CN103952020A - 一种水性外墙耐候型热反射隔热涂料及其制备方法 - Google Patents
一种水性外墙耐候型热反射隔热涂料及其制备方法 Download PDFInfo
- Publication number
- CN103952020A CN103952020A CN201410161046.1A CN201410161046A CN103952020A CN 103952020 A CN103952020 A CN 103952020A CN 201410161046 A CN201410161046 A CN 201410161046A CN 103952020 A CN103952020 A CN 103952020A
- Authority
- CN
- China
- Prior art keywords
- agent
- mixture
- exterior wall
- resistant heat
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种水性外墙耐候型热反射隔热涂料及其制备方法,涉及一种建筑涂料及其制备方法,各组分包括丙烯酸乳液、甲基丙烯酸双环戊二烯氧基乙酯(DPOMA)、钛白粉、云母粉、填料、空心玻璃微珠、防冻剂、中和剂、湿润剂、分散剂、消泡剂、罐内防腐剂、漆膜防霉剂、增稠剂、疏水剂。工业为按各组分的重量份配比准备物料,再将准备的乳液等物料按顺序加入搅拌缸中,将准备的物料中的粉料浆采用研磨机进行研磨,把研磨后的粉料浆加入到搅拌缸中,开启低速搅拌,再加入颜填料等物料,加完后再搅拌,对得到的产品进行检测、过滤、包装。制备的涂料具有耐候性好、抗开裂性强、无有机物挥发,涂料对于基材附着力好、热反射效率高。
Description
技术领域
本发明涉及一种建筑涂料及其制备方法,特别是涉及一种水性外墙耐候型热反射隔热涂料及其制备方法。
背景技术
目前,国内处于高端功能涂料的快速发展时期。传统热反射隔热涂料中的有机溶剂在涂附过程中大量挥发严重污染空气质量,同时浪费生产原料原料,生产过程污染严重,不符合当今绿色环保的理念。
针对传统热反射隔热涂料的弊端,我们研制出水性外墙耐候型热反射隔热涂料。其通过功能性单体兼活性稀释剂DPOMA与预聚物树脂产生网状交联结构,使涂料的附着力增强,延长使用年限,同时避免了有机溶剂的挥发,减少了对大气的污染。该涂料克服了市场上同类产品的通病,又有效的利用了石油精炼过程中产生的副产——双环戊二烯,扩大了应用领域,提升了双环戊二烯的经济价值。该涂料节能、低碳、环保、是真正意义上的绿色涂料。
发明内容
本发明的目的在于提供一种水性外墙耐候型热反射隔热涂料及其制备方法,本发明所制得的水性外墙耐候型热反射隔热涂料具有耐候性好、抗开裂性强、无有机物挥发,对于基材附着力好、热反射效率高等特点。
本发明的目的是通过以下技术方案实现的:
一种水性外墙耐候型热反射隔热涂料,所述涂料各组份的重量份为:丙烯酸乳液30-40份;DPOMA8-13份;钛白粉10-15份;云母粉3-8份;长石粉10-20份;重质珍珠岩粉10-20份;三聚磷酸铝2-5份;磷酸锌5-10份;空心玻璃微珠6-10份;混合助剂 0.5-2份。
所述的一种水性外墙耐候型热反射隔热涂料,所述乳液为有机硅氟改性苯丙乳液,该乳液是以N-烯丙基全氟戊及磺酰胺、乙烯基三乙氧基硅烷、苯乙烯、丙烯酸丁酯、丙烯酸为主要单体,马来酸十二酯为反应性乳化剂,过硫酸铵为引发剂而制得的,固含为55%,pH为5.0,颗粒的粒径为0.4微米,产品粘度为550cp,产品最低成膜温度10℃;
所述DPOMA,为甲基丙烯酸双环戊二烯氧基乙酯的英文名称首字母缩写,其是由甲基丙烯酸,双环戊二烯,乙二醇合成的具有增韧作用的水性/油性两用的增韧树脂;DPOMA外观透明液体,黏度为0.018( mPa·s) ,22℃折光系数为1.496,一个大气压下沸点为350℃,玻璃化温度为40-50℃;
所述钛白粉为采用氯化物工艺生产的多用途金红石二氧化钛颜料;
所述云母粉为白度为70-80%,pH值为7-8,松散密度为2.6g/cm3的湿法绢云母粉,其细度小于1250目;
所述填料为细度小于1250目的易分散型长石粉、重质珍珠岩、三聚磷酸铝、磷酸锌的任意一种或一种以上的混合物;
所述空心玻璃微珠为白色,成园率在97%以上,热传导系数为0.003-0.01BTU/in.hr.℉,表面经过偶联剂处理过的空心玻璃微珠;
所述防冻剂为丙二醇或聚丙二醇中的任意一种或一种以上的混合物;
所述中和剂为2-氨基-2-甲基-1-丙醇、二甲基乙醇胺、乙醇胺、氢氧化钠、氢氧化钾中的任意一种或一种以上的混合物;
所述湿润剂为非离子表面活性稀释剂,该湿润剂为聚氧乙烯烷芳基醚、聚氧乙烯多元醇醚、聚氧乙酯聚氧丙烯酸嵌段共聚物、脂肪酸聚乙二醇酯、多元醇酯、脂肪胺聚氧乙烯醚加成物中的任意一种或一种以上的混合物;
所述分散剂为高分子共聚物、聚羧酸铵、油酰基环氧烷共聚物、聚硅氧烷、聚丙烯酸铵中的任意一种或一种以上的混合物;
所述消泡剂为有机硅消泡剂、矿物油基含硅及多种混合物、脂肪烃的乳化物、非硅酮有机酯碳氢化合物、非硅酮胺类碳氢化合物、含疏水粒子矿物油混合物中的任意一种或一种以上的混合物;
所述罐内防腐剂为1,2-苯并异噻唑啉-3-酮(BIT)、2-甲基-5-氯-4-异噻咪唑-3-酮和 2-甲基-4-异噻咪唑-3-酮(CMIT/MIT)的混合物。
所述的一种水性外墙耐候型热反射隔热涂料,漆膜防霉剂为碘代丙炔基氨基甲酸酯、苯并咪唑氨基甲酸甲酯与N/-(3,4-二氯苯基)-N,N-二甲基脲的复配体中的任意一种或一种以上的混合物。
所述的一种水性外墙耐候型热反射隔热涂料,所述增稠剂为聚氨酯增稠剂和改性聚脲增稠剂的任意一种或一种以上的混合物。
所述的一种水性外墙耐候型热反射隔热涂料,所述疏水剂是改性的有机硅助剂。
一种水性外墙耐候型热反射隔热涂料的制备方法,所述方法包括如下制备步骤:
(1)首先将甲基丙烯酸酯、DPOMA及助剂混合物在配料缸中充分搅拌15min;
(2)加入颜填料等分散均匀至细小度小于30μm后加入空心玻璃微珠继续搅拌15min;
(3)对上一步骤得到的产品进行检测,检测合格后过滤、包装即可。
所述的一种水性外墙耐候型热反射隔热涂料的制备方法,所述过滤器的筛网目数为60-80目。
本发明的优点与效果是:
本发明通过添加功能单体兼活性稀释剂DPOMA、空心玻璃微珠等克服了传统热反射隔热涂料耐候性差、挥发有机溶剂、使用年限短等问题。所制得的水性外墙耐候型热反射隔热涂料具有耐候性好、抗开裂性强、无有机物挥发,对于基材附着力好、热反射效率高等优点。避免了有机溶剂挥发对空气的污染,使其成为绿色环保的涂料产品。
具体实施方式
下面结合实施例,对本发明作进一步详述。
本发明的水性外墙耐候型热反射隔热涂料的配方,各组合成份包括:
丙烯酸乳液30-40份;DPOMA8-13份;钛白粉10-15份;云母粉3-8份;长石粉10-20份;重质珍珠岩粉10-20份;三聚磷酸铝2-5份;磷酸锌5-10份;空心玻璃微珠6-10份;混合助剂 0.5-2份。
其中乳液是有机硅氟改性苯丙乳液,该乳液是以N-烯丙基全氟戊及磺酰胺、乙烯基三乙氧基硅烷、苯乙烯、丙烯酸丁酯、丙烯酸为主要单体,马来酸十二酯为反应性乳化剂,过硫酸铵为引发剂而制得的,固含为55%,pH为5.0,颗粒的粒径为0.4微米,产品粘度为550cp,产品最低成膜温度10℃。所述DPOMA,为甲基丙烯酸双环戊二烯氧基乙酯的英文名称首字母缩写,其是由甲基丙烯酸,双环戊二烯,乙二醇合成的具有增韧作用的水性/油性两用的增韧树脂。所述DPOMA外观透明液体,黏度为0.018( mPa·s) ,22℃折光系数为1.496,一个大气压下沸点为350℃,玻璃化温度为40-50℃。所述钛白粉是一种采用氯化物工艺生产的多用途金红石二氧化钛颜料,具有高光泽、易分散、高遮盖力和极佳的耐久性。所述云母粉为白度为70-80%,pH值为7-8,松散密度为2.6g/cm3的湿法绢云母粉,其细度小于1250目。所述填料为细度小于1250目的易分散型长石粉、重质珍珠岩、三聚磷酸铝、磷酸锌的任意一种或一种以上的混合物。所述空心玻璃微珠是白色,成园率在97%以上,热传导系数为0.003-0.01BTU/in.hr.℉的,表面经过偶联剂处理过的空心玻璃微珠。所述防冻剂为丙二醇或聚丙二醇中的任意一种或一种以上的混合物。所述中和剂为2-氨基-2-甲基-1-丙醇、二甲基乙醇胺、乙醇胺、氢氧化钠、氢氧化钾中的任意一种或一种以上的混合物。所述湿润剂为非离子表面活性稀释剂,该湿润剂为聚氧乙烯烷芳基醚、聚氧乙烯多元醇醚、聚氧乙酯聚氧丙烯酸嵌段共聚物、脂肪酸聚乙二醇酯、多元醇酯、脂肪胺聚氧乙烯醚加成物中的任意一种或一种以上的混合物。所述分散剂为高分子共聚物、聚羧酸铵、油酰基环氧烷共聚物、聚硅氧烷、聚丙烯酸铵中的任意一种或一种以上的混合物。所述消泡剂为有机硅消泡剂、矿物油基含硅及多种混合物、脂肪烃的乳化物、非硅酮有机酯碳氢化合物、非硅酮胺类碳氢化合物、含疏水粒子矿物油混合物中的任意一种或一种以上的混合物。所述罐内防腐剂为1,2-苯并异噻唑啉-3-酮(BIT)、2-甲基-5-氯-4-异噻咪唑-3-酮和2-甲基-4-异噻咪唑-3-酮(CMIT/MIT)的混合物。所述漆膜防霉剂为碘代丙炔基氨基甲酸酯、苯并咪唑氨基甲酸甲酯与N/-(3,4-二氯苯基)-N,N-二甲基脲的复配体中的任意一种或一种以上的混合物。所述增稠剂为聚氨酯增稠剂和改性聚脲增稠剂的任意一种或一种以上的混合物。所述疏水剂是一种改性的有机硅助剂。
采用上述水性外墙耐候型热反射隔热涂料的配方生产水性外墙耐候型热反射隔热涂料,包括如下步骤:
(1)首先将甲基丙烯酸酯、DPOMA及助剂混合物按配比混料后在配料缸中充分搅拌15min;
(2)加入颜填料等分散均匀至细小度小于30μm后加入空心玻璃微珠继续搅拌15min;
(3)对上一步骤得到的产品进行检测,检测合格后过滤、包装,其中过滤器的筛网目数为60-80目。
Claims (7)
1.一种水性外墙耐候型热反射隔热涂料,其特征在于,所述涂料各组份的重量份为:丙烯酸乳液30-40份;DPOMA8-13份;钛白粉10-15份;云母粉3-8份;长石粉10-20份;重质珍珠岩粉10-20份;三聚磷酸铝2-5份;磷酸锌5-10份;空心玻璃微珠6-10份;混合助剂 0.5-2份。
2.根据权利要求1所述的一种水性外墙耐候型热反射隔热涂料,其特征在于,所述乳液为有机硅氟改性苯丙乳液,该乳液是以N-烯丙基全氟戊及磺酰胺、乙烯基三乙氧基硅烷、苯乙烯、丙烯酸丁酯、丙烯酸为主要单体,马来酸十二酯为反应性乳化剂,过硫酸铵为引发剂而制得的,固含为55%,pH为5.0,颗粒的粒径为0.4微米,产品粘度为550cp,产品最低成膜温度10℃;
所述DPOMA,为甲基丙烯酸双环戊二烯氧基乙酯的英文名称首字母缩写,其是由甲基丙烯酸,双环戊二烯,乙二醇合成的具有增韧作用的水性/油性两用的增韧树脂;DPOMA外观透明液体,黏度为0.018( mPa·s) ,22℃折光系数为1.496,一个大气压下沸点为350℃,玻璃化温度为40-50℃;
所述钛白粉为采用氯化物工艺生产的多用途金红石二氧化钛颜料;
所述云母粉为白度为70-80%,pH值为7-8,松散密度为2.6g/cm3的湿法绢云母粉,其细度小于1250目;
所述填料为细度小于1250目的易分散型长石粉、重质珍珠岩、三聚磷酸铝、磷酸锌的任意一种或一种以上的混合物;
所述空心玻璃微珠为白色,成园率在97%以上,热传导系数为0.003-0.01BTU/in.hr.℉,表面经过偶联剂处理过的空心玻璃微珠;
所述防冻剂为丙二醇或聚丙二醇中的任意一种或一种以上的混合物;
所述中和剂为2-氨基-2-甲基-1-丙醇、二甲基乙醇胺、乙醇胺、氢氧化钠、氢氧化钾中的任意一种或一种以上的混合物;
所述湿润剂为非离子表面活性稀释剂,该湿润剂为聚氧乙烯烷芳基醚、聚氧乙烯多元醇醚、聚氧乙酯聚氧丙烯酸嵌段共聚物、脂肪酸聚乙二醇酯、多元醇酯、脂肪胺聚氧乙烯醚加成物中的任意一种或一种以上的混合物;
所述分散剂为高分子共聚物、聚羧酸铵、油酰基环氧烷共聚物、聚硅氧烷、聚丙烯酸铵中的任意一种或一种以上的混合物;
所述消泡剂为有机硅消泡剂、矿物油基含硅及多种混合物、脂肪烃的乳化物、非硅酮有机酯碳氢化合物、非硅酮胺类碳氢化合物、含疏水粒子矿物油混合物中的任意一种或一种以上的混合物;
所述罐内防腐剂为1,2-苯并异噻唑啉-3-酮(BIT)、2-甲基-5-氯-4-异噻咪唑-3-酮和 2-甲基-4-异噻咪唑-3-酮(CMIT/MIT)的混合物。
3.根据权利要求1所述的一种水性外墙耐候型热反射隔热涂料,其特征在于,漆膜防霉剂为碘代丙炔基氨基甲酸酯、苯并咪唑氨基甲酸甲酯与N/-(3,4-二氯苯基)-N,N-二甲基脲的复配体中的任意一种或一种以上的混合物。
4.根据权利要求1所述的一种水性外墙耐候型热反射隔热涂料,其特征在于,所述增稠剂为聚氨酯增稠剂和改性聚脲增稠剂的任意一种或一种以上的混合物。
5.根据权利要求1所述的一种水性外墙耐候型热反射隔热涂料,其特征在于,所述疏水剂是改性的有机硅助剂。
6.一种水性外墙耐候型热反射隔热涂料的制备方法,其特征在于,所述方法包括如下制备步骤:
(1)首先将甲基丙烯酸酯、DPOMA及助剂混合物在配料缸中充分搅拌15min;
(2)加入颜填料等分散均匀至细小度小于30μm后加入空心玻璃微珠继续搅拌15min;
(3)对上一步骤得到的产品进行检测,检测合格后过滤、包装即可。
7.根据权利要求6所述的一种水性外墙耐候型热反射隔热涂料的制备方法,其特征在于,所述过滤器的筛网目数为60-80目。