CN103483920A - 一种颜料紫19分散体的制备方法 - Google Patents
一种颜料紫19分散体的制备方法 Download PDFInfo
- Publication number
- CN103483920A CN103483920A CN201310412669.7A CN201310412669A CN103483920A CN 103483920 A CN103483920 A CN 103483920A CN 201310412669 A CN201310412669 A CN 201310412669A CN 103483920 A CN103483920 A CN 103483920A
- Authority
- CN
- China
- Prior art keywords
- pigment violet
- parts
- preparation
- dispersions
- dropping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种颜料紫19分散体的制备方法,制备过程步骤如下:首先取颜料紫19粉末为20~25份,放入搅拌罐中;向搅拌罐中加入丙烯酸酯为15~19份,温度设定为60℃,同时进行搅拌,搅拌转速为120rpm;再投入氯化聚氯乙烯树脂为21~23份,继续搅拌,转速为120rpm;再投入二甘醇为5~7份;最后投入己酸为8~11份;最后再搅拌2h,制备得到颜料紫19分散体。制备得到的分散体具有良好的稳定性。
Description
技术领域
本发明涉及一种颜料分散体的制备方法,特别是涉及一种颜料紫19分散体的制备方法。
背景技术
各种颜料在应用的过程中,由于颜料本身物理性质和化学性质的限制,制约了颜料的应用领域。如果能通过改性或者添加其他一些组合物对颜料的性质进行改变或者辅助,会大大的扩大颜料的使用范围。同时,还会增加颜料一些其他的性能,如稳定性、色彩附着力、色差小等特点。鉴于以上特点,开发一种颜料紫19的分散体来增强颜料紫19的稳定性非常有必要。
发明内容
要解决的技术问题:颜料紫19稳定性较差的问题。
技术方案:本发明公开了一种颜料紫19分散体的制备方法,制备过程步骤如下:首先取颜料紫19粉末为20~25份,放入搅拌罐中;向搅拌罐中加入丙烯酸酯为15~19份,温度设定为60℃,同时进行搅拌,搅拌转速为120rpm;再投入氯化聚氯乙烯树脂为21~23份,继续搅拌,转速为120rpm;再投入二甘醇为5~7份;最后投入己酸为8~11份;最后再搅拌2h,制备得到颜料紫19分散体。其中,颜料紫19粉末优选为20份;丙烯酸酯优选为19份;氯化聚氯乙烯树脂优选为21份;二甘醇优选为5份。
有益效果:通过本发明方法制备得到的颜料紫19的分散体,在常温常压下放置300天后,色差非常小,同时颜料紫19分散体也没有其他异常情况发生,具备了非常良好的稳定性,可以拓展它的使用范围。
具体实施方式
实施例1
首先取颜料紫19粉末为20kg,放入搅拌罐中;向搅拌罐中加入丙烯酸酯为15kg,温度设定为60℃,同时进行搅拌,搅拌转速为120rpm;再投入氯化聚氯乙烯树脂为21kg,继续搅拌,转速为120rpm;再投入二甘醇为5kg;最后投入己酸为8kg;最后再搅拌2h,制备得到颜料紫19分散体。
实施例2
首先取颜料紫19粉末为25kg,放入搅拌罐中;向搅拌罐中加入丙烯酸酯为19kg,温度设定为60℃,同时进行搅拌,搅拌转速为120rpm;再投入氯化聚氯乙烯树脂为23kg,继续搅拌,转速为120rpm;再投入二甘醇为7kg;最后投入己酸为11kg;最后再搅拌2h,制备得到颜料紫19分散体。
实施例3
首先取颜料紫19粉末为23kg,放入搅拌罐中;向搅拌罐中加入丙烯酸酯为17kg,温度设定为60℃,同时进行搅拌,搅拌转速为120rpm;再投入氯化聚氯乙烯树脂为22kg,继续搅拌,转速为120rpm;再投入二甘醇为6kg;最后投入己酸为9kg;最后再搅拌2h,制备得到颜料紫19分散体。
稳定性试验
取实施例1、实施例2、实施例3制备得到的颜料紫19分散体。进行稳定性测试,将三个样品分别放置在常温常压的环境下,放置300天。300天后测定其色差值,观察分散体色差值的变化。300天后实施例1、实施例2、实施例3的色差值分别为0.11、0.09、0.07。颜料紫19分散体具备了良好的稳定性。
Claims (5)
1.一种颜料紫19分散体的制备方法,其特征在于制备过程步骤如下:首先取颜料紫19粉末为20~25份,放入搅拌罐中;向搅拌罐中加入丙烯酸酯为15~19份,温度设定为60℃,同时进行搅拌,搅拌转速为120rpm;再投入氯化聚氯乙烯树脂为21~23份,继续搅拌,转速为120rpm;再投入二甘醇为5~7份;最后投入己酸为8~11份;最后再搅拌2h,制备得到颜料紫19分散体。
2.根据权利要求1所述的一种颜料紫19分散体的制备方法,其特征在于颜料紫19粉末为20份。
3.根据权利要求1所述的一种颜料紫19分散体的制备方法,其特征在于丙烯酸酯为19份。
4.根据权利要求1所述的一种颜料紫19分散体的制备方法,其特征在于氯化聚氯乙烯树脂为21份。
5.根据权利要求1所述的一种颜料紫19分散体的制备方法,其特征在于二甘醇为5份。