CN103589521A - Water-based cleaning agent for removal of silicon wafer surface stains and preparation method thereof - Google Patents
Water-based cleaning agent for removal of silicon wafer surface stains and preparation method thereof Download PDFInfo
- Publication number
- CN103589521A CN103589521A CN201310527754.8A CN201310527754A CN103589521A CN 103589521 A CN103589521 A CN 103589521A CN 201310527754 A CN201310527754 A CN 201310527754A CN 103589521 A CN103589521 A CN 103589521A
- Authority
- CN
- China
- Prior art keywords
- parts
- cleaning agent
- ethanol
- minute
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A water-based cleaning agent for removal of silicon wafer surface stains comprises the following raw materials: by weight, 3-4 parts of octyl benzene alkyl polyoxyethylene phosphate, 2-3 parts of sodium dodecylthio acetate, 3-4 parts of sodium citrate, 1-2 parts of sodium perborate, 30-40 parts of ethanol, 4-5 parts of an auxiliary agent and 100-120 parts of deionized water. The cleaning agent has excellent cleaning effects to metal ions, lipids, inorganic matter particles and the like; the cleaning agent has good cleaning effects to the stains on the surface of a circuit board by use of the sodium perborate, has the effect for preventing producing of the stains on the surface of the circuit board, and is convenient to operate. The auxiliary agent of the cleaning agent can form a protective film on the surface of the circuit board for isolating air to prevent water and other molecules in the atmosphere from corroding the circuit board, is anti-oxidizing, and facilitates performing of a next-step manufacture process.
Description
Technical field
The present invention relates to clean-out system field, relate in particular to a kind of aqueous cleaning agent of removing silicon chip surface stain and preparation method thereof.
Background technology
The industry Wafer Cleanings such as silicon slice detergent is widely used in photovoltaic, electronics; Because silicon chip can pollute to some extent in transportation, surface cleanliness is not very high, the corrosion and the etching that are about to carry out is had a huge impact, so first will carry out a series of cleaning operation to silicon chip surface.First the general thinking of cleaning is to remove surperficial organic contaminations, and dissolved oxygen film then, because zone of oxidation is " contamination fall into into ", can cause epitaxy defect; Remove again particle, metal etc., make the surface passivation of silicon chip simultaneously.
Current most silicon slice detergent adopts a liquid and No. three liquid in RAC cleaning, but the aobvious alkalescence of liquid may cause silicon face coarse, strictly control temperature, concentration and time; No. three liquid is aobvious acid, has severe corrosive, also unfavorable to HUMAN HEALTH, production cost is high, irritant smell, contaminate environment, therefore require further improvement formula, with reach clean thorough, pollution-free, corrode little, to HUMAN HEALTH, circuit safety, the object that reduces costs.
Summary of the invention
The object of the present invention is to provide a kind of aqueous cleaning agent of removing silicon chip surface stain and preparation method thereof, this clean-out system have advantages of clean thoroughly, cleaning speed removes stain soon, fast.
Technical scheme of the present invention is as follows:
Remove an aqueous cleaning agent for silicon chip surface stain, it is characterized in that being made by the raw material of following weight part: octyl group benzene alkyl polyoxyethylene phosphate 3-4, dodecyl sodium thioglycolate 2-3, Trisodium Citrate 3-4, Sodium peroxoborate 1-2, ethanol 30-40, auxiliary agent 4-5, deionized water 100-120;
Described auxiliary agent is made by the raw material of following weight part: Silane coupling reagent KH-570 2-3, oxidation inhibitor 1035 1-2, phytic acid 1-2, morpholine 3-4, methacrylic acid-2-hydroxy methacrylate 3-4, ethanol 12-15; Preparation method mixes Silane coupling reagent KH-570, phytic acid, ethanol, is heated to 60-70 ℃, stirs after 20-30 minute, then adds other remaining component, is warming up to 80-85 ℃, stirs 30-40 minute, obtains.
The preparation method of the aqueous cleaning agent of described removal silicon chip surface stain, it is characterized in that comprising the following steps: deionized water, octyl group benzene alkyl polyoxyethylene phosphate, dodecyl sodium thioglycolate, Trisodium Citrate, ethanol are mixed, under 1000-1200 rev/min of stirring, speed with 6-8 ℃/minute is heated to 60-70 ℃, cool to again below 25 ℃, add other remaining components, continue to stir 15-20 minute, obtain.
Beneficial effect of the present invention
Clean-out system of the present invention all has excellent cleaning performance to metal ion, lipid, particles of inorganic material etc.; And by using Sodium peroxoborate, good to the cleaning performance of circuit board surface stain, also have simultaneously and prevent that circuit board surface from forming the effect of stain, easy to operate.Auxiliary agent of the present invention can form protective membrane at circuit board surface, and isolated air, prevents water and other molecule open circuit potential plates in atmosphere, anti-oxidant, facilitates next step manufacture craft to carry out.
Embodiment
Remove an aqueous cleaning agent for silicon chip surface stain, by following weight part (kilogram) raw material make: octyl group benzene alkyl polyoxyethylene phosphate 3.6, dodecyl sodium thioglycolate 2.5, Trisodium Citrate 3.5, Sodium peroxoborate 1.5, ethanol 35, auxiliary agent 4.5, deionized water 110;
Described auxiliary agent by following weight part (kilogram) raw material make: Silane coupling reagent KH-570 2.5, oxidation inhibitor 1,035 1.5, phytic acid 1.5, morpholine 3.5, methacrylic acid-2-hydroxy methacrylate 3.5, ethanol 14; Preparation method mixes Silane coupling reagent KH-570, phytic acid, ethanol, is heated to 65 ℃, stirs after 25 minutes, then adds other remaining component, is warming up to 84 ℃, stirs 34 minutes, obtains.
The preparation method of the aqueous cleaning agent of described removal silicon chip surface stain, comprise the following steps: deionized water, octyl group benzene alkyl polyoxyethylene phosphate, dodecyl sodium thioglycolate, Trisodium Citrate, ethanol are mixed, under 1100 revs/min of stirrings, with the speed of 7 ℃/minute, be heated to 65 ℃, cool to again 22 ℃, add other remaining components, continue to stir 18 minutes, obtain.
This aqueous cleaning agent of removing silicon chip surface stain is for cleaning silicon chip, and clean rate is 99.4%, can residual insolubles to cleaning silicon chip surface, do not produce new pollution, and do not affect the quality of product, the silicon chip surface after cleaning is clean, and color and luster is consistent, without piebald.
Claims (2)
1. remove an aqueous cleaning agent for silicon chip surface stain, it is characterized in that being made by the raw material of following weight part: octyl group benzene alkyl polyoxyethylene phosphate 3-4, dodecyl sodium thioglycolate 2-3, Trisodium Citrate 3-4, Sodium peroxoborate 1-2, ethanol 30-40, auxiliary agent 4-5, deionized water 100-120;
Described auxiliary agent is made by the raw material of following weight part: Silane coupling reagent KH-570 2-3, oxidation inhibitor 1035 1-2, phytic acid 1-2, morpholine 3-4, methacrylic acid-2-hydroxy methacrylate 3-4, ethanol 12-15; Preparation method mixes Silane coupling reagent KH-570, phytic acid, ethanol, is heated to 60-70 ℃, stirs after 20-30 minute, then adds other remaining component, is warming up to 80-85 ℃, stirs 30-40 minute, obtains.
2. remove according to claim 1 the preparation method of the aqueous cleaning agent of silicon chip surface stain, it is characterized in that comprising the following steps: deionized water, octyl group benzene alkyl polyoxyethylene phosphate, dodecyl sodium thioglycolate, Trisodium Citrate, ethanol are mixed, under 1000-1200 rev/min of stirring, speed with 6-8 ℃/minute is heated to 60-70 ℃, cool to again below 25 ℃, add other remaining components, continue to stir 15-20 minute, obtain.