CN103489540A - 一种电气化铁路接触网用绝缘子 - Google Patents

一种电气化铁路接触网用绝缘子 Download PDF

Info

Publication number
CN103489540A
CN103489540A CN201310480564.5A CN201310480564A CN103489540A CN 103489540 A CN103489540 A CN 103489540A CN 201310480564 A CN201310480564 A CN 201310480564A CN 103489540 A CN103489540 A CN 103489540A
Authority
CN
China
Prior art keywords
parts
insulator
glaze
white
solid solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310480564.5A
Other languages
English (en)
Other versions
CN103489540B (zh
Inventor
朱静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangxi Pingchi Industrial Co., Ltd.
Original Assignee
JURONG RUIYUAN TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JURONG RUIYUAN TECHNOLOGY Co Ltd filed Critical JURONG RUIYUAN TECHNOLOGY Co Ltd
Priority to CN201310480564.5A priority Critical patent/CN103489540B/zh
Publication of CN103489540A publication Critical patent/CN103489540A/zh
Application granted granted Critical
Publication of CN103489540B publication Critical patent/CN103489540B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种电气化铁路接触网用绝缘子，包括绝缘子本体、设置在绝缘子办呢提外部的绝缘伞群护套和设置在绝缘子本体两端的金具附件，所述的绝缘子本体上涂敷有半导体釉，所述的半导体釉包括以下组分：锡锑固溶体、白釉基料和氧化锌，其中，所述的锡锑固溶体和氧化锌的加入质量分别为白釉基料质量的20-25%和3-5%，且所述的白釉基料包括以下组分且各组分的重量份数为：纳长石30-35份；煅烧后的滑石粉8-15份；石英20-25份；新会粉8-10份；高岭土10-15份；石灰石4-5份；上店土3-8份；钛白0.5-1份；左云土5-10份；硅酸锆1-3份；煅烧粘土5-10份。利用本发明所述的绝缘伞群护套和半导体釉的配方制备得到的绝缘子，机械性能显著增强，且大幅提高了绝缘子的耐污性能。

Description

一种电气化铁路接触网用绝缘子
 
技术领域
本发明涉及一种一种电气化铁路接触网用绝缘子，尤其是涉及一种电气化铁路接触网用绝缘子的半导体釉的配方，属于电瓷产品配方技术领域。
背景技术
目前电气化铁路接触网大量使用的绝缘子抗弯抗扭好、机械性能优异，污闪电压高、电气性能卓越，其已大量使用在电气化铁路接触网供电系统，为铁路系统安全运行和经济社会快速发展做出了巨大贡献。
但是，运行中的绝缘子表面易粘附污秽，天气状况适合可能出现外部闪络，比较笨重，搬运安装相对困难。随着市场对于电力需求的不断提升，电力系统的不断发展，超高压输电正得到越来越多的应用，与此同时，对于绝缘子的性能要求也日益提高，目前的绝缘子在性能上仍然存在着缺陷。
发明内容
为解决现有技术的不足，本发明的目的在于提供一种电气化铁路接触网用绝缘子。
为达到上述目的，本发明是通过以下的技术方案来实现的：
一种电气化铁路接触网用绝缘子，包括绝缘子本体、设置在绝缘子办呢提外部的绝缘伞群护套和设置在绝缘子本体两端的金具附件，所述的绝缘子本体上涂敷有半导体釉，其特征在于，所述的半导体釉包括以下组分：锡锑固溶体、白釉基料和氧化锌，其中，所述的锡锑固溶体和氧化锌的加入质量分别为白釉基料质量的20-25%和3-5%，且所述的白釉基料包括以下组分且各组分的重量份数为：
纳长石                 30-35份；（均匀瓷质，改善机械性能）
煅烧后的滑石粉         8-15份；
石英                   20-25份；
新会粉                 8-10份；
高岭土                 10-15份；（提高釉浆悬浮性和结合强度）
石灰石                 4-5份；（增强机械强度）
上店土                 3-8份；
钛白                   0.5-1份；
左云土                 5-10份；
硅酸锆                 1-3份；
煅烧粘土               5-10份。（减少干燥或烧成收缩）
进一步，所述的锡锑固溶体中氧化锡和氧化锑的质量比为93:7。
而所述的绝缘伞群护套包括以下组分且各组分的重量份数为： 110-2甲基乙烯基硅橡胶100份、气相法二氧化硅40份、氢氧化铝微粉120份、色母胶1.5份、氧化锌5份、硅烷1.5份、硅油15份、三乙醇胺0.9份、γ-三氟丙基甲基聚硅氧烷6.0份、双二五硫化剂1.5份。
本发明的有益效果是：利用本发明所述的绝缘伞群护套和半导体釉的配方制备得到的绝缘子，机械性能显著增强，且大幅提高了绝缘子的耐污性能，有效地发挥泄漏距离的作用，即使在污秽地区也不需要加强绝缘，简化了绝缘子的结构，防止局部电弧的产生与发展，减少污闪事故的发生及其造成的损失。
具体实施方式
以下结合具体实施例对本发明进行具体的介绍。
实施例1：
一种电气化铁路接触网用绝缘子，包括绝缘子本体、设置在绝缘子办呢提外部的绝缘伞群护套和设置在绝缘子本体两端的金具附件，所述的绝缘子本体上涂敷有半导体釉，所述的半导体釉包括以下组分：锡锑固溶体、白釉基料和氧化锌，其中，所述的锡锑固溶体和氧化锌的加入质量分别为白釉基料质量的20%和5%，且所述的锡锑固溶体中氧化锡和氧化锑的质量比为93:7。
而所述的白釉基料包括以下组分且各组分的重量份数为：纳长石30份；煅烧后的滑石粉8份；石英25份；新会粉10份；高岭土10份；石灰石5份；上店土3份；钛白1份；左云土5份；硅酸锆3份；煅烧粘土10份。所述的绝缘伞群护套包括以下组分且各组分的重量份数为： 110-2甲基乙烯基硅橡胶100份、气相法二氧化硅40份、氢氧化铝微粉120份、色母胶1.5份、氧化锌5份、硅烷1.5份、硅油15份、三乙醇胺0.9份、γ-三氟丙基甲基聚硅氧烷6.0份、双二五硫化剂1.5份。
 
实施例2：
一种电气化铁路接触网用绝缘子，包括绝缘子本体、设置在绝缘子办呢提外部的绝缘伞群护套和设置在绝缘子本体两端的金具附件，所述的绝缘子本体上涂敷有半导体釉，其特征在于，所述的半导体釉包括以下组分：锡锑固溶体、白釉基料和氧化锌，其中，所述的锡锑固溶体和氧化锌的加入质量分别为白釉基料质量的25%和3%，且所述的锡锑固溶体中氧化锡和氧化锑的质量比为93:7。
而所述的白釉基料包括以下组分且各组分的重量份数为：纳长石35份；煅烧后的滑石粉15份；石英20份；新会粉8份；高岭土15份；石灰石4份；上店土8份；钛白0.5份；左云土10份；硅酸锆1份；煅烧粘土5份。所述的绝缘伞群护套包括以下组分且各组分的重量份数为： 110-2甲基乙烯基硅橡胶100份、气相法二氧化硅40份、氢氧化铝微粉120份、色母胶1.5份、氧化锌5份、硅烷1.5份、硅油15份、三乙醇胺0.9份、γ-三氟丙基甲基聚硅氧烷6.0份、双二五硫化剂1.5份。
 
实施例3：
一种电气化铁路接触网用绝缘子，包括绝缘子本体、设置在绝缘子办呢提外部的绝缘伞群护套和设置在绝缘子本体两端的金具附件，所述的绝缘子本体上涂敷有半导体釉，其特征在于，所述的半导体釉包括以下组分：锡锑固溶体、白釉基料和氧化锌，其中，所述的锡锑固溶体和氧化锌的加入质量分别为白釉基料质量的23%和4%，且所述的锡锑固溶体中氧化锡和氧化锑的质量比为93:7。
而所述的白釉基料包括以下组分且各组分的重量份数为：纳长石32份；煅烧后的滑石粉12份；石英22份；新会粉9份；高岭土12份；石灰石5份；上店土5份；钛白0.8份；左云土8份；硅酸锆2份；煅烧粘土7份。所述的绝缘伞群护套包括以下组分且各组分的重量份数为： 110-2甲基乙烯基硅橡胶100份、气相法二氧化硅40份、氢氧化铝微粉120份、色母胶1.5份、氧化锌5份、硅烷1.5份、硅油15份、三乙醇胺0.9份、γ-三氟丙基甲基聚硅氧烷6.0份、双二五硫化剂1.5份。
上述实施例1-3制备的锑锡型绝缘子，其中，配方中的纳长石的加入及其含量的提高，有效均匀了瓷质，同时结合石灰石，可有效改善整个绝缘子的机械性能，而高岭土的添加，则有效提高了釉浆的悬浮性和结合强度，而烧结粘土则可有效减少干燥或烧成收缩。本发明大幅提高了绝缘子的耐污性能，有效地发挥泄漏距离的作用，即使在污秽地区也不需要加强绝缘，简化了绝缘子的结构，防止局部电弧的产生与发展，减少污闪事故的发生及其造成的损失。
本发明按照上述实施例进行了说明，应当理解，上述实施例不以任何形式限定本发明，凡采用等同替换或等效变换方式所获得的技术方案，均落在本发明的保护范围之内。

Claims (3)

1.一种电气化铁路接触网用绝缘子，包括绝缘子本体、设置在绝缘子办呢提外部的绝缘伞群护套和设置在绝缘子本体两端的金具附件，所述的绝缘子本体上涂敷有半导体釉，其特征在于，所述的半导体釉包括以下组分：锡锑固溶体、白釉基料和氧化锌，其中，所述的锡锑固溶体和氧化锌的加入质量分别为白釉基料质量的20-25%和3-5%，且所述的白釉基料包括以下组分且各组分的重量份数为：
纳长石                 30-35份；
煅烧后的滑石粉         8-15份；
石英                   20-25份；
新会粉                 8-10份；
高岭土                 10-15份；
石灰石                 4-5份；
上店土                 3-8份；
钛白                   0.5-1份；
左云土                 5-10份；
硅酸锆                 1-3份；
煅烧粘土               5-10份。
2.根据权利要求1所述的电气化铁路接触网用绝缘子，其特征在于，所述的锡锑固溶体中氧化锡和氧化锑的质量比为93:7。
3.根据权利要求1所述的电气化铁路接触网用绝缘子，其特征在于，所述的绝缘伞群护套包括以下组分且各组分的重量份数为： 110-2甲基乙烯基硅橡胶100份、气相法二氧化硅40份、氢氧化铝微粉120份、色母胶1.5份、氧化锌5份、硅烷1.5份、硅油15份、三乙醇胺0.9份、γ-三氟丙基甲基聚硅氧烷6.0份、双二五硫化剂1.5份。
CN201310480564.5A 2013-10-15 2013-10-15 一种电气化铁路接触网用绝缘子 Expired - Fee Related CN103489540B (zh)