CN103496283A - Slurry painting creating method - Google Patents
Slurry painting creating method Download PDFInfo
- Publication number
- CN103496283A CN103496283A CN201310492964.8A CN201310492964A CN103496283A CN 103496283 A CN103496283 A CN 103496283A CN 201310492964 A CN201310492964 A CN 201310492964A CN 103496283 A CN103496283 A CN 103496283A
- Authority
- CN
- China
- Prior art keywords
- sludge
- mold base
- painting
- slurry
- releasing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A slurry painting creating method solves the problems that a traditional clay figurine painting is dull in decoration style, not firm and not resistant to corrosion, paint materials are disengaged easily, regular yellow clay, black clay and red clay which are selected as the raw material of the traditional clay figurine painting react with pigment easily, and the traditional clay figurine painting is fragile, not resistant to wearing, unavailable in detailed dermatoglyphic patterns and sterile in hue. According to the slurry painting creating method, slurry generated during ore grinding and ore crushing when 200-500m underground mining is carried out is selected as the raw and basic material of a slurry painting, a slurry painting blank is made through mold reversing, baking and other machining methods, colored drawing is carried out on the surface of the slurry painting blank with pigment, and then a product which is simple in hue, rich in color and vivid is obtained. The product can be placed in a picture frame to form a slurry painting artwork which is novel and unique in layout, well arranged, simple and elegant in color and has unique romantic charm.
Description
Technical field
The present invention relates to a kind of sludge method for making picture, belong to sludge picture handicraf field.
Background technology
It is to utilize the mine tailing refuse produced in a kind of water law ore dressing of Resourcization of Mining Solid Waste or washup operation that sludge is drawn, and discharge with the pulpous state form, after precipitation, wastewater reuse, its sediment is called sludge, and make sludge by processing modes such as model reverse mould, bakings and draw the embryo, then at its color drawing for curved surface of body pigment.The products made thereby tone is simple, rich color, and lifelike image, be contained in picture frame, just become composition new and original, and picture is well arranged, and the simple and tasteful original in style sludge of color is drawn the art work.
Because various mud are in the market drawn merely as appreciating and collection is developed for the purpose consumer group, it is at appearance forrns, performing content, creation subject matter and intersperse the aspects such as decoration and large innovation and improvement are not arranged, the trend that is out of step with the times and people's esthetic sentiment always.The tradition clay figurine is drawn and is had shell type, the decorated style dullness, easily de-oiling material, the shortcoming such as insecure, not anticorrosive, it is the principal element that the restriction clay figurine is drawn development, and clay figurine is drawn in raw material and selects, with common Huang, black, red soil is made, plays the disadvantages such as chemistry reflection with pigment, simultaneously frangible, not wear-resisting and without the bald aobvious defect such as stiff of fine and closely woven natural grain pattern, tone again, be badly in need of a kind of new sludge picture of exploitation and solve this fraud.
Summary of the invention
The technical problem to be solved in the present invention is, take sludge as base material, by die sinking, and the color technique of painting among the people and draw the sludge picture that skill organically blends into a kind of novelty.
Sludge method for making picture of the present invention, its manufacturing procedure is:
(1), select mud
Choosing is less than sludge that the ore of 5～10mm produces in ore grinding, Crushing process for making raw base substrate,
(2), die sinking
Camphor tree is delivered to wood-working factory and be cut into thick about 10cm, be about the sheet material of 60～65cm, wide approximately 30～32cm, as die sinking use, then sheet material is put into to engraving machine be engraved as a matrix template, matrix template engraving matrix pattern can be the calligraphy pattern, also personage's pattern.
(3), brush releasing agent
After with wool brush, releasing agent being brushed to one time in the matrix template, place to ventilate in dry, the time is 1 hour, and purpose plays isolation and lubrication, also can make sludge mold base surface smoothing after the demoulding, and releasing agent is the epoxy resin releasing agent.
(4), reverse mould
The sludge mixed up being poured in board mould, with bricklayer’s's scraper plate, sludge is flattened along the board mould outer, place and dry in the sun 6 days, dries in the shade and needs 15 days in the dry place of room ventilation.
(5), the demoulding
Dried sludge mould horizontal is put on the table, with the wooden mallet back side of tapping board timber die gently, make the sludge mold base become flexible break away from moulds, obtain convex pattern sludge mold base.
(6), baking: the sludge mold base after break away from moulds is placed in electric oven and dries moisture content, increase sludge mold base firmness, during baking, temperature is 800 degree, and baking time is 50 minutes, cuts off the power supply and within parked 2 hours, after temperature is fallen, opens door of electric oven taking-up sludge mold base.
(7), polishing
To taking out the sludge mold base in electric oven, modify unnecessary assorted mud with paper knife, then with 1500 purpose carpenter sand paper are manual, sludge mold base appearance is carried out to sanding and polishing, make its surface Paint Gloss, produce gloss.
(8), whitewash
With wool brush by the extra white water paint after grinded sludge mold base surface is brushed one time, place the ventilation drying, the time is 3 hours, purpose plays a part to beat white background, the extra white water paint is environment-friendly type aqueous baking whitewash.
(9), paint coloured silk
Each the color powder in dispersion end Thailand produced with the watercolor goat hair brush is equipped with the required of all kinds colored paste of crude vegetal furnishing, then picks colored paste pigment, join coloured silk according to picture proof and require hand drawing on the sludge mold base, sludge draw.
(10), be stained with frame
Sludge is drawn to the back side to be encapsulated in picture frame by resin glue sticking.
(11), packing
The sludge that with overlay, will install picture frame is drawn as product externally to be sold after packing.
Beneficial effect of the present invention is: a kind of sludge method for making picture, having solved traditional clay figurine is drawn on decorated style dull, easily de-oiling material, the shortcoming such as insecure, not anticorrosive, and traditional clay figurine is drawn in raw material to select take common Huang, black, red soil is raw material, easily with pigment rise the chemistry reflection and frangible, not wear-resisting, show the disadvantage such as stiff without fine and closely woven natural grain pattern, tone are bald; Choose the sludge produced in underground 200-500m mining and draw raw base substrate for making sludge in ore grinding, Crushing process, make sludge by processing modes such as model reverse mould, bakings and draw the embryo, again at its color drawing for curved surface of body pigment, the products made thereby tone is simple, rich color, lifelike image, be contained in picture frame, just become composition new and original, picture is well arranged, and the sludge of the simple and tasteful unique romantic charm of color is drawn the art work.
The specific embodiment:
Embodiment
Sludge method for making picture of the present invention, its manufacturing procedure is:
(1), select mud
Choosing is less than sludge that the ore of 5～10mm produces in ore grinding, Crushing process for making raw base substrate, and described sludge is the sludge produced in ore grinding, Crushing process in underground 200-500m mining.
(2), die sinking
Camphor tree is delivered to wood-working factory and be cut into thick about 10cm, be about the sheet material of 60～65cm, wide approximately 30～32cm, as die sinking use, then sheet material is put into to engraving machine be engraved as a matrix template, matrix template engraving matrix pattern can be the calligraphy pattern, also personage's pattern.
(3), brush releasing agent
After with wool brush, releasing agent being brushed to one time in the matrix template, place the ventilation drying, the time is 1 hour, and purpose plays isolation and lubrication, also can make sludge mold base surface smoothing after the demoulding, and described releasing agent is the epoxy resin releasing agent.
(4), reverse mould
The sludge mixed up being poured in board mould, with bricklayer’s's scraper plate, sludge is flattened along the board mould outer, place and dry in the sun 6 days, dries in the shade and needs 15 days in the dry place of room ventilation.
(5), the demoulding
Dried sludge mould horizontal is put on the table, with the wooden mallet back side of tapping board timber die gently, make the sludge mold base become flexible break away from moulds, obtain convex pattern sludge mold base.
(6), baking: the sludge mold base after break away from moulds is placed in electric oven and dries moisture content, increase sludge mold base firmness, during baking, temperature is 800 degree, and baking time is 50 minutes, cuts off the power supply and within parked 2 hours, after temperature is fallen, opens door of electric oven taking-up sludge mold base.
(7), polishing
To taking out the sludge mold base in electric oven, modify unnecessary assorted mud with paper knife, then with 1500 purpose carpenter sand paper are manual, sludge mold base appearance is carried out to sanding and polishing, make its surface Paint Gloss, produce gloss.
(8), whitewash
With wool brush by the extra white water paint after grinded sludge mold base surface is brushed one time, place and ventilate in dry, the time is 3 hours, purpose plays a part to beat white background, described extra white water paint is environment-friendly type aqueous baking whitewash.
(9), paint coloured silk
Each the color powder in dispersion end Thailand produced with the watercolor goat hair brush is equipped with the required of all kinds colored paste of crude vegetal furnishing, then picks colored paste pigment, join coloured silk according to picture proof and require hand drawing on the sludge mold base, sludge draw.
(10), be stained with frame
Sludge is drawn to the back side to be encapsulated in picture frame by resin glue sticking.
(11), packing
The sludge that with overlay, will install picture frame is drawn as product externally to be sold after packing.
Finally explanation: above embodiment is only in order to the technology of the present invention master case to be described but not be limited, although describe the present invention with reference to preferred embodiment, those of ordinary skill in the art is to be understood that, it still can be modified or be equal to replacement technical scheme of the present invention, and these modifications or be equal to replacement and can not make amended technical scheme break away from the spirit and scope of technical solution of the present invention.
Claims (3)
1. a sludge method for making picture, is characterized in that take that the sludge that ore produces in ore grinding, Crushing process is to make sludge to draw raw base substrate, by following operation, makes:
(1), select mud
Choosing is less than sludge that the ore of 5～10mm produces in ore grinding, Crushing process for making raw base substrate, and described sludge is the sludge produced in ore grinding, Crushing process in underground 200-500m mining.
(2), die sinking
Camphor tree is delivered to wood-working factory and be cut into thick about 10cm, be about the sheet material of 60～65cm, wide approximately 30～32cm, as die sinking use, then sheet material is put into to engraving machine be engraved as a matrix template, matrix template engraving matrix pattern can be the calligraphy pattern, also personage's pattern.
(3), brush releasing agent
After with wool brush, releasing agent being brushed to one time in the matrix template, place the ventilation drying, the time is 1 hour, and purpose plays isolation and lubrication, also can make sludge mold base surface smoothing after the demoulding.
(4), reverse mould
The sludge mixed up being poured in board mould, with bricklayer’s's scraper plate, sludge is flattened along the board mould outer, place and dry in the sun 6 days, dries in the shade and needs 15 days in the dry place of room ventilation.
(5), the demoulding
Dried sludge mould horizontal is put on the table, with the wooden mallet back side of tapping board timber die gently, make the sludge mold base become flexible break away from moulds, obtain convex pattern sludge mold base.
(6), baking: the sludge mold base after break away from moulds is placed in electric oven and dries moisture content, increase sludge mold base firmness, during baking, temperature is 800 degree, and baking time is 50 minutes, cuts off the power supply and within parked 2 hours, after temperature is fallen, opens door of electric oven taking-up sludge mold base.
(7), polishing
To taking out the sludge mold base in electric oven, modify unnecessary assorted mud with paper knife, then with 1500 purpose carpenter sand paper are manual, sludge mold base appearance is carried out to sanding and polishing, make its surface Paint Gloss, produce gloss.
(8), whitewash
With wool brush by the extra white water paint after grinded sludge mold base surface is brushed one time, place the ventilation drying, the time is 3 hours, purpose works to beat white background.
(9), paint coloured silk
Each the color powder in dispersion end Thailand produced with the watercolor goat hair brush is equipped with the required of all kinds colored paste of crude vegetal furnishing, then picks colored paste pigment, join coloured silk according to picture proof and require hand drawing on the sludge mold base, sludge draw.
(10), be stained with frame
Sludge is drawn to the back side to be encapsulated in picture frame by resin glue sticking.
(11), packing
The sludge that with overlay, will install picture frame is drawn as product externally to be sold after packing.
The 3rd of a kind of sludge method for making picture according to claim 1 the described brush releasing agent, it is characterized in that: described releasing agent is the epoxy resin releasing agent.
The 8th of a kind of sludge method for making picture according to claim 1 the extra white water paint, it is characterized in that: described extra white water paint is environment-friendly type aqueous baking whitewash.