CN103737204A - 一种氧化银焊接材料的制备方法 - Google Patents

一种氧化银焊接材料的制备方法 Download PDF

Info

Publication number
CN103737204A
CN103737204A CN201310714930.9A CN201310714930A CN103737204A CN 103737204 A CN103737204 A CN 103737204A CN 201310714930 A CN201310714930 A CN 201310714930A CN 103737204 A CN103737204 A CN 103737204A
Authority
CN
China
Prior art keywords
silver oxide
welding material
stainless steel
steel band
spraying machine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310714930.9A
Other languages
English (en)
Other versions
CN103737204B (zh
Inventor
钱云春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Laixun Environmental System Technology Co ltd
Original Assignee
SUZHOU HONGQUAN HIGH VOLTAGE CAPACITOR Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU HONGQUAN HIGH VOLTAGE CAPACITOR Co Ltd filed Critical SUZHOU HONGQUAN HIGH VOLTAGE CAPACITOR Co Ltd
Priority to CN201310714930.9A priority Critical patent/CN103737204B/zh
Publication of CN103737204A publication Critical patent/CN103737204A/zh
Application granted granted Critical
Publication of CN103737204B publication Critical patent/CN103737204B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种氧化银焊接材料的制备方法，包括以下步骤：（1）取不锈钢带，清洁表面；（2）将氧化银粉末装入喷雾机中，再将喷雾机固定移动装置上匀速移动；（3）在不锈钢带的上表面涂上一层粘胶；（4）开启喷雾机对不锈钢带上表面进行喷雾形成涂层，重复喷雾2-4次得涂层，自然干燥；（5）再对不锈钢带的下表面进行同样处理最后得到氧化银焊接材料。本发明采用粘胶方式制备氧化银焊接材料，方法简单，易操作，所得焊接材料表面平整，性能上，银具有良好的导电性和流动性，所以焊接材料在焊接时与基板之间润湿力大，接头韧性好。另外，本发明的焊接材料可以作为母材使用，扎压后的不同规格的焊材接料。

Description

一种氧化银焊接材料的制备方法
技术领域
本发明涉及一种氧化银焊接材料的制备方法。
背景技术
银具有良好的导电、导热性，作为焊接材料，焊接点平整，接触电阻低且稳定。常规的焊接材料都采用熔炼的方法制备，由于不同种材料混合，冷轧过程也会造成各成分分布不均。银的价格昂贵，因为要采用高效利用银材料的制备方法，提高焊接材料的质量和性能。
发明内容
针对现有技术的不足，本发明提供了一种氧化银焊接材料的制备方法。
为解决现有技术问题本发明采用的技术方案为：一种氧化银焊接材料的制备方法，包括以下步骤：
（1）取厚度为0.5-0.8mm不锈钢带，清洁表面；
（2）将氧化银粉末装入喷雾机中，喷雾机的喷头直径为0.05-0.10cm，再将喷雾机固定移动装置上，匀速移动速率为0.05-0.10cm/s； 
（3）在不锈钢带的上表面涂上一层粘胶，厚度为0.01-0.03mm；
（4）开启喷雾机对不锈钢带上表面进行喷雾形成涂层，重复喷雾2-4次得涂层，自然干燥；
（5）再对不锈钢带的下表面进行同样处理最后得到氧化银焊接材料。
优选的是，所述的氧化银粉末粒径为100-180nm。
优选的是，所述的涂层厚度为0.01-0.03mm。
有益效果：本发明采用粘胶方式制备氧化银焊接材料，方法简单，易操作，所得焊接材料表面平整，性能上，银具有良好的导电性和流动性，所以焊接材料在焊接时与基板之间润湿力大，接头韧性好。另外，本发明的焊接材料可以作为母材使用，扎压后的不同规格的焊材接料。 
具体实施方式
下面通过具体实施例对本发明作进一步详细介绍。
实施例1
一种氧化银焊接材料的制备方法，包括以下步骤：
（1）取厚度为0.5mm不锈钢带，清洁表面；
（2）将氧化银粉末装入喷雾机中，喷雾机的喷头直径为0.05cm，再将喷雾机固定移动装置上，匀速移动速率为0.05cm/s； 
（3）在不锈钢带的上表面涂上一层粘胶，厚度为0.01mm；
（4）开启喷雾机对不锈钢带上表面进行喷雾形成涂层，重复喷雾2次得涂层厚度为0.01mm，自然干燥；
（5）再对不锈钢带的下表面进行同样处理最后得到氧化银焊接材料。
实施例2
一种氧化银焊接材料的制备方法，包括以下步骤：
（1）取厚度为0.8mm不锈钢带，清洁表面；
（2）将氧化银粉末装入喷雾机中，喷雾机的喷头直径为0.10cm，再将喷雾机固定移动装置上，匀速移动速率为0.10cm/s； 
（3）在不锈钢带的上表面涂上一层粘胶，厚度为0.03mm；
（4）开启喷雾机对不锈钢带上表面进行喷雾形成涂层，重复喷雾4次得涂层厚度为0.03mm，自然干燥；
（5）再对不锈钢带的下表面进行同样处理最后得到氧化银焊接材料。
实施例3
一种氧化银焊接材料的制备方法，包括以下步骤：
（1）取厚度为0.6mm不锈钢带，清洁表面；
（2）将氧化银粉末装入喷雾机中，喷雾机的喷头直径为0.08cm，再将喷雾机固定移动装置上，匀速移动速率为0.08cm/s； 
（3）在不锈钢带的上表面涂上一层粘胶，厚度为0.02mm；
（4）开启喷雾机对不锈钢带上表面进行喷雾形成涂层，重复喷雾3次得涂层厚度为0.02mm，自然干燥；
（5）再对不锈钢带的下表面进行同样处理最后得到氧化银焊接材料。
将本发明所得的焊接材料应用于试验，所得结果为熔点在500-610℃，润角为25-30°，接头有较好的任性，导线能力强，耐腐蚀性能好。
另外，本发明不限于上述实施方式，只要在不超出本发明的范围内，可以采取各种方式实施本发明。

Claims (3)

1.一种氧化银焊接材料的制备方法，其特征在于包括以下步骤：
（1）取厚度为0.5-0.8mm不锈钢带，清洁表面；
（2）将氧化银粉末装入喷雾机中，喷雾机的喷头直径为0.05-0.10cm，再将喷雾机固定移动装置上，匀速移动速率为0.05-0.10cm/s； 
（3）在不锈钢带的上表面涂上一层粘胶，厚度为0.01-0.03mm；
（4）开启喷雾机对不锈钢带上表面进行喷雾形成涂层，重复喷雾2-4次得涂层，自然干燥；
（5）再对不锈钢带的下表面进行同样处理最后得到氧化银焊接材料。
2.根据权利要求1所述的一种氧化银焊接材料的制备方法，其特征在于：所述的氧化银粉末粒径为100-180nm。
3.根据权利要求1所述的一种氧化银焊接材料的制备方法，其特征在于：所述的涂层厚度为0.01-0.03mm。
CN201310714930.9A 2013-12-23 2013-12-23 一种氧化银焊接材料的制备方法 Active CN103737204B (zh)