CN103483006B - 一种陶瓷颜料的制备方法 - Google Patents
一种陶瓷颜料的制备方法 Download PDFInfo
- Publication number
- CN103483006B CN103483006B CN201310411007.8A CN201310411007A CN103483006B CN 103483006 B CN103483006 B CN 103483006B CN 201310411007 A CN201310411007 A CN 201310411007A CN 103483006 B CN103483006 B CN 103483006B
- Authority
- CN
- China
- Prior art keywords
- parts
- mixture
- preparation
- gum arabic
- pigment red
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种陶瓷颜料的制备方法，制备方法包括以下步骤：（1）取颜料红254和永固红F5RK粉末，用球磨机研磨至粒径为1～3um；（2）取磷脂酰胆碱8～10份，阿拉伯胶5～7份，将两者搅拌均匀；（3）向磷脂酰胆碱和阿拉伯胶的混合体中加入3～5份的去离子水，再次混合均匀，得到混合体；（4）向混合体中加入碳酸钠粉末为2～4份，混合均匀；（5）取研磨后的颜料红254为4～6份，永固红F5RK为3～4份，添加到混合体中，将上述所有成分混合均匀。制备得到的红色颜料可以用于陶瓷中，具有良好的着色效果和稳定性。
Description
技术领域
本发明涉及一种颜料的制备方法，特别是涉及一种陶瓷颜料的制备方法。
背景技术
陶瓷作为一种瓷器，在其表面涂有颜料后，可以增加陶瓷制品的观赏性。陶瓷颜料在应用在陶瓷表面时，也对陶瓷颜料有很高的要求，若陶瓷颜料的着色力较低，则较难附着在陶瓷表面，此外若陶瓷颜料的稳定性较差，则放置一段时间后会产生色差，影响着陶瓷制品的外观。找到一种对环境污染较小，并且可以提高陶瓷制品表现力的陶瓷颜料已经成为了一个必然的方向。
发明内容
要解决的技术问题：陶瓷颜料着色效果和稳定性较差的问题。
技术方案：本发明公开了一种陶瓷颜料的制备方法，制备方法包括以下步骤：（1）取颜料红254和永固红F5RK粉末，用球磨机研磨至粒径为1～3um；（2）取磷脂酰胆碱8～10份，阿拉伯胶5～7份，将两者搅拌均匀；（3）向磷脂酰胆碱和阿拉伯胶的混合体中加入3～5份的去离子水，再次混合均匀，得到混合体；（4）向混合体中加入碳酸钠粉末为2～4份，混合均匀；（5）取研磨后的颜料红254为4～6份，永固红F5RK为3～4份，添加到混合体中，将上述所有成分混合均匀。其中，颜料红254和永固红F5RK粉末用球磨机研磨至粒径优选为1um。磷脂酰胆碱优选为10份。阿拉伯胶优选为5份。混合体中加入碳酸钠粉末优选为4份。
有益效果：本发明制备方法得到的红色陶瓷颜料具有良好的着色效果和稳定性。制备得到的红色颜料在陶瓷表面后，常温下放置1年后色泽依然十分鲜亮，具有良好的稳定性。
具体实施方式
实施例1
（1）取颜料红254和永固红F5RK粉末，用球磨机研磨至粒径为1um；（2）取磷脂酰胆碱8kg，阿拉伯胶6kg，将两者搅拌均匀；（3）向磷脂酰胆碱和阿拉伯胶的混合体中加入3kg的去离子水，再次混合均匀，得到混合体；（4）向混合体中加入碳酸钠粉末为4kg，混合均匀；（5）取研磨后的颜料红254为4kg，永固红F5RK为4kg，添加到混合体中，将上述所有成分混合均匀。
实施例2
（1）取颜料红254和永固红F5RK粉末，用球磨机研磨至粒径为2um；（2）取磷脂酰胆碱10kg，阿拉伯胶5kg，将两者搅拌均匀；（3）向磷脂酰胆碱和阿拉伯胶的混合体中加入5kg的去离子水，再次混合均匀，得到混合体；（4）向混合体中加入碳酸钠粉末为2kg，混合均匀；（5）取研磨后的颜料红254为6kg，永固红F5RK为4kg，添加到混合体中，将上述所有成分混合均匀。
实施例3
（1）取颜料红254和永固红F5RK粉末，用球磨机研磨至粒径为3um；（2）取磷脂酰胆碱9kg，阿拉伯胶7kg，将两者搅拌均匀；（3）向磷脂酰胆碱和阿拉伯胶的混合体中加入4kg的去离子水，再次混合均匀，得到混合体；（4）向混合体中加入碳酸钠粉末为3kg，混合均匀；（5）取研磨后的颜料红254为4kg，永固红F5RK为3kg，添加到混合体中，将上述所有成分混合均匀。
实施例1、实施例2、实施例3制备得到的陶瓷颜料均匀的涂抹在在陶瓷表面后，附着效果非常好，颜色非常鲜亮。将附着有颜料的陶瓷在常温下静置1年。1年后测定了陶瓷颜料的色差变化。
| 实施例1 | 实施例2 | 实施例3 | |
| 色差变化 | 0.01 | 0.03 | 0.03 |
实施例1、实施例2、实施例3的色差变化非常小，有良好的稳定性。
Claims (5)
1. 一种陶瓷颜料的制备方法，其特征在于制备方法包括以下步骤：（1）取颜料红254和永固红F5RK粉末，用球磨机研磨至粒径为1～3μm；（2）取磷脂酰胆碱8～10份，阿拉伯胶5～7份，将两者搅拌均匀；（3）向磷脂酰胆碱和阿拉伯胶的混合体中加入3～5份的去离子水，再次混合均匀，得到混合体1；（4）向混合体1中加入碳酸钠粉末为2～4份，混合均匀；（5）取研磨后的颜料红254为4～6份，永固红F5RK为3～4份，添加到步骤（4）得到的混合体中，将上述所有成分混合均匀。
2.根据权利要求1所述的一种陶瓷颜料的制备方法，其特征在于颜料红254和永固红F5RK粉末用球磨机研磨至粒径为1μm。
3.根据权利要求1所述的一种陶瓷颜料的制备方法，其特征在于磷脂酰胆碱为10份。
4.根据权利要求1所述的一种陶瓷颜料的制备方法，其特征在于阿拉伯胶为5份。
5.根据权利要求1所述的一种陶瓷颜料的制备方法，其特征在于混合体中加入碳酸钠粉末为4份。