CN103571114A - 聚四氟乙烯活塞密封圈及其制备方法 - Google Patents

聚四氟乙烯活塞密封圈及其制备方法 Download PDF

Info

Publication number
CN103571114A
CN103571114A CN201210256442.3A CN201210256442A CN103571114A CN 103571114 A CN103571114 A CN 103571114A CN 201210256442 A CN201210256442 A CN 201210256442A CN 103571114 A CN103571114 A CN 103571114A
Authority
CN
China
Prior art keywords
parts
piston sealing
sealing ring
polytetrafluoroethylene
ring
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210256442.3A
Other languages
English (en)
Inventor
宋国新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI LILONG CHEMICAL FIBER Co Ltd
Original Assignee
SHANGHAI LILONG CHEMICAL FIBER Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI LILONG CHEMICAL FIBER Co Ltd filed Critical SHANGHAI LILONG CHEMICAL FIBER Co Ltd
Priority to CN201210256442.3A priority Critical patent/CN103571114A/zh
Publication of CN103571114A publication Critical patent/CN103571114A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种聚四氟乙烯活塞密封圈及其制备方法，所述聚四氟乙烯活塞密封圈，由下述组分按重量份组成：聚四氟乙烯100份，甲基苯基乙烯基硅橡胶30-40份，过氧化二异丙苯3-5份，三辛酰基钛酸异丙酯1-3份,玻璃纤维18-28份，二硫化钼10-18份，青铜粉6-12份，石墨2-4份。具体制备步骤为（1）将各原料搅拌混合均匀，装入模具中加压，压力10-15Mpa；（2）烧结，烧结温度380-390℃；再恒温保持2-4小时；（3）二次加压处理，压力为8-15Mpa；（4）自然冷却定型。本发明的聚四氟乙烯密封圈，具有良好的耐燃、耐温、不黏性的特点，热稳定性强和回弹性高。

Description

聚四氟乙烯活塞密封圈及其制备方法
技术领域
本发明涉及一种密封圈及其制备方法，尤其涉及一种聚四氟乙烯活塞密封圈及其制备方法。
背景技术
密封圈，是指由一个或几个零件组成的环形罩，固定在轴承的一个套圈或垫圈上并与另一套圈或垫圈接触或形成窄的迷宫间隙，防止润滑油漏出及外物侵入。
密封圈一般采用丁腈橡胶、天然橡胶、氯丁橡胶、乙丙橡胶、氟橡胶、硅橡胶以及共混胶制造。除了O型外还有三角型、矩型、D型、T型、方型、心型、X型、五棱型、橄榄型等。
聚四氟乙烯（Polytetrafluoroethene，英文缩写为PTFE，(俗称"塑料王")，商标名该商标中文译名则各地相异：中国大陆译为特富香港译为特氟
Figure BDA00001917317800013
台湾译为铁氟
Figure BDA00001917317800014
），这种材料的产品一般统称作“不粘涂层”；是一种使用了氟取代聚乙烯中所有氢原子的人工合成高分子材料。这种材料具有抗酸抗碱、抗各种有机溶剂的特点，几乎不溶于所有的溶剂。同时，聚四氟乙烯具有耐高温的特点，它的摩擦系数极低，所以可作润滑作用之余，亦成为了不沾锅和水管内层的理想涂料。
聚四氟乙烯具有杰出的优良综合性能，耐高温，耐腐蚀、不粘、自润滑、优良的介电性能、很低的摩擦系数。用作工程塑料，可制成聚四氟乙烯管、棒、带、板、薄膜等，一般应用于性能要求较高的耐腐蚀的管道、容器、泵、阀以及制雷达、高频通讯器材、无线电器材等。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题之一是提供一种聚四氟乙烯活塞密封圈。
本发明所要解决的技术问题之二是提供一种聚四氟乙烯活塞密封圈的制备方法。
本发明所要解决的技术问题，是通过如下技术方案实现的：
一种聚四氟乙烯活塞密封圈，由下述组分按重量份组成：聚四氟乙烯100份，甲基苯基乙烯基硅橡胶30-40份，过氧化二异丙苯3-5份，三辛酰基钛酸异丙酯1-3份,玻璃纤维18-28份，二硫化钼10-18份，青铜粉6-12份，石墨2-4份。
本发明所述聚四氟乙烯活塞密封圈，由下述步骤组成：
（1）将各原料搅拌混合均匀，装入模具中加压，压力10-15Mpa；
（2）烧结，烧结温度380-390℃；再恒温保持2-4小时；
（3）二次加压处理，压力为8-15Mpa；
（4）自然冷却定型。
本发明的聚四氟乙烯密封圈，具有良好的耐燃、耐温、不黏性的特点，热稳定性强和回弹性高。在工作温度很高的汽车内燃机活塞上使用本发明的聚四氟乙烯密封圈后，内燃机的寿命可以延长。
具体实施方式
通过实施例对本发明作进一步说明，但本发明并不受以下实施例所限定。
实施例1
称取：聚四氟乙烯100公斤，甲基苯基乙烯基硅橡胶35公斤，过氧化二异丙苯4公斤，三辛酰基钛酸异丙酯2公斤,玻璃纤维23公斤，二硫化钼14公斤，青铜粉9公斤，石墨3公斤。
（1）将上述各原料搅拌混合均匀，装入模具中加压，压力12Mpa；
（2）烧结，烧结温度385℃；再恒温保持3小时；
（3）二次加压处理，压力为13Mpa；
（4）自然冷却定型，即可制得本发明的聚四氟乙烯活塞密封圈。
经测试：
拉升强度19MPa；
断裂伸长率225%；
冲击强度23.5KJ/m；
弯曲强度28MPa；
磨耗4.3mm3。（负载250N，线速度2m/s，时间3分钟）
本发明的聚四氟乙烯密封圈，具有良好的耐燃、耐温、不黏性的特点，热稳定性强和回弹性高。在工作温度很高的汽车内燃机活塞上使用本发明的聚四氟乙烯密封圈后，内燃机的寿命可以延长。
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。

Claims (2)

1.一种聚四氟乙烯活塞密封圈，其特征在于，由下述组分按重量份组成：聚四氟乙烯100份，甲基苯基乙烯基硅橡胶30-40份，过氧化二异丙苯3-5份，三辛酰基钛酸异丙酯1-3份,玻璃纤维18-28份，二硫化钼10-18份，青铜粉6-12份，石墨2-4份。
2.如权利要求1所述的聚四氟乙烯活塞密封圈的制备方法，其特征在于，由下述步骤组成：
（1）将各原料搅拌混合均匀，装入模具中加压，压力10-15Mpa；
（2）烧结，烧结温度380-390℃；再恒温保持2-4小时；
（3）二次加压处理，压力为8-15Mpa；
（4）自然冷却定型。
CN201210256442.3A 2012-07-22 2012-07-22 聚四氟乙烯活塞密封圈及其制备方法 Pending CN103571114A (zh)