CN103478886A - 一种用膨胀梗制备造纸法再造烟叶的方法 - Google Patents
一种用膨胀梗制备造纸法再造烟叶的方法 Download PDFInfo
- Publication number
- CN103478886A CN103478886A CN201310475915.3A CN201310475915A CN103478886A CN 103478886 A CN103478886 A CN 103478886A CN 201310475915 A CN201310475915 A CN 201310475915A CN 103478886 A CN103478886 A CN 103478886A
- Authority
- CN
- China
- Prior art keywords
- expansion
- stems
- mass percent
- offal
- fragment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种用膨胀梗制备造纸法再造烟叶的方法，属于再造烟叶技术领域。方法步骤为：a.膨胀梗的制备；b.涂布液的制备；c.片基的抄造；d.造纸法再造烟叶的制备。其中：膨胀梗由复烤烟梗用微波膨胀设备进行微波膨胀处理后得到，其中：水分控制在质量百分比12.60%，蒸汽压力2bar，梗预热38℃，在转速为5.5r/min，倾角为7°，功率为57KW；分别取质量百分比50%的膨胀梗浸膏和50%的碎片/烟末混合浸膏，混合均匀制成涂布液；将膨胀梗残渣初磨浆，后与碎片和烟末混合残渣按质量比1∶1的比例进行混合，添加质量百分比10%的市售木浆纤维，混合均匀后进行磨浆，打浆度为32-45°SR，后制成片基；片基进行涂布、烘干。本发明的优点在于：方法简单、可行，再造烟叶的质量稳定。
Description
技术领域：
本发明涉及一种用膨胀梗制备造纸法再造烟叶的方法，属于再造烟叶技术领域。
背景技术：
造纸法再造烟叶是由烟梗、烟叶碎片和烟末加水萃取，固液分离，将固体残渣进行磨浆，并加入一定的外加纤维进行抄片制成片基，液体经浓缩并加料加香后涂布于片基上而制成。
传统的造纸法再造烟叶制备中，所使用的烟梗是复烤烟梗。
本发明将复烤烟梗进行膨胀处理后，再用于造纸法再造烟叶的制备。经文献检索，未见与本发明相同的公开报道。
发明内容：
本发明的目的在于提供一种简单、可行、质量稳定的用膨胀梗制备造纸法再造烟叶的方法。
本发明的用膨胀梗制备造纸法再造烟叶的方法，具体步骤如下：
a.膨胀梗的制备
膨胀梗由复烤烟梗用微波膨胀设备进行微波膨胀处理后得到，其中：水分控制在质量百分比12.60%，蒸汽压力2bar，梗预热38℃，转速5.5r/min，倾角7°，功率57KW。
b.涂布液的制备
以膨胀梗、碎片与烟末为原料。膨胀梗用水萃取70min，碎片与烟末按质量比7∶3混合以水为溶剂进行萃取70min。原料萃取后分别进行固液分离，液体置于旋转蒸发仪中在50℃条件下浓缩成密度为1.25g/cm3膏状；分别取质量百分比50%的膨胀梗浸膏和50%的碎片/烟末混合浸膏，混合均匀制成涂布液。
c.片基的抄造
将步骤b的膨胀梗残渣先进行初磨浆，后与碎片和烟末混合残渣按质量比1∶1的比例进行混合，添加质量百分比10%的市售木浆纤维，混合均匀后进行磨浆，打浆度为32-45°SR，后按常规方法制成片基；
d.造纸法再造烟叶的制备
用步骤b制备的涂布液对步骤c制备的片基进行常规的涂布、烘干，控制成品水分的质量百分比为10-12%，切片备用。
本发明的优点在于：方法简单、可行，再造烟叶的质量稳定。
具体实施方式：
本发明的具体步骤如下：
a.膨胀梗的制备
膨胀梗由复烤烟梗用微波膨胀设备进行微波膨胀处理后得到，其中：水分控制在质量百分比12.60%，蒸汽压力2bar，梗预热38℃，在转速5.5r/min，倾角7°，功率57KW。
b.涂布液的制备
以膨胀梗、碎片与烟末为原料。膨胀梗用水萃取70min，碎片与烟末按质量比7∶3混合以水为溶剂进行萃取70min。原料萃取后分别进行固液分离，液体置于旋转蒸发仪中在50℃条件下浓缩成密度为1.25g/cm3膏状；分别取质量百分比50%的膨胀梗浸膏和50%的碎片/烟末混合浸膏，混合均匀制成涂布液。
c.片基的抄造
将步将步骤b的膨胀梗残渣先进行初磨浆，后与碎片和烟末混合残渣按质量比1∶1的比例进行混合，添加质量百分比10%的市售木浆纤维，混合均匀后进行磨浆，打浆度为32°SR或40°SR或45°SR时，将其按常规方法抄造成片基。
d.造纸法再造烟叶的制备
用步骤b制备的涂布液对步骤c制备的片基进行常规的涂布、烘干，控制成品水分的质量百分比为在10%或11%或12%，并切片。
根据上述方法制备的造纸法再造烟叶产品，其中烟梗全部使用膨胀梗，经专家进行感官质量评价，结果见表1。由表1看出，全膨胀梗制成的再造烟叶产品口腔刺激较小，木质气较轻。
表1复烤烟梗和膨胀梗所制备的再造烟叶的感官评价结果
Claims (1)
1.一种用膨胀梗制备造纸法再造烟叶的方法，其特征在于该方法的具体步骤如下：
a.膨胀梗的制备
膨胀梗由复烤烟梗用微波膨胀设备进行微波膨胀处理后得到，其中：水分控制在质量百分比12.60%，蒸汽压力2bar，梗预热38℃，在转速为5.5r/min，倾角7°，功率57KW；
b.涂布液的制备
以膨胀梗、碎片与烟末为原料；膨胀梗用水萃取70min，碎片与烟末按质量比7∶3混合以水为溶剂进行萃取70min；原料萃取后分别进行固液分离，液体置于旋转蒸发仪中在50℃条件下浓缩成密度为1.25g/cm3膏状；分别取质量百分比50%的膨胀梗浸膏和50%的碎片/烟末混合浸膏，混合均匀制成涂布液；
c.片基的抄造
将步骤b的膨胀梗残渣先进行初磨浆，后与碎片和烟末混合残渣按质量比1∶1的比例进行混合，添加质量百分比10%的市售木浆纤维，混合均匀后进行磨浆，打浆度为32-45°SR，后按常规方法制成片基；
d.造纸法再造烟叶的制备
用步骤b制备的涂布液对步骤c制备的片基进行常规的涂布、烘干，控制成品水分的质量百分比为10-12%，切片备用。