CN103709860A - 一种有机硅自洁弹性拉毛涂料 - Google Patents
一种有机硅自洁弹性拉毛涂料 Download PDFInfo
- Publication number
- CN103709860A CN103709860A CN201310674195.3A CN201310674195A CN103709860A CN 103709860 A CN103709860 A CN 103709860A CN 201310674195 A CN201310674195 A CN 201310674195A CN 103709860 A CN103709860 A CN 103709860A
- Authority
- CN
- China
- Prior art keywords
- coating
- self
- organosilicon
- elastic
- cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的一种有机硅自洁弹性拉毛涂料的具体组分和重量比例是:水:3-8%;润湿剂:0.1-0.2%;分散剂:0.4-0.8%;丙二醇:1-2%;消泡剂:0.1-0.3%;钛白粉:1-2%;重钙:35-40%;沉淀硫酸钡:3-8%;硅灰石3-8%:有机硅荷性乳液:6-10%;弹性乳液:30-36%;Texanol:0.5-1%;杀菌剂0.1-0.2%;防腐剂:0.1-0.2%;增稠剂:0.6-0.9%。该弹性拉毛涂料不仅具有较强的质感,还具有较好的耐候性、耐水性、耐碱性,耐沾污性能优良,涂层具有“自洁”功能。
Description
技术领域 本发明涉及一种涂料,特别涉及一种用于建筑物内外墙表面的保护和装饰,具有较强质感装饰功能、高耐沾污性能的有机硅自洁弹性拉毛涂料,属于化工涂料技术领域。
背景技术 在建筑外墙涂料中,弹性涂料由于其具有弹性拉伸好、能够有效的遮盖墙体的裂纹,因而逐渐成为了外墙装饰中的主导材料。在弹性涂料中,弹性拉毛涂料具有凹凸质感和纹理,可以修补墙体裂纹,饰面效果突出,立体感强,因而受到了人们的喜爱。虽然弹性拉毛涂料立体装饰感强,能够形成强烈的视觉效果,但是其耐沾污性能差。尤其是在环境污染日益严重的今天,大气中的灰尘以及悬浮物质较多,凹凸的纹理更容易沾染污染物而影响墙体的装饰效果。因此提高弹性拉毛涂料的耐沾污性成了我们急需解决的问题。
发明内容 本发明的目的是提供一种有机硅自洁弹性拉毛涂料,该弹性拉毛涂料不仅具有较强的质感,还具有较好的耐候性、耐水性、耐碱性,耐沾污性能优良,涂层具有“自洁”功能。
本发明的一种有机硅自洁弹性拉毛涂料的具体组分和重量比例是:水:3-8%;润湿剂:0.1-0.2%;分散剂:0.4-0.8%;丙二醇:1-2%;消泡剂:0.1-0.3%;钛白粉:1-2%;重钙:35-40%;沉淀硫酸钡:3-8%;硅灰石3-8%:有机硅荷性乳液:6-10%;弹性乳液:30-36%;Texanol:0.5-1%;杀菌剂0.1-0.2%;防腐剂:0.1-0.2%;增稠剂:0.6-0.9%。
由于弹性拉毛涂料是使用涂膜拉毛的施工方法而得到一种凹凸起伏的涂膜外观,因此需要施工时的涂料粘度较高。因此需要涂料具有较高的触变粘度,即在高剪切作用下涂料粘度较低,而在低剪切作用下粘度较高,流动性较弱。因此我们在产品中使用了含有酸性基团的交联型高分子乳液增稠体系与碱溶胀增稠复配体系,使产品具有较好的施工粘度。同时有机硅荷性乳液的加入,利用Si-OH和-OH-的多重交联化学反应,可使涂层具有极低的表面张力,从而保持有极佳的疏水效果,使涂层具有良好的耐候性和耐沾污性。
本发明使用的乳液为新型特殊结构的有机硅氧烷改性聚合乳液,在干燥成膜中其中Si-OH之间以及和基材上的-OH-发生多重交联化学反应,可使涂层有极低的表面张力,能够保持极佳的疏水效果,耐沾污性能良好,并且与其他乳液有着良好的复配型,性能稳定。
本发明使用的乳液是一种100%纯丙烯酸弹性乳液,在室温下能够产生自交联,具有良好的弹性,常温不易回粘;不含保护胶体,无需成膜助剂,低VOV含量,绿色环保;并且与众多颜填料具有良好的相容性,使产品具有良好的弹性、耐擦洗性、耐水性和耐碱性,附着力良好。
本发明使用的分散剂使聚羧酸盐型的阴离子表面活性剂,具有卓越的润湿分散性能,发泡性地,能够有效的改善涂料的流动性,具有稳定浆料粘度的优异性能。
本发明使用的消泡剂是一种特殊非离子硅化合物,具备优异的消泡能力,并且消泡能力稳定,能够防止该产品在施工过程中再发泡,可以得到没有残泡的理想涂膜。
本发明使用的增稠剂是碱溶胀性与含有酸性基团的交联型高分子乳液增稠的复配增稠体系。该增稠体系能够有效的改进低剪切粘度,使涂料具有较高的加速性,具有优异的纹理保持性、极好的抗流挂性能,并且能够较好的降低滚飞溅性。
本发明的生产工艺将上述重量比的组分在常温下进行混合,在低速搅拌下加入部分水、润湿剂、分散剂、丙二醇、前期消泡剂、钛白粉、沉淀硫酸钡、重钙、硅灰石,高速分散后研磨至浆料细度≤100um后,低速搅拌加入有机硅荷性乳液、弹性乳液、Texanol、后期消泡剂、防腐剂、杀菌剂、增稠剂达到要求的粘度后,再低速搅拌10min,再经过检验、过滤、称重包装。
具体实施方式 下面是本发明的一个实施例。
本发明的一种有机硅自洁弹性拉毛涂料的组成(重量百分比)及生产工艺为:低速搅拌阶段依照顺序加入5份的去离子水、0.1份的润湿剂X405、0.5份聚羧酸盐分散剂5040、1份丙二醇、0.2份的消泡剂B-199、2份金红石型钛白粉237、6份细度为325目的沉淀硫酸钡、36份的细度为400目的重质碳酸钙、6份细度800目的硅灰石,待全部加入后进入高速搅拌阶段,待搅拌均匀后高速研磨至细度≤100um,然后在低速搅拌下依次加入9.5份的有机硅荷性乳液、32份弹性乳液3131、0.5份的Texanol、0.25份的消泡剂B-199、0.15份的防腐剂MV、0.4份碱溶胀增稠剂H1130,0.4份酸性基团增稠剂ASE-60,再低速搅拌10min,再经过检验、过滤、称重包装。
依据本发明制作的一种有机硅自洁弹性拉毛涂料其各项指标均达到JG/T172-2005关于弹性建筑涂料所规定的要求,而且具有优异的防水性能、耐候性,能显著改善墙体的防水性能;并且耐沾污性能有了良好的提升,弹性好,抗拉伸性能强,能够有效覆盖建筑物上的小裂缝,可保证建筑物外墙表面能长久地保持清洁华丽的表面,经过特殊工艺施工具有立体质感,装饰性能好,广泛适用于各种外墙的装饰装修当中。客户反应效果良好。
Claims (4)
1.本发明的一种有机硅自洁弹性拉毛涂料的具体组分和重量比例是:水:3-8%;润湿剂:0.1-0.2%;分散剂:0.4-0.8%;丙二醇:1-2%;消泡剂:0.1-0.3%;钛白粉:1-2%;重钙:35-40%;沉淀硫酸钡:3-8%;硅灰石3-8%:有机硅荷性乳液:6-10%;弹性乳液:30-36%;Texanol:0.5-1%;杀菌剂0.1-0.2%;防腐剂:0.1-0.2%;增稠剂:0.6-0.9%。
2.根据权利要求1所述的一种有机硅自洁弹性拉毛涂料,其特征是所说的利用Si-OH和-OH-的多重交联化学反应,可使涂层具有极低的表面张力,从而保持有极佳的疏水效果,使涂层具有良好的耐候性和耐沾污性。
3.根据权利要求1所述的一种有机硅自洁弹性拉毛涂料,其特征是所说的消泡剂是一种特殊非离子硅化合物,具备优异的消泡能力,并且消泡能力稳定。
4.根据权利要求1所述的一种有机硅自洁弹性拉毛涂料,其特征是所说的生产工艺将上述重量比的组分在常温下进行混合,在低速搅拌下加入部分水、润湿剂、分散剂、丙二醇、前期消泡剂、钛白粉、沉淀硫酸钡、重钙、硅灰石,高速分散后研磨至浆料细度≤100um后,低速搅拌加入有机硅荷性乳液、弹性乳液、Texanol、后期消泡剂、防腐剂、杀菌剂、增稠剂达到要求的粘度后,再低速搅拌10min,再经过检验、过滤、称重包装。