CN105670155A - 一种液体热稳定剂 - Google Patents
一种液体热稳定剂 Download PDFInfo
- Publication number
- CN105670155A CN105670155A CN201410656892.0A CN201410656892A CN105670155A CN 105670155 A CN105670155 A CN 105670155A CN 201410656892 A CN201410656892 A CN 201410656892A CN 105670155 A CN105670155 A CN 105670155A
- Authority
- CN
- China
- Prior art keywords
- parts
- liquid heat
- octoate
- iso
- stabilizing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种液体热稳定剂,它的原料及原料的重量份数为:异辛酸镧10~20份、异辛酸锌5~15份、异辛酸钙15~25份、亚磷酸酯20~30份、环氧脂肪酸甲酯10~20份、白油5~20份。首先将异辛酸镧、异辛酸锌和异辛酸钙投入反应釜中,搅拌均匀;然后升温至90℃,加入白油,搅拌0.5h,降温至70℃,加入亚磷酸酯和环氧脂肪酸甲酯,继续搅拌使各物料混合均匀;最后降至室温,出料,过滤,制得液体热稳定剂。该液体热稳定剂与PVC的相容性好,热稳定性能优良,无粉尘污染,用量较少,价格低廉,可应用于软质PVC加工业。
Description
技术领域
本发明属于PVC热稳定剂领域,涉及一种液体热稳定剂。
背景技术
热稳定剂是PVC加工必备助剂,主要有铅盐类、金属皂类、有机锡类、稀土盐类等品种,目前,热稳定剂的研究开始向复合、无毒、液体热稳定剂发展,尤其是液体热稳定剂,由于具有与树脂的相容性好、PVC制品透明性好、不易析出、用量少、无粉尘污染、价格低廉这些优点,用量越来愈大。
液体稳定剂是金属皂类等主稳定剂和亚磷酸酯、多元醇、溶剂等辅助稳定剂的复合物,热稳定性能优良,属于新型PVC热稳定剂品种,具有重要的开发潜力和广阔的应用前景。
发明内容
本发明的目的在于提供一种液体热稳定剂,该液体热稳定剂与PVC的相容性好,热稳定性能优良,无粉尘污染,价格低廉,可应用于软质PVC加工业。
为实现以上目的,本发明采用的技术方案为:
一种液体热稳定剂,其特征在于,它的原料及原料的重量份数为:
异辛酸镧10~20份,
异辛酸锌5~15份,
异辛酸钙15~25份,
亚磷酸酯20~30份,
环氧脂肪酸甲酯10~20份,
白油5~20份。
优选的,所述的液体热稳定剂的原料及原料的重量份数为:
异辛酸镧15份,
异辛酸锌10份,
异辛酸钙20份,
亚磷酸酯25份,
环氧脂肪酸甲酯16份,
白油14份。
本发明还提供了一种液体热稳定剂的制备方法,包括以下步骤:
(1)准确称取各物料,将异辛酸镧、异辛酸锌和异辛酸钙投入反应釜中,搅拌均匀;
(2)升温至90℃,加入白油,搅拌0.5h,降温至70℃,加入亚磷酸酯和环氧脂肪酸甲酯,继续搅拌使各物料混合均匀;
(3)降至室温后出料,过滤,制得液体热稳定剂。
本发明的有益效果:本发明将液体稀土热稳定剂、液体钙锌热稳定剂与其他辅助热稳定剂进行复配,发挥协同效应,制备的液体热稳定剂的热稳定性能优良,与PVC的相容性好,无粉尘污染,用量较少。
具体实施方式
下面结合具体实施例对本发明作进一步说明,但不限定本发明的保护范围。
实施例
一种液体热稳定剂,它的原料及原料的重量为:
异辛酸镧15Kg,
异辛酸锌10Kg,
异辛酸钙20Kg,
亚磷酸酯25Kg,
环氧脂肪酸甲酯16Kg,
白油14Kg。
制备步骤如下:
(1)准确称取各物料,将异辛酸镧、异辛酸锌和异辛酸钙投入反应釜中,搅拌均匀;
(2)升温90℃,加入白油,搅拌0.5h,降温至70℃,加入亚磷酸酯和环氧脂肪酸甲酯,继续搅拌使各物料混合均匀;
(3)降至室温后出料,过滤,制得液体热稳定剂。
上述实施例仅为本发明的较佳实施例之一,并非以此限制本发明的保护范围,故:凡依本发明的结构、形状、原理所做的等效变化,均应涵盖于本发明的保护范围之内。
Claims (3)
1.一种液体热稳定剂,其特征在于,它的原料及原料的重量份数为:
异辛酸镧10~20份,
异辛酸锌5~15份,
异辛酸钙15~25份,
亚磷酸酯20~30份,
环氧脂肪酸甲酯10~20份,
白油5~20份。
2.根据权利要求1所述的液体热稳定剂,其特征在于,它的原料及原料的重量份数为:
异辛酸镧15份,
异辛酸锌10份,
异辛酸钙20份,
亚磷酸酯25份,
环氧脂肪酸甲酯16份,
白油14份。
3.一种权利要求1所述的液体热稳定剂的制备方法,其特征在于,包括以下步骤:
(1)准确称取各物料,将异辛酸镧、异辛酸锌和异辛酸钙投入反应釜中,搅拌均匀;
(2)升温至90℃,加入白油,搅拌0.5h,降温至70℃,加入亚磷酸酯和环氧脂肪酸甲酯,继续搅拌使各物料混合均匀;
(3)降至室温后出料,过滤,制得液体热稳定剂。