CN103641941A - 纳米Fe2O3光引发聚合聚丙烯酰胺的方法 - Google Patents
纳米Fe2O3光引发聚合聚丙烯酰胺的方法 Download PDFInfo
- Publication number
- CN103641941A CN103641941A CN201310655345.6A CN201310655345A CN103641941A CN 103641941 A CN103641941 A CN 103641941A CN 201310655345 A CN201310655345 A CN 201310655345A CN 103641941 A CN103641941 A CN 103641941A
- Authority
- CN
- China
- Prior art keywords
- nanometer
- pam
- polyacrylamide
- fe2o3
- conical flask
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种纳米Fe2O3光引发聚合聚丙烯酰胺的方法，1)置于三角烧瓶中配制5.0mmol/L的FeCl3溶液，旋紧密封后置于干燥箱中并于95～98℃下保温1小时，保温1小时后冷却至室温，即得纳米Fe2O3；2)取含AM和纳米Fe2O3的反应液倒入反应槽中，通氮气后密封；将反应槽置于高压汞灯上方，经紫外截止型滤波片照射引发AM聚合，反应结束后，将产物在乙醇中沉淀、洗涤3次，过滤干燥。沉淀过程中不搅拌。本发明的有益效果为：本发明的纳米Fe2O3光引发聚合聚丙烯酰胺的方法，以纳米Fe2O3为光引发剂得到的PAM具有较好的絮凝性能，其絮凝效果优于以PEI-TX为光引发剂得到的PAM。
Description
技术领域
本发明涉及材料领域，具体是一种纳米Fe2O3光引发聚合聚丙烯酰胺的方法。
背景技术
丙烯酰胺类聚合物是丙烯酰胺及其衍生物的均聚物和共聚物的统称。丙烯酰胺类聚合物是一类具有特殊功能的线形水溶性聚合物，已广泛应用于钻井驱油、水处理、造纸、纺织印染、冶金、土壤改良等诸多领域。分子量大小在很大程度上决定着产品的用途及功能，高分子量的聚丙烯酰胺(105-107)对许多固体表面和溶解物质有着良好的粘附力，因而应用于增稠、絮凝、阻垢、采油及生物医学材料等领域；中等分子量的可用作造纸行业的纸张干燥剂；低分子量的则用作油墨分散剂。目前，超高分子量聚丙烯酰胺应用于三次采油时，可有效地提高原油采收率(EOR)，这已成为国内外许多油田保持高产稳产的重大技术措施之一。
发明内容
本发明的目的是提供一种纳米Fe2O3光引发聚合聚丙烯酰胺的方法。
本发明的技术方案是这样实现的：纳米Fe2O3光引发聚合聚丙烯酰胺的方法，1)置于三角烧瓶中配制5.0mmol/L的FeCl3溶液，旋紧密封后置于干燥箱中并于95～98℃下保温1小时，保温1小时后冷却至室温，即得纳米Fe2O3；2)取含AM和纳米Fe2O3的反应液倒入反应槽中，通氮气后密封；将反应槽置于高压汞灯上方，经紫外截止型滤波片照射引发AM聚合，反应结束后，将产物在乙醇中沉淀、洗涤3次，过滤干燥。沉淀过程中不搅拌。
本发明的有益效果为：本发明的纳米Fe2O3光引发聚合聚丙烯酰胺的方法，以纳米Fe2O3为光引发剂得到的PAM具有较好的絮凝性能，其絮凝效果优于以PEI-TX为光引发剂得到的PAM。
具体实施方式
下面结合具体实施例对本发明作进一步解释说明。
纳米Fe2O3光引发聚合聚丙烯酰胺的方法，1)置于三角烧瓶中配制5.0mmol/L的FeCl3溶液，旋紧密封后置于干燥箱中并于95～98℃下保温1小时，保温1小时后冷却至室温，即得纳米Fe2O3；2)取含AM和纳米Fe2O3的反应液倒入反应槽中，通氮气后密封；将反应槽置于高压汞灯上方，经紫外截止型滤波片照射引发AM聚合，反应结束后，将产物在乙醇中沉淀、洗涤3次，过滤干燥。沉淀过程中不搅拌。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明披露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (2)
1.纳米Fe2O3光引发聚合聚丙烯酰胺的方法，其特征在于，1)置于三角烧瓶中配制5.0mmol/L的FeCl3溶液，旋紧密封后置于干燥箱中并于95～98℃下保温1小时，保温1小时后冷却至室温，即得纳米Fe2O3；2)取含AM和纳米Fe2O3的反应液倒入反应槽中，通氮气后密封；将反应槽置于高压汞灯上方，经紫外截止型滤波片照射引发AM聚合，反应结束后，将产物在乙醇中沉淀、洗涤3次，过滤干燥。
2.根据权利要求1所述的纳米Fe2O3光引发聚合聚丙烯酰胺的方法，其特征在于，沉淀过程中不搅拌。