CN101439988A - 电瓷用无机接粘釉 - Google Patents

电瓷用无机接粘釉 Download PDF

Info

Publication number
CN101439988A
CN101439988A CNA2008102301440A CN200810230144A CN101439988A CN 101439988 A CN101439988 A CN 101439988A CN A2008102301440 A CNA2008102301440 A CN A2008102301440A CN 200810230144 A CN200810230144 A CN 200810230144A CN 101439988 A CN101439988 A CN 101439988A
Authority
CN
China
Prior art keywords
glaze
percent
sticking
porcelain
clay
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008102301440A
Other languages
English (en)
Inventor
叶立茂
张海滨
王丽芳
赵占才
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUSHUN ELECTRIC PORCELAIN MANUFACTURE Co Ltd
Original Assignee
FUSHUN ELECTRIC PORCELAIN MANUFACTURE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUSHUN ELECTRIC PORCELAIN MANUFACTURE Co Ltd filed Critical FUSHUN ELECTRIC PORCELAIN MANUFACTURE Co Ltd
Priority to CNA2008102301440A priority Critical patent/CN101439988A/zh
Publication of CN101439988A publication Critical patent/CN101439988A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种电瓷用无机接粘釉，由下述成分及其重量百分比组成：长石27－33％；硅石32－37％；坯土6－10％；滑石1－3％；田师傅粘土1－3％；石灰石2－6％；碳酸钡5－9％；法库粘土10－15％；色剂6－10％。本发明乳白釉具有如下特点及优点：1.本发明由无机组分构成，需粘接的两段在本接粘釉的存在下，经高温焙烧后能够较好的成为一体，不易老化，使得粘接的瓷套的电气性能得了到长久保证。2.本发明具有较强的浸蚀能力，与瓷体的结合性能较好。3.本发明属于石灰质釉，具有石灰质釉弹性好，有刚玉硬感等特点，其与高铝质坯结合良好，能生成良好的中间层，并有利于色剂呈色。4.本发明粘接强度高，经抗弯试验检测，抗弯强度可达到一体成型瓷套的水平。

Description

电瓷用无机接粘釉
一、技术领域
本发明属于电瓷技术领域，具体涉及一种电瓷用无机接粘釉。
二、背景技术
随着超高压输变电事业的发展，各种超高压电器，如330—500KV电流互感器、电压互感器、SF6断路器的外绝缘必须有两米至五米以上的大型瓷套与其配套。以现有的技术能力，无法通过一次成型生产如此高大的电瓷产品。目前多采用分段焙烧的方法，即先将大型瓷套分成若干小段焙烧成型，再用接粘釉将段与段对接处粘接起来，最后通过二次回烧使段与段之间粘接在一起，从而连接制成大型瓷套。目前，采用的接粘釉多为有机接粘釉，而有机接粘釉具有天生的缺陷就是性脆、弹性较差，易老化，粘接的瓷套的电气性能得不到长久保证。
三、发明内容
本发明的目的是提供一种弹性较好，不易老化，粘接的瓷套的电气性能得到长久保证的电瓷用无机接粘釉。
为实现上述目的，本发明采用的技术方案为：该接粘釉由下述成分及其重量百分比组成：长石27-33％；硅石32-37％；坯土6-10％；滑石1-3％；田师傅粘土1-3％；石灰石2-6％；碳酸钡5-9％；法库粘土10-15％；色剂6-10％。
上述色剂可为棕色色剂，其是由下述成分及其重量百分比组成：三氧化二铁(Fe2O3)9-13％；三氧化二铬(Cr2O3)19-24％；二氧化锰(MnO2)65-71％。
上述棕色色剂的制备方法为：将按照上述重量百分比称取的物料均匀混合，装入遂道窑内焙烧后，过去26目筛即得。
本发明接粘釉的制备方法为：按重量百分比称取上述原料，放入球磨机球磨，细度控制在300目筛，筛余为0.03-0.05，再经过除铁过筛(200目)、榨泥、烘干、粉碎(过26目筛)、验收即得。
本发明接粘釉为颗粒状物料，其使用方法为：将焙烧后的瓷件的上下接口磨成120°角的“V”形接口，上节为“∧”形，下节为“∨”型槽，用丙酮将接口清洗干净，上下接口处涂刷釉浆，在下节“∨”型槽内填满本发明接粘釉，将上下接口吻合对接后，装入遂道窑内，经1200-1600℃温度焙烧即可。
化学分析成分(％)：
 
IL SiO2 Al2O3 Fe2O3 CaO MgO K2O Na2O BaO MnO2 Cr2O3
4-5 63-67 10-12 1-2 2-3 1-2 3-4 0.5-1 4-5 4-5 1.5-2
物理性能：
 
性能 本发明接粘釉
熔融温度(℃) 1155-1175
高温流动度(mm) 45-55
本发明接粘釉具有如下特点及优点：
1、本发明接粘釉由无机组分构成，需粘接的两段在本接粘釉的存在下，经高温焙烧后能够较好的成为一体，不易老化，使得粘接的瓷套的电气性能得了到长久保证。
2、本发明接粘釉具有较强的浸蚀能力，与瓷体的结合性能较好。
3、本发明接粘釉属于石灰质釉，具有石灰质釉弹性好，有刚玉硬感等特点，其与高铝质坯结合良好，能生成良好的中间层，并有利于色剂呈色。
4、本发明接粘釉粘接强度高，经抗弯试验检测，接粘后的整体瓷套的抗弯破坏部位不是粘接接口处，而是底部胶装处，说明本发明的抗弯强度可达到一体成型瓷套的水平。
四、具体实施方式
1、制备棕色色剂：由下述成分及其重量百分比组成：三氧化二铁10.99％；三氧化二铬20.51％；二氧化锰68.5％。
2、制备接粘釉：
实施例1：由下述成分及其重量百分比组成：长石28.08％；硅石31.71％；坯土7.7％；滑石1.72％；田师傅粘土1.77％；石灰石3.77％；碳酸钡6.52％；法库粘土11.31％；棕色色剂7.42％。
实施例1由下述成分及其重量百分比组成：长石29.63％；硅石32.41％；坯土7.7％；滑石1.72％；田师傅粘土1.77％；石灰石3.77％；碳酸钡6.52％；法库9.07％；棕色色剂7.41％。
化学分析成分(％)：
 
实施例 IL SiO2 Al2O3 Fe2O3 CaO MgO K2O Na2O BaO MnO2 Cr2O3
1 4.49 64.43 9.95 1.75 2.31 1.66 3.92 0.82 4.4 4.38 1.85
2 4.19 64.72 9.58 1.12 2.28 0.66 3.95 0.79 5.05 4.38 1.85
物理性能：
 
性能 实施例1 实施例2
熔融温度(℃) 1150-1180 1150-1180
高温流动度(mm) 35 32

Claims (2)

1、一种电瓷用无机接粘釉，其特征是：由下述成分及其重量百分比组成：长石27-33％；硅石32-37％；坯土6-10％；滑石1-3％；田师傅粘土1-3％；石灰石2-6％；碳酸钡5-9％；法库粘土10-15％；色剂6-10％。
2、根据权利要求1所述的电瓷用无机接粘釉，其特征是：上述色剂为棕色色剂，其由下述成分及其重量百分比组成：三氧化二铁9-13％；三氧化二铬19-24％；二氧化锰65-71％。
CNA2008102301440A 2008-12-25 2008-12-25 电瓷用无机接粘釉 Pending CN101439988A (zh)