CN105419504A - 一种水性自清洁罩面漆及其制备方法 - Google Patents
一种水性自清洁罩面漆及其制备方法 Download PDFInfo
- Publication number
- CN105419504A CN105419504A CN201510881282.5A CN201510881282A CN105419504A CN 105419504 A CN105419504 A CN 105419504A CN 201510881282 A CN201510881282 A CN 201510881282A CN 105419504 A CN105419504 A CN 105419504A
- Authority
- CN
- China
- Prior art keywords
- water
- finishing paint
- automatically cleaning
- agent
- cleaning finishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种水性自清洁罩面漆,所述的罩面漆由以下组分并按照以下重量份数比配制而成:水30-40份、杀菌防腐剂0.1-0.2份、防霉剂0.1-0.2份、pH调节剂0.1-0.3份、消泡剂0.1-0.2份、防冻剂0.5-0.7份、成膜助剂3.3-3.9份、苯丙乳液55-65份、水性疏水剂0.1-0.3份、纳米氧化锌0.1-0.2份、增稠剂0.1-0.3份。本发明具有如下优点:采用本发明所述的组分及配比结合制备的一种水性自清洁罩面漆具有自清洁性,有着优异的耐沾污性、耐候保色性、耐水耐碱性以及卓越的附着性,而且安全无毒、环保无公害。
Description
技术领域
本发明涉及罩面漆技术领域,尤其涉及一种水性自清洁罩面漆及其制备方法。
背景技术
建筑外墙涂料可以美化环境和居室,但是由于传统涂料耐候、耐沾污性差,时间不长涂层就会发生色变、沾污。虽然使用玻璃幕墙或瓷砖贴面可以改善耐候性,但又会带来光污染,增加建筑物自重,存在安全隐患等问题。并且随着城市环境污染正在加剧,其中粉尘污染、气体污染尤为严重。建筑外墙特别是高层建筑,正在受到越来越严重的侵蚀。21世纪理想的外墙保护和装饰材料应具有防水性、防紫外光和自洁功能,能够长期保持洁净、靓丽的外表。如何让建筑外墙效果历久弥新,最有效的方法是施工一道罩面漆。然而,在现有的外墙罩面漆中,如耐候保色、耐水、耐沾污性等性能均不尽人意,尤其在涂装后,有的外墙漆膜容易开裂、泛白、变色等涂膜病态现象。所以,研究一种具有优良的耐沾污性、耐水性、耐候性且安全无毒的水性自清洁罩面漆有着重要的意义。
发明内容
本发明提供一种经济型净味防霉墙面漆及其制备方法,本发明制备的一种经济型净味防霉墙面漆不仅具有低气味、低VOC、对比率高的特点,而且具有优异的附着性、耐洗擦性及防霉性能。
本发明的技术方案如下:
一种水性自清洁罩面漆,所述的墙面漆由以下组分并按照以下重量份数比配制而成:
进一步地,所述杀菌防腐剂为异噻咪唑啉酮类或苯并咪唑类中的一种或多种任意组合。
进一步地,所述防霉剂为苯并咪唑氨基甲酸甲酯、2-正辛基-4-异噻咪唑-3-酮或3-碘-2炔丙基丁基氨基甲酸酯中的一种或多种任意组合。
进一步地,所述pH调节剂为采用碱性pH调节剂。
进一步地,所述消泡剂为矿物油消泡剂或有机硅消泡剂中的一种或两种任意混合。
进一步地,所述防冻剂为乙二醇、丙二醇的至少一种。所述成膜助剂为采用醇酯十二。
进一步地,所述苯丙乳液为采用一种自清洁的苯丙乳液,具有优异的耐候性、突出的耐沾污性,极好的耐水耐碱性和干、湿附着性,乳液的固含量为45-48%,玻璃化温度为22-28℃。
进一步地,所述的水性疏水剂为水溶性环保非离子型表面活性剂,它可提高漆膜的表面疏水性能及抗粘、防污性能。
进一步地,所述增稠剂为聚氨酯型缔合增稠剂或疏水基团改性的非离子型碱溶胀增稠剂中的一种或多种任意混合。
一种水性自清洁罩面漆的制备方法,其特征在于:它包括如下依序进行的步骤:
将30-40份的水加入分散缸中,在200-600r/min速度下依次加入0.1-0.2份杀菌防腐剂、0.1-0.2份防霉剂、0.1-0.3份pH调节剂、0.1-0.2份消泡剂、0.5-0.7份防冻剂和3.3-3.9份成膜助剂,搅拌3-5分钟;
然后,加入55-65份苯丙乳液,搅拌1-3分钟;
接着,加入0.1-0.3份水性疏水剂和0.1-0.2份纳米氧化锌,最后添加0.1-0.3份增稠剂,调节粘度为50-55KU,即得本发明产品。
本发明的有益效果为:本发明制备的一种水性自清洁罩面漆具有如下优点:采用本发明所述的组分及配比结合制备的一种水性自清洁罩面漆具有自清洁性,有着优异的耐沾污性、耐候保色性、耐水耐碱性以及卓越的附着性,而且安全无毒、环保无公害。
本发明一种水性自清洁罩面漆与现有的技术相比具有如下优点:本发明的水性自清洁罩面漆选用具有自清洁性的苯丙乳液为成膜物,使漆膜具有优异的耐沾污性、耐候性和耐水耐碱性,采用聚氨酯型缔合增稠剂和疏水改性碱溶胀型增稠剂的复配组合,使涂料具有良好的施工性能,并且添加纳米氧化锌,具有杀菌防腐、吸附甲醛的功能,加固了本发明罩面漆的安全性和环保性,而且通过多因素实验设计方法,确定的组分及重量配比,也使本发明产品具有卓越的附着性。
具体实施方式
以下实施例的组分中所述杀菌防腐剂为索尔ActicideRS杀菌防腐剂。所述防霉剂为特洛伊Polyphsae678型防霉剂。所述pH调节剂为陶氏生产的AMP95型pH调节剂。所述消泡剂为西班牙全保化工生产的PA240型消泡剂。所述防冻剂为采用乙二醇。所述成膜助剂为伊士曼生产的Texnol型醇酯十二。所述苯丙乳液为德国汉高生产的Napoly2900型苯丙乳液。所述水性疏水剂为博诚化工SP-2405型水性疏水剂。所述增稠剂为罗门哈斯生产的RM-8W型增稠剂和TT-615型增稠剂。所述每种组分也可采用同类其它型号产品。
具体实施案例1
一种水性自清洁罩面漆,由以下组分和重量份数比配制而成:
一种水性自清洁罩面漆的制备方法,它包括如下依序进行的步骤:
将35份的水加入分散缸中,在400r/min速度下依次加入0.15份杀菌防腐剂、0.15份防霉剂、0.2份pH调节剂、0.15份消泡剂、0.6份防冻剂和3.6份成膜助剂,搅拌4分钟。然后,加入60份苯丙乳液,搅拌2分钟。接着,加入0.2份水性疏水剂和0.15份纳米氧化锌,最后添加0.2份增稠剂,调节粘度为52KU,即得本发明产品。
进一步地,上述组分中所述杀菌防腐剂为索尔ActicideRS杀菌防腐剂。所述防霉剂为特洛伊Polyphsae678型防霉剂。所述pH调节剂为陶氏生产的AMP95型pH调节剂。所述消泡剂为西班牙全保化工生产的PA240型消泡剂。所述防冻剂为采用乙二醇。所述成膜助剂为伊士曼生产的Texnol型醇酯十二。所述苯丙乳液为德国汉高生产的Napoly2900型苯丙乳液。所述水性疏水剂为博诚化工SP-2405型水性疏水剂。所述增稠剂为罗门哈斯生产的RM-8W型增稠剂和TT-615型增稠剂。
具体实施案例2
一种水性自清洁罩面漆,由以下组分和重量份数比配制而成:
一种水性自清洁罩面漆的制备方法,它包括如下依序进行的步骤:
将30份的水加入分散缸中,在200r/min速度下依次加入0.1份杀菌防腐剂、0.2份防霉剂、0.1份pH调节剂、0.1份消泡剂、0.7份防冻剂和3.9份成膜助剂,搅拌3分钟。然后,加入65份苯丙乳液,搅拌1分钟。接着,加入0.3份水性疏水剂和0.1份纳米氧化锌,最后添加0.1份增稠剂,调节粘度为50KU,即得本发明产品。
进一步地,上述组分中所述杀菌防腐剂为索尔ActicideRS杀菌防腐剂。所述防霉剂为特洛伊Polyphsae678型防霉剂。所述pH调节剂为陶氏生产的AMP95型pH调节剂。所述消泡剂为西班牙全保化工生产的PA240型消泡剂。所述防冻剂为采用乙二醇。所述成膜助剂为伊士曼生产的Texnol型醇酯十二。所述水性疏水剂为博诚化工SP-2405型水性疏水剂。所述苯丙乳液为德国汉高生产的Napoly2900型苯丙乳液。所述增稠剂为罗门哈斯生产的RM-8W型增稠剂和TT-615型增稠剂。
具体实施案例3
一种水性自清洁罩面漆,由以下组分和重量份数比配制而成:
一种水性自清洁罩面漆的制备方法,它包括如下依序进行的步骤:
将40份的水加入分散缸中,在600r/min速度下依次加入0.2份杀菌防腐剂、0.1份防霉剂、0.3份pH调节剂、0.2份消泡剂、0.5份防冻剂和3.3份成膜助剂,搅拌5分钟。然后,加入55份苯丙乳液,搅拌3分钟。接着,加入0.1份水性疏水剂和0.2份纳米氧化锌,最后添加0.3份增稠剂,调节粘度为55KU,即得本发明产品。
进一步地,上述组分中所述杀菌防腐剂为索尔ActicideRS杀菌防腐剂。所述防霉剂为特洛伊Polyphsae678型防霉剂。所述pH调节剂为陶氏生产的AMP95型pH调节剂。所述消泡剂为西班牙全保化工生产的PA240型消泡剂。所述防冻剂为采用乙二醇。所述成膜助剂为伊士曼生产的Texnol型醇酯十二。所述苯丙乳液为德国汉高生产的Napoly2900型苯丙乳液。所述水性疏水剂为博诚化工SP-2405型水性疏水剂。所述增稠剂为罗门哈斯生产的RM-8W型增稠剂和TT-615型增稠剂。
经过对各实施例的测试,本发明水性自清洁罩面漆的各实施例依据GB/T9755-2014的标准要求测试产品的技术指标以及依据GB18582-2008测试产品的环保指标,实验数据如上表所示:由上述的实施例测试结果可知:本发明制备的一种水性自清洁罩面漆具有自清洁性,有着优异的耐沾污性、耐候保色性、耐水耐碱性以及卓越的附着性,而且安全无毒、环保无公害。
上述具体实施方式只是对本发明的技术方案进行详细解释,本发明并不只仅仅局限于上述实施例,本领域技术人员应该明白,凡是依据上述原理及精神在本发明基础上的改进、替代,都应在本发明的保护范围之内。
Claims (10)
1.一种水性自清洁罩面漆,其特征在于:所述的罩面漆由以下组分并按照以下重量份数比配制而成:
2.根据权利要求1所述的一种水性自清洁罩面漆,其特征在于:所述杀菌防腐剂为异噻咪唑啉酮类或苯并咪唑类中的一种或多种任意组合。
3.根据权利要求1所述的一种水性自清洁罩面漆,其特征在于:所述防霉剂为苯并咪唑氨基甲酸甲酯、2-正辛基-4-异噻咪唑-3-酮或3-碘-2炔丙基丁基氨基甲酸酯中的一种或多种任意组合。
4.根据权利要求1所述的一种水性自清洁罩面漆,其特征在于:所述pH调节剂为碱性pH调节剂。
5.根据权利要求1所述的一种水性自清洁罩面漆,其特征在于:所述消泡剂为矿物油消泡剂或有机硅消泡剂中的一种或两种任意混合。
6.根据权利要求1所述的一种水性自清洁罩面漆,其特征在于:所述防冻剂为乙二醇、丙二醇的一种或者两者任意比例混合;所述成膜助剂为醇酯十二。
7.根据权利要求1所述的一种水性自清洁罩面漆,其特征在于:所述的苯丙乳液为固含量为45-48%且玻璃化温度为22-28℃的自清洁的苯丙乳液。
8.根据权利要求1所述的一种水性自清洁罩面漆,其特征在于:所述的水性疏水剂为水溶性非离子型表面活性剂。
9.根据权利要求1所述的一种水性自清洁罩面漆,其特征在于:所述增稠剂为聚氨酯型缔合增稠剂或疏水基团改性的非离子型碱溶胀增稠剂中的一种或多种任意混合。
10.根据权利要求1-9中任意一项所述的一种水性自清洁罩面漆的制备方法,其特征在于:它包括如下依序进行的步骤:
将30-40份的水加入分散缸中,在200-600r/min速度下依次加入0.1-0.2份杀菌防腐剂、0.1-0.2份防霉剂、0.1-0.3份pH调节剂、0.1-0.2份消泡剂、0.5-0.7份防冻剂和3.3-3.9份成膜助剂,搅拌3-5分钟;
然后,加入55-65份苯丙乳液,搅拌1-3分钟;
接着,加入0.1-0.3份水性疏水剂和0.1-0.2份纳米氧化锌,最后添加0.1-0.3份增稠剂,调节粘度为50-55KU,即得本发明产品。