CN103695916B - A kind of antifouling antirust solution of water solublity and preparation method thereof - Google Patents
A kind of antifouling antirust solution of water solublity and preparation method thereof Download PDFInfo
- Publication number
- CN103695916B CN103695916B CN201310617720.8A CN201310617720A CN103695916B CN 103695916 B CN103695916 B CN 103695916B CN 201310617720 A CN201310617720 A CN 201310617720A CN 103695916 B CN103695916 B CN 103695916B
- Authority
- CN
- China
- Prior art keywords
- water
- antirust solution
- sodium
- nano
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of antifouling antirust solution of water solublity, be made up of the raw material of following weight portion: nano silicon 1-1.5, dimethyl sulfoxide 10-14, oleum lini 8-10, sodium benzoate 1-2, paregal O 2-4, oxine 1-2, nano aluminum nitride powder 0.4-0.7, cyanuric acid zinc 4-6, lemon yellow 5-6, aluminium octadecanoate 3-5, benzalkonium chloride 2-3, triethanolamine borate 3-5,6-hexanediyl ester 20-25, EDETATE SODIUM 1-2, auxiliary agent 4-5, water 280-300.By the present invention in that with macromolecule resin monomer and chelating agen, can form thin film in metal surface, by using nano aluminum nitride, add film property, being more likely formed protecting film fine and close continuously, rustless property increases；By using nano silicon so that antirust solution has self-cleaning anti-pollution effect, easily will not be covered with dust because of containing oils and fats, easy cleaning.
Description
Technical field
The present invention relates to technical field of rust prevention, particularly relate to a kind of antifouling antirust solution of water solublity and preparation method thereof.
Background technology
Metal surface is antirust is the important topic in commercial production, and traditional antirust solution, antirust oil have advantage also to have shortcoming.Containing substantial amounts of sodium nitrite in common aqueous rust preventive, there is carcinogenecity, be unfavorable for that environmental protection and the person are healthy, and adopt wetting agent to extend the life-span of aqueous rust preventive, bring again the disadvantage touched with one's hand, be covered with dust, and can not long-term rust prevention；Although general hard film rust preventive oil is suitable for long-term rust prevention, film forming is also transparent attractive in appearance, but water white resin types is less, and instability is easy oxidation discoloration also, in addition it is also necessary to organic solvent dissolution, brings inflammable and explosive danger to be also unfavorable for environmental protection and health；General antirust oil uses mineral oil, difficult degradation, and also brings along the problem that oil removing is difficult during for short-term rust prevention.Therefore, comprehensive study performance is more excellent, and the antirust product being more suitable for for different occasion researchs is new direction and trend.
Summary of the invention
It is an object of the invention to provide a kind of antifouling antirust solution of water solublity and preparation method thereof, this antirust solution has antirust time length, easily spraying, antifouling feature.
Technical scheme is as follows:
A kind of antifouling antirust solution of water solublity, it is characterised in that be made up of the raw material of following weight portion: nano silicon 1-1.5, dimethyl sulfoxide 10-14, oleum lini 8-10, sodium benzoate 1-2, paregal O 2-4, oxine 1-2, nano aluminum nitride powder 0.4-0.7, cyanuric acid zinc 4-6, lemon yellow 5-6, aluminium octadecanoate 3-5, benzalkonium chloride 2-3, triethanolamine borate 3-5,6-hexanediyl ester 20-25, EDETATE SODIUM 1-2, auxiliary agent 4-5, water 280-300.Described auxiliary agent is made up of the raw material of following weight portion: polyoxyethylene sorbitan monooleate 2-3, nano titanium oxide 0.1-0.2, sodium bicarbonate 1-2, diethanolamine 2-3, carboxymethyl cellulose 2-3, polyvinyl alcohol 1-2, Resina persicae 1-2, sodium silicate 1-2, carbamide 3-4, Ammonium persulfate. 1-2, water 20-24；Preparation method is after dissolving ammonium persulfate into water, adds other leftover materials, stirs 10-15 minute, heats to 70-80 DEG C, stirring reaction 1-2 hour, to obtain final product.
The preparation method of the antifouling antirust solution of described water solublity, it is characterised in that comprise the following steps: by water, benzalkonium chloride, paregal O mixing, heating is to 40-50 DEG C；Add dimethyl sulfoxide, oleum lini, aluminium octadecanoate, triethanolamine borate, 6-hexanediyl ester, EDETATE SODIUM, continue to be heated to 85-90 DEG C, stir 10-15 minute；Add other residual componentss, continue stirring 15-20 minute, to obtain final product.
Beneficial effects of the present invention
By the present invention in that with macromolecule resin monomer and chelating agen, thin film can be formed in metal surface, play isolation air; anti-oxidation effect, prevents antirust agent from coming off simultaneously, by using nano aluminum nitride; adding film property, be more likely formed protecting film fine and close continuously, rustless property increases；By using nano silicon so that antirust solution has self-cleaning anti-pollution effect, easily will not be covered with dust because of containing oils and fats, easy cleaning；Antirust solution of the present invention is suitable for inter process and longer-term is antirust, pollution-free, easy to use, easily sprays.
Detailed description of the invention
A kind of antifouling antirust solution of water solublity, is made up of the raw material of following weight portion (kilogram): nano silicon 1.3, dimethyl sulfoxide 13, oleum lini 9, sodium benzoate 1.5, paregal O 3, oxine 1.4, nano aluminum nitride powder 0.5, cyanuric acid zinc 5, lemon yellow 5.5, aluminium octadecanoate 4, benzalkonium chloride 2.5, triethanolamine borate 4,6-hexanediyl ester 23, EDETATE SODIUM 1.5, auxiliary agent 4.5, water 290.Described auxiliary agent is made up of the raw material of following weight portion (kilogram): polyoxyethylene sorbitan monooleate 2, nano titanium oxide 0.1, sodium bicarbonate 2, diethanolamine 2, carboxymethyl cellulose 3, polyvinyl alcohol 2, Resina persicae 1, sodium silicate 2, carbamide 3, Ammonium persulfate. 1, water 20；Preparation method is after dissolving ammonium persulfate into water, adds other leftover materials, stirs 10-15 minute, heats to 70-80 DEG C, stirring reaction 1-2 hour, to obtain final product.
The preparation method of the antifouling antirust solution of described water solublity, comprises the following steps: by water, benzalkonium chloride, paregal O mixing, heating is to 46 DEG C；Add dimethyl sulfoxide, oleum lini, aluminium octadecanoate, triethanolamine borate, 6-hexanediyl ester, EDETATE SODIUM, continue to be heated to 88 DEG C, stir 13 minutes；Add other residual componentss, continue stirring 17 minutes, to obtain final product.
The antifouling antirust solution of water solublity that this embodiment obtains detects by national standard, and damp heat test * (1) is qualified；Salt water immersion test * (1): qualified；Corrosion testing * (2): qualified；Rust removability (secondary) < 6.The prepared antifouling antirust solution of water solublity is brushed that be newly processed into and do not have the steel matrix surface of greasy dirt, within 20 days disposed within, to have no obvious iron mold.
Claims (2)
1. the antifouling antirust solution of water solublity, it is characterised in that be made up of the raw material of following weight portion: nano silicon 1-1.5, dimethyl sulfoxide 10-14, oleum lini 8-10, sodium benzoate 1-2, paregal O 2-4, oxine 1-2, nano aluminum nitride powder 0.4-0.7, cyanuric acid zinc 4-6, lemon yellow 5-6, aluminium octadecanoate 3-5, benzalkonium chloride 2-3, triethanolamine borate 3-5,6-hexanediyl ester 20-25, EDETATE SODIUM 1-2, auxiliary agent 4-5, water 280-300；Described auxiliary agent is made up of the raw material of following weight portion: polyoxyethylene sorbitan monooleate 2-3, nano titanium oxide 0.1-0.2, sodium bicarbonate 1-2, diethanolamine 2-3, carboxymethyl cellulose 2-3, polyvinyl alcohol 1-2, Resina persicae 1-2, sodium silicate 1-2, carbamide 3-4, Ammonium persulfate. 1-2, water 20-24；Preparation method is after dissolving ammonium persulfate into water, adds other leftover materials, stirs 10-15 minute, heats to 70-80 DEG C, stirring reaction 1-2 hour, to obtain final product.
2. the preparation method of the antifouling antirust solution of water solublity according to claim 1, it is characterised in that comprise the following steps: by water, benzalkonium chloride, paregal O mixing, heating is to 40-50 DEG C；Add dimethyl sulfoxide, oleum lini, aluminium octadecanoate, triethanolamine borate, 6-hexanediyl ester, EDETATE SODIUM, continue to be heated to 85-90 DEG C, stir 10-15 minute；Add other residual componentss, continue stirring 15-20 minute, to obtain final product.