CN103666062A - Ultraviolet light curing embossment ink and preparation method thereof - Google Patents
Ultraviolet light curing embossment ink and preparation method thereof Download PDFInfo
- Publication number
- CN103666062A CN103666062A CN201310601764.1A CN201310601764A CN103666062A CN 103666062 A CN103666062 A CN 103666062A CN 201310601764 A CN201310601764 A CN 201310601764A CN 103666062 A CN103666062 A CN 103666062A
- Authority
- CN
- China
- Prior art keywords
- parts
- ink
- minute
- ultraviolet curing
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses ultraviolet curing embossment ink which is characterized by being prepared from the following raw materials in parts by weight: 1-3 parts of organic dye, 10-12 parts of 196 unsaturated polyester resin, 10-12 parts of acrylic resin, 13-16 parts of phenolic resin, 2-3 parts of glycerin, 3-4 parts of N,N-dimethylformamide, 1-2 parts of trifluoroacetylacetone, 1-3 parts of tetrahydrofuran, 1-2 parts of monobutyltin oxide, 5-8 parts of triethylene tetramine, 6-9 parts of crylic acid-2-hydroxyethyl acrylate, 12-15 parts of tripropylene glycol, 12-15 parts of tripropylene glycol diacrylate, 5-8 parts of 184 photoinitiator and 4-5 parts of auxiliary. The auxiliary disclosed by the invention improves the toughness of the ink, the ink can be uniformly dispersed, and the stability of the ink is maintained; the ink disclosed by the invention can be printed on golden and silver card paper, PVC (Polyvinyl Chloride) or matt lamination in a screen printing mode at one time, an embossment character effect with gorgeous color can be formed through printing at one time, and the ink is applied to high-class package.
Description
Technical field
The present invention relates to a kind of ink and preparation method thereof, particularly a kind of ultraviolet curing embossed printing ink and preparation method thereof.
Background technology
Ultraviolet curing embossed printing ink is a kind of screen printing ink, the irradiation of the ultraviolet lamp of process specific wavelength forms type effect lucuriant in design, this ink can be widely used in high-grade packing aspect, according to customer requirement, can be formulated into the embossed printing ink that shades of colour is bright-coloured, its curing speed and sticking power are all good.Existing ultraviolet curing embossed printing ink all needs repeatedly to print and could form type effect, the easy like this register trouble expense material consuming time that occurs.
Summary of the invention
The object of this invention is to provide a kind of ultraviolet curing embossed printing ink and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
A kind of ultraviolet curing embossed printing ink, raw material by following weight part is made: pigment dyestuff 1-3,196 unsaturated polyester resin 10-12, acrylic resin 10-12, resol 13-16, glycerine 2-3, DMF 3-4, trifluoroacetylacetone europium 1-2, tetrahydrofuran (THF) 1-3, Mono-n-butyltin 1-2, triethylene tetramine 5-8, vinylformic acid-2-hydroxy methacrylate 6-9, tripropylene glycol diacrylate 12-15, tri (propylene glycol) diacrylate 12-15,184 light trigger 5-8, auxiliary agent 4-5;
Described auxiliary agent is prepared from by the raw material of following weight part: nano diatomite powder 0.2-0.3, nano mica powder 0.2-0.3, silane resin acceptor kh-550 2-3, methacrylic acid-2-hydroxy methacrylate 2-3, neopentyl glycol 5-8, vinyl acetate 12-15, linking agent TAC2-3, oxidation inhibitor 1035 2-3, N hydroxymethyl acrylamide 1-2, Tenox PG 2-3, coix seed oil 1-2; Its preparation method is by each mixing of materials, is heated to 60-70 ℃, and stirring reaction 30-40 minute, obtains.
Ultraviolet curing embossed printing ink of the present invention, by following concrete steps, made: first add pigment dyestuff, 196 unsaturated polyester resins, acrylic resin, resol, glycerine 2-3, N, dinethylformamide, trifluoroacetylacetone europium, tetrahydrofuran (THF), Mono-n-butyltin, triethylene tetramine stirring and evenly mixing, be heated to 80-90 ℃, stir 25-35 minute; Then add all the other remaining components except 184 light triggers, stirring reaction 3-5 hour; Finally be cooled to 60-70 ℃, add 184 light triggers, stirring reaction 40-50 minute, cooling after, grind and to obtain 20-40 μ m slurry, obtain.
The invention has the beneficial effects as follows: auxiliary agent of the present invention has improved the toughness of ink, make distributes ink even, and maintained the stability of ink; Ink provided by the invention can once be imprinted on it on gold and silver paperboard, PVC or mute film by screen painting mode, and it only needs one-step print just can form type effect lucuriant in design, for top grade, packs.
Specific embodiments
Below by specific examples, the present invention is described in detail.
A kind of ultraviolet curing embossed printing ink, by following weight part (kilogram) raw material make: pigment dyestuff 1,196 unsaturated polyester resins 10, acrylic resin 10, resol 13, glycerine 2, DMF 3, trifluoroacetylacetone europium 1, tetrahydrofuran (THF) 1, Mono-n-butyltin 1, triethylene tetramine 5, vinylformic acid-2-hydroxy methacrylate 6, tripropylene glycol diacrylate 12, tri (propylene glycol) diacrylate 12,184 light triggers 5, auxiliary agent 4;
Described auxiliary agent by following weight part (kilogram) raw material be prepared from: nano diatomite powder 0.2, nano mica powder 0.2, silane resin acceptor kh-550 2, methacrylic acid-2-hydroxy methacrylate 2, neopentyl glycol 5, vinyl acetate 12, linking agent TAC2, oxidation inhibitor 1,035 2, N hydroxymethyl acrylamide 1, Tenox PG 2, coix seed oil 1; Its preparation method is by each mixing of materials, is heated to 60-70 ℃, and stirring reaction 30-40 minute, obtains.
Ultraviolet curing embossed printing ink of the present invention, by following concrete steps, made: first add pigment dyestuff, 196 unsaturated polyester resins, acrylic resin, resol, glycerine 2-3, N, dinethylformamide, trifluoroacetylacetone europium, tetrahydrofuran (THF), Mono-n-butyltin, triethylene tetramine stirring and evenly mixing, be heated to 80-90 ℃, stir 25-35 minute; Then add all the other remaining components except 184 light triggers, stirring reaction 3-5 hour; Finally be cooled to 60-70 ℃, add 184 light triggers, stirring reaction 40-50 minute, cooling after, grind and to obtain 20-40 μ m slurry, obtain.
The ink of gained, is used cross-hatching ox-hide tape stripping, draws compartment apart from 1mm, and 100% adheres to; Spirituous cotton balls is soaked in use, and 300 grams of pressure wipings 50 times, are as good as shape; Be soaked in salad oil (normal temperature) 8 hours, be as good as shape; Use is soaked with the cotton balls of salt solution, and 300 grams of pressure wipings 50 times, are as good as shape.
Claims (2)
1. a ultraviolet curing embossed printing ink, it is characterized in that, raw material by following weight part is made: pigment dyestuff 1-3,196 unsaturated polyester resin 10-12, acrylic resin 10-12, resol 13-16, glycerine 2-3, DMF 3-4, trifluoroacetylacetone europium 1-2, tetrahydrofuran (THF) 1-3, Mono-n-butyltin 1-2, triethylene tetramine 5-8, vinylformic acid-2-hydroxy methacrylate 6-9, tripropylene glycol diacrylate 12-15, tri (propylene glycol) diacrylate 12-15,184 light trigger 5-8, auxiliary agent 4-5;
Described auxiliary agent is prepared from by the raw material of following weight part: nano diatomite powder 0.2-0.3, nano mica powder 0.2-0.3, silane resin acceptor kh-550 2-3, methacrylic acid-2-hydroxy methacrylate 2-3, neopentyl glycol 5-8, vinyl acetate 12-15, linking agent TAC2-3, oxidation inhibitor 1035 2-3, N hydroxymethyl acrylamide 1-2, Tenox PG 2-3, coix seed oil 1-2; Its preparation method is by each mixing of materials, is heated to 60-70 ℃, and stirring reaction 30-40 minute, obtains.
2. ultraviolet curing embossed printing ink according to claim 1, it is characterized in that, by following concrete steps, made: first add pigment dyestuff, 196 unsaturated polyester resins, acrylic resin, resol, glycerine 2-3, N, dinethylformamide, trifluoroacetylacetone europium, tetrahydrofuran (THF), Mono-n-butyltin, triethylene tetramine stirring and evenly mixing, be heated to 80-90 ℃, stir 25-35 minute; Then add all the other remaining components except 184 light triggers, stirring reaction 3-5 hour; Finally be cooled to 60-70 ℃, add 184 light triggers, stirring reaction 40-50 minute, cooling after, grind and to obtain 20-40 μ m slurry, obtain.