CN103496906A - 一种复合型防冻混凝土及其制备方法 - Google Patents

一种复合型防冻混凝土及其制备方法 Download PDF

Info

Publication number
CN103496906A
CN103496906A CN201310449496.6A CN201310449496A CN103496906A CN 103496906 A CN103496906 A CN 103496906A CN 201310449496 A CN201310449496 A CN 201310449496A CN 103496906 A CN103496906 A CN 103496906A
Authority
CN
China
Prior art keywords
parts
resistant concrete
concrete
compound
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310449496.6A
Other languages
English (en)
Other versions
CN103496906B (zh
Inventor
赵文法
王景洋
周黄山
金兆应
王钦霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rich green construction group Limited
Original Assignee
Zhangjiagang Shanmu New Material Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhangjiagang Shanmu New Material Technology Development Co Ltd filed Critical Zhangjiagang Shanmu New Material Technology Development Co Ltd
Priority to CN201310449496.6A priority Critical patent/CN103496906B/zh
Publication of CN103496906A publication Critical patent/CN103496906A/zh
Application granted granted Critical
Publication of CN103496906B publication Critical patent/CN103496906B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种复合型防冻混凝土及其制备方法，由以下原料按重量份配比而成：水泥20-25份；硅灰20-45份；水10-20份；黄沙10-20份；聚合物纤维1-2份；高强仿钢丝纤维4-6份；防冻剂15-20份。本发明中所采用的防冻剂组份能够有效的提升混凝土的上冻临界温度值，从而能够有效的阻止混凝土在规定的温度下上冻。

Description

一种复合型防冻混凝土及其制备方法
技术领域
本发明涉及建筑材料领域，特别涉及一种复合型防冻混凝土及其制备方法。
背景技术
建筑施工中，经常会遇到各种恶劣的天气环境，尤其是在冬季，长期的低温对混凝土的搅拌造成了很大的影响，如何才能防止混凝土在低温下上冻一直是工程人员比较头疼的问题。
现在市面上多采用硝酸盐、亚硝酸盐作为防冻组份来防止混凝土上冻，但是，这种方法使得混凝土含碱量骤然增高，甚至出现返碱现在，严重影响了工程质量。
发明内容
本发明的目的是：提出一种复合型防冻混凝土，其通过提高混凝土的临界温度值来达到防止上冻的目的。
本发明解决其技术问题所采用的技术方案是：
一种复合型防冻混凝土，由以下原料按重量份配比而成：
水泥                     20-25份；
硅灰                   20-45份；
水                       10-20份；
黄沙                     10-20份；
聚合物纤维               1-2份；
高强仿钢丝纤维               4-6份；
防冻剂                   15-20份。
优选地，所述聚合物纤维采用2份。
优选地，所述聚合物纤维由聚乙烯醇纤维和聚丙烯纤维混合制成。
优选地，所述聚乙烯醇纤维和所述聚丙烯纤维的重量份配比为7:3。
优选地，所述高强仿钢丝纤维采用6份。
优选地，所述防冻剂由聚乙二醇甲基丙烯酸、松香、六偏磷酸钠、聚羟酸葡萄糖酸钠和水混合制成。
优选地，所述聚乙二醇甲基丙烯酸、松香、六偏磷酸钠、聚羟酸葡萄糖酸钠和水的重量配比为50:5:30：5：10。
一种复合型防冻混凝土的制备方法，包括如下步骤：
步骤（1）：称取以下按重量份配比的原料混合搅拌：
水泥                     20-25份；
硅灰                   20-45份；
水                       10-20份；
黄沙                     10-20份；
高强仿钢丝纤维               4-6份；
步骤（2）：称取7份的聚乙烯醇纤维和3份的聚丙烯纤维混合后搅拌40分钟，制得聚合物纤维；
步骤（3）：在步骤（1）中制得的混合物中加入2份步骤（2）制得的聚合物纤维，搅拌1小时；
步骤（4）：将50份的聚乙二醇甲基丙烯酸和10份的水混合后加热搅拌升温至35℃-40℃，然后加入5份的聚羟酸葡萄糖酸钠，继续搅拌30min，再加入5份松香和30份六偏磷酸钠继续搅拌30min后制得防冻剂；
步骤（5）：将步骤（4）中制得的防冻剂，添加至步骤（3）中所得混合物中，再搅拌2-3个小时，即可使用。
本发明的有益效果是：本发明中所采用的防冻剂组份能够有效的提升混凝土的上冻临界温度值，从而能够有效的阻止混凝土在规定的温度下上冻。
具体实施方式
以下显示的是本发明的较佳实施例之一，供实施人员作为参考。
实施例1：一种复合型防冻混凝土，由以下原料按重量份配比而成：
水泥                     25份；
硅灰                   20份；
水                       20份
黄沙                     15份；
聚合物纤维               2份；
高强仿钢丝纤维               6份；
防冻剂                   12份。
优选地，所述聚合物纤维由聚乙烯醇纤维和聚丙烯纤维混合制成。
优选地，所述聚乙烯醇纤维和所述聚丙烯纤维的重量份配比为7:3。
优选地，所述防冻剂由聚乙二醇甲基丙烯酸、松香、六偏磷酸钠、聚羟酸葡萄糖酸钠和水混合制成。
优选地，所述聚乙二醇甲基丙烯酸、松香、六偏磷酸钠、聚羟酸葡萄糖酸钠和水的重量配比为50:5:30：5：10。
本产品的制备方法如下：
步骤（1）：称取以下按重量份配比的原料混合搅拌：
水泥                     25份；
硅灰                   20份；
水                       20份
黄沙                     15份；
高强仿钢丝纤维               6份；
步骤（2）：称取7份的聚乙烯醇纤维和3份的聚丙烯纤维混合后搅拌40分钟，制得聚合物纤维；
步骤（3）：在步骤（1）中制得的混合物中加入2份步骤（2）制得的聚合物纤维，搅拌1小时；
步骤（4）：将50份的聚乙二醇甲基丙烯酸和10份的水混合后加热搅拌升温至35℃-40℃，然后加入5份的聚羟酸葡萄糖酸钠，继续搅拌30min，再加入5份松香和30份六偏磷酸钠继续搅拌30min后制得防冻剂；
步骤（5）：将步骤（4）中制得的防冻剂，添加至步骤（3）中所得混合物中，再搅拌2个小时，即可使用。
经发明人实验证明，本方法制得的混凝土能够有效抵御-15℃的低温环境，并能够在负温环境下养护7天左右，再转为标准养护28的养护强度标准。

Claims (8)

1.一种复合型防冻混凝土，其特征在于，由以下原料按重量份配比而成：
水泥                     20-25份；
硅灰                   20-45份；
水                       10-20份；
黄沙                     10-20份；
聚合物纤维               1-2份；
高强仿钢丝纤维               4-6份；
防冻剂                   15-20份。
2.如权利要求1所述的一种复合型防冻混凝土，其特征在于，所述聚合物纤维采用2份。
3.如权利要求2所述的一种复合型防冻混凝土，其特征在于，所述聚合物纤维由聚乙烯醇纤维和聚丙烯纤维混合制成。
4.如权利要求3所述的一种复合型防冻混凝土，其特征在于，所述聚乙烯醇纤维和所述聚丙烯纤维的重量份配比为7:3。
5.如权利要求1所述的一种复合型防冻混凝土，其特征在于，所述高强仿钢丝纤维采用6份。
6.如权利要求1所述的一种复合型防冻混凝土，其特征在于，所述防冻剂由聚乙二醇甲基丙烯酸、松香、六偏磷酸钠、聚羟酸葡萄糖酸钠和水混合制成。
7.如权利要求6所述的一种复合型防冻混凝土，其特征在于，所述聚乙二醇甲基丙烯酸、松香、六偏磷酸钠、聚羟酸葡萄糖酸钠和水的重量配比为50:5:30：5：10。
8.一种复合型防冻混凝土的制备方法，其特征在于，包括如下步骤：
步骤（1）：称取以下按重量份配比的原料混合搅拌：
水泥                     20-25份；
硅灰                   20-45份；
水                       10-20份；
黄沙                     10-20份；
高强仿钢丝纤维               4-6份；
步骤（2）：称取7份的聚乙烯醇纤维和3份的聚丙烯纤维混合后搅拌40分钟，制得聚合物纤维；
步骤（3）：在步骤（1）中制得的混合物中加入2份步骤（2）制得的聚合物纤维，搅拌1小时；
步骤（4）：将50份的聚乙二醇甲基丙烯酸和10份的水混合后加热搅拌升温至35℃-40℃，然后加入5份的聚羟酸葡萄糖酸钠，继续搅拌30min，再加入5份松香和30份六偏磷酸钠继续搅拌30min后制得防冻剂；
步骤（5）：将步骤（4）中制得的防冻剂，添加至步骤（3）中所得混合物中，再搅拌2-3个小时，即可使用。
CN201310449496.6A 2013-09-29 2013-09-29 一种复合型防冻混凝土及其制备方法 Expired - Fee Related CN103496906B (zh)