CN103695887A - 邦迪管镀锌无铬军绿色钝化剂ⅱ - Google Patents

邦迪管镀锌无铬军绿色钝化剂ⅱ Download PDF

Info

Publication number
CN103695887A
CN103695887A CN201310722062.9A CN201310722062A CN103695887A CN 103695887 A CN103695887 A CN 103695887A CN 201310722062 A CN201310722062 A CN 201310722062A CN 103695887 A CN103695887 A CN 103695887A
Authority
CN
China
Prior art keywords
pipe
free
passivation
bondy
army
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310722062.9A
Other languages
English (en)
Other versions
CN103695887B (zh
Inventor
石磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Jianzhu University
Original Assignee
石磊
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 石磊 filed Critical 石磊
Priority to CN201310722062.9A priority Critical patent/CN103695887B/zh
Publication of CN103695887A publication Critical patent/CN103695887A/zh
Application granted granted Critical
Publication of CN103695887B publication Critical patent/CN103695887B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及了邦迪管镀锌无铬军彩色钝化剂II，采用钼酸钠、柠檬酸钠、亚硫酸钠、乙二酸、硫酸镍等物品通过一定的比例溶解混合均匀而成，合成的钝化膜提高了镀层的耐蚀性能，同时赋予镀层军绿色的钝化膜。

Description

邦迪管镀锌无铬军绿色钝化剂Ⅱ
技术领域
本发明涉及邦迪管镀锌无铬军绿色钝化剂II，尤其涉及邦迪管镀锌无铬军绿色钝化剂的成分、各成分的作用及配制方法。 
背景技术
邦迪管就是指直径在4.6-10.6mm的细钢管。主要用于汽车工业、制冷业、加热器制造工业中的油压表管路、燃油管路、刹车管路以及类似的装置，还可以广泛用于替代铜管，降低使用成本，邦迪管是用冷轧带钢薄板卷管、焊接、以氰化镀铜打底，铜层镀锌完成的。铜镀层在使用过程中起到保护邦迪管，减缓腐蚀基体的作用，并能够帮助完成焊接，所以邦迪管必须要表面覆铜或者铜基体。由于邦迪管对耐磨耐蚀性能要求较高，所以一般都采用军绿色钝化来满足其要求。传统的军绿色钝化工艺都是采用六价铬钝化，但是六价铬有剧毒，具有致癌致畸的危害。根据GB-2008《电镀污染物排放标准》，对Pd、Hg、Cd、Cr6+、聚溴二苯醚和聚溴联苯等6种第一类污染物的排放标准有了更低的限制，欧盟于2006年7月1日起实施的《关于在电子电气设备中禁止使用某些有害物质指令》(ROHS)，禁止欧盟市场上投放的电子和电器设备中含六价铬等6种有害物质，所以环保型的产品替代六价铬钝化成为迫切要求。 
环保型的钝化主要采用三价铬和无铬钝化两个方向。三价铬钝化剂如：邦迪管三价铬军绿色钝化剂ZL201210147166.7，其适用于铁基体或铜基体，但三价铬有一定的毒性，因此并不满足无毒环保的要求。无铬钝化体系有钛酸盐、钼酸盐、钨酸盐、稀土、硅酸盐，近年来无铬钝化的钝化膜无毒环保，耐蚀性和外观都有很大的提高，满足了普通五金件电镀要求，所以无铬钝化工艺在工业上有广泛的应用前景。 
目前钼酸盐无铬军绿色钝化体系在铁基体上的钝化膜发灰、发黑，军绿色显示浅、少，而在铜基体或铜镀层镀锌后进行钝化，钝化膜有明显的军绿色，因此本邦迪管镀锌无铬军绿色钝化剂II适用于铜基体或铜镀层镀锌后进行钝化，得到的钝化膜均匀细密。 
发明内容
本发明为了提高镀锌层钝化膜无毒环保，同时使钝化液中不含有Cr6+、Cr3+而发明了邦迪管镀锌无铬军绿色钝化剂II。 
本发明采用钼酸钠、柠檬酸钠、亚硫酸钠、乙二酸、硫酸镍等物品组成邦迪管镀锌无铬军绿色钝化剂II。 
本发明的具体制备方法包括如下顺序的步骤： 
a.将计算量的钼酸钠倒入少量水中，搅拌使其充分溶解； 
b.将计算量的柠檬酸钠和亚硫酸钠缓慢加入，搅拌使其充分溶解； 
c.将计算量的乙二酸倒入，搅拌均匀； 
d.将计算量的硫酸镍缓慢加入，迅速搅拌，使其充分溶解； 
e.将计算量的水(电导率＜5us/cm)定容后，静置10分钟，用硝酸调pH在2～2.5范围内。 
本发明所得邦迪管镀锌无铬军绿色钝化剂II，为澄清呈浅绿色的液体。 
实验说明 
本发明通过铜基体或铜镀层镀锌后进行无铬军绿色钝化液中实施钝化处理，经过不同时间的处理后，观察镀层的色泽，并进行中性盐雾试验测定其耐蚀性能。 
附图说明
图为钝化后的样片在扫描电镜下×2000倍的截面形貌。 
具体实施方式
实施例1 
本实施例的具体制备步骤如下： 
钼酸钠15g/L，硫酸镍25g/L，柠檬酸钠10g/L，亚硫酸钠10g/L，乙二酸10g/L。 
a.将15g/L的钼酸钠倒入少量水中，搅拌使其充分溶解； 
b.将10g/L的柠檬酸钠和10g/L的亚硫酸钠缓慢加入，搅拌使其充分溶解； 
c.将10g/L的乙二酸倒入，搅拌均匀； 
d.将25g/L的硫酸镍缓慢加入，迅速搅拌，使其充分溶解； 
e.将计算量的水(电导率＜5us/cm)定容后，静置10分钟，用硝酸调pH在2.5范围内。 
f.配制通用的低氰镀锌溶液，并调整pH值，进行电镀。 
g.一定时间后取出试样，在3％的硝酸中出光后进行钝化处理，钝化时间为15s。 
根据实施例1所配制的钝化液的极化曲线如下： 
测极化曲线的仪器采用PARSTAT2273advanced Electrochemical System 
试验使用的扫描电镜是由日本电子有限公司生产，型号为JSM-6380LA，加速电压为20KV 
钝化后的样片在扫描电镜下×1000倍的表面形貌如下： 
Figure BSA0000099431220000041
钝化后的样片在扫描电镜下×5000倍的表面形貌如下： 
Figure BSA0000099431220000042
钝化后的样片在XRD观察到的钝化膜的物象分析表如下： 
Bruker D8Advance50kV，30mA，Mo靶 
Figure BSA0000099431220000051

Claims (1)

1.邦迪管镀锌无铬军彩色钝化剂II，其特征在于钝化剂的原料组成如下：含钼酸钠10～20g/L、柠檬酸钠5～15g/L、亚硫酸钠10～20g/L、乙二酸5～15g/L、硫酸镍10～20g/L，其余为水(电导率＜5us/cm)；邦迪管镀锌无铬军彩色钝化剂II使用时pH值维持在2～2.5范围内。
CN201310722062.9A 2013-12-24 2013-12-24 邦迪管镀锌无铬军绿色钝化剂 ii Expired - Fee Related CN103695887B (zh)