CN103708784A - Colored glass concrete and production method thereof - Google Patents
Colored glass concrete and production method thereof Download PDFInfo
- Publication number
- CN103708784A CN103708784A CN201310734242.9A CN201310734242A CN103708784A CN 103708784 A CN103708784 A CN 103708784A CN 201310734242 A CN201310734242 A CN 201310734242A CN 103708784 A CN103708784 A CN 103708784A
- Authority
- CN
- China
- Prior art keywords
- glass
- red
- purple
- parts
- concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses colored glass concrete. The colored glass concrete comprises components according to the following weight ratio: 20-30 parts of purple glass, 10-15 parts of aubergine glass, 25-35 parts of red glass, 0-10 parts of milky white glass, 120-150 parts of fly ash, 180-200 parts of cement, 75-100 parts of fine sand, 2-5 parts of a foaming agent, and the rest of water, wherein the water-binder ratio is kept to be 0.3-0.5, the purple glass, the aubergine glass, the red glass and the milky white glass are one of square, triangular, circular and elliptic, the appearance size of the glass is less than 6cm, and the foaming agent is alkyl benzene sulfonic acid ester. Through the way, the colored glass concrete disclosed by the invention changes the current situation that the surface of existing concrete is all gray, and is high in transparency and brightness, good in surface aesthetics, wide in application range, and lower in using cost. The production method of the colored glass concrete disclosed by the invention is easy and convenient, and the production process is easy to control.
Description
Technical field
The present invention relates to concrete and production field thereof, particularly relate to a kind of tinted shade concrete and preparation method thereof.
Background technology
Concrete is one of contemporary topmost civil engineering material, after existing concrete formation, its surface is all grey, color is comparatively dull, along with the raising of people's living standard, the raising of mental attitude, concrete is more and more used in the internal structure of building, and the coverings such as ceramic tile, floor tile, plank are used on concrete surface more, to meet the personalized not shortcoming in its surface.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of existing concrete surface that changed and is all tinted shade concrete that present situation, transparency and brightness are high, surface aesthetic degree is good, use range is wide of grey and preparation method thereof.
For solving the problems of the technologies described above, the invention provides a kind of tinted shade concrete, the component that comprises following weight proportioning: purple glass 20-30 part, red-purple glass 10-15 part, red glass 25-35 part, opal glass 0-10 part, flyash 120-150 part, cement 180-200 part, fine sand 75-100 part, pore forming material 2-5 part, all the other are water, described water-cement ratio remains on 0.3-0.5, described purple glass, red-purple glass, red glass and opal glass are square, trilateral, circular, a kind of in ellipse, and its apparent size is less than 6 centimetres, described pore forming material is benzene sulfonamide acid esters.
In a preferred embodiment of the present invention, the component that comprises following weight proportioning: purple glass 20-25 part, red-purple glass 10-12 part, red glass 25-30 part, flyash 120-130 part, cement 180-190 part, fine sand 75-85 part, pore forming material 2-3 part, all the other are water, described water-cement ratio remains on 0.3-0.4, described purple glass, red-purple glass and red glass are all square, and its length of side is less than 6 centimetres, described pore forming material is benzene sulfonamide acid esters.
In a preferred embodiment of the present invention, the component that comprises following weight proportioning: purple glass 25-30 part, red-purple glass 10-15 part, red glass 30-35 part, opal glass 3-10 part, flyash 130-150 part, cement 180-200 part, fine sand 80-100 part, pore forming material 2-5 part, all the other are water, described water-cement ratio remains on 0.3-0.5, described purple glass, red-purple glass, red glass and opal glass are all circle, and its diameter is less than 6 centimetres.
The present invention also provides a kind of tinted shade concrete making method, comprises the following steps:
(1) concrete component takes, take the component of following weight proportion: purple glass 20-30 part, red-purple glass 10-15 part, red glass 25-35 part, opal glass 0-10 part, flyash 120-150 part, cement 180-200 part, fine sand 75-100 part, pore forming material 2-5 part, all the other are water
(2) first flyash, cement, fine sand and pore forming material are evenly mixed, after evenly mixing, add water to carry out fully stirring and obtaining mixture,
(3) again purple glass, red-purple glass, red glass and opal glass are evenly mixed, after mixing, add in the mixture in step (2), again stir, and in the process stirring, constantly increase water consumption, until water-cement ratio remains on 0.3-0.5 after stirring, obtain tinted shade concrete.
The invention has the beneficial effects as follows: tinted shade concrete of the present invention has changed existing concrete surface and has been all that present situation, transparency and the brightness of grey is high, surface aesthetic degree is good, use range wide, use cost is lower, and the concrete making method of tinted shade of the present invention is easy, making processes is easy to control.
Embodiment
Below the technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is only a part of embodiment of the present invention, rather than whole embodiment.Embodiment based in the present invention, those of ordinary skills, not making all other embodiment that obtain under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1
A kind of tinted shade concrete, the component that comprises following weight proportioning: 20 parts of purple glass, 10 parts, red-purple glass, 25 parts of red glass, 2 parts of opal glasses, 120 parts, flyash, 180 parts of cement, 75 parts of fine sands, 2 parts of pore forming materials, all the other are water, described water-cement ratio remains on 0.3, described purple glass, red-purple glass, red glass and opal glass are all isosceles triangle, and its length of side is less than 6 centimetres, described pore forming material is benzene sulfonamide acid esters.
The concrete making method of tinted shade, is characterized in that, comprises the following steps:
(1) taking of concrete component, takes the component of following weight proportion: 20 parts of purple glass, 10 parts, red-purple glass, 25 parts of red glass, 2 parts of opal glasses, 120 parts, flyash, 180 parts of cement, 75 parts of fine sands, 2 parts of pore forming materials, and all the other are water,
(2) first flyash, cement, fine sand and pore forming material are evenly mixed, after evenly mixing, add water to carry out fully stirring and obtaining mixture,
(3) again purple glass, red-purple glass, red glass and opal glass are evenly mixed, after mixing, add in the mixture in step (2), again stir, and in the process stirring, constantly increase water consumption, until water-cement ratio remains on 0.3-0.5 after stirring, obtain tinted shade concrete.
Existing concrete is all grey, appearance color is dull, having no aesthetic feeling can say, and by changing conventional concrete composition and ratio, and added tinted shade, make this concrete strength suitable with conventional concrete, tinted shade concrete in the present embodiment 1, when thickness is 3-5 centimetre, 96% of the conventional concrete strength of the corresponding condition of equivalent thickness of its intensity, when thickness is 15-20 centimetre, its intensity is 99% of the conventional concrete strength of corresponding condition of equivalent thickness, as can be seen here, its intensity is suitable with conventional concrete strength, and for proof strength also only need increase the requirement that a dot thickness can meet its intensity a little, but the concrete surface aesthetic degree of this tinted shade increases, not only there is redness, purple, being uniformly distributed of the coloured glasss such as red-purple, also make tinted shade concrete have certain transparency and brightness, greatly increased its surperficial aesthetics, changed the present situation that conventional concrete surface color is all grey.
Embodiment 2
A kind of tinted shade concrete, the component that comprises following weight proportioning: 25 parts of purple glass, 12 parts, red-purple glass, 30 parts of red glass, 130 parts, flyash, 190 parts of cement, 85 parts of fine sands, 3 parts of pore forming materials, all the other are water, described water-cement ratio remains on 0.4, described purple glass, red-purple glass and red glass are all square, and its length of side is less than 6 centimetres.
The concrete making method of tinted shade, is characterized in that, comprises the following steps:
(1) taking of concrete component, takes the component of following weight proportion: 25 parts of purple glass, 12 parts, red-purple glass, 30 parts of red glass, 130 parts, flyash, 190 parts of cement, 85 parts of fine sands, 3 parts of pore forming materials, and all the other are water,
(2) first flyash, cement, fine sand and pore forming material are evenly mixed, after evenly mixing, add water to carry out fully stirring and obtaining mixture,
(3) again purple glass, red-purple glass and red glass are evenly mixed, after mixing, add in the mixture in step (2), again stir, and constantly increase water consumption in the process stirring, until water-cement ratio remains on 0.3-0.5 after stirring, obtain tinted shade concrete.
Tinted shade concrete in the present embodiment 2, when thickness is 3-5 centimetre, 95.2% of the conventional concrete strength of the corresponding condition of equivalent thickness of its intensity, when thickness is 15-20 centimetre, its intensity is 98.5% of the conventional concrete strength of corresponding condition of equivalent thickness, thickness is the tinted shade concrete of 3.15 centimetres, its intensity and thickness are that the concrete Strength retention of routine of 3 centimetres is consistent, and the thickness of 0.15 centimetre is more or less the same, in the situation that not being much too high to thickness requirement, tinted shade concrete can substitute conventional concrete completely.
Embodiment 3
A kind of tinted shade concrete, the component that comprises following weight proportioning: 30 parts of purple glass, 15 parts, red-purple glass, 35 parts of red glass, 10 parts of opal glasses, 150 parts, flyash, 200 parts of cement, 100 parts of fine sands, 5 parts of pore forming materials, all the other are water, described water-cement ratio remains on 0.3-0.5, described purple glass, red-purple glass, red glass and opal glass are all circle, and its diameter is less than 6 centimetres.
The concrete making method of tinted shade, is characterized in that, comprises the following steps:
(1) concrete component takes, take the component of following weight proportion: 30 parts of purple glass, 15 parts, red-purple glass, 35 parts of red glass, 10 parts of opal glasses, 150 parts, flyash, 200 parts of cement, 100 parts of fine sands, 5 parts of pore forming materials, all the other are water
(2) first flyash, cement, fine sand and pore forming material are evenly mixed, after evenly mixing, add water to carry out fully stirring and obtaining mixture,
(3) again purple glass, red-purple glass and red glass are evenly mixed, after mixing, add in the mixture in step (2), again stir, and constantly increase water consumption in the process stirring, until water-cement ratio remains on 0.3-0.5 after stirring, obtain tinted shade concrete.
Tinted shade concrete in the present embodiment 3, when thickness is 3-5 centimetre, 96.3% of the conventional concrete strength of the corresponding condition of equivalent thickness of its intensity, when thickness is 15-20 centimetre, its intensity is 99.1% of the conventional concrete strength of corresponding condition of equivalent thickness, thickness is the tinted shade concrete of 3.1 centimetres, its intensity and thickness are that the concrete Strength retention of routine of 3 centimetres is consistent, thickness is the tinted shade concrete of 15.36 centimetres, its intensity and thickness are that the concrete Strength retention of routine of 15 centimetres is consistent, in the situation that not being much too high to thickness requirement, tinted shade concrete can substitute conventional concrete completely.
This tinted shade concrete scope of application is wider, not only can use within the use range of existing concrete, can also be frozen into solid-state after, grinding process is carried out in its surface, then directly as floor, floor tile, wall brick, use, cost is added the cost of laying floor tile or floor on concrete surface lower than conventional concrete, and result of use is identical.
Tinted shade concrete of the present invention is by adding tinted shade, make this concrete strength suitable with conventional concrete, and its surface aesthetic degree increases, not only there is being uniformly distributed of the coloured glasss such as redness, purple, red-purple, also make tinted shade concrete have certain transparency and brightness, greatly increase its surperficial aesthetics, changed the present situation that conventional concrete surface color is all grey.
Be different from prior art, tinted shade concrete of the present invention has changed existing concrete surface and has been all that present situation, transparency and the brightness of grey is high, surface aesthetic degree is good, use range wide, use cost is lower, and the concrete making method of tinted shade of the present invention is easy, making processes is easy to control.
The foregoing is only embodiments of the invention; not thereby limit the scope of the claims of the present invention; every equivalent structure or conversion of equivalent flow process that utilizes description of the present invention to do; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (4)
1. a tinted shade concrete, it is characterized in that, the component that comprises following weight proportioning: purple glass 20-30 part, red-purple glass 10-15 part, red glass 25-35 part, opal glass 0-10 part, flyash 120-150 part, cement 180-200 part, fine sand 75-100 part, pore forming material 2-5 part, all the other are water, described water-cement ratio remains on 0.3-0.5, described purple glass, red-purple glass, red glass and opal glass are square, trilateral, circular, a kind of in ellipse, and its apparent size is less than 6 centimetres, described pore forming material is benzene sulfonamide acid esters.
2. tinted shade concrete according to claim 1, it is characterized in that, the component that comprises following weight proportioning: purple glass 20-25 part, red-purple glass 10-12 part, red glass 25-30 part, flyash 120-130 part, cement 180-190 part, fine sand 75-85 part, pore forming material 2-3 part, all the other are water, described water-cement ratio remains on 0.3-0.4, described purple glass, red-purple glass and red glass are all square, and its length of side is less than 6 centimetres, described pore forming material is benzene sulfonamide acid esters.
3. tinted shade concrete according to claim 1, it is characterized in that, the component that comprises following weight proportioning: purple glass 25-30 part, red-purple glass 10-15 part, red glass 30-35 part, opal glass 3-10 part, flyash 130-150 part, cement 180-200 part, fine sand 80-100 part, pore forming material 2-5 part, all the other are water, described water-cement ratio remains on 0.3-0.5, described purple glass, red-purple glass, red glass and opal glass are all circle, and its diameter is less than 6 centimetres.
4. the concrete making method of tinted shade, is characterized in that, comprises the following steps:
(1) concrete component takes, take the component of following weight proportion: purple glass 20-30 part, red-purple glass 10-15 part, red glass 25-35 part, opal glass 0-10 part, flyash 120-150 part, cement 180-200 part, fine sand 75-100 part, pore forming material 2-5 part, all the other are water
(2) first flyash, cement, fine sand and pore forming material are evenly mixed, after evenly mixing, add water to carry out fully stirring and obtaining mixture,
(3) again purple glass, red-purple glass, red glass and opal glass are evenly mixed, after mixing, add in the mixture in step (2), again stir, and in the process stirring, constantly increase water consumption, until water-cement ratio remains on 0.3-0.5 after stirring, obtain tinted shade concrete.