CN103571345A - 一种强力白乳胶 - Google Patents

一种强力白乳胶 Download PDF

Info

Publication number
CN103571345A
CN103571345A CN201310276901.9A CN201310276901A CN103571345A CN 103571345 A CN103571345 A CN 103571345A CN 201310276901 A CN201310276901 A CN 201310276901A CN 103571345 A CN103571345 A CN 103571345A
Authority
CN
China
Prior art keywords
parts
water
white latex
alcohol
mentioned
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310276901.9A
Other languages
English (en)
Inventor
黄美玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN TIANZHIJIAO FIREPROOF MATERIALS Co Ltd
Original Assignee
TIANJIN TIANZHIJIAO FIREPROOF MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN TIANZHIJIAO FIREPROOF MATERIALS Co Ltd filed Critical TIANJIN TIANZHIJIAO FIREPROOF MATERIALS Co Ltd
Priority to CN201310276901.9A priority Critical patent/CN103571345A/zh
Publication of CN103571345A publication Critical patent/CN103571345A/zh
Pending legal-status Critical Current

Abstract

一种强力白乳胶，由下列原料按照如下的重量配比制成：醋酸乙烯酯44-46份、聚乙烯醇5-8份、邻苯二甲酸二丁酯1-5份、过硫酸铵0.1份、醇13-16份、憎水剂0.1份、水21-24份。该产品耐低温性能和耐水性能好、产品粘接强度高、使用方便，并且可降低生产成本。

Description

一种强力白乳胶
技术领域：
本发明属于一种粘合剂，特别涉及一种强力白乳胶。 
背景技术：
白乳胶是目前用途最广，用量最大的粘合剂品种之一，广泛用于木材加工、建筑装饰、印刷品装订、皮革、纺织等行业。传统白乳胶大多以醋酸乙烯、聚乙烯醇、甚至淀粉为主要原料，不仅聚合工艺复杂，生产周期长，而且所制得的白乳胶本身存在耐水性差、粘结处遇水易脱胶等不足，尤其在冬季低温条件下胶凝现象普遍，且干燥速度慢、初粘力弱、拉丝，使用不便。 
发明内容：
本发明的目的就在于克服上述现有技术中存在的不足，而提供一种强力白乳胶，该产品耐低温性能和耐水性能好、产品粘接强度高、使用方便，并且可降低生产成本。 
如上构思，本发明的技术方案是：一种强力白乳胶，其特征在于：由下列原料按照如下的重量配比制成：醋酸乙烯酯44-46份、聚乙烯醇5-8份、邻苯二甲酸二丁酯1-5份、过硫酸铵0.1份、醇13-16份、憎水剂0.1份、水21-24份。 
上述原料中加入异氰酸酯0.001份。 
上述憎水剂采用A171。 
上述醇采用乙醇。 
上述醇采用辛醇。 
上述醇采用乙醇和辛醇。 
本发明中的各种原料的主要性能是： 
1、聚乙烯醇（简称PVA)外观为白色粉末，是一种用途相当广泛的水溶性高分子聚合物，性能介于塑料和橡胶之间，可分为纤维和非纤维两大用途。PVA具有独特的强力粘接性、皮膜柔韧性、平滑性、耐油性、耐溶剂性、保护胶体性、气体阻绝性、耐磨性以及耐水性。 
2、邻苯二甲酸二丁酯是最常用的增塑剂，可使制品具有良好的柔软性。 
3、辛醇主要用于制邻苯二甲酸酯类及脂肪族二元酸酯类增塑剂，分别用作塑料的主增塑剂和耐寒辅助增塑剂、消泡剂、分散剂等。 
4、憎水剂是外墙防水专用防水剂，它主要用于瓷砖外墙防水（喷涂）、卫生间、厨房、阳台等瓷砖缝防水，混凝土墙面、瓷砖、石材、木材、水泥面和路面防水的应用具有抗酸碱、耐老化、防碳化、泛碱、防潮、防霉等。 
5、过硫酸铵是漂白剂和氧化剂。 
6、醋酸乙烯酯属于低成本内墙用无光乳胶漆，具有适宜的硬度、柔韧性、溶解性和附着力。 
综上，本发明将上述各种原料进行综合利用，利用它们互相的协同作用，使本发明具有如下的优点： 
1、本发明原料易购、生产工艺简单、生产成本低、产品高质量。广泛用于木材、纸张、织物、皮革、化工建材、装饰装修等行业，市场前景极为广阔。 
2、本发明产品的外观为乳白色粘稠液体，耐低温性能优异，不沉淀，不分层，不会凝胶。 
3、本发明产品的耐水性能好，产品粘接强度高，柔软而富有弹性，初粘性好，不拉丝，干燥快、使用方便。 
4、本发明以水和醇类为介质，不含有机溶剂，无毒，不燃，无刺激性臭味，生产无污染。 
具体实施方式：
下面结合具体实施例对本发明作进一步详述，以下实施例只是描述性的，不是限定性的，不能以此限定本发明的保护范围。 
实施例1：一种强力白乳胶，由下列原料按照如下的重量制成：醋酸乙烯酯44Kg、聚乙烯醇5Kg、邻苯二甲酸二丁酯1Kg、过硫酸铵0.1Kg、乙醇13Kg、憎水剂（A171）0.1Kg、水21-24Kg和异氰酸酯0.001Kg。 
实施例2：一种强力白乳胶，由下列原料按照如下的重量制成：醋酸乙烯酯46Kg、聚乙烯醇8Kg、邻苯二甲酸二丁酯5Kg、过硫酸铵0.1Kg、乙醇16Kg、憎水剂（A171）0.1Kg、水24Kg和异氰酸酯0.001Kg。 
实施例3：一种强力白乳胶，由下列原料按照如下的重量制成：醋酸乙烯酯45Kg、聚乙烯醇7Kg、邻苯二甲酸二丁酯3Kg、过硫酸铵0.1Kg、乙醇15Kg、憎水剂（A171）0.1Kg、异氰酸酯0.001Kg、辛醇1Kg和水20Kg。 
本发明产品耐低温性能和耐水性能好、产品粘接强度高、使用方便，并且可降低生产成本。 
尽管为说明目的公开了本发明的实施例，但是本领域的技术人员可以理解：在不脱离本发明及所附权利要求的精神和范围内，各种替换、变化和修改都是可能的，因此，本发明的范围不局限于实施例所公开的内容。 

Claims (6)

1.一种强力白乳胶，其特征在于：由下列原料按照如下的重量配比制成：醋酸乙烯酯44-46份、聚乙烯醇5-8份、邻苯二甲酸二丁酯1-5份、过硫酸铵0.1份、醇13-16份、憎水剂0.1份、水21-24份。
2.根据权利要求1所述的一种强力白乳胶，其特征在于：上述原料中加入异氰酸酯0.001份。
3.根据权利要求1所述的一种强力白乳胶，其特征在于：上述憎水剂采用A171。
4.根据权利要求1所述的一种强力白乳胶，其特征在于：上述醇采用乙醇。
5.根据权利要求1所述的一种强力白乳胶，其特征在于：上述醇采用辛醇。
6.根据权利要求1所述的一种强力白乳胶，其特征在于：上述醇采用乙醇和辛醇。
CN201310276901.9A 2013-07-03 2013-07-03 一种强力白乳胶 Pending CN103571345A (zh)