CN103224413B - 紫金釉的制作方法 - Google Patents

紫金釉的制作方法 Download PDF

Info

Publication number
CN103224413B
CN103224413B CN201310116213.6A CN201310116213A CN103224413B CN 103224413 B CN103224413 B CN 103224413B CN 201310116213 A CN201310116213 A CN 201310116213A CN 103224413 B CN103224413 B CN 103224413B
Authority
CN
China
Prior art keywords
parts
glaze
zijin
component
plagioclase
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310116213.6A
Other languages
English (en)
Other versions
CN103224413A (zh
Inventor
谢泉英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN EKA CERAMICS CO Ltd
Original Assignee
HUNAN EKA CERAMICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN EKA CERAMICS CO Ltd filed Critical HUNAN EKA CERAMICS CO Ltd
Priority to CN201310116213.6A priority Critical patent/CN103224413B/zh
Publication of CN103224413A publication Critical patent/CN103224413A/zh
Application granted granted Critical
Publication of CN103224413B publication Critical patent/CN103224413B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种紫金釉的制作方法,该方法的步骤如下:(1)按照以下组份和各组份重量份备料:紫金熔块30份~40份;碳酸锰5份~8份;氧化铁红5份~8份;骨炭6份~10份;高岭土10份~15份;斜长石40份~50份;滑石粉3份~6份;其中,紫金熔块按以下组份和各组份重量份备料后高温烧制而成:斜长石25份~35份;碳酸锂5份~10份;硼砂10份~15份;铁红5份~10份;碳酸锰5份~10份;(2)按料︰球︰水=1︰1.5︰0.5,湿法球磨6~8小时;(3)球磨后的釉料过160目筛后,再调成50~70波美度的釉浆;(4)取外表光洁的坯体喷上该釉浆干燥后,经?1160℃~1200℃的氧化气氛下烧制成品。通过本发明制作的紫金釉釉面形成紫金效果,拿在手里金光闪闪,有让人爱不释手的感觉。<!--1--><!--2-->

Description

紫金釉的制作方法
技术领域
[0001 ] 本发明涉及一种紫金釉的制作方法。
背景技术
[0002] 目前,在陶瓷行业中,瓷坯的造型是优质产品的基础釉料的调配使瓷器更加的耀眼夺目,同一造型的瓷坯,往往因釉面不同,而使消费者的视觉产生不同的影响,那种釉表面形成紫金效果,拿在手里金光闪闪,有让人爱不释手的感觉的釉器,这也是当今瓷器行业的一种时品。
发明内容
[0003] 本发明所要解决的技术问题是提供一种紫金釉的制作方法,通过它制作的紫金釉釉面形成紫金效果,拿在手里金光闪闪,有让人爱不释手的感觉。
[0004] 为了解决上述技术问题,本发明的技术方案是:一种紫金釉的制作方法,该方法的步骤如下:(1)按照以下组份和各组份重量份备料:紫金熔块30份~40份;碳酸锰5份~8份;氧化铁红5份~8份;骨炭6份~10份;尚岭土 10份~15份;斜长石40份~50份;滑石粉3份~6份;其中,紫金熔块按以下组份和各组份重量份备料后高温烧制而成:斜长石25份~35份;碳酸锂5份~10份;硼砂10份~15份;铁红5份~10份;碳酸猛5份~10份;(2)按料:球:水=1: 1.5: 0.5,湿法球磨6~8小时;(3)球磨后的釉料过160目筛后,再调成50~70波美度的釉浆;(4)取外表光洁的坯体喷上该釉浆干燥后,经1160°C -1200°C的氧化气氛下烧制成品。
[0005] 采用了上述技术方案后,本发明具有以下的有益效果:经过实验人员的多次实验制备发现,制备的釉器釉表面形成紫金效果,拿在手里金光闪闪,让人爱不释手。
具体实施方式
[0006] 为了使本发明的内容更容易被清楚地理解,下面根据具体实施例,对本发明作进一步详细的说明,
[0007] 实施例一
[0008] 一种紫金釉的制作方法,该方法的步骤如下:(1)按照以下组份和各组份重量份备料:紫金熔块30份;碳酸锰5份;氧化铁红6份滑炭6份;高岭土 10份;斜长石40份;滑石粉3份;其中,紫金熔块按以下组份和各组份重量份备料后高温烧制而成:斜长石25份;碳酸锂5份;硼砂10份;铁红5份;碳酸锰5份;(2)按料:球:水=1: 1.5: 0.5,湿法球磨6~8小时;(3)球磨后的釉料过160目筛后,再调成50~70波美度的釉浆;(4)取外表光洁的坯体喷上该釉浆干燥后,经1160°C ~1200°C的氧化气氛下烧制成品。
[0009] 该方法烧成的紫金釉釉面釉面形成紫金效果,拿在手里金光闪闪,有让人爱不释手的感觉。
[0010] 实施例二
[0011] —种紫金釉的制作方法,该方法的步骤如下:(1)按照以下组份和各组份重量份备料:紫金熔块40份;碳酸锰8份;氧化铁红8份;骨炭10份;高岭土 15份;斜长石50份;滑石粉6份;其中,紫金熔块按以下组份和各组份重量份备料后高温烧制而成:斜长石35份;碳酸锂10份;硼砂15份;铁红10份;碳酸锰10份;(2)按料:球:水=1: 1.5:
0.5,湿法球磨6~8小时;(3)球磨后的釉料过160目筛后,再调成50~70波美度的釉浆;(4)取外表光洁的坯体喷上该釉浆干燥后,经1160°C ~1200°C的氧化气氛下烧制成品。
[0012] 该方法烧成的紫金釉釉面釉面形成紫金效果,拿在手里金光闪闪,有让人爱不释手的感觉。
[0013] 实施例三
[0014] 一种紫金釉的制作方法,该方法的步骤如下:(1)按照以下组份和各组份重量份备料:紫金熔块35份;碳酸锰7份;氧化铁红6份滑炭8份;高岭土 13份;斜长石45份;滑石粉5份;其中,紫金熔块按以下组份和各组份重量份备料后高温烧制而成:斜长石30份;碳酸锂8份;硼砂13份;铁红7份;碳酸锰7份;(2)按料:球:水=1: 1.5: 0.5,湿法球磨6~8小时;(3)球磨后的釉料过160目筛后,再调成50~70波美度的釉浆;(4)取外表光洁的坯体喷上该釉浆干燥后,经1160°C ~1200°C的氧化气氛下烧制成品。
[0015] 该方法烧成的紫金釉釉面釉面形成紫金效果,拿在手里金光闪闪,有让人爱不释手的感觉。
[0016] 上述三个实施例,分别取了各组份重量份的上、中、下三个范围的值进行了检测,可以得出经过实验人员的多次的制备,所得成品釉面仍然会形成紫金效果,拿在手里金光闪闪,有让人爱不释手的感觉。
[0017] 以上所述的具体实施例,对本发明的目的、技术方案和有益效果进行了进一步详细说明,所应理解的是,以上所述仅为本发明的具体实施例而已,并不用于限制本发明,凡在本发明的精神和原则之内,所做的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。

Claims (1)

1.一种紫金釉的制作方法,其特征在于该方法的步骤如下: (1)按照以下组份和各组份重量份备料: 紫金熔块30份~40份;碳酸锰5份~8份; 氧化铁红5份~8份;骨炭6份~10份; 尚岭土 10份~15份;斜长石40份~50份;滑石粉3份~6份; 其中,紫金熔块按以下组份和各组份重量份备料后高温烧制而成:斜长石25份~35份;碳酸锂5份~10份;硼砂10份~15份;铁红5份~10份;碳酸猛5份~10份; (2)按料:球:水=1: 1.5: 0.5,湿法球磨6~8小时; (3)球磨后的釉料过160目筛后,再调成50~70波美度的釉浆; (4 )取外表光洁的坯体喷上该釉浆干燥后,经1160 °C -1200 °C的氧化气氛下烧制成品。
CN201310116213.6A 2013-04-06 2013-04-06 紫金釉的制作方法 Active CN103224413B (zh)