CN102757258A - 等静压电瓷用无机接粘釉 - Google Patents

等静压电瓷用无机接粘釉 Download PDF

Info

Publication number
CN102757258A
CN102757258A CN2012102678091A CN201210267809A CN102757258A CN 102757258 A CN102757258 A CN 102757258A CN 2012102678091 A CN2012102678091 A CN 2012102678091A CN 201210267809 A CN201210267809 A CN 201210267809A CN 102757258 A CN102757258 A CN 102757258A
Authority
CN
China
Prior art keywords
percent
glaze
inorganic bonding
porcelain
bonding glaze
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012102678091A
Other languages
English (en)
Inventor
张海滨
张文胜
陈雷
汤晓中
许成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUSHUN ELECTRIC PORCELAIN MANUFACTURE Co Ltd
Original Assignee
FUSHUN ELECTRIC PORCELAIN MANUFACTURE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUSHUN ELECTRIC PORCELAIN MANUFACTURE Co Ltd filed Critical FUSHUN ELECTRIC PORCELAIN MANUFACTURE Co Ltd
Priority to CN2012102678091A priority Critical patent/CN102757258A/zh
Publication of CN102757258A publication Critical patent/CN102757258A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种等静压电瓷用无机接粘釉,由下述成分及其重量百分比组成:长石30-33%;硅石15-20%;坯土7-10%;碳酸钡8-15%;田师傅粘土1-10%;石灰石1-6%;滑石1-9%;水化法库粘土5-10%;硅酸锆4-8%;色剂5-10%。本发明无机接粘釉具有如下特点及优点:1、本发明由多种无机组分构成,经本产品粘接的两段等静压电瓷产品,经高温焙烧后能够较好的成为一体,不易老化,产品性能得了到长久保证。2、本发明具有较强的抗浸蚀能力,与瓷体的结合性能较好。3、本发明具有弹性好,有刚玉硬感等特点,其与高铝质等静压瓷坯结合良好,能生成良好的中间层。4、本发明粘接强度高,经抗弯试验检测,抗弯强度可达到一体成型等静压瓷的水平。

Description

等静压电瓷用无机接粘釉
一、     技术领域
本发明属于等静压电瓷技术领域,具体涉及一种等静压电瓷用无机接粘釉。
二、背景技术
随着百万伏超高压输变电事业的发展,各种超高压电器,如1000kV电流互感器、电压互感器、1000kV断路器的外绝缘必须有多节粘接的大型高强度电瓷产品与其配套。目前,为了达到强度等要求需采用等静压电瓷制作技术,大型等静压电瓷产品采用分段焙烧的方法,即将大型瓷体分成若干小段成型、焙烧,再用无机接粘釉将段与段对接处粘接起来,最后通过二次回烧使段与段之间粘接在一起,从而连接制成大型等静压瓷产品。目前湿法成型电瓷用无机接粘釉不能匹配等静压电瓷产品,而有机接粘釉具有天生的缺陷:性脆、弹性较差、易老化,粘接的瓷套的电气性能得不到长久保证。
三、发明内容
本发明的目的是提供一种接粘强度高、弹性较好、不易老化,粘接瓷体的电气性能得到长久保证的等静压电瓷用无机接粘釉。
为实现上述目的,本发明采用的技术方案为:该接粘釉由下述成分及其重量百分比组成:长石30-33%;硅石15-20%;坯土7-10%;碳酸钡8-15%;田师傅粘土1-10%;石灰石1-6%; 滑石1-9%;水化法库粘土5-10%;硅酸锆4-8%;色剂5-10%。
上述色剂为棕色色剂,其是由下述成分及其重量百分比组成:三氧化二铁(Fe2O3)9-13%;三氧化二铬(Cr2O3)19-24%;二氧化锰(MnO2)65-71%。
上述棕色色剂的制备方法为:将按照上述重量百分比称取的物料均匀混合,装入遂道窑内焙烧后,过去26目筛即得。
本发明接粘釉的制备方法为:按重量百分比称取上述原料,放入
球磨机球磨,细度控制在300目筛,筛余为0.03-0.05,再经过除铁过筛(200目)、榨泥、烘干、粉碎(过26目筛)、验收即得。
本发明接粘釉为颗粒状物料,其使用方法为:将焙烧后的瓷件的上下接口磨成120°角的“V”形接口,上节为“∧”形,下节为“∨”型槽,用丙酮将接口清洗干净,上下接口处涂刷釉浆,在下节“∨”型槽内填满本发明接粘釉,将上下接口吻合对接后,装入遂道窑内,经1220-1280℃温度焙烧即可。
化学分析成分(%):
IL SiO2 Al2O3 Fe2O3 CaO MgO K2O Na2O BaO MnO2 ZrO2 Cr2O3
5-6 55-63 16-24 2-3 3-4 0.5-1 2-3 0.5-1 1-2 4-5 2.5-6.0 0.5-1
物理性能:
性能 本发明接粘釉
熔融温度(℃) 1190-1210
高温流动度(mm) 20-35                        
本发明接粘釉具有如下特点及优点:
1、本发明由多种无机组分构成,经本产品粘接的两段等静压电瓷产品,经高温焙烧后能够较好的成为一体,不易老化,产品性能得了到长久保证。
2、本发明具有较强的抗浸蚀能力,与瓷体的结合性能较好。
3、本发明具有弹性好,有刚玉硬感等特点,其与高铝质等静压瓷坯结合良好,能生成良好的中间层。
4、本发明粘接强度高,经抗弯试验检测,抗弯强度可达到一体成型等静压瓷的水平。
四、具体实施方式
实施例1:
①制作棕色色剂:
色剂由下述成分及其重量百分比组成:三氧化二铁10.99%;三氧化二铬20.51%;二氧化锰68.50%。
②制作接粘釉:
由下述成分及其重量百分比组成:长石31.05%;硅石20.00%;坯土9.70%;碳酸钡8.72%;田师傅粘土2.00%;石灰石3.50%; 滑石6.53%;水化法库粘土5.50%;硅酸锆6.00;棕色色剂7.00%。
实施例2:
①制作棕色色剂:
色剂由下述成分及其重量百分比组成:三氧化二铁10.99%;三氧化二铬20.51%;二氧化锰68.50%。
②制作接粘釉:
由下述成分及其重量百分比组成:长石29.05%;硅石20.00%;坯土8.70%;碳酸钡8.72%;田师傅粘土3.00%;石灰石2.50%; 滑石3.53%;水化法库粘土9.50%;硅酸锆8.00;棕色色剂7.00%。
实施例3:
①制作棕色色剂:
色剂由下述成分及其重量百分比组成:三氧化二铁12.00%;三氧化二铬22.50%;二氧化锰65.50%。
②制作接粘釉:
由下述成分及其重量百分比组成:长石31.05%;硅石20.00%;坯土9.70%;碳酸钡8.72%;田师傅粘土2.00%;石灰石3.50%; 滑石6.53%;水化法库粘土5.50%;硅酸锆6.00;棕色(B)色剂7.00%。
实施例4:
①制作棕色色剂:
色剂由下述成分及其重量百分比组成:三氧化二铁12.00%;三氧化二铬22.50%;二氧化锰65.50%。
②制作接粘釉:
由下述成分及其重量百分比组成:长石29.05%;硅石20.00%;坯土8.70%;碳酸钡8.72%;田师傅粘土3.00%;石灰石2.50%; 滑石3.53%;水化法库粘土9.50%;硅酸锆8.00;棕色色剂7.00%。
化学分析成分(%):
实施例 IL SiO2 Al2O3 Fe2O3 CaO MgO K2O Na2O BaO MnO2 ZrO2 Cr2O3
1 5.20 59.11 16.69 2.11 3.08 0.66 2.13 0.86 1.32 4.65 3.52 0.67
2 5.51 56.87 19.12 2.15 3.02 0.55 2.11 0.85 1.35 4.09 3.72 0.66
3 5.23 59.09 16.65 2.20 3.06 0.65 2.11 0.82 1.29 4.54 3.54 0.82
4 5.67 56.76 19.11 2.22 3.01 0.53 2.12 0.84 1.35 3.90 3.70 0.79
物理性能:
性能 实施例1 实施例2 实施例3 实施例4
熔融温度(℃) 1150-1180 1150-1180 1150-1180 1150-1180
高温流动度(mm) 35 32 33 30

Claims (2)

1.一种等静压电瓷用无机接粘釉,其特征是:由下述成分及其重量百分比组成:长石30-33%;硅石15-20%;坯土7-10%;碳酸钡8-15%;田师傅粘土1-10%;石灰石1-6%; 滑石1-9%;水化法库粘土5-10%;硅酸锆4-8%;色剂5-10%。
2.根据权利要求2所述的等静压电瓷用无机接粘釉,其特征是:上述色剂为棕色色剂,其由下述成分及其重量百分比组成:三氧化二铁9-13%;三氧化二铬19-24%;二氧化锰65-71%。
CN2012102678091A 2012-07-31 2012-07-31 等静压电瓷用无机接粘釉 Pending CN102757258A (zh)