反应釜，搅拌1小时，反应结束，加适量液碱将反应物中和至PH至6-7。
所述原料的摩尔比为：a：b：c=1:2:0.3。
所述原料e的用量为a、b和c总重量的1%。
所述原料d的用量为a、b和c总重量的1%。
实施例3
聚羧酸减水剂的简易合成方法，原料组成：a烯丙基聚乙二醇、b顺丁烯二酸酐、c烯丙基磺酸钠、d次硫酸氢钠、e双氧水；合成步骤：将a，b，c，d加入装有适量水的反应釜中，搅拌至完全溶化，混合均匀，用适量水将e稀释后加入反应釜，搅拌1小时，反应结束，加适量液碱将反应物中和至PH至6-7。
所述原料的摩尔比为：a：b：c=1:2: 0.5。
所述原料e的用量为a、b和c总重量的2%。
所述原料d的用量为a、b和c总重量的0.9%。
按上述方法合成40%聚羧酸减水剂，对本合成产品检测结果见下表。
产品 掺量% 减水率 含气量
实施例1 0.5 26.5 4.1%
实施例2 0.5 25.6 3.9%
实施例3 0.5 25.7 4.4%
   以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明披露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (5)

1.聚羧酸减水剂的简易合成方法，其特征在于：
原料组成：a烯丙基聚乙二醇、b顺丁烯二酸酐、c烯丙基磺酸钠、d次硫酸氢钠、e双氧水；
合成步骤：将a，b，c，d加入装有适量水的反应釜中，搅拌至完全溶化，混合均匀，用适量水将e稀释后加入反应釜，搅拌1小时，反应结束，加适量液碱将反应物中和至PH至6-7。
2.根据权利要求1所述的聚羧酸减水剂的简易合成方法，其特征在于:所述原料的摩尔比为：a：b：c=1:2:0.3～0.5。
3.根据权利要求1所述的聚羧酸减水剂的简易合成方法，其特征在于:所述原料e的用量为a、b和c总重量的1-2%。
4.根据权利要求1所述的聚羧酸减水剂的简易合成方法，其特征在于:所述原料d的用量为a、b和c总重量的0.8-1%。
5.根据权利要求2所述的聚羧酸减水剂的简易合成方法，其特征在于，所述原料的摩尔比为：a：b：c=1:2:0.4。
CN201310749183.2A 2013-12-31 2013-12-31 一种聚羧酸减水剂的简易合成方法 Pending CN103739789A (zh)