CN103695851B - 溅射法制备柔性太阳能电池cigs吸收层和缓冲层的方法 - Google Patents

溅射法制备柔性太阳能电池cigs吸收层和缓冲层的方法 Download PDF

Info

Publication number
CN103695851B
CN103695851B CN201310740650.5A CN201310740650A CN103695851B CN 103695851 B CN103695851 B CN 103695851B CN 201310740650 A CN201310740650 A CN 201310740650A CN 103695851 B CN103695851 B CN 103695851B
Authority
CN
China
Prior art keywords
layer
buffer layer
target
absorption layer
sputtering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310740650.5A
Other languages
English (en)
Other versions
CN103695851A (zh
Inventor
陈进中
莫经耀
吴伯增
林东东
甘振英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGXI HUAXI GROUP Co.,Ltd.
Original Assignee
LIUZHOU BAIRENTE ADVANCED MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIUZHOU BAIRENTE ADVANCED MATERIALS CO Ltd filed Critical LIUZHOU BAIRENTE ADVANCED MATERIALS CO Ltd
Priority to CN201310740650.5A priority Critical patent/CN103695851B/zh
Publication of CN103695851A publication Critical patent/CN103695851A/zh
Application granted granted Critical
Publication of CN103695851B publication Critical patent/CN103695851B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉CIGS太阳能电池，具体说是溅射法制备柔性太阳能电池CIGS吸收层和缓冲层的方法,其包括制备吸收层靶材和缓冲层靶材、将上述两靶材和对应的溅射源置于加热的真空室内、在两靶材下侧设置工作台，含有钼电极层的基板可沿工作台移动、基板沿工作台正向移动时，溅射源由上向下轰击吸收层靶材，使钼电极层上沉积吸收层、吸收层沉积完成后，基板沿工作台反向移动，溅射源由上向下轰击缓冲层靶材，使吸收层上沉积缓冲层。本发明采用靶源沉积吸收层，不仅可进行大面积的生产，而且成膜质量高；并采用向由上向下的溅射法沉积吸收层与缓冲层，避免了因重力的影响使得沉积不够均匀的现象。

Description

溅射法制备柔性太阳能电池CIGS吸收层和缓冲层的方法
技术领域
本发明涉及CIGS太阳能电池的制备，具体说是柔性CIGS太阳能电池吸收层和缓冲层的制备方法。
背景技术
现有的CIGS(铜铟镓硒)太阳能电池包括基板，基板材料可包括玻璃、铝、不锈钢、聚合物或任何具相似可挠性的金属及塑料，在基板表面沉积有数层薄膜。首先，基板上沉积有碱硅酸盐层。一般而言，来自碱硅酸盐层的钠穿过底部电极层至吸收层，增加电池效率；接着，含有钼(Mo)的底部电极层溅射至碱硅酸盐层上，在底部电极层上沉积有吸收层，吸收层上沉积有缓冲层，缓冲层是由硫化镉(CdS)组成。硫化镉具有毒性。由氧化锌(ZnO)组成的快闪层溅镀形成于缓冲层上。快闪层用于防止太阳能电池在进行发电过程中，因Shunting及薄膜针孔(pinhole)的问题导致CIGS薄膜效能下降；最后，由铝掺杂氧化锌所构成的顶部电极层是溅射于快闪层上。
其中，CIGS吸收层是太阳能电池的核心部分，吸收层的制备方法如多元共蒸法和磁控溅射后硒化法。共蒸法由于采用四种不同的元素各具有不同的熔点，使得要控制整比化合物在大型基板上的形成是很困难的。目前，市场上出现有一种通过溅射法直接制备吸收层和缓冲层的方法，其采用的方法是使基板圆周运行，在圆周外通过溅射法使基板上形成吸收层和缓冲层。这种方法由于采用的是水平溅射，由于重力的作用，其在基板上沉积的吸收层和缓冲层不够均匀，影响电池的质量。
发明内容
针对上述技术问题，本发明提供一种沉积较均匀、可连续制备吸收层和缓冲的方法。
本发明解决上述技术问题采用的技术方案是：溅射法制备柔性太阳能电池CIGS吸收层和缓冲层的方法,其包括以下步骤：
（1）制备吸收层靶材和缓冲层靶材；
（2）将上述两靶材和对应的溅射源置于加热的真空室内；
（3）在两靶材下侧设置工作台，含有钼电极层的基板可沿工作台移动；
（4）基板沿工作台正向移动时，溅射源由上向下轰击吸收层靶材，使钼电极层上沉积吸收层；
（5）吸收层沉积完成后，基板沿工作台反向移动，溅射源由上向下轰击缓冲层靶材，使吸收层上沉积缓冲层。
进一步地，所述吸收层靶材和缓冲层靶材设置于同一个旋转体上，旋转体内设有溅射源，通过转动旋转体切换吸收层靶材和缓冲层靶材。
进一步地，所述吸收层靶材由CIGS粉末压制而成。
进一步地，将CuCl2、InCl3、GaCl3、Na2Se加入乙二胺中反应合成CIGS粉末。
本发明与现有技术相比具有如下优点：
1、本发明采用靶源沉积吸收层，不仅可进行大面积的生产，而且成膜质量高；
2、采用由上向下的溅射法沉积吸收层与缓冲层，避免了因重力的影响使得沉积不够均匀的现象。
3、采用可切换的靶材方式，配合基板的正、反向运动，以沉积吸收层和缓冲层，提高了生产效率。
具体实施方式
下面详细介绍本发明：
本发明的方法包括以下步骤：
（1）制备吸收层靶材和缓冲层靶材；
在制备吸收层靶材时，首先将CuCl2、InCl3、GaCl3、Na2Se加入乙二胺中搅拌，乙二胺可吸收合成反应所释放的多余热量，并可增加前驱盐在溶剂中的溶解度，从而使反应更完全；通过上述化合物进行反应，从而合成CIGS粉末，且CIGS的粒径较为均匀；然后将粉末压制成吸收层靶材，这种方式可使靶材的致密度可达90%以上。本发明的缓冲层靶材采用现有的CdS靶材。
（2）将上述两靶材和对应的溅射源置于加热的真空室内，使得溅射在真空中进行，并通过加热器进行加热，维持适当的温度条件；溅射源采用等离子化的惰性气体，如通过离化器使氩气生成等离子带电体等；溅射源通过轰击靶材，使相应的成分沉积在基板上。
（3）在两靶材下侧设置工作台，含有钼电极层的基板可沿工作台移动；工作台支撑基板，同时可通过滚子等现有装置使基板沿工作台正反向移动。
（4）基板沿工作台正向移动时，吸收层靶材位于基板正上方，溅射源由上向下轰击吸收层靶材，使钼电极层上沉积吸收层；
（5）吸收层沉积完成后，基板沿工作台反向移动，此时应将吸收层靶材切换成缓冲层靶材，使缓冲层靶材位于基板正上方，从而通过溅射源由上向下轰击缓冲层靶材，使吸收层上沉积缓冲层。
本方法由于采用向由上向下的溅射法沉积吸收层与缓冲层，避免了因重力的影响使得沉积不够均匀的现象，不仅可连续制备吸收层和缓冲层，生产效率高；而且成膜质量高。
在本发明中，为了实现吸收层靶材和缓冲层靶材的切换，可将吸收层靶材和缓冲层靶材设置于同一个旋转体上，旋转体内设有溅射源，溅射源透过旋转体轰击靶材，并通过转动旋转体切换吸收层靶材和缓冲层靶材。这种方式节约空间，降低生产成本。当然，也可以采用其他的方式实现。
上述实施方式仅供说明本发明之用，而并非是对本发明的限制，有关技术领域的普通技术人员，在不脱离本发明精神和范围的情况下，还可以作出各种变化和变型，因此所有等同的技术方案也应属于本发明的范畴。

Claims (3)

1.溅射法制备柔性太阳能电池CIGS吸收层和缓冲层的方法,其包括以下步骤：
（1）制备吸收层靶材和缓冲层靶材；
（2）将上述两靶材和对应的溅射源置于加热的真空室内；
（3）在两靶材下侧设置工作台，含有钼电极层的基板沿工作台移动；
（4）基板沿工作台正向移动时，溅射源由上向下轰击吸收层靶材，使钼电极层上沉积吸收层；
（5）吸收层沉积完成后，基板沿工作台反向移动，溅射源由上向下轰击缓冲层靶材，使吸收层上沉积缓冲层。
2.根据权利要求1所述的方法，其特征在于：所述吸收层靶材和缓冲层靶材设置于同一个旋转体上，旋转体内设有溅射源，通过转动旋转体切换吸收层靶材和缓冲层靶材。
3.根据权利要求2所述的方法，其特征在于：所述吸收层靶材由CIGS粉末压制而成。
CN201310740650.5A 2013-12-27 2013-12-27 溅射法制备柔性太阳能电池cigs吸收层和缓冲层的方法 Active CN103695851B (zh)