CN103255403A - 一种无铬黑色钝化剂 - Google Patents

一种无铬黑色钝化剂 Download PDF

Info

Publication number
CN103255403A
CN103255403A CN2013101804759A CN201310180475A CN103255403A CN 103255403 A CN103255403 A CN 103255403A CN 2013101804759 A CN2013101804759 A CN 2013101804759A CN 201310180475 A CN201310180475 A CN 201310180475A CN 103255403 A CN103255403 A CN 103255403A
Authority
CN
China
Prior art keywords
passivator
chrome
sodium
passivation
chrome black
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101804759A
Other languages
English (en)
Other versions
CN103255403B (zh
Inventor
石磊
张明晓
许斌
刘科高
林晓娟
石浩洋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Jianzhu University
Original Assignee
Shandong Jianzhu University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Jianzhu University filed Critical Shandong Jianzhu University
Priority to CN201310180475.9A priority Critical patent/CN103255403B/zh
Publication of CN103255403A publication Critical patent/CN103255403A/zh
Application granted granted Critical
Publication of CN103255403B publication Critical patent/CN103255403B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及了一种无铬黑色钝化剂，采用钼酸钠、柠檬酸钠、丙二酸、硫酸铜、亚硫酸钠、十二烷基磺酸钠等物品通过一定的比例溶解混合均匀而成，其能显著提高镀层的耐蚀性能，转化膜浸油后，使其具有明亮的黑色。

Description

一种无铬黑色钝化剂
技术领域
本发明涉及一种无铬黑色钝化剂，尤其涉及一种无铬黑色钝化剂的成分、各成分的作用及配制方法。
背景技术
电镀锌是金属防腐的重要措施之一，而电镀行业的污染主要来源于镀后的钝化处理，目前市场上对镀锌层钝化工艺主要采用的是六价铬盐钝化和三价铬盐钝化。传统铬酸盐钝化液中含有的Cr6+具有毒性，环境污染严重，其应用在国内外已受到严格限制。目前为止，国内外还没有完全无铬的钝化工艺能够替代传统铬酸盐钝化，实现工业化生产。其中三价铬盐钝化膜在耐蚀性能上远不如六价铬盐，且三价铬盐钝化膜在放置的过程中会转化为六价铬，导致膜中六价铬含量超标而使产品的流通受到极大限制。因此研究具有良好装饰性且耐蚀性能好，低污染或无污染，从根本上解决铬盐钝化存在的问题的钝化工艺，对电镀行业突破欧盟绿色技术指标，推广环境友好型生产具有重要意义。
发明内容
本发明为了提高镀锌层钝化膜无毒环保，同时使钝化液中不含有Cr6+、Cr3+而发明了一种无铬黑色钝化剂。
本发明采用钼酸钠、柠檬酸钠、丙二酸、硫酸铜、亚硫酸钠、十二烷基磺酸钠等物品组成无铬黑色钝化剂。
本发明的具体制备方法包括如下顺序的步骤：
a.将烧杯及玻璃棒用纯水涮洗；
b.将称好的一定质量柠檬酸钠倒入呈有少量纯水中的烧杯中，用玻璃棒搅拌使其充分溶解；
c.将称量好的的钼酸钠和亚硫酸钠缓慢加入到b液中，搅拌使其充分溶解；
d.将称量好的丙二酸加入到c液中，搅拌均匀；
e.将称量好的十二烷基磺酸钠加入到d液中，搅拌均匀；
f.将称量好的硫酸铜缓慢加入到上述溶液中，搅拌使其充分溶解；
g.加入纯水到所需体积，用硝酸调pH在1～2范围内。
本发明所得一种无铬黑色钝化剂，为澄清呈深棕黑色的液体。
实验说明
本发明通过镀锌实验后，在无铬黑色钝化液中实施钝化处理，经过不同时间的处理后，观察镀层的色泽，并进行中性盐雾试验测定其耐蚀性能。此黑色并不是真正意义上的黑色，需要对转化膜浸油来做进一步观察，此时更接近我们需要的黑色。
具体实施方式
本实施例的具体制备步骤如下：
a.配制通用的低氰镀锌溶液，并调整pH值，进行电镀。
b.一定时间后取出试样，在3％的硝酸中出光后进行钝化处理，钝化时间为10～20s。
c.观察转化膜层的色泽，并进行中性盐雾试验。
一种无铬黑色钝化剂工艺规范为：
钼酸钠、柠檬酸钠、丙二酸、硫酸铜、亚硫酸钠、十二烷基磺酸钠
Figure BSA00000895663100031
注：当有搅拌时，钝化时间可以缩短且钝化膜更加均匀。

Claims (1)

1.一种无铬黑色钝化剂，其特征在于钝化剂的原料组成如下：含钼酸钠20～50g/L、柠檬酸钠5～15g/L、丙二酸5～15g/L、硫酸铜15～25g/L、亚硫酸钠15～25g/L、十二烷基磺酸钠1～5g/L，其余为纯水；无铬黑色钝化剂使用时pH值维持在1～2.5范围内，温度为室温。
CN201310180475.9A 2013-05-16 2013-05-16 一种无铬黑色钝化剂 Expired - Fee Related CN103255403B (zh)