CN103496907A - 一种超低温防冻混凝土及其制备方法 - Google Patents

一种超低温防冻混凝土及其制备方法 Download PDF

Info

Publication number
CN103496907A
CN103496907A CN201310449591.6A CN201310449591A CN103496907A CN 103496907 A CN103496907 A CN 103496907A CN 201310449591 A CN201310449591 A CN 201310449591A CN 103496907 A CN103496907 A CN 103496907A
Authority
CN
China
Prior art keywords
parts
low temperature
resistant concrete
concrete
temperature frost
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310449591.6A
Other languages
English (en)
Other versions
CN103496907B (zh
Inventor
周启龙
王辉
覃光英
李帅涛
顾永新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing Gongyi Commercial Concrete Co.,Ltd.
Duan Zhongda
Original Assignee
Zhangjiagang Shanmu New Material Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhangjiagang Shanmu New Material Technology Development Co Ltd filed Critical Zhangjiagang Shanmu New Material Technology Development Co Ltd
Priority to CN201310449591.6A priority Critical patent/CN103496907B/zh
Publication of CN103496907A publication Critical patent/CN103496907A/zh
Application granted granted Critical
Publication of CN103496907B publication Critical patent/CN103496907B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种超低温防冻混凝土及其制备方法，其特征在于，由以下原料按重量份配比而成：水泥20-25份；橡胶颗粒20-45份；水10-20份；有机化合物10-20份；聚合物纤维1-2份；丙烯酸乳液4-6份；防冻剂15-20份。本方案制备简单，操作容易，投资成本低，且说采用的硝酸盐和亚硝酸盐对混凝土的耐久性影响较小，并且本方案制得的混凝土能够抵御0℃~-40℃的低温环境，在我国严冬地区产生了良好的经济和社会效益。

Description

一种超低温防冻混凝土及其制备方法
技术领域
本发明涉及建筑材料领域，特别涉及一种超低温防冻混凝土及其制备方法。
背景技术
建筑施工中，经常会遇到各种恶劣的天气环境，尤其是在冬季，长期的低温对混凝土的搅拌造成了很大的影响，如何才能防止混凝土在低温下上冻一直是工程人员比较头疼的问题。
常见的防冻混凝土只能保证在-15℃左右的低温下不上冻，而对于我国黑龙江省西南地区，却存在着更为极端的温度，极端最低温达到了-42.6℃，由于普通防冻混凝土无法使用的缘故，在这个低温时间段内，通常会休假6个月左右，这严重影响了工程进度。为了解决这个问题，我国科学家一直在研究一种能够耐超低温的混凝土，用于这种超低温环境的建筑工程，这将对我国铁路建筑工程产生重大的意义。
发明内容
本发明目的是：提出一种能够抵御超低温环境的防冻混凝土，用于在超低温环境下的建筑作业活动，弥补现有技术的不足。
本发明解决其技术问题所采用的技术方案是：
一种超低温防冻混凝土，由以下原料按重量份配比而成：
水泥                     20-25份；
橡胶颗粒                   20-45份；
水                       10-20份；
有机化合物                     10-20份；
聚合物纤维               1-2份；
丙烯酸乳液               4-6份；
防冻剂                   15-20份。
优选地，所述有机化合物采用甲醇或乙醇。
优选地，所述聚合物纤维采用2份。
优选地，所述聚合物纤维由7份的聚乙烯醇纤维和3份的聚丙烯纤维混合制成。
优选地，所述丙烯酸乳液采用6份。
优选地，所述防冻剂由硝酸盐、甲酸钙、和水混合构成。
优选地，所述硝酸盐、甲酸钙、和水的重量份配比为45:30：25。
优选地，所述硝酸盐采用硝酸钙或亚硝酸钙。
一种超低温防冻混凝土的制备方法，包括如下步骤：
步骤（1）：称取以下按重量份配比的原料混合搅拌：
水泥                     20-25份；
橡胶颗粒                   20-45份；
水                       10-20份；
甲醇                     10-20份；
丙烯酸乳液               4-6份；
步骤（2）：称取7份的聚乙烯醇纤维和3份的聚丙烯纤维混合后搅拌40分钟，制得聚合物纤维；
步骤（3）：在步骤（1）中制得的混合物中加入2份步骤（2）制得的聚合物纤维，搅拌1小时；
步骤（4）：先将45份的硝酸盐和35份的甲酸钙预热，再加热至50℃-70℃，再加入25份的水，搅拌至均匀后，放置15min制得防冻剂；
步骤（5）：将步骤（4）中制得的防冻剂，添加至步骤（3）中所得混合物中，再搅拌2-3个小时，即可使用。
本发明的有益效果是：本方案制备简单，操作容易，投资成本低，且说采用的硝酸盐和亚硝酸盐对混凝土的耐久性影响较小，并且本方案制得的混凝土能够抵御0℃~-40℃的低温环境，在我国严冬地区产生了良好的经济和社会效益。
具体实施方式
以下显示的是本发明的较佳实施例之一，供实施人员作为参考。
实施例1：一种超低温防冻混凝土，由以下原料按重量份配比而成：
水泥                     25份；
橡胶颗粒                   20份；
水                       20份
甲醇                     15份；
聚合物纤维               2份；
丙烯酸乳液               6份；
防冻剂                   12份。
优选地，所述聚合物纤维由7份聚乙烯醇纤维和3份聚丙烯纤维混合制成。
优选地，所述防冻剂由硝酸钙、甲酸钙、和水混合构成。
优选地，所述硝酸钙、甲酸钙、和水的重量份配比为45:30：25。
本产品的制备方法如下：
步骤（1）：称取以下按重量份配比的原料混合搅拌：
水泥                     25份；
橡胶颗粒                   20份；
水                       20份
甲醇                     15份；
丙烯酸乳液               6份；
步骤（2）：称取7份的聚乙烯醇纤维和3份的聚丙烯纤维混合后搅拌40分钟，制得聚合物纤维；
步骤（3）：在步骤（1）中制得的混合物中加入2份步骤（2）制得的聚合物纤维，搅拌1小时；
步骤（4）：先将45份的硝酸钙和35份的甲酸钙预热，再加热至50℃-70℃，再加入25份的水，搅拌至均匀后，放置15min制得防冻剂；
步骤（5）：将步骤（4）中制得的防冻剂，添加至步骤（3）中所得混合物中，再搅拌2个小时，即可使用。
经发明人实验证明，搅拌时需将混凝土的含气量控制在3%-5%的范围内，通过本方法制得的混凝土能够有效抵御0℃~-40℃的低温环境。

Claims (9)

1.一种超低温防冻混凝土，其特征在于，由以下原料按重量份配比而成：
水泥                     20-25份；
橡胶颗粒                   20-45份；
水                       10-20份；
有机化合物                     10-20份；
聚合物纤维               1-2份；
丙烯酸乳液               4-6份；
防冻剂                   15-20份。
2.如权利要求1所述的一种超低温防冻混凝土，其特征在于，所述有机化合物采用甲醇或乙醇。
3.如权利要求1所述的一种超低温防冻混凝土，其特征在于，所述聚合物纤维采用2份。
4.如权利要求3所述的一种超低温防冻混凝土，其特征在于，所述聚合物纤维由7份的聚乙烯醇纤维和3份的聚丙烯纤维混合制成。
5.如权利要求1所述的一种超低温防冻混凝土，其特征在于，所述丙烯酸乳液采用6份。
6.如权利要求1所述的一种超低温防冻混凝土，其特征在于，所述防冻剂由硝酸盐、甲酸钙、和水混合构成。
7.如权利要求6所述的一种超低温防冻混凝土，其特征在于，所述硝酸盐、甲酸钙、和水的重量份配比为45:30：25。
8.如权利要求7所述的一种超低温防冻混凝土，其特征在于，所述硝酸盐采用硝酸钙或亚硝酸钙。
9.一种超低温防冻混凝土的制备方法，其特征在于，包括如下步骤：
步骤（1）：称取以下按重量份配比的原料混合搅拌：
水泥                     20-25份；
橡胶颗粒                   20-45份；
水                       10-20份；
甲醇                     10-20份；
丙烯酸乳液               4-6份；
步骤（2）：称取7份的聚乙烯醇纤维和3份的聚丙烯纤维混合后搅拌40分钟，制得聚合物纤维；
步骤（3）：在步骤（1）中制得的混合物中加入2份步骤（2）制得的聚合物纤维，搅拌1小时；
步骤（4）：先将45份的硝酸盐和35份的甲酸钙预热，再加热至50℃-70℃，再加入25份的水，搅拌至均匀后，放置15min制得防冻剂；
步骤（5）：将步骤（4）中制得的防冻剂，添加至步骤（3）中所得混合物中，再搅拌2-3个小时，即可使用。
CN201310449591.6A 2013-09-29 2013-09-29 一种超低温防冻混凝土及其制备方法 Active CN103496907B (zh)